WO2019128168A1 - Manufacturing process for cigarette case inner liner with clay layer attached - Google Patents

Abstract

A manufacturing process for a cigarette case inner liner with a clay layer attached, comprising the following steps: (1) preparing raw materials: removing impurities of Indonesian volcanic rock, purple sand, selenium soil, Jinsha River red sand, Shandong black pottery, Taiwan clay, and Guangdong Zijin sandy soil, and preparing for standby; (2) firing: firing the raw materials using a kiln, separately; (3) cooling and drawing; (4) manufacturing: crushing fired raw materials into 600-mesh powders; (5) mixing: mixing the raw materials in a certain proportion; (6) blending: adding the resin varnish to the blended clay powder for blending; and (7) coating the cigarette case inner liner with the blended slurry by means of backcoating, and drying naturally.

Description

Cigarette box lining paper making process with ceramic layer Technical field

The invention relates to the field of materials, in particular to a process for making a cigarette liner liner paper with a clay layer.

Background technique

At present, environmental pollution is becoming more and more serious, and environmental protection issues are imminent. According to different fields of use, most of the materials will be treated accordingly, such as providing insulation layer, sterilizing layer, etc. in the inner layer of packaging materials, although these measures can play a certain role to some extent, but at the same time Environmental pollution problems, such as the aluminum foil in the inner layer of many packaging materials, are not easily decomposed.

The development of environmentally friendly new materials only addresses the root of such problems. The present invention proposes an environmentally friendly ceramic slurry to reduce environmental pollution.

Summary of the invention

Based on this, it is necessary to provide a method for manufacturing a cigarette liner lining paper with a clay layer for the prior art problem, which is environmentally friendly and energy-saving.

In order to solve the prior art problem, the present invention discloses a manufacturing process of a cigarette liner lining paper with a clay layer, wherein the manufacturing process is as follows:

(1) Alternative raw materials: remove the impurities from Indonesian volcanic stone, purple sand, selenium, Jinshajiang red sand, Shandong black pottery, Taiwan clay, and Guangdong Zijin sand soil;

(2) Firing: firing in a ceramic kiln, different raw materials are separately fired, the firing temperature is maintained at 1000-1200 degrees, and firing is performed for 180 hours;

(3) cooling out of the kiln: after the above-mentioned firing time is completed, natural cooling is performed, and after cooling, the fired raw materials are discharged out of the kiln;

(4) Production: then the fired raw material is beaten into a 600-mesh powder;

(5) Mixing: Mix various raw material powders according to the following ratios to form clay powder:

Indonesia volcanic stone 5% to 10%;

Purple sand 5% ~ 10%;

Selenium 15% to 22%;

Jinshajiang red sand 8% to 12%;

Shandong black pottery 20% ~ 23%;

Taiwan clay is 25% to 30%;

Guangdong Zijin sand soil 5% to 10%;

(6) Harmonization: adding resin varnish to the blended clay powder for reconciliation, the ratio of resin varnish to clay powder is: 1 to 0.25, forming a blend, and the ceramic pulp is finished;

(7) Apply the above-mentioned blended ceramic slurry to the paper in the cigarette case by back coating, and then dry it naturally to form a layer of clay on the paper.

Further, the fifth step is mixed: mixing various raw material powders according to the following ratios to form clay powder:

Indonesia volcanic stone 8%;

Purple sand 7%;

Selenium 18%;

Jinsha River red sand 10%;

Shandong black pottery 22%;

Taiwan clay is 27%;

Guangdong Zijin sand soil 6%.

The invention has the beneficial effects that the manufacturing process of the lining of the cigarette case of the invention replaces the aluminum foil paper used in the traditional cigarette case, and has a very positive significance for environmental protection. At the same time, the cigarette case has a good anti-mildew, moisture-proof and fresh-keeping effect.

Detailed ways

In order to further understand the features, technical means, and specific objects and functions of the present invention, the present invention will be described in further detail.

The invention discloses a manufacturing process of a cigarette liner lining paper with a clay layer, and the manufacturing process is as follows:

(1) Alternative raw materials: remove the impurities from Indonesian volcanic stone, purple sand, selenium, Jinshajiang red sand, Shandong black pottery, Taiwan clay, and Guangdong Zijin sand soil;

(2) Firing: firing in a ceramic kiln, different raw materials are separately fired, and the firing temperature is maintained at 1000-1200 degrees for 180 hours of firing;

(3) cooling out of the kiln: after the above-mentioned firing time is completed, natural cooling is performed, and after cooling, the fired raw materials are discharged out of the kiln;

(4) Production: then the fired raw material is beaten into a 600-mesh powder;

(5) Mixing: Mix various raw material powders according to the following ratios to form clay powder:

Indonesia volcanic stone 5% to 10%;

Purple sand 5% ~ 10%;

Selenium 15% to 22%;

Jinshajiang red sand 8% to 12%;

Shandong black pottery 20% ~ 23%;

Taiwan clay is 25% to 30%;

Guangdong Zijin sand soil 5% to 10%;

(6) Harmonization: adding resin varnish to the blended clay powder for reconciliation, the ratio of resin varnish to clay powder is: 1 to 0.25, forming a blend, and the ceramic pulp is finished;

(7) Apply the above-mentioned blended ceramic slurry to the paper in the cigarette case by back coating, and then dry it naturally to form a layer of clay on the paper.

Of course, according to actual needs, the pigment is added to the prepared ceramic pulp, and the ceramic pulp is made into ceramic pulp of various colors.

Specifically, the above fifth step is mixed: mixing various raw material powders in the following ratios to form clay powder:

Indonesia volcanic stone 8%;

Purple sand 7%;

Selenium 18%;

Jinsha River red sand 10%;

Shandong black pottery 22%;

Taiwan clay is 27%;

Guangdong Zijin sand soil 6%.

The clay container originated in the Neolithic Age, which means that 5,000 years ago, our ancestors had mastered the production of clay containers and applied them to natural winemaking and wine.

The clay is a hydrated alumina or magnesium silicate with a porous structure or a sheet structure. The main component is kaolinite Al2SiO5(OH)4, illite/mica KAl3Si3O10(OH)4, and Montmorillonite Al2Si4O10(OH)2. . When the clay is sintered at a high temperature of 1000-1200 °C for 160-170 hours, the organic matter contained in the clay is burned off, thereby forming capillary voids of various sizes, and the pore network structure and the great surface area enable the clay container to have Oxidation and adsorption; while most of the minerals in clay exist as ionic bonds, which have a strong catalytic effect.

The above-mentioned embodiments are merely illustrative of several embodiments of the present invention, and the description thereof is more specific and detailed, but is not to be construed as limiting the scope of the invention. It should be noted that a number of variations and modifications may be made by those skilled in the art without departing from the spirit and scope of the invention. Therefore, the scope of the invention should be determined by the appended claims.

Claims (2)

1. A manufacturing process of a cigarette liner lining paper with a clay layer, characterized in that the manufacturing process is as follows:

   (1) Alternative raw materials: remove the impurities from Indonesian volcanic stone, purple sand, selenium, Jinshajiang red sand, Shandong black pottery, Taiwan clay, and Guangdong Zijin sand soil;

   (2) Firing: firing in a ceramic kiln, different raw materials are separately fired, the firing temperature is maintained at 1000-1200 degrees, and firing is performed for 180 hours;

   (3) cooling out of the kiln: after the above-mentioned firing time is completed, natural cooling is performed, and after cooling, the fired raw materials are discharged out of the kiln;

   (4) Production: then the fired raw material is beaten into a 600-mesh powder;

   (5) Mixing: Mix various raw material powders according to the following ratios to form clay powder:

   Indonesia volcanic stone 5% to 10%;

   Purple sand 5% to 10%;

   Selenium 15% to 22%;

   Jinshajiang red sand 8% to 12%;

   Shandong black pottery 20% to 23%;

   Taiwan clay 25% to 30%;

   Guangdong Zijin sandy soil 5% to 10%;

   (6) Harmonization: adding resin varnish to the blended clay powder for reconciliation, the ratio of resin varnish to clay powder is: 1 to 0.25, forming a blend, and the ceramic pulp is finished;

   (7) Apply the above-mentioned blended ceramic slurry to the paper in the cigarette case by back coating, and then dry it naturally to form a layer of clay on the paper.
2. The method for manufacturing a lining paper with a ceramic layer according to claim 1, wherein the fifth step is mixed: mixing various raw material powders according to the following ratios to form clay powder:

   Indonesian volcanic rock 8%;

   Purple sand 7%;

   Selenium 18%;

   Jinsha River red sand 10%;

   Shandong Black Pottery 22%;

   Taiwan clay 27%;

   Guangdong Zijin sandy soil 6%.