CN105367046B - A kind of preparation technology for the alumina ceramic prilling powder for being suitable for high temperature co-firing - Google Patents
A kind of preparation technology for the alumina ceramic prilling powder for being suitable for high temperature co-firing Download PDFInfo
- Publication number
- CN105367046B CN105367046B CN201510838983.0A CN201510838983A CN105367046B CN 105367046 B CN105367046 B CN 105367046B CN 201510838983 A CN201510838983 A CN 201510838983A CN 105367046 B CN105367046 B CN 105367046B
- Authority
- CN
- China
- Prior art keywords
- slurry
- powder
- ball milling
- firing
- high temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of preparation technology for the alumina ceramic prilling powder for being suitable for high temperature co-firing, it is granulated using non-aqueous solvent and the binding agent to be mixed with it to modulate slurry, including step in detail below:Dispensing, ball milling slurry, slurry agitation, granulation powder, sieving iron removaling.Through the above way; the preparation technology of the alumina ceramic prilling powder provided by the invention for being suitable for high temperature co-firing; it is granulated using non-aqueous solvent and the binding agent to be mixed with it to modulate slurry; the bad phenomenon such as metal layer peeling, rupture in sintering process is avoided subsequently in hydrogen shield atmosphere furnace, while also assures that the bond strength and air-tightness of metal layer and ceramics.
Description
Technical field
The present invention relates to the field of ceramic component, more particularly to a kind of alumina ceramic prilling powder for being suitable for high temperature co-firing
Preparation technology, burn metallized product altogether suitable for dry-pressing or isostatic pressing ceramic high temperature.
Background technology
Traditional alumina powder prilling is to make solvent using water, and paraffin or polyvinyl alcohol etc. are used as binding agent, is adjusted
Raw embryo after the pelletizing shaping produced after being granulated into slurry is due to containing water, during being sintered after metal layer printing, embryo
Moisture content in body can be evaporated, and destroy the functional attributes of the additives such as binding agent in metallizing paste, cause to burn till
Metal layer leaves ceramic surface, metal layer contraction crack etc. in journey.
The content of the invention
The present invention solves the technical problem of provide a kind of alumina ceramic prilling powder for being suitable for high temperature co-firing
Preparation technology, it is granulated, is avoided subsequently in hydrogen to modulate slurry using non-aqueous solvent and the binding agent to be mixed with it
The bad phenomenon such as metal layer peeling, rupture in sintering process in special atmosphere oven, while also assures that metal layer and ceramics
Bond strength and air-tightness.
In order to solve the above technical problems, one aspect of the present invention is:Provide one kind and be suitable for high temperature and be total to
The preparation technology of the alumina ceramic prilling powder of burning, carried out using non-aqueous solvent and the binding agent to be mixed with it to modulate slurry
It is granulated, including step in detail below:
A, dispensing, alumina powder and sintering aid are added in ball milling bucket, then add non-aqueous solvent and bonding
Agent;
B, ball milling slurry, ball milling 20 hours is carried out by ball milling bucket is closed;
C, slurry agitation, the good slurry of ball milling is added in closed agitator and carries out slurry agitation;
D, granulation powder, the atomizer comminutor progress powder that the above-mentioned slurry being stirred is poured into totally-enclosed are done
It is dry, obtain granulation powder;
E, sieving iron removaling, dried granulation powder sieving iron removaling is standby.
In a preferred embodiment of the present invention, described solvent uses alcohol, and binding agent uses PVB.
In a preferred embodiment of the present invention, the atomizer comminutor of described totally-enclosed is using the special of totally-enclosed
Door is used for the atomizer comminutor that spirit solvent is granulated.
The beneficial effects of the invention are as follows:The preparation work of the alumina ceramic prilling powder for being suitable for high temperature co-firing of the present invention
Skill, it is granulated, is avoided subsequently in hydrogen shield gas to modulate slurry using non-aqueous solvent and the binding agent to be mixed with it
The bad phenomenon such as metal layer peeling, rupture in sintering process in atmosphere stove, while also assures that the combination of metal layer and ceramics
Intensity and air-tightness.
Brief description of the drawings
Technical scheme in order to illustrate the embodiments of the present invention more clearly, make required in being described below to embodiment
Accompanying drawing is briefly described, it should be apparent that, drawings in the following description are only some embodiments of the present invention, for
For those of ordinary skill in the art, on the premise of not paying creative work, it can also be obtained according to these accompanying drawings other
Accompanying drawing, wherein:
Fig. 1 is the preferred embodiment of the preparation technology for the alumina ceramic prilling powder that the present invention is suitable for high temperature co-firing
Flow chart.
Embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation
Example is only the part of the embodiment of the present invention, rather than whole embodiments.It is common based on the embodiment in the present invention, this area
All other embodiment that technical staff is obtained under the premise of creative work is not made, belong to the model that the present invention protects
Enclose.
As shown in figure 1, the embodiment of the present invention includes:
A kind of preparation technology for the alumina ceramic prilling powder for being suitable for high temperature co-firing, using non-aqueous solvent and with its phase
Molten binding agent is granulated to modulate slurry, including step in detail below:
A, dispensing, alumina powder and sintering aid are added in ball milling bucket, then add non-aqueous solvent and bonding
Agent;
B, ball milling slurry, ball milling 20 hours is carried out by ball milling bucket is closed;
C, slurry agitation, the good slurry of ball milling is added in closed agitator and carries out slurry agitation;
D, granulation powder, the atomizer comminutor progress powder that the above-mentioned slurry being stirred is poured into totally-enclosed are done
It is dry, obtain granulation powder;
E, sieving iron removaling, dried granulation powder sieving iron removaling is standby.
In above-mentioned, described solvent uses alcohol, and binding agent uses PVB(Polyvinyl butyral resin), select suitable viscous
Tie agent, that is, select the PVB of appropriate molecular weight, the size of PVB molecular weight can influence the preparation technology of slurry, be granulated after powder it is each
Item performance.
Further, the atomizer comminutor of described totally-enclosed being made dedicated for spirit solvent using totally-enclosed
The atomizer comminutor of grain.
Exploitation one kind is applied to dry-pressing or isostatic pressing alumina ceramic prilling powder, and raw embryo surface passes through after ceramics shaping
Screen printing mode is directly metallized(Coat molybdenum manganese metal layer or ferrotungsten metal layer), ceramic raw embryo and metal layer
Pass through high temperature once-firing in hydrogen shield atmosphere furnace.
In summary, the preparation technology of the alumina ceramic prilling powder for being suitable for high temperature co-firing of the invention, use are non-aqueous
Property solvent and the binding agent to be mixed with it are granulated to modulate slurry, are avoided subsequently sintered in hydrogen shield atmosphere furnace
The bad phenomenon such as metal layer peeling, rupture in journey, while also assures that the bond strength and air-tightness of metal layer and ceramics.
Embodiments of the invention are the foregoing is only, are not intended to limit the scope of the invention, it is every to utilize this hair
The equivalent structure or equivalent flow conversion that bright description is made, or directly or indirectly it is used in other related technology necks
Domain, it is included within the scope of the present invention.
Claims (2)
1. a kind of preparation technology for the alumina ceramic prilling powder for being suitable for high temperature co-firing, it is characterised in that using non-aqueous molten
Agent and the binding agent to be mixed with it are granulated to modulate slurry, including step in detail below:
A, dispensing, alumina powder and sintering aid are added in ball milling bucket, then add non-aqueous solvent and binding agent, its
In, described non-aqueous solvent uses alcohol, and binding agent uses PVB;
B, ball milling slurry, ball milling 20 hours is carried out by ball milling bucket is closed;
C, slurry agitation, the good slurry of ball milling is added in closed agitator and carries out slurry agitation;
D, granulation powder, the atomizer comminutor that the above-mentioned slurry being stirred is poured into totally-enclosed carry out powder drying, obtained
To granulation powder;
E, sieving iron removaling, dried granulation powder sieving iron removaling is standby.
2. the preparation technology of the alumina ceramic prilling powder according to claim 1 for being suitable for high temperature co-firing, its feature exist
In the atomizer comminutor of described totally-enclosed uses the atomizer being granulated dedicated for spirit solvent of totally-enclosed
Comminutor.