WO2019089516A1 - Procédés d'utilisation de dispersions aqueuses de polyuréthane et articles fabriqués à partir de celles-ci - Google Patents

Procédés d'utilisation de dispersions aqueuses de polyuréthane et articles fabriqués à partir de celles-ci Download PDF

Info

Publication number
WO2019089516A1
WO2019089516A1 PCT/US2018/058109 US2018058109W WO2019089516A1 WO 2019089516 A1 WO2019089516 A1 WO 2019089516A1 US 2018058109 W US2018058109 W US 2018058109W WO 2019089516 A1 WO2019089516 A1 WO 2019089516A1
Authority
WO
WIPO (PCT)
Prior art keywords
prepolymer
dispersion
aqueous polyurethane
apparel
polyurethane dispersion
Prior art date
Application number
PCT/US2018/058109
Other languages
English (en)
Inventor
Douglas K. Farmer
Ting He
Original Assignee
A&At Llc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by A&At Llc filed Critical A&At Llc
Priority to KR1020207015657A priority Critical patent/KR20200075872A/ko
Priority to CN201880071504.9A priority patent/CN111492105A/zh
Priority to JP2020544328A priority patent/JP2021502500A/ja
Priority to US16/760,920 priority patent/US20210172114A1/en
Priority to MX2020004505A priority patent/MX2020004505A/es
Priority to EP18801228.0A priority patent/EP3704296A1/fr
Priority to BR112020008659-2A priority patent/BR112020008659B1/pt
Publication of WO2019089516A1 publication Critical patent/WO2019089516A1/fr

Abstract

L'invention concerne des procédés d'amélioration de fonctionnalités de mise en forme et/ou de maintien localisé, de maintien de forme, de confort et/ou de tenue de vêtements et d'autres articles en tissu par application d'une dispersion aqueuse de polyuréthane à une intensité sélectionnée et/ou à un ou plusieurs emplacements sélectionnés du vêtement ou autre article en tissu. L'invention concerne également un vêtement et d'autres articles en tissu ayant des fonctionnalités de mise en forme et/ou de soutien localisé améliorées, un confort de maintien de forme et/ou une préparation de maintien conformément à ces procédés.
PCT/US2018/058109 2017-11-03 2018-10-30 Procédés d'utilisation de dispersions aqueuses de polyuréthane et articles fabriqués à partir de celles-ci WO2019089516A1 (fr)

Priority Applications (7)

Application Number Priority Date Filing Date Title
KR1020207015657A KR20200075872A (ko) 2017-11-03 2018-10-30 수성 폴리우레탄 분산물의 사용 방법 및 그것에 의해 제조된 물품
CN201880071504.9A CN111492105A (zh) 2017-11-03 2018-10-30 水性聚氨酯分散液的使用方法和由其制成的物品
JP2020544328A JP2021502500A (ja) 2017-11-03 2018-10-30 水性ポリウレタン分散体を使用する方法およびそれにより作製された製品
US16/760,920 US20210172114A1 (en) 2017-11-03 2018-10-30 Methods for use of aqueous polyurethane dispersions and articles made thereby
MX2020004505A MX2020004505A (es) 2017-11-03 2018-10-30 Metodos para el uso de dispersiones acuosas de poliuretano y articulos fabricados de esta manera.
EP18801228.0A EP3704296A1 (fr) 2017-11-03 2018-10-30 Procédés d'utilisation de dispersions aqueuses de polyuréthane et articles fabriqués à partir de celles-ci
BR112020008659-2A BR112020008659B1 (pt) 2017-11-03 2018-10-30 Método para melhorar as funcionalidades e artigo de tecido

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201762581240P 2017-11-03 2017-11-03
US62/581,240 2017-11-03

Publications (1)

Publication Number Publication Date
WO2019089516A1 true WO2019089516A1 (fr) 2019-05-09

Family

ID=64277915

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2018/058109 WO2019089516A1 (fr) 2017-11-03 2018-10-30 Procédés d'utilisation de dispersions aqueuses de polyuréthane et articles fabriqués à partir de celles-ci

Country Status (9)

Country Link
US (1) US20210172114A1 (fr)
EP (1) EP3704296A1 (fr)
JP (1) JP2021502500A (fr)
KR (1) KR20200075872A (fr)
CN (1) CN111492105A (fr)
BR (1) BR112020008659B1 (fr)
MX (1) MX2020004505A (fr)
TW (1) TW201925385A (fr)
WO (1) WO2019089516A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114457599A (zh) * 2022-01-20 2022-05-10 珠海赫基服饰有限公司 一种具有独特风格牛仔裤及加工方法

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114561802A (zh) * 2022-01-26 2022-05-31 冠和卫生用品有限公司 一种天然抗菌无纺布及其制备方法
US11771144B1 (en) 2023-01-17 2023-10-03 Mast Industries (Far East) Limited Bra, bra cup, and method of manufacturing same

Citations (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4387181A (en) 1980-04-09 1983-06-07 Textron, Inc. Polymer compositions and manufacture
US5270433A (en) 1990-04-09 1993-12-14 Henkel Kommanditgesellschaft Auf Aktien Polyurethane-based universal household adhesive
US5563208A (en) 1992-06-02 1996-10-08 Bayer Aktiengesellschaft Aqueous binder mixture and use thereof
EP0519135B1 (fr) 1991-05-22 1996-11-20 Wacoal Corp. Article vestimentaire avec fonction de bande de contention
US5703193A (en) 1996-06-03 1997-12-30 Uniroyal Chemical Company, Inc. Removal of unreacted diisocyanate monomer from polyurethane prepolymers
US6555613B1 (en) 1999-03-10 2003-04-29 Basf Coatings Ag Polyurethane and its use for producing solvent-free coating substances
US6586523B1 (en) 1999-04-01 2003-07-01 Bayer Aktiengesellschaft Self-crosslinking polyurethane, polyurethane polyurea or polyurea dispersions for sizing agents
US20030220463A1 (en) 2002-05-24 2003-11-27 Crompton Corporation Polyurethane dispersions
US20040014880A1 (en) 2002-07-19 2004-01-22 Dainippon Ink And Chemicals, Inc. Aqueous polyurethane resin dispersion and aqueous adhesive
US7240371B2 (en) 2005-02-11 2007-07-10 Invista North America S.A.R.L. Solvent free aqueous polyurethane dispersions and adhesive films therefrom for stretch fabrics
US7341500B2 (en) 2005-05-13 2008-03-11 Victoria's Secret Stores Brand Management, Inc. Garment with lifting feature
US20090181599A1 (en) 2008-01-15 2009-07-16 Invista North America S.A R.L. Garment with altered stress profile
US20100064409A1 (en) 2005-06-22 2010-03-18 Bruce Bary Buckley Shape enhancing garment
US7945970B2 (en) 2004-12-24 2011-05-24 Decathlon Tights presenting a localized compression effect for practicing a sport
US7950069B2 (en) 2005-11-16 2011-05-31 Eun Hyo Cho Pants having body-shaping function
GB2477754A (en) 2010-02-11 2011-08-17 Marks Spencer Plc Support garment
US20110214216A1 (en) 2010-03-04 2011-09-08 Frank Zarabi Supportive and slimming apparel
EP2280619B1 (fr) 2008-05-01 2013-07-17 Invista Technologies S.à.r.l. Bandes de vêtement comportant des compositions polymères
WO2013154445A1 (fr) 2012-04-12 2013-10-17 Irmãos Vila Nova, S.A. Pantalon en jean pour femme
US9346932B2 (en) 2005-02-11 2016-05-24 Invista North America S.A.R.L. Solvent free aqueous polyurethane dispersions and shaped articles therefrom
US20170226691A1 (en) * 2008-01-15 2017-08-10 Invista North America S.A R.L. Garment incorporating aqueous polyurethane dispersions having altered stress profile

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20060183850A1 (en) * 2005-02-11 2006-08-17 Invista North America S.A.R.L. Solvent free aqueous polyurethane dispersions and shaped articles therefrom
US20080004395A1 (en) * 2005-02-11 2008-01-03 Invista North America S.A.R.L. Aqueous polyurethaneurea compositions including dispersions and films
KR101409607B1 (ko) * 2006-07-12 2014-06-18 미쓰비시 가가꾸 가부시키가이샤 폴리우레탄의 제조 방법 및 그것으로부터 얻어진 폴리우레탄의 용도
US20080153388A1 (en) * 2006-12-21 2008-06-26 Zhen Qiang Liu Brassieres
JP2009114589A (ja) * 2007-11-07 2009-05-28 M2 Kikaku:Kk ガードル及び２ｗａｙアップガードル
BRPI0914431A2 (pt) * 2008-10-17 2015-10-27 Invista Technologies Srl composição, película vazada e seca produzida a partir de uma composição e método para a redução do amarelamento em uma pelicula
JP2010111954A (ja) * 2008-11-04 2010-05-20 Seiren Co Ltd 樹脂加工布

Patent Citations (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4387181A (en) 1980-04-09 1983-06-07 Textron, Inc. Polymer compositions and manufacture
US5270433A (en) 1990-04-09 1993-12-14 Henkel Kommanditgesellschaft Auf Aktien Polyurethane-based universal household adhesive
EP0519135B1 (fr) 1991-05-22 1996-11-20 Wacoal Corp. Article vestimentaire avec fonction de bande de contention
US5563208A (en) 1992-06-02 1996-10-08 Bayer Aktiengesellschaft Aqueous binder mixture and use thereof
US5703193A (en) 1996-06-03 1997-12-30 Uniroyal Chemical Company, Inc. Removal of unreacted diisocyanate monomer from polyurethane prepolymers
US6555613B1 (en) 1999-03-10 2003-04-29 Basf Coatings Ag Polyurethane and its use for producing solvent-free coating substances
US6586523B1 (en) 1999-04-01 2003-07-01 Bayer Aktiengesellschaft Self-crosslinking polyurethane, polyurethane polyurea or polyurea dispersions for sizing agents
US20030220463A1 (en) 2002-05-24 2003-11-27 Crompton Corporation Polyurethane dispersions
US20040014880A1 (en) 2002-07-19 2004-01-22 Dainippon Ink And Chemicals, Inc. Aqueous polyurethane resin dispersion and aqueous adhesive
US7945970B2 (en) 2004-12-24 2011-05-24 Decathlon Tights presenting a localized compression effect for practicing a sport
US7240371B2 (en) 2005-02-11 2007-07-10 Invista North America S.A.R.L. Solvent free aqueous polyurethane dispersions and adhesive films therefrom for stretch fabrics
US9346932B2 (en) 2005-02-11 2016-05-24 Invista North America S.A.R.L. Solvent free aqueous polyurethane dispersions and shaped articles therefrom
US7341500B2 (en) 2005-05-13 2008-03-11 Victoria's Secret Stores Brand Management, Inc. Garment with lifting feature
US20100064409A1 (en) 2005-06-22 2010-03-18 Bruce Bary Buckley Shape enhancing garment
US7950069B2 (en) 2005-11-16 2011-05-31 Eun Hyo Cho Pants having body-shaping function
US20090181599A1 (en) 2008-01-15 2009-07-16 Invista North America S.A R.L. Garment with altered stress profile
US20170226691A1 (en) * 2008-01-15 2017-08-10 Invista North America S.A R.L. Garment incorporating aqueous polyurethane dispersions having altered stress profile
EP2280619B1 (fr) 2008-05-01 2013-07-17 Invista Technologies S.à.r.l. Bandes de vêtement comportant des compositions polymères
GB2477754A (en) 2010-02-11 2011-08-17 Marks Spencer Plc Support garment
US20110214216A1 (en) 2010-03-04 2011-09-08 Frank Zarabi Supportive and slimming apparel
WO2013154445A1 (fr) 2012-04-12 2013-10-17 Irmãos Vila Nova, S.A. Pantalon en jean pour femme

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114457599A (zh) * 2022-01-20 2022-05-10 珠海赫基服饰有限公司 一种具有独特风格牛仔裤及加工方法

Also Published As

Publication number Publication date
US20210172114A1 (en) 2021-06-10
CN111492105A (zh) 2020-08-04
EP3704296A1 (fr) 2020-09-09
KR20200075872A (ko) 2020-06-26
MX2020004505A (es) 2020-08-13
JP2021502500A (ja) 2021-01-28
BR112020008659B1 (pt) 2024-01-16
BR112020008659A2 (pt) 2021-03-23
TW201925385A (zh) 2019-07-01

Similar Documents

Publication Publication Date Title
US11473237B2 (en) Garment incorporating aqueous polyurethane dispersions having altered stress profile
JP4950072B2 (ja) 無溶媒の水性ポリウレタン分散液およびそれからの造形品
US9346932B2 (en) Solvent free aqueous polyurethane dispersions and shaped articles therefrom
EP2181132B1 (fr) Compositions de polyuréthanneurée aqueuses comprenant des dispersions et des films
US20070264462A1 (en) Laminated fabric construction with heat activated polyurethaneurea compositions
EP2237688A2 (fr) Vêtement ayant un profil de contrainte modifié
US11312808B2 (en) Aqueous polyurethane dispersions, prepolymers, and shaped articles made therefrom
WO2019089516A1 (fr) Procédés d'utilisation de dispersions aqueuses de polyuréthane et articles fabriqués à partir de celles-ci
US11692304B2 (en) Garment incorporating waterproof or water resilient aqueous polyurethane dispersions and/or having altered stress profile
BR122016024838B1 (pt) Article, methods for making the article, clothing and clothing piece

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18801228

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2020544328

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 20207015657

Country of ref document: KR

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 2018801228

Country of ref document: EP

Effective date: 20200603

REG Reference to national code

Ref country code: BR

Ref legal event code: B01A

Ref document number: 112020008659

Country of ref document: BR

ENP Entry into the national phase

Ref document number: 112020008659

Country of ref document: BR

Kind code of ref document: A2

Effective date: 20200430