WO2019082341A1 - Charbon moulé et procédé de fabrication associé - Google Patents

Charbon moulé et procédé de fabrication associé

Info

Publication number
WO2019082341A1
WO2019082341A1 PCT/JP2017/038750 JP2017038750W WO2019082341A1 WO 2019082341 A1 WO2019082341 A1 WO 2019082341A1 JP 2017038750 W JP2017038750 W JP 2017038750W WO 2019082341 A1 WO2019082341 A1 WO 2019082341A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
material portion
shaped article
article according
modeling
Prior art date
Application number
PCT/JP2017/038750
Other languages
English (en)
Japanese (ja)
Inventor
隆司 當間
Original Assignee
武藤工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 武藤工業株式会社 filed Critical 武藤工業株式会社
Priority to PCT/JP2017/038750 priority Critical patent/WO2019082341A1/fr
Priority to JP2019549778A priority patent/JPWO2019082341A1/ja
Publication of WO2019082341A1 publication Critical patent/WO2019082341A1/fr

Abstract

L'article moulé selon la présente invention est caractérisé en ce qu'il comprend un matériau composite obtenu par combinaison d'un premier matériau qui est un matériau fritté en poudre, et d'un second matériau qui est différent du premier matériau, les premier et second matériaux, dans le matériau composite, limitent mutuellement le mouvement relatif dans trois directions dans lesquelles les deux matériaux se croisent mutuellement.
PCT/JP2017/038750 2017-10-26 2017-10-26 Charbon moulé et procédé de fabrication associé WO2019082341A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
PCT/JP2017/038750 WO2019082341A1 (fr) 2017-10-26 2017-10-26 Charbon moulé et procédé de fabrication associé
JP2019549778A JPWO2019082341A1 (ja) 2017-10-26 2017-10-26 造形物及びその製造方法

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/JP2017/038750 WO2019082341A1 (fr) 2017-10-26 2017-10-26 Charbon moulé et procédé de fabrication associé

Publications (1)

Publication Number Publication Date
WO2019082341A1 true WO2019082341A1 (fr) 2019-05-02

Family

ID=66247254

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/038750 WO2019082341A1 (fr) 2017-10-26 2017-10-26 Charbon moulé et procédé de fabrication associé

Country Status (2)

Country Link
JP (1) JPWO2019082341A1 (fr)
WO (1) WO2019082341A1 (fr)

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000272018A (ja) * 1999-03-25 2000-10-03 Matsushita Electric Works Ltd 三次元形状物製造法
JP2016027595A (ja) * 2014-07-02 2016-02-18 住友電工焼結合金株式会社 ヒートシンクおよびその製法
JP2016531770A (ja) * 2013-06-24 2016-10-13 プレジデント アンド フェローズ オブ ハーバード カレッジ 印刷３次元（３ｄ）機能部品および製造方法

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000272018A (ja) * 1999-03-25 2000-10-03 Matsushita Electric Works Ltd 三次元形状物製造法
JP2016531770A (ja) * 2013-06-24 2016-10-13 プレジデント アンド フェローズ オブ ハーバード カレッジ 印刷３次元（３ｄ）機能部品および製造方法
JP2016027595A (ja) * 2014-07-02 2016-02-18 住友電工焼結合金株式会社 ヒートシンクおよびその製法

Also Published As

Publication number Publication date
JPWO2019082341A1 (ja) 2020-10-22

Similar Documents

Publication Publication Date Title
US10259160B2 (en) Wear resistance in 3D printing of composites
US11214003B2 (en) Device and method for producing a three-dimensional object with a fibre feeding device
JP5920859B2 (ja) 三次元プリンター
US20150077215A1 (en) Device and Method to Additively Fabricate Structures Containing Embedded Electronics or Sensors
CN105216322B (zh) 一种3d打印机的xy轴联动装置及联动方法
CN104708812B (zh) 立体打印装置以及打印头组件
KR101575061B1 (ko) 3d 프린터의 노즐 가변수단
KR101736568B1 (ko) 다중재료 성형을 위한 3d 프린터용 헤드
KR20160016985A (ko) 단일의 노즐과 단일의 노즐히터를 사용해서 멀티컬러 제품성형이 가능한 3차원 프린터장치 및 그 구동 방법
CN107914387A (zh) 碳纤维增强复合材料结构件五自由度3d打印成型装置及方法
CN206276911U (zh) 一种熔融沉积成型的金属三维打印机
JPWO2017130515A1 (ja) 三次元造形装置、及びその制御方法、並びにその造形物
CN105666888B (zh) 一种基于fdm技术的数控成型设备
CN103817939A (zh) 粉末打印机及粉末材料成型方法
KR20180100875A (ko) 3d 프린터 및 이를 구비한 생산 시스템
CN112477133B (zh) 一种混合式连续纤维增强材料3d打印挤出系统
WO2019082341A1 (fr) Charbon moulé et procédé de fabrication associé
WO2015028809A1 (fr) Améliorations relatives au prototypage par dépôt de fil
JP2010120320A (ja) 圧縮賦形装置および圧縮賦形方法、ならびにこれらを用いて製造された繊維強化複合材料
CN204526179U (zh) 一种用于3d打印机的送丝装置
CN107964205A (zh) 一种适用于快速成型的pp/sebs的制备方法
CN107856295B (zh) 一种3d打印机
KR20190114125A (ko) 고기능성 친환경 3d 필라멘트 제조를 위한 원스탑 공정 및 그를 이용한 3d 필라멘트
CN106554594A (zh) 一种适用于3d打印的sebs复合材料及其制备方法
JP7376971B2 (ja) 造形物

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17929600

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2019549778

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17929600

Country of ref document: EP

Kind code of ref document: A1