WO2017182628A1 - Matériau en couches à traitement ignifuge, panneau de finition, procédé de fabrication d'un matériau en couches et utilisation d'un matériau d'étanchéité - Google Patents
Matériau en couches à traitement ignifuge, panneau de finition, procédé de fabrication d'un matériau en couches et utilisation d'un matériau d'étanchéité Download PDFInfo
- Publication number
- WO2017182628A1 WO2017182628A1 PCT/EP2017/059516 EP2017059516W WO2017182628A1 WO 2017182628 A1 WO2017182628 A1 WO 2017182628A1 EP 2017059516 W EP2017059516 W EP 2017059516W WO 2017182628 A1 WO2017182628 A1 WO 2017182628A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- layers
- fire
- retardant
- adhesive
- Prior art date
Abstract
L'invention concerne un matériau en couches (10) à traitement ignifuge notamment conçu en tant que matériau en forme de panneau, de préférence pour des applications d'habillage intérieur et/ou de constructions sèches. Le matériau présente plusieurs couches reliées les unes aux autres, au moins une des couches étant conçue en tant que couche de matériau cellulosique, notamment en tant que couche de bois (11). Les couches sont reliées les unes aux autres de façon durable au moyen d'une couche d'adhésif (12). Le matériau en couches (10) est caractérisé en ce que la couche d'adhésif (12) et l'au moins une couche de matériau cellulosique sont conçues de façon ignifuge. L'invention concerne également un panneau de finition, un procédé de fabrication d'un matériau en couches (10) et l'utilisation d'un matériau d'étanchéité.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP17720413.8A EP3445580A1 (fr) | 2016-04-21 | 2017-04-21 | Matériau en couches à traitement ignifuge, panneau de finition, procédé de fabrication d'un matériau en couches et utilisation d'un matériau d'étanchéité |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE102016107441 | 2016-04-21 | ||
DE102016107441.1 | 2016-04-21 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2017182628A1 true WO2017182628A1 (fr) | 2017-10-26 |
WO2017182628A9 WO2017182628A9 (fr) | 2018-08-23 |
Family
ID=58645033
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2017/059516 WO2017182628A1 (fr) | 2016-04-21 | 2017-04-21 | Matériau en couches à traitement ignifuge, panneau de finition, procédé de fabrication d'un matériau en couches et utilisation d'un matériau d'étanchéité |
Country Status (3)
Country | Link |
---|---|
EP (1) | EP3445580A1 (fr) |
DE (1) | DE102017108527A1 (fr) |
WO (1) | WO2017182628A1 (fr) |
Citations (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
BE680195A (fr) * | 1964-03-04 | 1966-10-03 | ||
US20070102238A1 (en) * | 2005-11-09 | 2007-05-10 | Low Reginald W | Acoustical panel using wood veneer |
FR2897883A1 (fr) * | 2006-02-08 | 2007-08-31 | Cooperative Ouvriere De Menuis | Structure de type panneau, d'isolation acoustique et/ou thermique |
FR2943699A1 (fr) * | 2009-03-31 | 2010-10-01 | Vincent Damour | Panneau sandwich resistant au feu,avec une ame a base de silicate renforce. |
US20120118629A1 (en) * | 2009-07-02 | 2012-05-17 | Fujitsu Limited | Plate member for housing, housing, and method of fabricating the same |
EP2522503A2 (fr) * | 2011-05-12 | 2012-11-14 | List components & furniture GmbH | Élément composite |
EP2818315A1 (fr) * | 2012-02-20 | 2014-12-31 | KCC Corporation | Élément d'étanchéité en matériau d'isolation sous vide remarquablement résistant aux chocs et incombustible |
WO2015061905A1 (fr) * | 2013-10-31 | 2015-05-07 | Blh Technologies Inc. | Article résistant au feu, et procédé de production associé |
WO2015181263A1 (fr) * | 2014-05-27 | 2015-12-03 | Patrick Leleu Furnier Gmbh | Matériau ignifuge, panneau de construction, procédé de fabrication d'un matériau ignifuge et procédé de fabrication d'un panneau de construction |
EP3205496A1 (fr) * | 2016-02-11 | 2017-08-16 | SWISS KRONO Tec AG | Plaque composite en materiau derive du bois comprenant un palier intermediaire en contreplaque |
-
2017
- 2017-04-21 DE DE102017108527.0A patent/DE102017108527A1/de not_active Withdrawn
- 2017-04-21 WO PCT/EP2017/059516 patent/WO2017182628A1/fr active Application Filing
- 2017-04-21 EP EP17720413.8A patent/EP3445580A1/fr not_active Withdrawn
Patent Citations (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
BE680195A (fr) * | 1964-03-04 | 1966-10-03 | ||
US20070102238A1 (en) * | 2005-11-09 | 2007-05-10 | Low Reginald W | Acoustical panel using wood veneer |
FR2897883A1 (fr) * | 2006-02-08 | 2007-08-31 | Cooperative Ouvriere De Menuis | Structure de type panneau, d'isolation acoustique et/ou thermique |
FR2943699A1 (fr) * | 2009-03-31 | 2010-10-01 | Vincent Damour | Panneau sandwich resistant au feu,avec une ame a base de silicate renforce. |
US20120118629A1 (en) * | 2009-07-02 | 2012-05-17 | Fujitsu Limited | Plate member for housing, housing, and method of fabricating the same |
EP2522503A2 (fr) * | 2011-05-12 | 2012-11-14 | List components & furniture GmbH | Élément composite |
EP2818315A1 (fr) * | 2012-02-20 | 2014-12-31 | KCC Corporation | Élément d'étanchéité en matériau d'isolation sous vide remarquablement résistant aux chocs et incombustible |
WO2015061905A1 (fr) * | 2013-10-31 | 2015-05-07 | Blh Technologies Inc. | Article résistant au feu, et procédé de production associé |
WO2015181263A1 (fr) * | 2014-05-27 | 2015-12-03 | Patrick Leleu Furnier Gmbh | Matériau ignifuge, panneau de construction, procédé de fabrication d'un matériau ignifuge et procédé de fabrication d'un panneau de construction |
EP3205496A1 (fr) * | 2016-02-11 | 2017-08-16 | SWISS KRONO Tec AG | Plaque composite en materiau derive du bois comprenant un palier intermediaire en contreplaque |
Also Published As
Publication number | Publication date |
---|---|
WO2017182628A9 (fr) | 2018-08-23 |
DE102017108527A1 (de) | 2017-10-26 |
EP3445580A1 (fr) | 2019-02-27 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
DE3686583T2 (de) | Mehrschichtiges holzprodukt. | |
AT511513B1 (de) | Verbundelement | |
EP1963596A1 (fr) | Panneau de plancher avec une couche ignifuge | |
DE202006013553U1 (de) | Bauplatte | |
EP3174707B1 (fr) | Élément composite comprenant une couche de recouvrement formée d'une feuille de placage | |
DE102006041305A1 (de) | Bauplatte und Verfahren zur Herstellung einer Bauplatte | |
DE202010003580U1 (de) | Feuerfeste und wasserfeste Wabenstruktur | |
EP2893101B1 (fr) | Panneau de lames de bois multicouche | |
EP1283926A1 (fr) | Element sandwich en bois en forme de panneau | |
EP3445580A1 (fr) | Matériau en couches à traitement ignifuge, panneau de finition, procédé de fabrication d'un matériau en couches et utilisation d'un matériau d'étanchéité | |
DE102015103893B4 (de) | Brandschutz für Holzwerkstoffplatten | |
DE102007018209A1 (de) | Dämmplatte | |
EP0328921B1 (fr) | Panneau sandwich pour la construction | |
DE202012104480U1 (de) | Holzfurnier und damit furnierte Baustoffplatte | |
DE60311310T2 (de) | Platte für thermoakustische wandisolierung | |
EP2921270B1 (fr) | Élément de placage | |
DE102005028465A1 (de) | Schallisolierendes Material | |
DE102015001635A1 (de) | Verfahren zur Herstellung von Bauteilen aus Holz oder Holzwerkstoffen mit Klebstoff und Verbindungselementen | |
AT15882U1 (de) | Verfahren zur Herstellung eines Brettsperrholzelementes | |
EP3290607A1 (fr) | Plaque d'isolant contenant du kaolin | |
EP3148799A1 (fr) | Matériau ignifuge, panneau de construction, procédé de fabrication d'un matériau ignifuge et procédé de fabrication d'un panneau de construction | |
EP0936063A2 (fr) | Elément de construction composite thermo-isolant | |
DE3010141A1 (de) | Bauelement, insbesondere platte, brett, balken o.dgl. | |
DE202014105591U1 (de) | Nicht brennbare Baustofftür | |
DE102020106627A1 (de) | Brandschutzanordnung und Verfahren, insbesondere zur Verwendung im Stahlhochbau |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2017720413 Country of ref document: EP |
|
ENP | Entry into the national phase |
Ref document number: 2017720413 Country of ref document: EP Effective date: 20181121 |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 17720413 Country of ref document: EP Kind code of ref document: A1 |