WO2017165634A1 - Articles contenant des revêtements améliorant l'adhérence et leurs procédés de production - Google Patents

Articles contenant des revêtements améliorant l'adhérence et leurs procédés de production Download PDF

Info

Publication number
WO2017165634A1
WO2017165634A1 PCT/US2017/023791 US2017023791W WO2017165634A1 WO 2017165634 A1 WO2017165634 A1 WO 2017165634A1 US 2017023791 W US2017023791 W US 2017023791W WO 2017165634 A1 WO2017165634 A1 WO 2017165634A1
Authority
WO
WIPO (PCT)
Prior art keywords
coating
textured coating
textured
electrodeposited
substrate
Prior art date
Application number
PCT/US2017/023791
Other languages
English (en)
Inventor
Atieh HAGHDOOST
Mehdi KARGAR
Original Assignee
Maxterial, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US15/392,330 external-priority patent/US20170190139A1/en
Application filed by Maxterial, Inc. filed Critical Maxterial, Inc.
Publication of WO2017165634A1 publication Critical patent/WO2017165634A1/fr

Abstract

Certains modes de réalisation de la présente invention concernent des articles contenant des revêtements texturés susceptibles d'améliorer l'adhérence d'un revêtement de surface. Dans certains exemples, le revêtement texturé contient au moins un métal ou un composé métallique présent dans une pluralité de microstructures individuelles qui peuvent être positionnées dans différents plans et à différentes hauteurs par rapport à un point zéro de référence dans le revêtement texturé. Dans certaines configurations, un revêtement de surface contenant un matériau répulsif peut être disposé sur le revêtement texturé et peut s'imprégner dans le revêtement texturé, ou y adhérer, de façon à améliorer l'adhérence du revêtement de surface.
PCT/US2017/023791 2016-03-23 2017-03-23 Articles contenant des revêtements améliorant l'adhérence et leurs procédés de production WO2017165634A1 (fr)

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
US201662312267P 2016-03-23 2016-03-23
US62/312,267 2016-03-23
US201662358513P 2016-07-05 2016-07-05
US62/358,513 2016-07-05
US15/392,330 2016-12-28
US15/392,330 US20170190139A1 (en) 2015-12-30 2016-12-28 Coatings and coated surfaces with selected surface characteristics and features

Publications (1)

Publication Number Publication Date
WO2017165634A1 true WO2017165634A1 (fr) 2017-09-28

Family

ID=59900867

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2017/023791 WO2017165634A1 (fr) 2016-03-23 2017-03-23 Articles contenant des revêtements améliorant l'adhérence et leurs procédés de production

Country Status (1)

Country Link
WO (1) WO2017165634A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114150343A (zh) * 2022-01-19 2022-03-08 西南石油大学 一种纳米茸状NiMoCu催化剂及其制备方法
US11753518B1 (en) * 2022-09-22 2023-09-12 Cast Masters LLC Ceramic coatings containing particles

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4371430A (en) * 1979-04-27 1983-02-01 Printing Developments, Inc. Electrodeposition of chromium on metal base lithographic sheet
US20060135281A1 (en) * 2004-12-17 2006-06-22 Integran Technologies, Inc. Strong, lightweight article containing a fine-grained metallic layer
US20100127125A1 (en) * 2008-08-05 2010-05-27 Ming Li Metal sheets and plates having friction-reducing textured surfaces and methods of manufacturing same
US20130319868A1 (en) * 2011-02-18 2013-12-05 Aisin Keikinzoku Co., Ltd. Surface treatment method for metal member and metal member obtained by the same
US20140004352A1 (en) * 2012-06-29 2014-01-02 Integran Technologies Inc. Metal-clad hybrid article having synergistic mechanical properties
WO2014179283A2 (fr) * 2013-04-29 2014-11-06 Gvd Corporation Revêtements imprégnés de liquide et dispositifs les contenant
US20150368821A1 (en) * 2013-02-15 2015-12-24 Virginia Tech Intellectual Properties, Inc. Fabricating Porous Metallic Coatings Via Electrodeposition and Compositions Thereof

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4371430A (en) * 1979-04-27 1983-02-01 Printing Developments, Inc. Electrodeposition of chromium on metal base lithographic sheet
US20060135281A1 (en) * 2004-12-17 2006-06-22 Integran Technologies, Inc. Strong, lightweight article containing a fine-grained metallic layer
US20100127125A1 (en) * 2008-08-05 2010-05-27 Ming Li Metal sheets and plates having friction-reducing textured surfaces and methods of manufacturing same
US20130319868A1 (en) * 2011-02-18 2013-12-05 Aisin Keikinzoku Co., Ltd. Surface treatment method for metal member and metal member obtained by the same
US20140004352A1 (en) * 2012-06-29 2014-01-02 Integran Technologies Inc. Metal-clad hybrid article having synergistic mechanical properties
US20150368821A1 (en) * 2013-02-15 2015-12-24 Virginia Tech Intellectual Properties, Inc. Fabricating Porous Metallic Coatings Via Electrodeposition and Compositions Thereof
WO2014179283A2 (fr) * 2013-04-29 2014-11-06 Gvd Corporation Revêtements imprégnés de liquide et dispositifs les contenant

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114150343A (zh) * 2022-01-19 2022-03-08 西南石油大学 一种纳米茸状NiMoCu催化剂及其制备方法
CN114150343B (zh) * 2022-01-19 2024-02-06 西南石油大学 一种纳米茸状NiMoCu催化剂及其制备方法
US11753518B1 (en) * 2022-09-22 2023-09-12 Cast Masters LLC Ceramic coatings containing particles

Similar Documents

Publication Publication Date Title
KR102262640B1 (ko) 표면 코팅을 포함하는 물품 및 이의 제조 방법
US20170190139A1 (en) Coatings and coated surfaces with selected surface characteristics and features
JP2020536177A5 (fr)
US20230295827A1 (en) Coatings and coated surfaces including low-surface energy inorganic particles
AU2009302806B9 (en) Highly durable superhydrophobic, oleophobic and anti-icing coatings and methods and compositions for their preparation
JP5727156B2 (ja) 疎水性コーティングおよびそのプロセス
JP2011526835A5 (fr)
US20180028029A1 (en) Drying apparatus comprising a hydrophobic material
JP2011526835A (ja) パーフルオロ化合物を必要としない、またはフッ素を含まない、超疎水性エアロゲル
WO2010147738A1 (fr) Revêtements super-non mouillants et anti-empreintes pour le verre
Zhang et al. Volcano-like hierarchical superhydrophobic surface synthesized via facile one-step secondary anodic oxidation
JP2017518895A (ja) 疎水性物品
US20200010688A1 (en) Oleophobic coatings and wipes and applicators used to produce them
Birjandi et al. Super-non-wettable surfaces: a review
Jena et al. Fabrication of silanized GO hybrid coating on 316L SS with enhanced corrosion resistance and antibacterial properties for marine applications
JP2011528063A (ja) 基材上に金属を電着する方法
US20170334170A1 (en) Articles including adhesion enhancing coatings and methods of producing them
WO2017165634A1 (fr) Articles contenant des revêtements améliorant l'adhérence et leurs procédés de production
Mrad et al. Effect of AA2024‐T3 surface pretreatment on the physicochemical properties and the anticorrosion performance of poly (γ‐glycidoxypropyltrimethoxysilane) sol‐gel coating
RU2400510C1 (ru) Состав для получения супергидрофобного покрытия
Selim et al. Bioinspired graphene oxide–magnetite nanocomposite coatings as protective superhydrophobic antifouling surfaces
Wankhede et al. Development of hydrophobic non-fluorine sol-gel coatings on aluminium using long chain alkyl silane precursor
Ouyang et al. Silica nanoparticles enhanced polysiloxane-modified nickel-based coatings on Mg alloy for robust superhydrophobicity and high corrosion resistance
He et al. Experimental and molecular dynamics simulation study of chemically stable superhydrophobic surfaces
JP5434775B2 (ja) 親水性膜形成用塗工液及び塗膜

Legal Events

Date Code Title Description
NENP Non-entry into the national phase

Ref country code: DE

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17771146

Country of ref document: EP

Kind code of ref document: A1

122 Ep: pct application non-entry in european phase

Ref document number: 17771146

Country of ref document: EP

Kind code of ref document: A1