WO2017159738A1 - Acier en barres micro-allié - Google Patents

Acier en barres micro-allié Download PDF

Info

Publication number
WO2017159738A1
WO2017159738A1 PCT/JP2017/010440 JP2017010440W WO2017159738A1 WO 2017159738 A1 WO2017159738 A1 WO 2017159738A1 JP 2017010440 W JP2017010440 W JP 2017010440W WO 2017159738 A1 WO2017159738 A1 WO 2017159738A1
Authority
WO
WIPO (PCT)
Prior art keywords
content
steel
steel bar
tin
hot
Prior art date
Application number
PCT/JP2017/010440
Other languages
English (en)
Japanese (ja)
Inventor
有祐 宮越
幹 高須賀
長谷川　達也
Original Assignee
新日鐵住金株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 新日鐵住金株式会社 filed Critical 新日鐵住金株式会社
Priority to JP2018505980A priority Critical patent/JP6528898B2/ja
Priority to CN201780017775.1A priority patent/CN108779534B/zh
Publication of WO2017159738A1 publication Critical patent/WO2017159738A1/fr

Abstract

L'invention concerne un acier en barres microallié qui présente d'excellentes performances de fissuration même si de la bainite se forme après un forgeage à chaud. L'acier en barres micro-allié selon le présent mode de réalisation comprend, en % en masse, 0,39 à 0,55 % de C, 0,10 à 1,00 % de Si, 0,50 à 1,50 % de Mn, 0,010 à 0,100 % de P, 0,04 à 0,13 % de S, 0,05 à 0,50% de Cr, 0,05 à 0,40% de V, 0,15 à 0,25% de Ti, 0,005 à 0,050% d'Al et 0,002 à 0,020% de N, le reste comprenant du Fe et des impuretés ; et sa structure chimique satisfait la formule (1). La densité en nombre des particules de TiN dans l'acier qui ont un diamètre circulaire équivalent d'au moins 20 µm est de 0,3 à 4,0 particules/mm2. Formule (1) : 0,60 ≤ C + 0,2Mn + 0,25Cr + 0,75V + 0,81Mo ≤ 1,00. Les symboles chimiques dans la formule (1) sont substitués par la teneur (en % en masse) de l'élément correspondant.
PCT/JP2017/010440 2016-03-16 2017-03-15 Acier en barres micro-allié WO2017159738A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
JP2018505980A JP6528898B2 (ja) 2016-03-16 2017-03-15 非調質棒鋼
CN201780017775.1A CN108779534B (zh) 2016-03-16 2017-03-15 非调质棒钢

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2016053026 2016-03-16
JP2016-053026 2016-03-16

Publications (1)

Publication Number Publication Date
WO2017159738A1 true WO2017159738A1 (fr) 2017-09-21

Family

ID=59852119

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/010440 WO2017159738A1 (fr) 2016-03-16 2017-03-15 Acier en barres micro-allié

Country Status (3)

Country Link
JP (1) JP6528898B2 (fr)
CN (1) CN108779534B (fr)
WO (1) WO2017159738A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN112567061A (zh) * 2018-08-24 2021-03-26 日本制铁株式会社 钢材、锻造热处理品和锻造热处理品的制造方法

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111647797B (zh) * 2020-04-29 2021-08-24 樟树市兴隆高新材料有限公司 一种高速工具钢及其钢热处理方法
CN111471920B (zh) * 2020-04-30 2021-09-17 江苏利淮钢铁有限公司 一种u型螺栓用非调质钢及其生产方法
CN111441005B (zh) * 2020-05-25 2021-08-20 江苏联峰实业有限公司 一种易切削非调质钢及其生产方法
CN114196884B (zh) * 2021-12-13 2022-06-17 芜湖新兴铸管有限责任公司 一种400MPa级微合金化耐腐蚀钢筋及其生产方法
CN114959420A (zh) * 2022-05-30 2022-08-30 江苏联峰能源装备有限公司 一种圆坯生产塑机料筒用非调质钢的制备方法

Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH09111412A (ja) * 1995-10-19 1997-04-28 Sumitomo Metal Ind Ltd 高強度・高降伏比・低延性非調質鋼
JPH09310152A (ja) * 1996-05-21 1997-12-02 Kobe Steel Ltd 熱間鍛造用非調質鋼
JPH10204578A (ja) * 1996-11-25 1998-08-04 Sumitomo Metal Ind Ltd 高強度快削非調質鋼材
JPH11286746A (ja) * 1998-04-06 1999-10-19 Sumitomo Metal Ind Ltd 被削性に優れた低延性非調質鋼材
JP2004277817A (ja) * 2003-03-14 2004-10-07 Daido Steel Co Ltd 破断分離に適した高強度非調質鋼及びこれを用いた鍛造部品
JP2005002367A (ja) * 2003-06-09 2005-01-06 Sanyo Special Steel Co Ltd 破断分割性に優れる機械構造用非調質鋼
JP2005036310A (ja) * 2003-06-27 2005-02-10 Daido Steel Co Ltd 破断分離が容易な高周波焼入れコンロッド用非調質鋼
JP2008240130A (ja) * 2007-03-29 2008-10-09 Sumitomo Metal Ind Ltd 非調質鋼材
JP2011032545A (ja) * 2009-08-03 2011-02-17 Aichi Steel Works Ltd 熱間鍛造非調質鋼
WO2012157455A1 (fr) * 2011-05-19 2012-11-22 住友金属工業株式会社 Acier non trempé et article en acier non trempé
WO2012164710A1 (fr) * 2011-06-02 2012-12-06 新日鐵住金株式会社 Acier en barre pour bielles non traitées thermiquement

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN104775081A (zh) * 2015-04-21 2015-07-15 宝山钢铁股份有限公司 一种撑断连杆用高碳非调质钢及其制造方法
CN105154774A (zh) * 2015-09-23 2015-12-16 宝山钢铁股份有限公司 一种易切削中碳非调质裂解连杆用钢及其制造方法

Patent Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH09111412A (ja) * 1995-10-19 1997-04-28 Sumitomo Metal Ind Ltd 高強度・高降伏比・低延性非調質鋼
JPH09310152A (ja) * 1996-05-21 1997-12-02 Kobe Steel Ltd 熱間鍛造用非調質鋼
JPH10204578A (ja) * 1996-11-25 1998-08-04 Sumitomo Metal Ind Ltd 高強度快削非調質鋼材
JPH11286746A (ja) * 1998-04-06 1999-10-19 Sumitomo Metal Ind Ltd 被削性に優れた低延性非調質鋼材
JP2004277817A (ja) * 2003-03-14 2004-10-07 Daido Steel Co Ltd 破断分離に適した高強度非調質鋼及びこれを用いた鍛造部品
JP2005002367A (ja) * 2003-06-09 2005-01-06 Sanyo Special Steel Co Ltd 破断分割性に優れる機械構造用非調質鋼
JP2005036310A (ja) * 2003-06-27 2005-02-10 Daido Steel Co Ltd 破断分離が容易な高周波焼入れコンロッド用非調質鋼
JP2008240130A (ja) * 2007-03-29 2008-10-09 Sumitomo Metal Ind Ltd 非調質鋼材
JP2011032545A (ja) * 2009-08-03 2011-02-17 Aichi Steel Works Ltd 熱間鍛造非調質鋼
WO2012157455A1 (fr) * 2011-05-19 2012-11-22 住友金属工業株式会社 Acier non trempé et article en acier non trempé
WO2012164710A1 (fr) * 2011-06-02 2012-12-06 新日鐵住金株式会社 Acier en barre pour bielles non traitées thermiquement

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN112567061A (zh) * 2018-08-24 2021-03-26 日本制铁株式会社 钢材、锻造热处理品和锻造热处理品的制造方法

Also Published As

Publication number Publication date
JPWO2017159738A1 (ja) 2018-12-13
CN108779534B (zh) 2020-10-16
CN108779534A (zh) 2018-11-09
JP6528898B2 (ja) 2019-06-12

Similar Documents

Publication Publication Date Title
WO2017159738A1 (fr) Acier en barres micro-allié
JP7063386B2 (ja) 鋼材、鍛造熱処理品、及び、鍛造熱処理品の製造方法
JP4268194B2 (ja) 破断分離性に優れた破断分離型コネクティングロッド用圧延材、破断分離性に優れた破断分離型コネクティングロッド用熱間鍛造部品、及び破断分離型コネクティングロッド
JP5563926B2 (ja) 摩擦圧接に適した機械構造用鋼材および衝撃特性、曲げ疲労特性に優れた摩擦圧接部品
JP6614393B2 (ja) 非調質棒鋼
JP5858996B2 (ja) 非調質コネクティングロッド用棒鋼
WO2017213166A1 (fr) Barre en acier laminé pour forgeage à chaud
JP6597945B1 (ja) 鋼材
JP6617852B2 (ja) 熱間鍛造用棒鋼
JP6298898B2 (ja) クラッキングコンロッド用圧延鋼材
JP4676817B2 (ja) 破断分割性に優れたコネクティングロッド用鋼
JP2003342671A (ja) 破断分離可能な高強度非調質鋼及びその中間製品
JP6515301B2 (ja) 熱間圧延鋼材および鋼部品
JP2017179475A (ja) 破断分離型コネクティングロッド用成型部品、及びコネクティングロッド、並びに該コネクティングロッドの製造方法
WO2018061642A1 (fr) Acier laminé à chaud et pièce d'acier
WO2017126407A1 (fr) Acier à forger et produit de grande taille en acier forgé
JP2005298943A (ja) 白鋳鉄系鍛造ロールの製造方法

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 2018505980

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: DE

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17766734

Country of ref document: EP

Kind code of ref document: A1

122 Ep: pct application non-entry in european phase

Ref document number: 17766734

Country of ref document: EP

Kind code of ref document: A1