WO2016128704A2 - A weld - Google Patents
A weld Download PDFInfo
- Publication number
- WO2016128704A2 WO2016128704A2 PCT/GB2016/000028 GB2016000028W WO2016128704A2 WO 2016128704 A2 WO2016128704 A2 WO 2016128704A2 GB 2016000028 W GB2016000028 W GB 2016000028W WO 2016128704 A2 WO2016128704 A2 WO 2016128704A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- laser
- weld
- pulse
- hole
- width
- Prior art date
Abstract
Description
Claims