WO2016118862A1

WO2016118862A1 - Seed selection and growth methods for reduced-crack group iii nitride bulk crystals

Info

Publication number: WO2016118862A1
Application number: PCT/US2016/014522
Authority: WO
Inventors: Tadao Hashimoto; Edward Letts; Daryl KEY
Original assignee: Sixpoint Materials, Inc.; Seoul Semiconductor Co., Ltd.
Priority date: 2015-01-22
Filing date: 2016-01-22
Publication date: 2016-07-28
Also published as: KR102069277B1; EP3247824A1; KR20170121182A; JP6448155B2; JP2018504355A; CN107208305A

Abstract

In one instance, the invention provides a method of growing bulk crystal of group III nitride using a seed crystal selected by (a) measuring x-ray rocking curves of a seed crystal at more than one point, (b) quantifying the peak widths of the measured x-ray rocking curves, and (c) evaluating the distribution of the quantified peak widths. The invention also includes the method of selecting a seed crystal for growing bulk crystal of group III nitride. The bulk crystal of group III nitride can be grown in supercritical ammonia or a melt of group III metal using at least one seed selected by the method above.

Description

SEED SELECTION AND GROWTH METHODS FOR REDUCED-CRACK GROUP III NITRIDE BULK CRYSTALS

CROSS REFERENCE TO RELATED APPLICATIONS [0001] This application claims benefit of priority to U.S. application serial number 62/106,709 filed Jan. 22, 2015, entitled "Seed Selection and Growth Methods for Reduced- Crack Group III Nitride Bulk Crystals," inventors Tadao Hashimoto, Edward Letts, and Daryl Key, attorney docket no. SIXPOI-024USPRV1, and this application is also related to the following:

[0002] PCT Utility Patent Application Serial No. US2005/024239, filed on July 8, 2005, by Kenji Fujito, Tadao Hashimoto and Shuji Nakamura, entitled "METHOD FOR GROWING GROUP III-NITRIDE CRYSTALS IN SUPERCRITICAL AMMONIA USING AN AUTOCLAVE," attorneys' docket number 30794.0129-WO-Ol (2005-339-1);

[0003] United States Utility Patent Application Serial No. 11/784,339, filed on April 6, 2007, by Tadao Hashimoto, Makoto Saito, and Shuji Nakamura, entitled "METHOD FOR GROWING LARGE SURFACE AREA GALLIUM NITRIDE CRYSTALS IN SUPERCRITICAL AMMONIA AND LARGE SURFACE AREA GALLIUM NITRIDE CRYSTALS," attorneys docket number 30794.179-US-U1 (2006-204), which application claims the benefit under 35 U.S.C. Section 119(e) of United States Provisional Patent Application Serial No. 60/790,310, filed on April 7, 2006, by Tadao Hashimoto, Makoto Saito, and Shuji Nakamura, entitled "A METHOD FOR GROWING LARGE SURFACE AREA GALLIUM NITRIDE CRYSTALS IN SUPERCRITICAL AMMONIA AND LARGE SURFACE AREA GALLIUM NITRIDE CRYSTALS," attorneys docket number 30794.179-US-P1 (2006-204);

[0004] United States Utility Patent Application Serial No. 60/973,602 , filed on September 19, 2007, by Tadao Hashimoto and Shuji Nakamura, entitled "GALLIUM NITRIDE BULK CRYSTALS AND THEIR GROWTH METHOD," attorneys docket number 30794.244-US-P1 (2007-809-1);

[0005] United States Utility Patent Application Serial No. 11/977,661, filed on October 25, 2007, by Tadao Hashimoto, entitled "METHOD FOR GROWING GROUP III- NITRIDE CRYSTALS IN A MIXTURE OF SUPERCRITICAL AMMONIA AND NITROGEN, AND GROUP III-NITRIDE CRYSTALS GROWN THEREBY," now U.S. Pat. No. 7,803,344, attorneys docket number 30794.253-US-U1 (2007-774-2); [0006] United States Utility Patent Application Serial No. 61/067,117, filed on February 25, 2008, by Tadao Hashimoto, Edward Letts, Masanori Ikari, entitled "METHOD FOR PRODUCING GROUP III-NITRIDE WAFERS AND GROUP III-NITRIDE WAFERS," now U.S. Pat. No. 8,728,234, attorneys docket number 62158-30002.00 or SIXPOI-003;

[0007] United States Utility Patent Application Serial No. 61/058,900, filed on June 4, 2008, by Edward Letts, Tadao Hashimoto, Masanori Ikari, entitled "METHODS FOR PRODUCING IMPROVED CRYSTALLINITY GROUP III-NITRIDE CRYSTALS FROM INITIAL GROUP III-NITRIDE SEED BY AMMONOTHERMAL GROWTH," now U.S. Pat. No. 8,728,234, attorneys docket number 62158-30004.00 or SIXPOI-002;

[0008] United States Utility Patent Application Serial No. 61/058,910, filed on June 4, 2008, by Tadao Hashimoto, Edward Letts, Masanori Ikari, entitled "HIGH-PRESSURE VESSEL FOR GROWING GROUP III NITRIDE CRYSTALS AND METHOD OF GROWING GROUP III NITRIDE CRYSTALS USING HIGH-PRESSURE VESSEL AND GROUP III NITRIDE CRYSTAL," now U.S. Pat. No. 8,236,267 and 8,420,041, attorneys docket number 62158-30005.00 or SIXPOI-005;

[0009] United States Utility Patent Application Serial No. 61/131,917, filed on June 12, 2008, by Tadao Hashimoto, Masanori Ikari, Edward Letts, entitled "METHOD FOR TESTING III-NITRIDE WAFERS AND III-NITRIDE WAFERS WITH TEST DATA," now U.S. Pat. No. 8,357,243, 8,577,043, and 8,585,822, attorneys docket number 62158- 30006.00 or SrXPOI-001;

[0010] United States Utility Patent Application Serial No. 61/106,110, filed on October 16, 2008, by Tadao Hashimoto, Masanori Ikari, Edward Letts, entitled "REACTOR

DESIGN FOR GROWING GROUP III NITRIDE CRYSTALS AND METHOD OF GROWING GROUP III NITRIDE CRYSTALS," attorneys docket number SIXPOI-004;

[0011] United States Utility Patent Application Serial No. 61/694,119, filed on August 28, 2012, by Tadao Hashimoto, Edward Letts, Sierra Hoff, entitled "GROUP III NITRIDE WAFER AND PRODUCTION METHOD," now U.S. Pat. No. 8,921,231, attorneys docket number SIXPOI-015;

[0012] United States Utility Patent Application Serial No. 61/705,540, filed on

September 25, 2012, by Tadao Hashimoto, Edward Letts, Sierra Hoff, entitled "METHOD OF GROWING GROUP III NITRIDE CRYSTALS," not U.S. Pat. No. 9,202,872, attorneys docket number SIXPOI-014; [0013] all of which are incorporated by reference herein in their entirety as if put forth in full below.

BACKGROUND

Field of the invention. [0014] The invention relates to a bulk crystal of semiconductor material used to produce semiconductor wafers for various devices including optoelectronic devices such as light emitting diodes (LEDs) and laser diodes (LDs), and electronic devices such as transistors. More specifically, the invention provides a bulk crystal of group III nitride such as gallium nitride. The invention also provides a method of selecting seed crystals for growth of group III nitride bulk crystals.

Description of the existing technology.

[0015] This document refers to several publications and patents as indicated with numbers within brackets, e.g., [x]. Following is a list of these publications and patents:

[1] R. Dwilinski, R. Doradzihski, J. Garczyhski, L. Sierzputowski, Y. Kanbara, U.S. Patent No. 6,656,615.

[2] R. Dwilinski, R. Doradzihski, J. Garczyhski, L. Sierzputowski, Y. Kanbara, U.S. Patent No. 7,132,730.

[3] R. Dwilinski, R. Doradzihski, J. Garczyhski, L. Sierzputowski, Y. Kanbara, U.S. Patent No. 7,160,388.

[4] K. Fujito, T. Hashimoto, S. Nakamura, International Patent Application No.

PCT/US2005/024239, WO07008198.

[5] T. Hashimoto, M. Saito, S. Nakamura, International Patent Application No.

PCT/US2007/008743, WO07117689. See also US20070234946, U.S. Application Serial Number 11/784,339 filed April 6, 2007.

[6] D' Evelyn, U. S. Patent No. 7,078,731.

[7] Wang et al., Journal of Crystal Growth volume 318 (2011) pl030.

[0016] Each of the references listed in this document is incorporated by reference in its entirety as if put forth in full herein, and particularly with respect to their description of methods of making and using group III nitride substrates. [0017] Gallium nitride (GaN) and its related group III nitride alloys are the key material for various optoelectronic and electronic devices such as LEDs, LDs, microwave power transistors, and solar-blind photo detectors. Currently LEDs are widely used in displays, indicators, general illuminations, and LDs are used in data storage disk drives. However, the majority of these devices are grown epitaxially on heterogeneous substrates, such as sapphire and silicon carbide because GaN substrates are extremely expensive compared to these heteroepitaxial substrates. The heteroepitaxial growth of group III nitride causes highly defected or even cracked films, which hinder the realization of high-end optical and electronic devices, such as high-brightness LEDs for general lighting or high-power microwave transistors.

[0018] To solve fundamental problems caused by heteroepitaxy, it is indispensable to utilize crystalline group III nitride wafers sliced from bulk group III nitride crystal ingots. For the majority of devices, crystalline GaN wafers are favorable because it is relatively easy to control the conductivity of the wafer and GaN wafer will provide the smallest lattice/thermal mismatch with device layers. However, due to the high melting point and high nitrogen vapor pressure at elevated temperature, it has been difficult to grow GaN crystal ingots. Currently, the majority of commercially available GaN substrates are produced by a method called hydride vapor phase epitaxy (HVPE). HVPE is one of vapor phase methods, which has difficulty in reducing dislocation density less than 10⁵ cm^"2.

[0019] To obtain high-quality GaN substrates for which dislocation density is less than 10⁵ cm^"2, various growth methods such as ammonothermal growth, flux growth, high- temperature solution growth have been developed. Ammonothermal method grows group III nitride crystals in supercritical ammonia [1-6]. The flux method and the high- temperature solution growth use a melt of group III metal.

[0020] Recently, high-quality GaN substrates having dislocation density less than 10⁵ cm^"2 can be obtained by ammonothermal growth. Since the ammonothermal method can produce a true bulk crystal, one can grow one or more thick crystals and slice them to produce GaN wafers. We have been developing bulk crystals of GaN by the

ammonothermal method. However, we found it quite challenging to avoid cracking of bulk crystals, especially when the total thickness of the bulk crystal exceeds 1 mm. We believe that the cracking problem in bulk group III nitride is a universal problem for any bulk growth methods including the ammonothermal method. Thus, this invention is intended to obtain crack-free bulk group III nitride crystals using any bulk growth method, such as growth in supercritical ammonia or from a melt of group III metals.

SUMMARY OF THE INVENTION [0021] In one instance, the invention provides a method of growing bulk crystal of group III nitride using a seed crystal selected by (a) measuring x-ray rocking curves of the seed crystal at more than one point, (b) quantifying the peak widths of the measured x-ray rocking curves, and (c) evaluating the distribution of the quantified peak widths. The invention also includes the method of selecting a seed crystal for growing bulk crystal of group III nitride.

BRIEF DESCRIPTION OF THE DRAWINGS

[0022] Referring now to the drawings in which like reference numbers represent corresponding parts throughout: [0023] FIG. 1 is an example of a process flow of this invention.

[0024] FIG. 2 shows full width half maximum (FWHM) of 201 X-ray rocking curves from seed crystals (square dots), FWHM of 201 X-ray rocking curves from bulk GaN crystals using the corresponding seeds (diamond dots), and a photograph of a wafer sliced from the corresponding bulk GaN crystals, (a) for a seed with scattered distribution of FWHM, (b) for a seed with less scattered distribution of FWHM. The zero-point is at approximately the center of the seed's face along the longest line on an m-plane. XRD data in the examples was collected at various points across the seed crystal's face and along this line.

DETAILED DESCRIPTION OF THE INVENTION

Overview [0025] The bulk crystal of the present invention is typically sliced to produce group III nitride wafers suitable for fabricating various optoelectronic and electronic devices such as LEDs, LD, transistors, and photodetectors by known techniques. Many optoelectronic and electronic devices are fabricated with thin films of group III nitride alloys (i.e. alloys of GaN, A1N and InN). The group III nitride alloys are typically expressed as GaxAl_yIni-x-_yN (0<χ<1, 0<x+y<l). Since the group III metallic elements (i.e. Al, Ga, In) shows similar chemical characteristics, nitrides of these group III elements makes alloys or solid solution. In addition, crystal growth nature of these group III nitrides are quite similar.

[0026] Due to limited availability and high cost of single crystalline substrates of group III nitride, these devices have been fabricated on so-called heteroepitaxial substrates such as sapphire and silicon carbide. Since the heteroepitaxial substrates are chemically and physically different from the group III nitride, the device typically has a high density of dislocations (10⁸~10¹⁰ cm^"2) generated at the interface between the heteroepitaxial substrate and the device layer. Such dislocations deteriorate performance and reliability of devices, thus substrates composed of crystalline group III nitride such as GaN and A1N are favorable.

[0027] Currently, the majority of commercially available GaN substrates is produced with HVPE, in which it is difficult to reduce the dislocation density to less than 10⁵ cm^"2. Although the dislocation density of HVPE-GaN substrates is a few orders of magnitude lower than GaN film on heteroepitaxial substrates, the dislocation density is still a few orders of magnitude higher than typical silicon devices in electronics. To achieve higher device performance, lower dislocation density is required.

[0028] To attain dislocation density less than 10⁵ cm^"2, ammonothermal growth, which utilizes supercritical ammonia, has been developed. The ammonothermal method can produce GaN substrates with dislocation density less than 10⁵ cm^"2. One advantage of the ammonothermal method is that bulk crystals having a thickness larger than 1 mm can be grown. The ammonothermal method can also be used to grow crystals having various dopants such as donors (i.e. electron), acceptors (i.e. hole) or magnetic dopants. However, it is challenging to obtain a bulk crystal over 1 mm thick without cracking. It is a common practice to evaluate seed crystals and select a good seed for the ammonothermal growth. For example, Wang et al., disclosed a procedure to evaluate FWHM of X-ray rocking curve to select a good seed [7]. Nevertheless, we have experienced cracking problem even with such selection procedure. Although the origin and mechanism for crack formation are not well known, a possible cause would be stress accumulation inside the crystal due to a slight mismatch of thermal expansion coefficient or other physical properties between the seed crystal and grown crystal. To produce group III nitride substrates without cracks, it is necessary to obtain crack-free bulk crystal of group III nitride. Technical Description of the Invention

[0029] In an effort to reduce or eliminate cracking inside the bulk crystal of group III nitride having thickness larger than 1 mm, the current invention provides a method of making a bulk crystal of group III nitride in which a seed crystal is selected by (a) measuring x-ray rocking curves of the seed crystal at more than one point, (b) quantifying the peak widths of the measured x-ray rocking curves, and (c) evaluating the distribution of the quantified peak widths. FIG 1 presents a process flow of this invention.

[0030] First, a seed crystal for growing bulk crystal of group III nitride such as GaN is prepared. Seed crystal is preferably a single crystal of group III nitride such as GaN. The orientation of the seed crystal can be c-plane, a-plane, m-plane or other semipolar planes, although c-plane crystal is preferable. The single-crystal seed may be grown by hydride vapor-phase epitaxy (HVPE), molecular beam epitaxy (MBE), metal organic vapor-phase epitaxy (MOVPE), ammonothermal growth, flux method, high-pressure solution growth or other method.

[0031] Then, the seed crystal is measured with X-ray diffractometer to obtain rocking curves from more than one spot of the seed crystal. One example of selecting the measurement location is a straight line along one crystallographic orientation such as indirection or a-direction. Another example is to select points at intersections or within a square grid plotted over the seed's face. Another example is to take a statistically significant number of random measurements of the seed crystal's structure over the seed's face.

[0032] When a c-plane group III nitride crystal such as c-plane GaN is used, off-axis diffraction such as 201 and 102 reflections is preferably used. This is because the off-axis reflections turned out to be more sensitive to the quality of the seed crystals for growing bulk crystals. Consequently, it is helpful to first determine which directions are more sensitive to crystal structure of the seed crystal for the particular seed used (e.g. c-plane, m-plane, a-plane), and then use those directions in measuring quality of crystal structure at various points across the surface of the seed.

[0033] To quantify the peak width of the X-ray rocking curve, FWUM is commonly used although other methods of quantifying the peak width is also used. As commonly known, the peak width of the X-ray rocking curve represents the quality of microstructure of the crystal. The peak width is typically measured in the unit of arcsec, arcmin, or degree.

[0034] To evaluate the distribution of the peak widths, statistic value such as a standard deviation can be used. Alternately, one can plot the peak width data on a graph, and visually determine the distribution of the data. The magnitude of data scattering can be evaluated in an absolute value with a unit of arcsec, arcmin or degree. Alternately, the magnitude of data scattering can be evaluated relative to a representative value such as a mean value of all data.

[0035] If a standard deviation and a mean value is used to select a good seed crystal, the standard deviation is preferably less than 30% of the mean value, more preferably less than 20% of the mean value, or more preferably less than 10% of the mean value.

[0036] The selected seed crystal will be used to grow a bulk crystal of group III nitride such as bulk GaN. Depending on the growth method of a bulk crystal, one can select most preferable seed orientation and polarity. For example, when a bulk crystal is grown in supercritical ammonia, nitrogen polar c-plane GaN is preferably used.

Example 1

[0037] Single crystalline GaN seed crystal having a basal plane of c-plane was prepared with HVPE. The thickness of the GaN seed was approximately 430 microns. X-ray rocking curves from 201 reflection were recorded from multiple spots of the nitrogen polar side of the seed crystal. The measurement was conducted along the m-direction with the spot separation of 0.5 mm. The peak width is quantified with FWHM in arcsec. The square dots in FIG. 2 (a) show FWHM at each measurement spot. As shown in the FIG. 2(a) the FWHM values have a large scattering. The mean value of the FWHM was 78 arcsec and the standard deviation was 29 arcsec, which was 37% of the mean value. The data scattering is seen throughout the scanned line.

[0038] Then, a bulk crystal of GaN was grown in supercritical ammonia using a high- pressure reactor. The chamber within the high-pressure reactor was divided into a lower part and an upper part with baffle plates. Approximately 15 g of poly crystalline GaN is used as a nutrient and approximately 3.1 g of sodium is used as a mineralizer. Mineralizer and the seed crystal were placed in the lower part of the high-pressure reactor and the nutrient was placed in the upper part of the high-pressure reactor. Then, the high-pressure reactor was sealed, pumped to a vacuum and filled with anhydrous liquid ammonia. The volumetric ammonia fill factor was approximately 53%. The high-pressure reactor was heated at about 510~520°C to allow crystal growth of GaN on the seed. After sufficient amount of time, the ammonia was released and the high-pressure reactor was cooled. The resultant bulk GaN crystal has a thickness of approximately 5 mm. [0039] X-ray rocking curves from 201 reflection were measured at multiple spots on the surface of the grown bulk GaN crystal as described above and as described in Example 2. The FWHMs are plotted in FIG. 2(a) with diamond dots. As shown in the figure, the FWFDVIs from the grown bulk crystal also showed large scattering. The mean value of the FWFDVI was 89 arcsec and the standard deviation was 38 arcsec, which was 43% of the mean value. Then, the bulk crystal was sliced into wafers with a multiple wire saw. The inset picture in FIG. 2(a) is a photograph of the sliced wafer. The wafer had numerous cracks.

Example 2 [0040] Similar to Example 1, a c-plane GaN seed crystal was prepared with HVPE. The thickness of the GaN seed was approximately 430 microns. X-ray rocking curves from 201 reflection were recorded from multiple spots of the nitrogen polar side of the seed crystal. The measurement was conducted along a m-direction with spot separation of 0.5 mm. The peak width is quantified with FWHM in arcsec. The square dots in FIG. 2 (b) show FWHM at each measurement spot. As shown in the FIG. 2(b) the FWHM values have a small scattering. The mean value of the FWHM was 41 arcsec and the standard deviation was 7 arcsec, which was 17% of the mean value.

[0041] Then bulk GaN was grown on this seed crystal in a similar way as in Example 1. The FWHMs of 201 X-ray rocking curves from multiple spots on the grown bulk crystal are plotted with diamond dots in FIG. 2(b), showing small data scattering. The mean value of the FWHM was 48 arcsec and the standard deviation was 18 arcsec, which was 38% of the mean value. As seen in FIG. 2(b) between the +12 and +16 mm positions, the large standard deviation is caused by an edge effect of the measurement, causing XRD data to be less reliable. The center portion of the wafer has much less data scattering. A wafer sliced from this bulk GaN crystal showed much reduced cracks as shown in the picture of FIG. 2(b). The crack density was less than 1 cm^"2. Comparing Example 1 and Example 2, we discovered a strong correlation between the data scattering of peak widths of X-ray rocking curve from the seed crystal and crack density in the bulk crystal using the seed.

[0042] The evaluation of the data scattering can be performed by combining a standard deviation, visual judgment and other criteria. For example, if we use the center portion of the data from the seed crystal in this example (FIG. 2(b)), the standard deviation can be smaller than 10% of the mean value. This way one can eliminate the edge effect of the measurement. Taking a correlation between the data scattering of the rocking curve peak width and cracking density, one can obtain a crack-free bulk crystal.

Advantages and Improvements [0043] The bulk GaN crystal obtained with the method disclosed in this invention contains no or reduced amount of cracks. The obtained crack-free bulk GaN crystals are sliced into wafers. These wafers are used for optical devices such as LEDs and laser diodes or electronic devices such as high-power transistors. Since cracks deteriorate performances and reliability of these devices significantly, this invention can improve the device performance and reliability.

Possible modifications

[0044] Although the preferred embodiment describes bulk crystals of GaN, similar benefit of this invention can be expected for other group III nitride alloys of various compositions, such as A1N, AlGaN, InN, InGaN, or GaAlInN.

[0045] Although the preferred embodiment describes GaN seed crystal having thickness about 430 microns, similar benefit of this invention can be expected for other thicknesses between 100 microns to 2000 microns.

[0046] Although the preferred embodiment describes ammonothermal growth, similar benefit of this invention can be expected for other bulk growth methods such as a flux method or high-pressure, high-temperature solution growth. In the flux method, a group III metal and a flux such as sodium are melted together, and nitrogen then dissolves into the melt. One flux method is disclosed in U.S. Pat. No. 5,868,837. One suitable high-pressure, high-temperature solution growth method is disclosed in U.S. Pat. No. US 6273948 Bl . Each of these patents is incorporated by reference herein.

[0047] Although the preferred embodiment describes a seed crystal of approximately 50 mm in size, similar benefit of this invention is expected for smaller or larger seed such as 1", 2", 4", 6".

[0048] A bulk crystal as described, as made, or as used in any of the description above may have a thickness greater than or equal to: 1mm, 2mm, 3mm, 4mm, 5mm, 6mm, 7mm, 8mm, 9mm, 10mm, for instance.

Claims

WHAT IS CLAIMED IS:

1. A method of growing a bulk crystal of group III nitride having a composition of GaxiAlyilni-xi-yiN (0<xl<l, 0<xl+yl<l) comprising:

(a) measuring x-ray rocking curves of the seed crystal at more than one point;

(b) quantifying peak widths of the measured x-ray rocking curves;

(c) comparing a measure of the distribution of the quantified peak widths to an acceptable value; and

(d) growing single crystal GaxiAl_yiIni-xi-_yiN on a face of the seed crystal having the acceptable value of the distribution of quantified peak widths to form the bulk crystal of group III nitride.

2. A method according to claim 1, wherein the method of quantifying the peak widths comprises calculating a full width half maximum of peaks of the x-ray rocking curves.

3. A method according to claim 1 or claim 2, wherein the distribution of the

quantified peak widths is determined with a standard deviation.

4. A method according to claim 3, wherein the standard deviation is less than 30 % of the mean value of the quantified peak widths.

5. A method according to claim 3, wherein the standard deviation is less than 20 % of the mean value of the quantified peak widths.

6. A method according to claim 3, wherein the standard deviation is less than 10 % of the mean value of the quantified peak widths.

7. A method according to any one of claim 1 through claim 6, wherein the seed

crystal is primarily c-plane oriented and the x-ray rocking curves are measured on one or more off-axis planes.

8. A method according to claim 7, wherein the x-ray rocking curves are measured in the m-direction.

9. A method according to claim 7, wherein the off-axis plane is 201 reflection.

10. A method according to claim 7, wherein the off-axis plane is 102 reflection.

11. A method according to any one of claim 1 through claim 10, wherein the seed crystal is gallium nitride.

12. A method according to any one of claim 1 through claim 11, wherein the group III nitride is GaN.

13. A method according to any one of claim 1 through claim 12, wherein the group III nitride is grown in supercritical ammonia.

14. A method according to any one of claim 1 through claim 13, wherein the bulk crystal of group III nitride has crack density less than 1 cm^"2.

15. A method of selecting a seed crystal for growing bulk crystal of group III nitride having a composition of GaxiAl_yiIni-xi-_yiN (0<xl<l, 0<xl+yl<l) comprising,

(a) measuring x-ray rocking curves of a seed crystal at more than one point;

(b) quantifying peak widths of the measured x-ray rocking curves;

(d) designating the seed crystal as acceptable or unacceptable based on said measure of the distribution of quantified peak widths.

16. A method according to claim 15, wherein the method of quantifying the peak widths comprises calculating a full width half maximum of peaks of the x-ray rocking curves.

17. A method according to claim 15 or claim 16, wherein the distribution of the

quantified peak widths is determined with a standard deviation.

18. A method according to claim 17, wherein the standard deviation is less than 30 % of the mean value of the quantified peak widths.

19. A method according to claim 17, wherein the standard deviation is less than 20 % of the mean value of the quantified peak widths.

20. A method according to claim 17, wherein the standard deviation is less than 10 % of the mean value of the quantified peak widths.

21. A method according to any one of claim 15 through claim 20, wherein the seed crystal is primarily c-plane oriented and the x-ray rocking curves are measured on one or more off-axis planes.

22. A method according to claim 21, wherein the x-ray rocking curves are measured in the m-direction.

23. A method according to claim 21, wherein the off-axis plane is 201 reflection.

24. A method according to claim 21, wherein the off-axis plane is 102 reflection.

25. A method according to any one of claim 15 through claim 24, wherein the seed crystal is gallium nitride.

26. A method according to any one of claim 15 through claim 25, wherein the group III nitride is GaN.

27. Bulk group III nitride grown by a method of any claim above.

28. A wafer of group III nitride formed by a method of any claim above.