Classifications

• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
  • C04B28/14—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements containing calcium sulfate cements
• • E—FIXED CONSTRUCTIONS
  • E04—BUILDING
  • E04C—STRUCTURAL ELEMENTS; BUILDING MATERIALS
  • E04C2/00—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels
  • E04C2/02—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by specified materials
  • E04C2/04—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by specified materials of concrete or other stone-like material; of asbestos cement; of cement and other mineral fibres
  • E04C2/043—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by specified materials of concrete or other stone-like material; of asbestos cement; of cement and other mineral fibres of plaster
• • E—FIXED CONSTRUCTIONS
  • E04—BUILDING
  • E04C—STRUCTURAL ELEMENTS; BUILDING MATERIALS
  • E04C2/00—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels
  • E04C2/02—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by specified materials
  • E04C2/04—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by specified materials of concrete or other stone-like material; of asbestos cement; of cement and other mineral fibres
  • E04C2/06—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by specified materials of concrete or other stone-like material; of asbestos cement; of cement and other mineral fibres reinforced
• • E—FIXED CONSTRUCTIONS
  • E04—BUILDING
  • E04C—STRUCTURAL ELEMENTS; BUILDING MATERIALS
  • E04C2/00—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels
  • E04C2/30—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by the shape or structure
  • E04C2/38—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by the shape or structure with attached ribs, flanges, or the like, e.g. framed panels
  • E04C2/386—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by the shape or structure with attached ribs, flanges, or the like, e.g. framed panels with a frame of unreconstituted or laminated wood
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
  • C04B2111/00474—Uses not provided for elsewhere in C04B2111/00
  • C04B2111/00612—Uses not provided for elsewhere in C04B2111/00 as one or more layers of a layered structure
  • C04B2111/0062—Gypsum-paper board like materials
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
  • C04B2111/00474—Uses not provided for elsewhere in C04B2111/00
  • C04B2111/00612—Uses not provided for elsewhere in C04B2111/00 as one or more layers of a layered structure
  • C04B2111/0062—Gypsum-paper board like materials
  • C04B2111/00629—Gypsum-paper board like materials the covering sheets being made of material other than paper

Definitions

• the present invention relates to timber frame-based partitions have improved resistance to deformation, in particular to partitions having improved resistance to wind loading.
• Gypsum sheathing boards are often less preferred for use in timber frame construction, because they do not provide the structure with sufficient resistance to wind loading to meet regulatory requirements. Therefore, other boards such as oriented strand board and plywood have previously been used.
• Resistance to wind loading is generally characterised through the racking strength of the board, that is, the ability of the board to resist shear loading in the plane of the board.
• the present invention may provide a partition for a building structure, the partition comprising a support frame and at least one plasterboard affixed to the support frame, wherein: the support frame comprises a plurality of elongate timber members; and the plasterboard comprises a gypsum matrix having fibres embedded therein in an amount of at least 1 wt% relative to the gypsum, the gypsum matrix further comprising a polymeric additive that is present in an amount of at least 1 wt% relative to the gypsum.
• the fibres are present in an amount of at least 3 wt% relative to the gypsum, more preferably in an amount of at least 5 wt% relative to the gypsum.
• the polymeric additive is present in an amount of at least 3 wt% relative to the gypsum, more preferably in an amount of at least 5 wt% relative to the gypsum.
• the fibre length is less than 20mm, preferably less than 15mm, more preferably less than 10mm.
• the fibre length is preferably greater than 1 mm.
• the fibres are glass fibres.
• the plasterboard is provided with a backing lamina such as a fibreglass sheet.
• the lamina represents a layer that provides a discrete component of the panel, that is, it is not integrally formed with the substrate. Effectively, there is a well-defined interface or boundary between the substrate and the lamina.
• the lamina has a thickness of at least 0.25 mm, preferably at least 0.5 mm, more preferably at least 1 mm. Typically, the thickness of the lamina is less than 4 mm, preferably less than 3 mm, more preferably less than 2.5 mm.
• the polymeric additive is a starch, In other cases, the polymeric additive is a synthetic polymer such as polyvinyl acetate.
• the racking stiffness of the partition measured in accordance with British standard BS EN 594: 1996 is greater than 1500 N/m, preferably greater than 2000N/m.
• the plasterboard is prepared through a process comprising mixing stucco and water to form a stucco slurry, and allowing the slurry to set.
• the plasterboard is distinguished from boards such as fibreboard, which are prepared through a process of mixing water, fibres and calcium dihydrate to form a slurry, heating the slurry to calcine the gypsum, removing water from the slurry to form a filter cake, and forming the filter cake into the desired shape prior to the complete setting of the calcined gypsum.
• Figure 1 shows a schematic elevation view of a test apparatus for measuring racking resistance.
• a 2400mm high x 2400 mm long test specimen 10 was constructed and placed within the test rig.
• the test specimen comprised a frame consisting of 90mm x 38mm cross-section timber top and bottom rails, and 90mm x 38mm cross-section timber studs extending therebetween at 600mm intervals.
• a head binder 12 was rigidly attached to the top and bottom rails.
• the test specimen was bolted into the test rig by means of bolts 13 inserted through the bottom rail of the frame.
• Plasterboard sheathing 14 was fixed to the frame in a single layer below the head binder.
• the boards were screw fixed with 41 mm British Gypsum drywall timber screws at 300mm intervals around the perimeter of the boards.
• a downward vertical pre-load F v was applied to the test specimen at the positions of the studs. This load was subsequently removed.
• a racking load F was applied horizontally to the top of the test specimen onto a metal plate 16 attached to the top rail of the panel and the head binder. The deformation d of the board was measured as the displacement at transducer A minus the displacement at transducer B
• the racking stiffness is calculated as the ratio of racking load F to the deformation d of the board.
• a plasterboard having a gypsum core containing the following additional components:
• the board has a thickness of 12.5 mm and a weight of 12.3 kg/m 2 .
• the board has a liner provided by a pre-coated glass mat having a weight of 360 g/m 2 and a mineral coating.
• a plasterboard having a gypsum core containing the following additional components:
• the plasterboard has a paper liner on both sides of the board, the liner having a weight of 240 g/m 2 , and additionally a backing lamina provided by a 1.5 mm fibre glass sheet.
• the total thickness of the composite board (including the gypsum board and the backing lamina) is 15 mm.
• the total weight of the composite board is 15.6 kg/m 2 .
• a plasterboard having a gypsum core containing the following additional components:
• the plasterboard has a paper liner on each side of the board.
• the weight of the paper liner is 190 g/m 2 on the side of the board facing away from the support frame and 180 g/m 2 on the side of the board facing towards the support frame. It is 12.5mm thick product with a weight of approx. 12 kg/m 2 .
• the board has a liner provided by a pre-coated glass mat.
• the weight of the board is 1 1 kg/m 2 .

Landscapes

• Engineering & Computer Science (AREA)
• Architecture (AREA)
• Structural Engineering (AREA)
• Chemical & Material Sciences (AREA)
• Civil Engineering (AREA)
• Ceramic Engineering (AREA)
• Inorganic Chemistry (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Materials Engineering (AREA)
• Organic Chemistry (AREA)
• Panels For Use In Building Construction (AREA)
• Building Environments (AREA)
• Curing Cements, Concrete, And Artificial Stone (AREA)
• Rod-Shaped Construction Members (AREA)

Priority Applications (5)

Applications Claiming Priority (2)

Publications (1)

Family

ID=52001178

Family Applications (1)

Country Status (10)

Cited By (2)

Citations (3)

Family Cites Families (11)

• 2014
  • 2014-10-09 GB GBGB1417904.8A patent/GB201417904D0/en not_active Ceased
• 2015
  • 2015-10-08 TW TW104133195A patent/TW201623767A/zh unknown
  • 2015-10-09 JP JP2017518266A patent/JP2017536316A/ja active Pending
  • 2015-10-09 EP EP15794612.0A patent/EP3204341A1/en not_active Withdrawn
  • 2015-10-09 AR ARP150103275A patent/AR102232A1/es unknown
  • 2015-10-09 WO PCT/GB2015/052971 patent/WO2016055809A1/en not_active Ceased
  • 2015-10-09 US US15/517,259 patent/US20170305794A1/en not_active Abandoned
  • 2015-10-09 CA CA2963192A patent/CA2963192A1/en not_active Abandoned
  • 2015-10-09 AU AU2015329731A patent/AU2015329731B2/en not_active Expired - Fee Related
  • 2015-10-09 MA MA040494A patent/MA40494A/fr unknown

Patent Citations (3)

Non-Patent Citations (1)

Also Published As

Similar Documents

Legal Events