WO2016033259A1 - Produits fluoro-minéraux pour inhiber la formation de dépôts de silice ou de silicate métallique ou pour éliminer ces dépôts - Google Patents

Produits fluoro-minéraux pour inhiber la formation de dépôts de silice ou de silicate métallique ou pour éliminer ces dépôts Download PDF

Info

Publication number
WO2016033259A1
WO2016033259A1 PCT/US2015/047065 US2015047065W WO2016033259A1 WO 2016033259 A1 WO2016033259 A1 WO 2016033259A1 US 2015047065 W US2015047065 W US 2015047065W WO 2016033259 A1 WO2016033259 A1 WO 2016033259A1
Authority
WO
WIPO (PCT)
Prior art keywords
composition
acid
cleaning
acid composition
equipment
Prior art date
Application number
PCT/US2015/047065
Other languages
English (en)
Inventor
Anthony G. Sommese
Jabir S. GILL
Thomas M. Miller
David Rodman
Carol B. Batton
John E. Hoots
Michael Patrick WEBERSKI, Jr.
Martin Ray GODFREY
Original Assignee
Ecolab Usa Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US14/469,323 external-priority patent/US9404067B2/en
Priority to CA2996063A priority Critical patent/CA2996063C/fr
Priority to EP15836029.7A priority patent/EP3245270B1/fr
Priority to JP2017511270A priority patent/JP6820833B2/ja
Priority to AU2015308923A priority patent/AU2015308923B2/en
Priority to CR20170103A priority patent/CR20170103A/es
Application filed by Ecolab Usa Inc. filed Critical Ecolab Usa Inc.
Priority to ES15836029T priority patent/ES2839207T3/es
Priority to NZ729498A priority patent/NZ729498A/en
Priority to MX2017002440A priority patent/MX2017002440A/es
Priority to EP20172655.1A priority patent/EP3708633A1/fr
Publication of WO2016033259A1 publication Critical patent/WO2016033259A1/fr
Priority to PH12017500355A priority patent/PH12017500355A1/en
Priority to AU2019271980A priority patent/AU2019271980B2/en
Priority to AU2022203865A priority patent/AU2022203865B2/en

Abstract

La présente invention concerne d'une manière générale des procédés pour éliminer des dépôts et inhiber leur formation, pour réduire le pH de mélanges aqueux, et pour augmenter la récupération de pétrole brut depuis des formations souterraines, les procédés comprenant les étapes consistant à mettre en contact une composition acide avec un liquide qui est en contact avec une surface métallique ou avec un puits ou une formation.
PCT/US2015/047065 2014-08-26 2015-08-27 Produits fluoro-minéraux pour inhiber la formation de dépôts de silice ou de silicate métallique ou pour éliminer ces dépôts WO2016033259A1 (fr)

Priority Applications (12)

Application Number Priority Date Filing Date Title
EP20172655.1A EP3708633A1 (fr) 2015-08-18 2015-08-27 Methode d'obtention de naphte
NZ729498A NZ729498A (en) 2014-08-26 2015-08-27 Fluro-inorganics for inhibiting or removing silica or metal silicate deposits
JP2017511270A JP6820833B2 (ja) 2015-08-18 2015-08-27 シリカまたは金属ケイ酸塩析出物を抑制または除去するためのフルオロ無機物
AU2015308923A AU2015308923B2 (en) 2014-08-26 2015-08-27 Fluro-inorganics for inhibiting or removing silica or metal silicate deposits
CR20170103A CR20170103A (es) 2014-08-26 2015-08-27 Fluro-inorgánicos para inhibir o eliminar los depósitos de sílice o silicato metálico
CA2996063A CA2996063C (fr) 2014-08-26 2015-08-27 Produits fluoro-mineraux pour inhiber la formation de depots de silice ou de silicate metallique ou pour eliminer ces depots
ES15836029T ES2839207T3 (es) 2015-08-18 2015-08-27 Compuestos inorgánicos de flúor para inhibir o eliminar los depósitos de sílice o de silicato de metal
EP15836029.7A EP3245270B1 (fr) 2015-08-18 2015-08-27 Produits fluoro-minéraux pour inhiber la formation de dépôts de silice ou de silicate métallique ou pour éliminer ces dépôts
MX2017002440A MX2017002440A (es) 2014-08-26 2015-08-27 Fluoro-inorganicos para inhibir o remover depositos de silice o silicato metalico.
PH12017500355A PH12017500355A1 (en) 2014-08-26 2017-02-27 Fluro-inorganics for inhibiting or removing silica or metal silicate deposits
AU2019271980A AU2019271980B2 (en) 2014-08-26 2019-11-27 Fluro-inorganics for inhibiting or removing silica or metal silicate deposits
AU2022203865A AU2022203865B2 (en) 2014-08-26 2022-06-03 Fluro-inorganics for inhibiting or removing silica or metal silicate deposits

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
US14/469,323 2014-08-26
US14/469,323 US9404067B2 (en) 2014-08-26 2014-08-26 Fluoro-inorganics for inhibiting or removing silica or metal silicate deposits
US201562206669P 2015-08-18 2015-08-18
US201562206658P 2015-08-18 2015-08-18
US62/206,669 2015-08-18
US62/206,658 2015-08-18

Publications (1)

Publication Number Publication Date
WO2016033259A1 true WO2016033259A1 (fr) 2016-03-03

Family

ID=55400541

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2015/047065 WO2016033259A1 (fr) 2014-08-26 2015-08-27 Produits fluoro-minéraux pour inhiber la formation de dépôts de silice ou de silicate métallique ou pour éliminer ces dépôts

Country Status (9)

Country Link
AU (3) AU2015308923B2 (fr)
CA (2) CA3201890A1 (fr)
CR (1) CR20170103A (fr)
GT (1) GT201700038A (fr)
MX (2) MX2017002440A (fr)
NZ (1) NZ729498A (fr)
PH (1) PH12017500355A1 (fr)
SV (1) SV2017005394A (fr)
WO (1) WO2016033259A1 (fr)

Cited By (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2019523347A (ja) * 2016-07-29 2019-08-22 エコラブ ユーエスエイ インク 腐食軽減のためのベンゾトリアゾールおよびトリルトリアゾール誘導体
WO2020197559A1 (fr) * 2019-03-28 2020-10-01 Ecolab Usa Inc. Mélanges synergiques de composés inorganiques fluorés et d'acides inorganiques pour l'élimination de dépôts et la stimulation de puits géothermiques
WO2020198839A1 (fr) 2019-04-05 2020-10-08 Fluid Energy Group Ltd. Composition d'acide de boue comprenant de l'acide fluorhydrique inhibé
WO2020248740A1 (fr) * 2019-06-10 2020-12-17 中国石油大学(华东) Procédé de réalisation de régulation d'obturation intégrale pour la pénétration d'eau et la canalisation de vapeur d'un réservoir de pétrole lourd avec eau de bordure/fond
WO2021021860A1 (fr) * 2019-07-30 2021-02-04 Solenis Technologies Cayman, L.P. Inhibiteurs de tartre de silice
US20220325169A1 (en) * 2019-08-12 2022-10-13 Solugen, Inc. Multifunctional additive for use in wellbore servicing
US11518936B2 (en) 2019-04-05 2022-12-06 Fluid Energy Group Ltd Inhibited hydrofluoric acid composition
US11525085B2 (en) 2020-06-12 2022-12-13 Fluid Energy Group Ltd. Process to manufacture novel inhibited hydrofluoric acid composition
RU2816422C2 (ru) * 2019-07-30 2024-03-28 Соленис Текнолоджиз Кеймэн, Л.П. Ингибиторы образования отложений диоксида кремния
US11981578B2 (en) 2019-04-05 2024-05-14 Dorf Ketal Chemicals Fze Inhibited hydrofluoric acid composition

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10329674B2 (en) * 2016-12-01 2019-06-25 Vitech International, Inc. Fluorinated acid compounds, compositions and methods of use

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1995016006A1 (fr) * 1993-12-10 1995-06-15 Armor All Products Corporation Composition contenant des sels de fluorures acides pour le nettoyage de roues de vehicules
US5571447A (en) 1995-03-20 1996-11-05 Ashland Inc. Stripping and cleaning composition
WO2001070922A1 (fr) 2000-03-21 2001-09-27 Bbj Environmental Solutions Inc. Composition de nettoyage aqueuse a ph regule
US8034253B2 (en) * 2004-11-12 2011-10-11 Battelle Memorial Insitute Decontaminant
US8389453B2 (en) 2007-11-07 2013-03-05 Vitech International, Inc. Tetrafluoroborate compounds, compositions and related methods of use

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3889753A (en) * 1974-02-21 1975-06-17 Shell Oil Co Buffer regulated mud acid
US4479543A (en) * 1983-07-28 1984-10-30 Union Oil Company Of California Method for deeper penetrating acidizing of siliceous formations
US4703803A (en) * 1986-06-24 1987-11-03 Cities Service Oil & Gas Corporation Composition and method for slowly dissolving siliceous material
US6924253B2 (en) * 2000-04-07 2005-08-02 Bentley J. Palmer Scale removal
US7192908B2 (en) * 2003-04-21 2007-03-20 Schlumberger Technology Corporation Composition and method for treating a subterranean formation
US9027647B2 (en) * 2006-08-04 2015-05-12 Halliburton Energy Services, Inc. Treatment fluids containing a biodegradable chelating agent and methods for use thereof
US7712536B2 (en) * 2007-11-29 2010-05-11 Schlumberger Technology Corporation Filtercake removal
US8316941B2 (en) * 2008-01-24 2012-11-27 Schlumberger Technology Corporation Method for single-stage treatment of siliceous subterranean formations
WO2015126397A1 (fr) * 2014-02-20 2015-08-27 Halliburton Energy Services, Inc. Composition d'acidification pratiquement solide servant au traitement de formations souterraines

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1995016006A1 (fr) * 1993-12-10 1995-06-15 Armor All Products Corporation Composition contenant des sels de fluorures acides pour le nettoyage de roues de vehicules
US5571447A (en) 1995-03-20 1996-11-05 Ashland Inc. Stripping and cleaning composition
WO2001070922A1 (fr) 2000-03-21 2001-09-27 Bbj Environmental Solutions Inc. Composition de nettoyage aqueuse a ph regule
US8034253B2 (en) * 2004-11-12 2011-10-11 Battelle Memorial Insitute Decontaminant
US8389453B2 (en) 2007-11-07 2013-03-05 Vitech International, Inc. Tetrafluoroborate compounds, compositions and related methods of use
US8796195B2 (en) 2007-11-07 2014-08-05 Vitech International, Inc. Tetrafluoroborate compounds, compositions and related methods of use

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
HEINS, W.: "Technical Advancements in SAGD Evaporative Produced Water Treatment", INTERNATIONAL WATER CONFERENCE IN SAN ANTONIO, TEXAS, 2008

Cited By (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2019523347A (ja) * 2016-07-29 2019-08-22 エコラブ ユーエスエイ インク 腐食軽減のためのベンゾトリアゾールおよびトリルトリアゾール誘導体
JP7026672B2 (ja) 2016-07-29 2022-02-28 エコラブ ユーエスエイ インク 腐食軽減のためのベンゾトリアゾールおよびトリルトリアゾール誘導体
WO2020197559A1 (fr) * 2019-03-28 2020-10-01 Ecolab Usa Inc. Mélanges synergiques de composés inorganiques fluorés et d'acides inorganiques pour l'élimination de dépôts et la stimulation de puits géothermiques
US12037538B2 (en) 2019-03-28 2024-07-16 Ecolab Usa Inc. Synergistic blends of fluoro-inorganics and inorganic acids for removing deposits and stimulating geothermal wells
US11725135B2 (en) 2019-04-05 2023-08-15 Dorf Ketal Chemicals Fze Mud acid composition and methods of using such
WO2020198839A1 (fr) 2019-04-05 2020-10-08 Fluid Energy Group Ltd. Composition d'acide de boue comprenant de l'acide fluorhydrique inhibé
US11370961B2 (en) 2019-04-05 2022-06-28 Fluid Energy Group Ltd. Mud acid composition and methods of using such
US11981578B2 (en) 2019-04-05 2024-05-14 Dorf Ketal Chemicals Fze Inhibited hydrofluoric acid composition
US11518936B2 (en) 2019-04-05 2022-12-06 Fluid Energy Group Ltd Inhibited hydrofluoric acid composition
WO2020248740A1 (fr) * 2019-06-10 2020-12-17 中国石油大学(华东) Procédé de réalisation de régulation d'obturation intégrale pour la pénétration d'eau et la canalisation de vapeur d'un réservoir de pétrole lourd avec eau de bordure/fond
US11897801B2 (en) 2019-07-30 2024-02-13 Solenis Technologies, L.P. Silica scale inhibitors
RU2816422C2 (ru) * 2019-07-30 2024-03-28 Соленис Текнолоджиз Кеймэн, Л.П. Ингибиторы образования отложений диоксида кремния
WO2021021860A1 (fr) * 2019-07-30 2021-02-04 Solenis Technologies Cayman, L.P. Inhibiteurs de tartre de silice
US20220325169A1 (en) * 2019-08-12 2022-10-13 Solugen, Inc. Multifunctional additive for use in wellbore servicing
US11525085B2 (en) 2020-06-12 2022-12-13 Fluid Energy Group Ltd. Process to manufacture novel inhibited hydrofluoric acid composition

Also Published As

Publication number Publication date
CA2996063C (fr) 2023-08-08
AU2019271980B2 (en) 2022-03-03
MX2022013377A (es) 2022-11-30
AU2022203865B2 (en) 2024-01-11
CR20170103A (es) 2017-07-21
GT201700038A (es) 2019-09-20
AU2015308923A1 (en) 2017-03-16
PH12017500355A1 (en) 2017-07-10
CA3201890A1 (fr) 2016-03-03
CA2996063A1 (fr) 2016-03-03
MX2017002440A (es) 2017-05-19
SV2017005394A (es) 2018-02-26
AU2022203865A1 (en) 2022-06-30
NZ729498A (en) 2023-09-29
AU2015308923B2 (en) 2019-08-29
AU2019271980A1 (en) 2020-01-02

Similar Documents

Publication Publication Date Title
AU2022203865B2 (en) Fluro-inorganics for inhibiting or removing silica or metal silicate deposits
JP7483576B2 (ja) シリカまたは金属ケイ酸塩析出物を抑制または除去するためのフルオロ無機物
US20170051194A1 (en) Fluoro-inorganics for acidification or neutralization of water systems
US10035949B2 (en) Fluoro-inorganics for well cleaning and rejuvenation
US9404067B2 (en) Fluoro-inorganics for inhibiting or removing silica or metal silicate deposits
EP3491171B1 (fr) Dérivés de benzotriazole et de tolyltriazole destinés à atténuer la corrosion
US9221701B2 (en) Methods for reducing scale formation on and removing deposits from heat transfer surfaces
US20220411295A1 (en) Multifunctional additive
US9932255B2 (en) Metal silicate and organic deposit inhibitor/dispersant for thermal recovery operations of hydrocarbon fuels
RU2350880C1 (ru) Способ очистки от отложений на внутренних стенках теплообменного аппарата системы охлаждения природного газа
WO2016049735A1 (fr) Compositions d'acide synthétique et leurs utilisations
Majnouni et al. Improved Performance In Steam Plants With New Guidelines For Corrosion And Scale Control: An Overview
CA2866522A1 (fr) Compositions d'acide synthetique et leurs utilisations
CA2886149A1 (fr) Compositions d'acide synthetique et leurs utilisations

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15836029

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: MX/A/2017/002440

Country of ref document: MX

ENP Entry into the national phase

Ref document number: 2017511270

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 12017500355

Country of ref document: PH

REEP Request for entry into the european phase

Ref document number: 2015836029

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 2015836029

Country of ref document: EP

ENP Entry into the national phase

Ref document number: 2015308923

Country of ref document: AU

Date of ref document: 20150827

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: 2017103

Country of ref document: CR

Ref document number: CR2017-000103

Country of ref document: CR

ENP Entry into the national phase

Ref document number: 2996063

Country of ref document: CA