WO2016009801A1 - Gas barrier film and electronic device - Google Patents
Gas barrier film and electronic device Download PDFInfo
- Publication number
- WO2016009801A1 WO2016009801A1 PCT/JP2015/068227 JP2015068227W WO2016009801A1 WO 2016009801 A1 WO2016009801 A1 WO 2016009801A1 JP 2015068227 W JP2015068227 W JP 2015068227W WO 2016009801 A1 WO2016009801 A1 WO 2016009801A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- gas barrier
- film
- anchor coat
- coat layer
- Prior art date
Abstract
Description
本発明のガスバリア性フィルムに用いられる基材としては、例えば、シリコン等の金属基板、ガラス基板、セラミックス基板、プラスチックフィルム等が挙げられるが、好ましくはプラスチックフィルムが用いられる。用いられるプラスチックフィルムは、バリア層、クリアハードコート層等を保持できるフィルムであれば材質、厚み等に特に制限はなく、使用目的等に応じて適宜選択することができる。前記プラスチックフィルムとしては、具体的には、ポリエステル樹脂、メタクリル樹脂、メタクリル酸-マレイン酸共重合体、ポリスチレン樹脂、透明フッ素樹脂、ポリイミド、フッ素化ポリイミド樹脂、ポリアミド樹脂、ポリアミドイミド樹脂、ポリエーテルイミド樹脂、セルロースアシレート樹脂、ポリウレタン樹脂、ポリエーテルエーテルケトン樹脂、ポリカーボネート樹脂、脂環式ポリオレフィン樹脂、ポリアリレート樹脂、ポリエーテルスルホン樹脂、ポリスルホン樹脂、シクロオレフィルンコポリマー、フルオレン環変性ポリカーボネート樹脂、脂環変性ポリカーボネート樹脂、フルオレン環変性ポリエステル樹脂、アクリロイル化合物などの熱可塑性樹脂が挙げられる。 [Base material]
Examples of the base material used in the gas barrier film of the present invention include a metal substrate such as silicon, a glass substrate, a ceramic substrate, a plastic film, and the like, and a plastic film is preferably used. The plastic film to be used is not particularly limited in material, thickness and the like as long as it can hold a barrier layer, a clear hard coat layer, and the like, and can be appropriately selected according to the purpose of use. Specific examples of the plastic film include polyester resin, methacrylic resin, methacrylic acid-maleic acid copolymer, polystyrene resin, transparent fluororesin, polyimide, fluorinated polyimide resin, polyamide resin, polyamideimide resin, and polyetherimide. Resin, Cellulose acylate resin, Polyurethane resin, Polyether ether ketone resin, Polycarbonate resin, Alicyclic polyolefin resin, Polyarylate resin, Polyether sulfone resin, Polysulfone resin, Cycloolefin copolymer, Fluorene ring modified polycarbonate resin, Alicyclic Examples thereof include thermoplastic resins such as modified polycarbonate resins, fluorene ring-modified polyester resins, and acryloyl compounds.
アンカーコート層は、ポリシラザン化合物を含む塗布液を基材上に塗布し、得られたポリシラザンを含有する層にエネルギーを印加し改質処理して得られる層である。また、本発明に係るアンカーコート層は、アンカーコート層の厚さをA(nm)とし、アンカーコート層全体のN/Si比率をBとしたときに、A×B≦60である。該アンカーコート層は、単層でもよいし、2層以上の積層構造であってもよい。 [Anchor coat layer]
The anchor coat layer is a layer obtained by applying a coating solution containing a polysilazane compound on a substrate and applying energy to the resulting polysilazane-containing layer for modification treatment. In the anchor coat layer according to the present invention, A × B ≦ 60, where A (nm) is the thickness of the anchor coat layer and B is the N / Si ratio of the entire anchor coat layer. The anchor coat layer may be a single layer or a laminated structure of two or more layers.
ポリシラザンを含有する層の改質処理時にN/Si比率を低減させる方法としては、ポリシラザンを含有する層の膜厚を10~130nm程度の薄層とする方法が挙げられる。 (1) Method of reducing the N / Si ratio during the modification treatment of the layer containing polysilazane As a method of reducing the N / Si ratio during the modification treatment of the layer containing polysilazane, the film thickness of the layer containing polysilazane Is a thin layer of about 10 to 130 nm.
ポリシラザンを含有する層の改質処理後にエイジング(加温、加湿)を行うことによって、アンカーコート層のN/Si比率を調整することができる。エイジングの条件としては、40~90℃で、相対湿度40~100%RHで、1時間~10日間のエイジングを行うことが好ましい。 (2) Method of performing aging after the modification treatment of the layer containing polysilazane By adjusting the N / Si ratio of the anchor coat layer by performing aging (heating, humidification) after the modification treatment of the layer containing polysilazane. be able to. As aging conditions, it is preferable to perform aging at 40 to 90 ° C. and
改質処理の照射エネルギー量を一回の改質処理として印加するよりも、複数回に分割して改質処理を行うことで、N/Si比率を大きく低減させることができるため好ましい。改質処理の回数としては、2~10回が好ましい。例えば、2回改質処理を行う場合、改質処理の間隔は6時間以上であることが好ましく、12時間以上であることがより好ましい。2回改質処理を行う場合の間隔の上限は特に制限されないが、工程コスト面や上述のエイジング効果との関係から、7日以内であることが好ましい。この態様におけるポリシラザンを含有する層の膜厚は、同様に好ましいN/Si比率にまで酸化を進行させるという観点から、好ましくは40~500nm、より好ましくは60~400nmである。 (3) Method of performing additional modification process after modification process of layer containing polysilazane Rather than applying the amount of irradiation energy of modification process as one modification process, the modification process is divided into multiple times Is preferable because the N / Si ratio can be greatly reduced. The number of reforming treatments is preferably 2 to 10 times. For example, when the reforming process is performed twice, the interval between the reforming processes is preferably 6 hours or more, and more preferably 12 hours or more. The upper limit of the interval when performing the twice reforming treatment is not particularly limited, but is preferably within 7 days from the viewpoint of process cost and the above-mentioned aging effect. The film thickness of the polysilazane-containing layer in this embodiment is preferably 40 to 500 nm, more preferably 60 to 400 nm, from the viewpoint that oxidation proceeds to a preferable N / Si ratio.
ポリシラザンにアルミニウム化合物を添加した層を改質処理することにより、ポリシラザンの改質が著しく進行し、N/Si比率をほぼ0とすることができるとともに、ガスバリア性を有するアンカーコート層を得ることができる。 (4) Method of modifying the layer in which the aluminum compound is added to polysilazane By modifying the layer in which the aluminum compound is added to polysilazane, the modification of the polysilazane proceeds remarkably, and the N / Si ratio is almost zero. In addition, an anchor coat layer having gas barrier properties can be obtained.
・装置:アルバックファイ製QUANTERASXM
・X線源:単色化Al-Kα
・測定領域:Si2p、C1s、N1s、O1s
・スパッタイオン:Ar(2keV)
・デプスプロファイル:一定時間スパッタ後、測定を繰り返す。1回の測定は、SiO2換算で約2.8nmとなるようにスパッタ時間を調整する
・定量:バックグラウンドをShirley法で求め、得られたピーク面積から相対感度係数法を用いて定量した。データ処理は、アルバックファイ社製のMultiPakを用いた。 << XPS analysis conditions >>
・ Equipment: ULVAC-PHI QUANTERASXM
・ X-ray source: Monochromatic Al-Kα
Measurement area: Si2p, C1s, N1s, O1s
・ Sputtering ion: Ar (2 keV)
Depth profile: repeats measurement after sputtering for a certain time. In one measurement, the sputtering time is adjusted so as to be about 2.8 nm in terms of SiO 2. Quantification: The background was obtained by the Shirley method, and quantified using the relative sensitivity coefficient method from the obtained peak area. For data processing, MultiPak manufactured by ULVAC-PHI was used.
本発明に係るアンカーコート層は、成膜性、クラック等の欠陥が少ないことからポリシラザンを含有する塗布液を塗布して形成される塗膜に、さらにエネルギーを印加して形成する方法(塗膜形成法)により形成される。以下、塗膜形成法を説明する。 <Coating method>
The anchor coat layer according to the present invention is formed by applying energy to a coating film formed by applying a coating liquid containing polysilazane since the defects such as film formability and cracks are few (coating film) Forming method). Hereinafter, the coating film forming method will be described.
アンカーコート層形成用塗布液を調製するための溶剤としては、ポリシラザンを溶解できるものであれば特に制限されないが、ポリシラザンと容易に反応してしまう水および反応性基(例えば、ヒドロキシル基、あるいはアミン基等)を含まず、ポリシラザンに対して不活性の有機溶剤が好ましく、非プロトン性の有機溶剤がより好ましい。具体的には、溶剤としては、非プロトン性溶剤;例えば、ペンタン、ヘキサン、シクロヘキサン、トルエン、キシレン、ソルベッソ、ターペン等の、脂肪族炭化水素、脂環式炭化水素、芳香族炭化水素等の炭化水素溶媒;塩化メチレン、トリクロロエタン等のハロゲン炭化水素溶媒;酢酸エチル、酢酸ブチル等のエステル類;アセトン、メチルエチルケトン等のケトン類;ジブチルエーテル、ジオキサン、テトラヒドロフラン等の脂肪族エーテル、脂環式エーテル等のエーテル類:例えば、テトラヒドロフラン、ジブチルエーテル、モノ-およびポリアルキレングリコールジアルキルエーテル(ジグライム類)などを挙げることができる。上記溶剤は、ケイ素化合物の溶解度や溶剤の蒸発速度等の目的にあわせて選択され、単独で使用されてもまたは2種以上の混合物の形態で使用されてもよい。 (Coating solution for anchor coat layer formation)
The solvent for preparing the coating solution for forming the anchor coat layer is not particularly limited as long as it can dissolve polysilazane, but water and reactive groups (for example, hydroxyl group or amine) that easily react with polysilazane. An organic solvent inert to polysilazane, and more preferably an aprotic organic solvent. Specifically, the solvent is an aprotic solvent; for example, carbon such as aliphatic hydrocarbons, alicyclic hydrocarbons, aromatic hydrocarbons such as pentane, hexane, cyclohexane, toluene, xylene, solvesso, terpenes, etc. Hydrogen solvents; Halogen hydrocarbon solvents such as methylene chloride and trichloroethane; Esters such as ethyl acetate and butyl acetate; Ketones such as acetone and methyl ethyl ketone; Aliphatic ethers such as dibutyl ether, dioxane and tetrahydrofuran; Alicyclic ethers and the like Ethers: Examples include tetrahydrofuran, dibutyl ether, mono- and polyalkylene glycol dialkyl ethers (diglymes), and the like. The solvent is selected according to purposes such as the solubility of the silicon compound and the evaporation rate of the solvent, and may be used alone or in the form of a mixture of two or more.
ポリシラザンを含有する層は、上記のアンカーコート層形成用塗布液を基材上に塗布することによって形成することができる。塗布方法としては、従来公知の適切な湿式塗布方法が採用され得る。具体例としては、スピンコート法、ロールコート法、フローコート法、インクジェット法、スプレーコート法、プリント法、ディップコート法、流延成膜法、バーコート法、ダイコート法、グラビア印刷法等が挙げられる。 (Method for forming a layer containing polysilazane)
The layer containing polysilazane can be formed by applying the above-described coating liquid for forming an anchor coat layer on a substrate. As a coating method, a conventionally known appropriate wet coating method can be adopted. Specific examples include spin coating method, roll coating method, flow coating method, ink jet method, spray coating method, printing method, dip coating method, casting film forming method, bar coating method, die coating method, gravure printing method and the like. It is done.
続いて、上記のようにして形成されたポリシラザンを含有する層に対して、エネルギーを印加し、ポリシラザンの改質処理を行い、アンカーコート層への改質を行う。 <Application of energy>
Subsequently, energy is applied to the polysilazane-containing layer formed as described above to modify the polysilazane and modify the anchor coat layer.
本発明において、改質処理として用いることのできるプラズマ処理は、公知の方法を用いることができるが、好ましくは大気圧プラズマ処理等を挙げることが出来る。大気圧近傍でのプラズマCVD処理を行う大気圧プラズマCVD法は、真空下のプラズマCVD法に比べ、減圧にする必要がなく生産性が高いだけでなく、プラズマ密度が高密度であるために成膜速度が速く、さらには通常のCVD法の条件に比較して、大気圧下という高圧力条件では、ガスの平均自由工程が非常に短いため、極めて均質の膜が得られる。 (Plasma treatment)
In the present invention, a known method can be used as the plasma treatment that can be used as the modification treatment, and an atmospheric pressure plasma treatment or the like can be preferably used. The atmospheric pressure plasma CVD method, which performs plasma CVD processing near atmospheric pressure, does not need to be reduced in pressure and is more productive than the plasma CVD method under vacuum. The film speed is high, and further, under a high pressure condition under atmospheric pressure as compared with the conditions of a normal CVD method, the gas mean free process is very short, so that a very homogeneous film can be obtained.
改質処理の方法の1つとして、紫外線照射による処理が好ましい。紫外線(紫外光と同義)によって生成されるオゾンや活性酸素原子は高い酸化能力を有しており、低温で高い緻密性と絶縁性を有する酸化ケイ素膜または酸窒化ケイ素膜を形成することが可能である。 (UV irradiation treatment)
As one of the modification treatment methods, treatment by ultraviolet irradiation is preferable. Ozone and active oxygen atoms generated by ultraviolet rays (synonymous with ultraviolet light) have high oxidation ability, and can form silicon oxide films or silicon oxynitride films with high density and insulation at low temperatures It is.
本発明において、アンカーコート層の最も好ましい改質処理方法は、真空紫外線照射による処理(エキシマ照射処理)である。真空紫外線照射による処理は、ポリシラザン化合物内の原子間結合力より大きい100~200nmの光エネルギーを用い、好ましくは100~180nmの波長の光エネルギーを用い、原子の結合を光量子プロセスと呼ばれる光子のみの作用により、直接切断しながら活性酸素やオゾンによる酸化反応を進行させることで、比較的低温(約200℃以下)で、酸化ケイ素膜の形成を行う方法である。 (Vacuum ultraviolet irradiation treatment: excimer irradiation treatment)
In the present invention, the most preferable modification treatment method for the anchor coat layer is a treatment by vacuum ultraviolet irradiation (excimer irradiation treatment). The treatment by the vacuum ultraviolet irradiation uses light energy of 100 to 200 nm, preferably light energy of a wavelength of 100 to 180 nm, which is larger than the interatomic bonding force in the polysilazane compound, and bonds atoms with only photons called photon processes. This is a method of forming a silicon oxide film at a relatively low temperature (about 200 ° C. or lower) by causing an oxidation reaction with active oxygen or ozone to proceed while cutting directly by action.
本発明に係るガスバリア性フィルムは、上記アンカーコート層の上部に、前記アンカーコート層に接しており、真空成膜法により形成されるガスバリア層を有する。 [Gas barrier layer]
The gas barrier film according to the present invention has a gas barrier layer which is in contact with the anchor coat layer and formed by a vacuum film formation method on the anchor coat layer.
物理気相成長法(Physical Vapor Deposition、PVD法)は、気相中で物質の表面に物理的手法により、目的とする物質、例えば、炭素膜等の薄膜を堆積する方法であり、例えば、スパッタ法(DCスパッタ法、RFスパッタ法、イオンビームスパッタ法、およびマグネトロンスパッタ法等)、真空蒸着法、イオンプレーティング法などが挙げられる。 <Gas deposition method>
The physical vapor deposition method (PVD method) is a method of depositing a target material, for example, a thin film such as a carbon film, on the surface of the material in a gas phase by a physical method. Examples thereof include a DC sputtering method, an RF sputtering method, an ion beam sputtering method, and a magnetron sputtering method, a vacuum deposition method, and an ion plating method.
本発明のガスバリア性フィルムにおいては、種々の機能を有する層を設けることができる。 [Layers with various functions]
In the gas barrier film of the present invention, layers having various functions can be provided.
本発明のガスバリア性フィルムにおいては、基材上には、クリアハードコート層が設けられていてもよい。 (Clear hard coat layer)
In the gas barrier film of the present invention, a clear hard coat layer may be provided on the substrate.
本発明のガスバリア性フィルムは、上記基材の上記アンカーコート層を設けた面とは反対側の面にブリードアウト防止層を有してもよい。 (Bleed-out prevention layer)
The gas barrier film of the present invention may have a bleed-out preventing layer on the surface of the substrate opposite to the surface on which the anchor coat layer is provided.
本発明のガスバリア性フィルムは、空気中の化学成分(酸素、水、窒素酸化物、硫黄酸化物、オゾン等)によって性能が劣化するデバイスに好ましく適用できる。すなわち、本発明は、本発明のガスバリア性フィルムと、該ガスバリア性フィルム上に形成される電子デバイス本体と、を含む電子デバイスを提供する。 [Electronic device body]
The gas barrier film of the present invention can be preferably applied to a device whose performance is deteriorated by chemical components (oxygen, water, nitrogen oxide, sulfur oxide, ozone, etc.) in the air. That is, this invention provides the electronic device containing the gas barrier film of this invention, and the electronic device main body formed on this gas barrier film.
(2)陽極/正孔輸送層/発光層/陰極
(3)陽極/発光層/電子輸送層/陰極
(4)陽極/正孔輸送層/発光層/電子輸送層/陰極
(5)陽極/陽極バッファー層(正孔注入層)/正孔輸送層/発光層/電子輸送層/陰極バッファー層(電子注入層)/陰極
(陽極)
有機EL素子における陽極(透明電極)としては、仕事関数の大きい(4eV以上)金属、合金、電気伝導性化合物およびこれらの混合物を電極物質とするものが好ましく用いられる。このような電極物質の具体例としては、Au等の金属、CuI、インジウムチンオキシド(ITO)、SnO2、ZnO等の導電性透明材料が挙げられる。また、IDIXO(In2O3-ZnO)等非晶質で透明導電膜を作製可能な材料を用いてもよい。 (1) Anode / light emitting layer / cathode (2) Anode / hole transport layer / light emitting layer / cathode (3) Anode / light emitting layer / electron transport layer / cathode (4) Anode / hole transport layer / light emitting layer / electron Transport layer / cathode (5) Anode / anode buffer layer (hole injection layer) / hole transport layer / light emitting layer / electron transport layer / cathode buffer layer (electron injection layer) / cathode (anode)
As the anode (transparent electrode) in the organic EL element, an electrode material made of a metal, an alloy, an electrically conductive compound or a mixture thereof having a high work function (4 eV or more) is preferably used. Specific examples of such electrode materials include metals such as Au, and conductive transparent materials such as CuI, indium tin oxide (ITO), SnO 2 , and ZnO. Alternatively, an amorphous material such as IDIXO (In 2 O 3 —ZnO) capable of forming a transparent conductive film may be used.
有機EL素子における陰極としては、仕事関数の小さい(4eV以下)金属(電子注入性金属と称する)、合金、電気伝導性化合物およびこれらの混合物を電極物質とするものが用いられる。このような電極物質の具体例としては、ナトリウム、ナトリウム-カリウム合金、マグネシウム、リチウム、マグネシウム/銅混合物、マグネシウム/銀混合物、マグネシウム/アルミニウム混合物、マグネシウム/インジウム混合物、アルミニウム/酸化アルミニウム(Al2O3)混合物、インジウム、リチウム/アルミニウム混合物、希土類金属等が挙げられる。これらの中で、電子注入性および酸化等に対する耐久性の点から、電子注入性金属とこれより仕事関数の値が大きく安定な金属である第二金属との混合物、例えば、マグネシウム/銀混合物、マグネシウム/アルミニウム混合物、マグネシウム/インジウム混合物、アルミニウム/酸化アルミニウム(Al2O3)混合物、リチウム/アルミニウム混合物、アルミニウム等が陰極として好適である。 (cathode)
As the cathode in the organic EL element, a material having a small work function (4 eV or less) metal (referred to as an electron injecting metal), an alloy, an electrically conductive compound, and a mixture thereof is used. Specific examples of such electrode materials include sodium, sodium-potassium alloy, magnesium, lithium, magnesium / copper mixture, magnesium / silver mixture, magnesium / aluminum mixture, magnesium / indium mixture, aluminum / aluminum oxide (Al 2 O 3 ) Mixtures, indium, lithium / aluminum mixtures, rare earth metals and the like. Among these, from the point of durability against electron injection and oxidation, a mixture of an electron injecting metal and a second metal which is a stable metal having a larger work function value than this, for example, a magnesium / silver mixture, Magnesium / aluminum mixtures, magnesium / indium mixtures, aluminum / aluminum oxide (Al 2 O 3 ) mixtures, lithium / aluminum mixtures, aluminum and the like are suitable as the cathode.
注入層には電子注入層と正孔注入層があり、電子注入層と正孔注入層を必要に応じて設け、陽極と発光層または正孔輸送層の間、および陰極と発光層または電子輸送層との間に存在させる。 (Injection layer: electron injection layer, hole injection layer)
The injection layer includes an electron injection layer and a hole injection layer. An electron injection layer and a hole injection layer are provided as necessary, and between the anode and the light emitting layer or the hole transport layer, and between the cathode and the light emitting layer or the electron transport. Exist between the layers.
有機EL素子における発光層は、電極(陰極、陽極)または電子輸送層、正孔輸送層から注入されてくる電子および正孔が再結合して発光する層であり、発光する部分は発光層の層内であっても発光層と隣接層との界面であってもよい。 (Light emitting layer)
The light emitting layer in the organic EL element is a layer that emits light by recombination of electrons and holes injected from the electrode (cathode, anode) or electron transport layer, hole transport layer, and the light emitting portion is the light emitting layer. It may be in the layer or the interface between the light emitting layer and the adjacent layer.
発光ドーパントは、大きく分けて蛍光を発光する蛍光性ドーパントとリン光を発光するリン光性ドーパントの2種類がある。 (Luminescent dopant)
There are two types of luminescent dopants: a fluorescent dopant that emits fluorescence and a phosphorescent dopant that emits phosphorescence.
発光ホスト(単にホストとも言う)とは、2種以上の化合物で構成される発光層中にて混合比(質量)の最も多い化合物のことを意味し、それ以外の化合物については「ドーパント化合物(単に、ドーパントとも言う)」という。例えば、発光層を化合物A、化合物Bという2種で構成し、その混合比がA:B=10:90であれば化合物Aがドーパント化合物であり、化合物Bがホスト化合物である。さらに発光層を化合物A、化合物B、化合物Cの3種から構成し、その混合比がA:B:C=5:10:85であれば、化合物A、化合物Bがドーパント化合物であり、化合物Cがホスト化合物である。 (Light emitting host)
A light-emitting host (also simply referred to as a host) means a compound having the largest mixing ratio (mass) in a light-emitting layer composed of two or more kinds of compounds. It is also simply called a dopant). For example, if the light emitting layer is composed of two types of compound A and compound B and the mixing ratio is A: B = 10: 90, compound A is a dopant compound and compound B is a host compound. Furthermore, if a light emitting layer is comprised from 3 types of a compound A, a compound B, and the compound C and the mixing ratio is A: B: C = 5: 10: 85, the compound A and the compound B are dopant compounds, and a compound C is a host compound.
正孔輸送層とは正孔を輸送する機能を有する正孔輸送材料からなり、広い意味で正孔注入層、電子阻止層も正孔輸送層に含まれる。正孔輸送層は単層または複数層設けることができる。 (Hole transport layer)
The hole transport layer is made of a hole transport material having a function of transporting holes, and in a broad sense, a hole injection layer and an electron blocking layer are also included in the hole transport layer. The hole transport layer can be provided as a single layer or a plurality of layers.
電子輸送層とは電子を輸送する機能を有する電子輸送材料からなり、広い意味で電子注入層、正孔阻止層も電子輸送層に含まれる。電子輸送層は単層または複数層設けることができる。 (Electron transport layer)
The electron transport layer is made of an electron transport material having a function of transporting electrons, and in a broad sense, an electron injection layer and a hole blocking layer are also included in the electron transport layer. The electron transport layer can be provided as a single layer or a plurality of layers.
有機EL素子の作製方法について説明する。 (Method for producing organic EL element)
A method for manufacturing the organic EL element will be described.
〔樹脂基材〕
基材1:両面に易接着処理した厚さ100μmのポリエチレンテレフタレートフィルム(東レ株式会社製、ルミラー(登録商標)(U48))のガスバリア層を形成する面とは反対の面に、厚さ0.5μmのアンチブロック機能を有するクリアハードコート層を形成して基材1とした。すなわち、UV硬化型樹脂(アイカ工業株式会社製、品番:Z731L)を乾燥膜厚が0.5μmになるように塗布した後、80℃で乾燥し、その後、空気下、高圧水銀ランプを用いて照射エネルギー量0.5J/cm2の条件で硬化を行った。 <Manufacture of gas barrier film>
[Resin substrate]
Substrate 1: A 100 μm-thick polyethylene terephthalate film (Lumirror (registered trademark) (U48), manufactured by Toray Industries, Inc.) with easy adhesion treatment on both sides has a thickness of 0. A substrate 1 was formed by forming a clear hard coat layer having an antiblock function of 5 μm. That is, a UV curable resin (manufactured by Aika Kogyo Co., Ltd., product number: Z731L) was applied so as to have a dry film thickness of 0.5 μm, and then dried at 80 ° C. Then, using a high-pressure mercury lamp in the air. Curing was performed under the condition of an irradiation energy amount of 0.5 J / cm 2 .
アンカーコート層の形成は、下記に示すような塗布液を塗布し塗膜を形成した後、真空紫外線照射による改質を行って形成した。 [Formation of anchor coat layer]
The anchor coat layer was formed by applying a coating solution as shown below to form a coating film, and then performing modification by irradiation with vacuum ultraviolet rays.
(株)エム・ディ・コム製エキシマ照射装置MODEL:MECL-M-1-200
波長:172nm
ランプ封入ガス:Xe
・改質処理条件
エキシマ光強度 :130mW/cm2(172nm)
試料と光源の距離 :2mm
ステージ加熱温度 :80℃
照射装置内の酸素濃度:0.3体積%
エキシマ光照射時のステージ搬送速度:10mm/秒
エキシマ光照射時のステージ搬送回数:3往復
このようなアンカーコート層の厚さ方向の組成分布(N/Si比率)は、下記のようなXPS(光電子分光法)分析を用いた方法で測定して求めた。 ・ Reforming treatment equipment Eximer irradiation equipment MODEL: MECL-M-1-200 manufactured by M.D.
Wavelength: 172nm
Lamp filled gas: Xe
-Modification treatment conditions Excimer light intensity: 130 mW / cm 2 (172 nm)
Distance between sample and light source: 2mm
Stage heating temperature: 80 ° C
Oxygen concentration in the irradiation device: 0.3% by volume
Stage transport speed during excimer light irradiation: 10 mm / second Stage transport count during excimer light irradiation: 3 reciprocations The composition distribution (N / Si ratio) in the thickness direction of such an anchor coat layer is expressed by the following XPS ( Measurement was made by a method using photoelectron spectroscopy) analysis.
・装置:アルバックファイ製QUANTERASXM
・X線源:単色化Al-Kα
・測定領域:Si2p、C1s、N1s、O1s
・スパッタイオン:Ar(2keV)
・デプスプロファイル:1分間スパッタ後、測定を繰り返す
※SiO2換算のエッチングレートで厚さ約2.8nmに相当
・定量:バックグラウンドをShirley法で求め、得られたピーク面積から相対感度係数法を用いて定量した。データ処理は、アルバックファイ社製のMultiPakを用いた。 (XPS analysis conditions)
・ Equipment: ULVAC-PHI QUANTERASXM
・ X-ray source: Monochromatic Al-Kα
Measurement area: Si2p, C1s, N1s, O1s
・ Sputtering ion: Ar (2 keV)
Depth profile: after 1 minute sputtering, the measurement is repeated ※ corresponds to the thickness of about 2.8nm in the etching rate of SiO 2 in terms and quantitative: seeking background Shirley method, the relative sensitivity coefficient method from the peak area obtained with And quantified. For data processing, MultiPak manufactured by ULVAC-PHI was used.
上記アンカーコート層上に、ガスバリア層を真空プラズマCVD法により成膜した。 [Formation of gas barrier layer]
A gas barrier layer was formed on the anchor coat layer by a vacuum plasma CVD method.
樹脂基材2のクリアハードコート層を形成した面上に、上記表2のガスバリア層CVD2を成膜し、ガスバリア性フィルム(試料No.1)を作製した。 (Comparative Example 1)
On the surface of the resin substrate 2 on which the clear hard coat layer was formed, the gas barrier layer CVD2 shown in Table 2 was formed to produce a gas barrier film (sample No. 1).
樹脂基材1のガスバリア層を形成する側の表面に上記表1のU1の条件でアンカーコート層を成膜し、さらにその上に上記表2のガスバリア層CVD2を成膜し、ガスバリア性フィルム(試料No.2)を作製した。 (Comparative Example 2)
On the surface of the resin substrate 1 on which the gas barrier layer is formed, an anchor coat layer is formed under the conditions of U1 in Table 1 above, and further, the gas barrier layer CVD2 in Table 2 above is formed thereon to form a gas barrier film ( Sample No. 2) was produced.
樹脂基材2を使用し、アンカーコート層の成膜を上記表1のU2の条件で行ったこと以外は、比較例2と同様にしてガスバリア性フィルム(試料No.3)を作製した。 (Comparative Example 3)
A gas barrier film (Sample No. 3) was produced in the same manner as in Comparative Example 2 except that the resin base material 2 was used and the anchor coat layer was formed under the conditions of U2 in Table 1 above.
アンカーコート層の成膜を上記表1のU3の条件で行ったこと以外は、比較例3と同様にしてガスバリア性フィルム(試料No.4)を作製した。 (Comparative Example 4)
A gas barrier film (sample No. 4) was produced in the same manner as in Comparative Example 3 except that the anchor coat layer was formed under the conditions of U3 in Table 1 above.
アンカーコート層の成膜を上記表1のU8の条件で行ったこと以外は、比較例3と同様にしてガスバリア性フィルム(試料No.5)を作製した。 (Comparative Example 5)
A gas barrier film (Sample No. 5) was produced in the same manner as in Comparative Example 3 except that the anchor coat layer was formed under the conditions of U8 in Table 1 above.
アンカーコート層の成膜を上記表1のU9の条件で行ったこと以外は、比較例3と同様にしてガスバリア性フィルム(試料No.6)を作製した。 (Comparative Example 6)
A gas barrier film (Sample No. 6) was produced in the same manner as in Comparative Example 3 except that the anchor coat layer was formed under the conditions of U9 in Table 1 above.
ポリシラザンを含有する層の改質処理の際にアンカーコート層の組成調整処理M2を実施したこと以外は、比較例2と同様にしてガスバリア性フィルム(試料No.7)を作製した。 (Example 1)
A gas barrier film (Sample No. 7) was produced in the same manner as in Comparative Example 2 except that the composition adjustment treatment M2 of the anchor coat layer was performed during the modification treatment of the layer containing polysilazane.
ポリシラザンを含有する層の改質処理の際にアンカーコート層の組成調整処理M1を実施したこと以外は、比較例3と同様にしてガスバリア性フィルム(試料No.8)を作製した。 (Example 2)
A gas barrier film (Sample No. 8) was produced in the same manner as in Comparative Example 3 except that the composition adjustment treatment M1 of the anchor coat layer was performed during the modification treatment of the layer containing polysilazane.
アンカーコート層の成膜を上記表1のU4の条件で行ったこと以外は、比較例3と同様にしてガスバリア性フィルム(試料No.9)を作製した。 (Example 3)
A gas barrier film (Sample No. 9) was produced in the same manner as in Comparative Example 3 except that the anchor coat layer was formed under the conditions of U4 in Table 1 above.
アンカーコート層の成膜を上記表1のU5の条件で行ったこと以外は、比較例3と同様にしてガスバリア性フィルム(試料No.10)を作製した。 Example 4
A gas barrier film (Sample No. 10) was produced in the same manner as in Comparative Example 3 except that the anchor coat layer was formed under the conditions of U5 in Table 1 above.
アンカーコート層の成膜を上記表1のU6の条件で行ったこと以外は、比較例3と同様にしてガスバリア性フィルム(試料No.11)を作製した。 (Example 5)
A gas barrier film (Sample No. 11) was produced in the same manner as in Comparative Example 3 except that the anchor coat layer was formed under the conditions of U6 in Table 1 above.
アンカーコート層の成膜において、上記表1のU7の条件で行ったこと以外は、比較例3と同様にしてガスバリア性フィルム(試料No.12)を作製した。 (Example 6)
A gas barrier film (Sample No. 12) was produced in the same manner as in Comparative Example 3 except that the anchor coat layer was formed under the conditions of U7 in Table 1 above.
ガスバリア層をCVD1に変更したこと以外は、実施例3と同様にしてガスバリア性フィルム(試料No.13)を作製した。 (Example 7)
A gas barrier film (Sample No. 13) was produced in the same manner as in Example 3 except that the gas barrier layer was changed to CVD1.
ガスバリア層をCVD3に変更したこと以外は、実施例3と同様にしてガスバリア性フィルム(試料No.14)を作製した。 (Example 8)
A gas barrier film (Sample No. 14) was produced in the same manner as in Example 3 except that the gas barrier layer was changed to CVD3.
ガスバリア層をCVD1に変更したこと以外は、比較例3と同様にしてガスバリア性フィルム(試料No.15)を作製した。 (Comparative Example 7)
A gas barrier film (Sample No. 15) was produced in the same manner as in Comparative Example 3 except that the gas barrier layer was changed to CVD1.
アンカーコート層の成膜を上記表1のU10の条件で行ったこと以外は、比較例3と同様にしてガスバリア性フィルム(試料No.16)を作製した。 Example 9
A gas barrier film (Sample No. 16) was produced in the same manner as in Comparative Example 3 except that the anchor coat layer was formed under the conditions of U10 in Table 1 above.
ガスバリア層の上に、上記表1のU2の条件でポリシラザンを含有する層をさらに形成し改質処理を実施したこと以外は、実施例4と同様にしてガスバリア性フィルム(試料No.17)を作製した。 (Example 10)
A gas barrier film (sample No. 17) was formed in the same manner as in Example 4 except that a layer containing polysilazane was further formed on the gas barrier layer under the conditions of U2 in Table 1 above and the modification treatment was performed. Produced.
上記比較例3において、ポリシラザンを含有する層の改質処理の際にアンカーコート層の組成調整処理M3を実施したこと以外は、比較例3と同様にしてガスバリア性フィルム(試料No.18)を作製した。 (Example 11)
In Comparative Example 3, the gas barrier film (Sample No. 18) was prepared in the same manner as Comparative Example 3 except that the anchor coat layer composition adjustment treatment M3 was performed during the modification treatment of the polysilazane-containing layer. Produced.
上記比較例3と同じ条件でガスバリア性フィルム(試料No.19)を作製した。 (Comparative Example 8)
A gas barrier film (Sample No. 19) was produced under the same conditions as in Comparative Example 3 above.
ガスバリア層の上に、上記表1のU2の条件でポリシラザンを含有する層をさらに形成し改質処理を実施したこと以外は、比較例3と同様にしてガスバリア性フィルム(試料No.20)を作製した。 (Comparative Example 9)
A gas barrier film (Sample No. 20) was formed in the same manner as in Comparative Example 3 except that a layer containing polysilazane was further formed on the gas barrier layer under the conditions of U2 in Table 1 above and the modification treatment was performed. Produced.
アンカーコート層の成膜を上記表1のU3の条件で行ったこと以外は、比較例9と同様にしてガスバリア性フィルム(試料No.21)を作製した。 (Comparative Example 10)
A gas barrier film (Sample No. 21) was produced in the same manner as in Comparative Example 9 except that the anchor coat layer was formed under the conditions of U3 in Table 1 above.
ガスバリア層の上に上記表1のU2の条件でポリシラザンを含有する層をさらに形成し改質処理を実施したこと以外は、実施例1と同様にしてガスバリア性フィルム(試料No.22)を作製した。 Example 12
A gas barrier film (Sample No. 22) was produced in the same manner as in Example 1 except that a layer containing polysilazane was further formed on the gas barrier layer under the conditions of U2 in Table 1 above and the modification treatment was performed. did.
ガスバリア層の上に上記表1のU2の条件でポリシラザンを含有する層をさらに形成し改質処理を実施したこと以外は、比較例5と同様にしてガスバリア性フィルム(試料No.23)を作製した。 (Comparative Example 11)
A gas barrier film (sample No. 23) was produced in the same manner as in Comparative Example 5 except that a layer containing polysilazane was further formed on the gas barrier layer under the conditions of U2 in Table 1 above and the modification treatment was performed. did.
ガスバリア層の上に上記表1のU2の条件でポリシラザンを含有する層をさらに形成し改質処理を実施したこと以外は、実施例3と同様にしてガスバリア性フィルム(試料No.24)を作製した。 (Example 13)
A gas barrier film (sample No. 24) was prepared in the same manner as in Example 3 except that a layer containing polysilazane was further formed on the gas barrier layer under the conditions of U2 in Table 1 and the modification treatment was performed. did.
ガスバリア層の上に上記表1のU2の条件でポリシラザンを含有する層をさらに形成し改質処理を実施したこと以外は、実施例4と同様にしてガスバリア性フィルム(試料No.25)を作製した。 (Example 14)
A gas barrier film (sample No. 25) was produced in the same manner as in Example 4 except that a layer containing polysilazane was further formed on the gas barrier layer under the conditions of U2 in Table 1 above and the modification treatment was performed. did.
ガスバリア層の上に上記表1のU2の条件でポリシラザンを含有する層をさらに形成し改質処理を実施したこと以外は、実施例5と同様にしてガスバリア性フィルム(試料No.26)を作製した。 (Example 15)
A gas barrier film (sample No. 26) was prepared in the same manner as in Example 5 except that a layer containing polysilazane was further formed on the gas barrier layer under the conditions of U2 in Table 1 and the reforming treatment was performed. did.
ガスバリア層の上に上記表1のU2の条件でポリシラザンを含有する層をさらに形成し改質処理を実施したこと以外は、実施例6と同様にしてガスバリア性フィルム(試料No.27)を作製した。 (Example 16)
A gas barrier film (sample No. 27) was prepared in the same manner as in Example 6 except that a layer containing polysilazane was further formed on the gas barrier layer under the conditions of U2 in Table 1 and the modification treatment was performed. did.
ガスバリア層の上に上記表1のU2の条件でポリシラザンを含有する層をさらに形成し改質処理を実施したこと以外は、実施例7と同様にしてガスバリア性フィルム(試料No.28)を作製した。 (Example 17)
A gas barrier film (Sample No. 28) was produced in the same manner as in Example 7 except that a layer containing polysilazane was further formed on the gas barrier layer under the conditions of U2 in Table 1 above and the modification treatment was performed. did.
ガスバリア層の上に上記表1のU2の条件でポリシラザンを含有する層をさらに形成し改質処理を実施したこと以外は、比較例7と同様にしてガスバリア性フィルム(試料No.29)を作製した。 (Comparative Example 12)
A gas barrier film (sample No. 29) was produced in the same manner as in Comparative Example 7 except that a layer containing polysilazane was further formed on the gas barrier layer under the conditions of U2 in Table 1 above and the modification treatment was performed. did.
ポリシラザンを含有する層の改質処理の際に組成調整処理M2を実施したこと以外は、比較例7と同様にしてガスバリア性フィルム(試料No.30)を作製した。 (Example 18)
A gas barrier film (Sample No. 30) was produced in the same manner as in Comparative Example 7 except that the composition adjustment treatment M2 was performed during the modification treatment of the layer containing polysilazane.
<真空成膜によるガスバリア層の欠陥数の評価>
上記で作製したガスバリア性フィルム試料1~18について、Ca蒸着面積・50mmの評価素子を作製した。85℃85%RHの条件下で、6時間保存した際に生じた円換算直径で100μm以上のCa腐食点の数を求めた。 "Evaluation methods"
<Evaluation of number of defects in gas barrier layer by vacuum film formation>
For the gas barrier film samples 1 to 18 produced as described above, evaluation elements having a Ca vapor deposition area of 50 mm were produced. The number of Ca corrosion points of 100 μm or more was determined in terms of a circle-equivalent diameter generated when stored at 85 ° C. and 85% RH for 6 hours.
◎:2以下
○:3~5
△:6~19
×:20~39
××:40以上。 (Rank evaluation)
◎: 2 or less ○: 3-5
Δ: 6 to 19
×: 20 to 39
XX: 40 or more.
上記で作製したガスバリア性フィルム試料19~30を用い、下記に示すような方法で、発光領域の面積が5cm×5cmとなるように、ボトムエミッション型の有機エレクトロルミネッセンス素子(有機EL素子)を作製した。 <Dark spot (DS) evaluation of organic EL devices>
Using the gas
ガスバリア性フィルムを、市販の真空蒸着装置の基材ホルダーに固定し、化合物118をタングステン製の抵抗加熱ボートに入れ、これら基材ホルダーと加熱ボートとを真空蒸着装置の第1真空槽内に取り付けた。また、タングステン製の抵抗加熱ボートに銀(Ag)を入れ、真空蒸着装置の第2真空槽内に取り付けた。 (Formation of underlayer and first electrode)
The gas barrier film is fixed to a substrate holder of a commercially available vacuum deposition apparatus, compound 118 is placed in a resistance heating boat made of tungsten, and the substrate holder and the heating boat are attached in the first vacuum chamber of the vacuum deposition apparatus. It was. Moreover, silver (Ag) was put into the resistance heating boat made from tungsten, and it attached in the 2nd vacuum chamber of a vacuum evaporation system.
引き続き、市販の真空蒸着装置を用い、真空度1×10-4Paまで減圧した後、基材を移動させながら化合物HT-1を、蒸着速度0.1nm/秒で蒸着し、20nmの正孔輸送層(HTL)を設けた。 (Organic functional layer to second electrode)
Subsequently, the pressure was reduced to a vacuum degree of 1 × 10 −4 Pa using a commercially available vacuum deposition apparatus, and then the compound HT-1 was deposited at a deposition rate of 0.1 nm / second while moving the base material. A transport layer (HTL) was provided.
次に、封止部材として厚さ25μmのアルミ箔を使用し、このアルミ箔の片面に封止樹脂層として熱硬化型のシート状接着剤(エポキシ系樹脂)を厚さ20μmで貼合した封止部材を用いて、第2電極までを作製した試料に重ね合わせた。このとき、第1電極及び第2電極の引き出し電極の端部が外に出るように、封止部材の接着剤形成面と、素子の有機機能層面とを連続的に重ね合わせた。 (Solid sealing)
Next, an aluminum foil with a thickness of 25 μm is used as a sealing member, and a thermosetting sheet adhesive (epoxy resin) is bonded as a sealing resin layer on one surface of the aluminum foil with a thickness of 20 μm. The stopper member was used to superimpose the sample up to the second electrode. At this time, the adhesive forming surface of the sealing member and the organic functional layer surface of the element were continuously overlapped so that the end portions of the extraction electrodes of the first electrode and the second electrode were exposed.
上記のようにして得られた有機EL素子を85℃、85%RHの環境下で100時間通電を行い、発行させて写真を撮り、写真画像からダークスポットのサイズと個数を計測、円換算直径で300μm以上のダークスポットの数を求めた。ダークスポットの数は、発行面積100cm2の換算値とし、以下のようにランク付けした。なお、ダークスポットの数が19以下(△評価以上)であれば、高温高湿環境での耐久性に優れた電子デバイスであることを意味し、用いられているガスバリア性フィルムが高いガスバリア性および優れたガスバリア性の面内均一性を有していることを意味する。また、ダークスポットの数が19以下(△評価以上)であれば、実使用上問題なく、合格品である。 (Dark spot (DS) evaluation)
The organic EL device obtained as described above was energized for 100 hours in an environment of 85 ° C. and 85% RH, issued and photographed, and the size and number of dark spots were measured from the photograph image. The number of dark spots of 300 μm or more was obtained. The number of dark spots was converted to an issue area of 100 cm 2 and ranked as follows. In addition, if the number of dark spots is 19 or less (Δ evaluation or more), it means that the electronic device has excellent durability in a high-temperature and high-humidity environment, and the gas barrier film used has a high gas barrier property and It means having excellent in-plane uniformity of gas barrier properties. Further, if the number of dark spots is 19 or less (Δevaluation or more), there is no problem in actual use and the product is acceptable.
◎:2以下
○:3~5
△:6~19
×:20~39
××:40。 (Rank evaluation)
◎: 2 or less ○: 3-5
Δ: 6 to 19
×: 20 to 39
XX: 40.
1、1a 基材、
1b、1c、1d、1e 成膜された基材、
10 送り出しロール、
11、12、13、14 搬送ロール、
15、15’ 第1成膜ロール、
16、16’ 第2成膜ロール、
17 巻取りロール、
18、18’ ガス供給管、
19、19’ プラズマ発生用電源、
20、20’、21、21’ 磁場発生装置、
30 真空チャンバ、
40、40’ 真空ポンプ、
41 制御部。 S deposition space,
1, 1a base material,
1b, 1c, 1d, 1e film-formed substrate,
10 Delivery roll,
11, 12, 13, 14 transport rolls,
15, 15 ′ first film forming roll,
16, 16 ′ second film forming roll,
17 winding roll,
18, 18 'gas supply pipe,
19, 19 'power source for plasma generation,
20, 20 ′, 21, 21 ′ magnetic field generator,
30 vacuum chamber,
40, 40 'vacuum pump,
41 Control unit.
Claims (7)
- 基材上に、アンカーコート層、前記アンカーコート層に接しており真空成膜法により形成されるガスバリア層をこの順に有するガスバリア性フィルムであって、
前記アンカーコート層は、ポリシラザンを含有する層にエネルギーを印加して改質処理を行って得られる層であり、かつ、前記アンカーコート層の厚さをA(nm)とし、前記アンカーコート層全体のケイ素原子に対する窒素原子の原子比(N/Si)をBとした時に、A×B≦60である、ガスバリア性フィルム。 On the base material, an anchor coat layer, a gas barrier film having a gas barrier layer in contact with the anchor coat layer and formed in this order by a vacuum film forming method,
The anchor coat layer is a layer obtained by applying energy to a layer containing polysilazane and performing a modification treatment, and the thickness of the anchor coat layer is A (nm), and the entire anchor coat layer A gas barrier film in which A × B ≦ 60 when the atomic ratio (N / Si) of nitrogen atoms to silicon atoms is B. - 前記ガスバリア層は、真空プラズマCVD法で成膜されたガスバリア層である、請求項1に記載のガスバリア性フィルム。 The gas barrier film according to claim 1, wherein the gas barrier layer is a gas barrier layer formed by a vacuum plasma CVD method.
- 前記ガスバリア層は、組成がSiCxで表される組成分布の領域であって、
xが0.8~1.2である領域を厚さ方向に有する、請求項1または2に記載のガスバリア性フィルム。 The gas barrier layer is a composition distribution region whose composition is represented by SiC x ,
3. The gas barrier film according to claim 1, having a region where x is 0.8 to 1.2 in the thickness direction. - 前記エネルギーの印加は、真空紫外光を照射することにより行われる、請求項1~3のいずれか1項に記載のガスバリア性フィルム。 The gas barrier film according to any one of claims 1 to 3, wherein the energy is applied by irradiation with vacuum ultraviolet light.
- 前記ガスバリア層の基材側とは反対側の面上に、さらに、ポリシラザンを含有する層にエネルギーを印加して改質処理を行って得られる層を有する、請求項1~4のいずれか1項に記載のガスバリア性フィルム。 5. The method according to claim 1, further comprising a layer obtained by applying energy to a layer containing polysilazane and performing a modification treatment on a surface opposite to the base material side of the gas barrier layer. The gas barrier film according to Item.
- 前記エネルギーの印加は、真空紫外光を照射することにより行われる、請求項5に記載のガスバリア性フィルム。 The gas barrier film according to claim 5, wherein the energy is applied by irradiation with vacuum ultraviolet light.
- 請求項1~6のいずれか1項に記載のガスバリア性フィルムと、
前記ガスバリア性フィルム上に形成される電子デバイス本体と、
を含む、電子デバイス。 A gas barrier film according to any one of claims 1 to 6;
An electronic device body formed on the gas barrier film;
Including electronic devices.