WO2014187032A1 - Oled显示面板及其封装方法、显示装置 - Google Patents

Oled显示面板及其封装方法、显示装置 Download PDF

Info

Publication number
WO2014187032A1
WO2014187032A1 PCT/CN2013/081460 CN2013081460W WO2014187032A1 WO 2014187032 A1 WO2014187032 A1 WO 2014187032A1 CN 2013081460 W CN2013081460 W CN 2013081460W WO 2014187032 A1 WO2014187032 A1 WO 2014187032A1
Authority
WO
WIPO (PCT)
Prior art keywords
moisture
oled
display panel
oxidation
adhesive film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/CN2013/081460
Other languages
English (en)
French (fr)
Inventor
姚继开
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BOE Technology Group Co Ltd
Original Assignee
BOE Technology Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BOE Technology Group Co Ltd filed Critical BOE Technology Group Co Ltd
Priority to US14/241,955 priority Critical patent/US20140346476A1/en
Publication of WO2014187032A1 publication Critical patent/WO2014187032A1/zh
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

一种OLED显示面板，包括OLED基板（201），与OLED基板（201）相对设置的封装盖板（203），以及设于OLED基板（201）和封装盖板（203）之间的胶膜（204），还包括用于吸收水汽的防潮物（205）；防潮物（205）设于所述胶膜（204）中。该方案避免了增大OLED显示面板的体积，还提供了该OLED显示面板的封装方法以及包括该OLED显示面板的显示装置。

Description

OLED显示面板及其封装方法、 显示装置 技术领域
本发明的实施例涉及一种 OLED显示面板及其封装方法、 显示装置。 背景技术
有机发光二极管 （Organic Light-Emitting Diode, OLED )显示器是一种 新型的显示器件。 与液晶显示器相比， OLED显示器具有自发光、 响应速度 快和宽视角等优点， 而且可以进行柔性显示、 透明显示和 3D显示， 因而得 到了快速发展与普及。
如图 1所示， 目前 OLED显示面板一般采用胶封装的方式进行封装。 采 用胶封装的方式进行封装的过程为： 在 OLED基板 101 (即， 形成有 OLED 结构的基板 )上形成胶膜 104,将 OLED基板 101与封装盖板 103相对设置， 完成封装。 由于空气中的水汽可能会渗透过胶膜 104, 对 OLED结构 102中 的有机发光材料的寿命产生消极影响， 因而为了尽可能地避免空气中的水汽 对 OLED结构 102中的有机发光材料的寿命产生消极影响，在对 OLED显示 面板进行胶封装时， 还会在 OLED基板 101与胶膜 104之间设有完全覆盖 OLED结构的防潮层 105。 由于防潮层 105具有一定的厚度和宽度， 因而防 潮层 105增大了 OLED显示面板的体积。
综上所述， 为了避免空气中的水汽对 OLED结构中的有机发光材料产生 消极影响， 目前的 OLED显示面板一般包括具有一定厚度和宽度的防潮层， 因而增大了 OLED显示面板的体积。 发明内容
本发明的实施例提供的一种 OLED显示面板及其封装方法、 显示装置， 用以解决 OLED显示面板由于包括防潮层而增大了体积的问题。
本发明的一个实施例提供的一种 OLED显示面板， 包括： OLED基板， 与所述 OLED基板相对设置的封装盖板，设于所述 OLED基板和封装盖板之 间的胶膜， 以及用于吸收水汽的防潮物； 所述防潮物设于所述胶膜中。 本发明的另一个实施例提供的一种显示装置，包括所述 OLED显示面板。 本发明的再一个实施例提供的一种 0LED显示面板封装方法， 包括： 在 0LED基板和 /或封装盖板上形成胶膜， 其中， 所述胶膜中包含有用于吸收水 汽的防潮物； 将所述 OLED基板与封装盖板相对设置， 完成封装。 附图说明
为了更清楚地说明本发明实施例的技术方案， 下面将对实施例的附图作 筒单地介绍，显而易见地，下面描述中的附图仅仅涉及本发明的一些实施例， 而非对本发明的限制。
图 1为现有技术中 OLED显示面板的结构示意图；
图 2为本发明实施例 OLED显示面板的结构示意图；
图 3为本发明实施例 OLED显示面板的侧视图；
图 4为本发明实施例 OLED显示面板的俯视图；
图 5八~图 5D为本发明实施例 OLED显示面板的侧视图；
图 6为本发明实施例 OLED显示面板的侧视图；
图 7为本发明实施例胶膜的结构示意图；
图 8为本发明实施例 OLED显示面板封装方法的流程示意图。 具体实施方式
为使本发明实施例的目的、 技术方案和优点更加清楚， 下面将结合本发 明实施例的附图，对本发明实施例的技术方案进行清楚、 完整地描述。显然， 所描述的实施例是本发明的一部分实施例， 而不是全部的实施例。 基于所描 述的本发明的实施例， 本领域普通技术人员在无需创造性劳动的前提下所获 得的所有其他实施例， 都属于本发明保护的范围。
根据本发明一个实施例的 OLED显示面板包括： OLED基板， 与所述
OLED基板相对设置的封装盖板， 以及设于所述 OLED基板和封装盖板之间 的胶膜， 该显示面板还包括用于吸收水汽的防潮物， 所述防潮物设于所述胶 膜中。 由于用于吸收水汽的防潮物设于胶膜中， 所以在空气中的水汽渗透胶 膜时， 胶膜中包含的防潮物会吸收空气中的水汽。 这就避免空气中的水汽对 OLED结构中的有机发光材料产生消极或不利影响。 因而， 根据本发明实施 例的 OLED显示面板不需要在 OLED基板与胶膜之间设有防潮层，从而避免 了增大 OLED显示面板的体积。
需要说明的是,本发明实施例的 OLED基板为形成有 OLED结构的基板。 如图 2所示， 本发明的一个实施例提供的 OLED显示面板包括形成有 OLED结构 202的 OLED基板 201 , 与 OLED基板 201相对设置的封装盖板
203,设于 OLED基板 201和封装盖板 203之间的胶膜 204, 以及用于吸收水 汽的防潮物 205。 防潮物 205设于胶膜 204中， 例如分散与胶膜 204中。
例如， 本发明实施例提供的 OLED显示面板包括至少一个防潮物 205。 OLED显示面板包括的防潮物 205越多， OLED显示面板吸收水汽的效 果越好。 防潮物 205可以为任何能够吸收水汽的物体， 比如， 干燥剂或者包 括干燥剂的物体。
例如， 防潮物 205可以为化学吸附干燥剂或者物理吸附干燥剂， 比如固 体干燥剂、 液体干燥剂、 透明干燥剂、 不透明干燥剂和黑色干燥剂等。
例如， 防潮物 205为颗粒状干燥剂， 比如硅胶干燥剂。
如果防潮物 205为硅胶干燥剂， 则在防潮物 205吸收水汽时， 不会带来 二次化学污染。
例如， 防潮物 205可以为任何形状， 比如规则形状或者不规则形状。 例如， 防潮物 205的形状为规则形状时， 其包括柱体、 锥体和球体中的 一种或多种。
例如，防潮物 205的大小可以根据具体需要设定，但需要保证防潮物 205 是设于胶膜 204中。
防潮物 205设于胶膜 204中的任何一种实施方式都适用于本发明实施例。 比如， 防潮物 205可混合于胶膜 204中， 防潮物 205可插入在胶膜 204中， 或者胶膜 204包覆防潮物 205等。
下面将以防潮物 205为颗粒状干燥剂或包括颗粒状干燥剂的物体为例， 对本发明实施例防潮物 205设于胶膜 204中的实施方式进行介绍。 其他的实 施方式与这些实施方式类似， 在此不再赘述。
一、 防潮物 205为颗粒状干燥剂。
较佳地， 防潮物 205例如混合于胶膜 204中。 防潮物 205可以均匀地混 合于胶膜 204中， 也可以不均匀地混合于胶膜 204中。 当在防潮物 205均匀地混合于胶膜 204中时， 混合于胶膜 204中的防潮 物 205均匀分布； 当在防潮物 205不均匀地混合于胶膜 204中时， 混合于胶 膜 204中的防潮物 205聚集在胶膜 204中的至少一个区域。
当在防潮物 205不均匀地混合于胶膜 204中时， 多个防潮物 205聚集在 一起时， 聚集防潮物的区域的形状可以为规则形状， 也可以为不规则形状。
例如， 聚集防潮物的区域的形状包括圓形和 /或多边形。
比如， 如图 2所示， 防潮物 205基本均匀地混合于胶膜 204中。
如图 3所示， 聚集防潮物的区域的形状可以为规则形状， 也可以为不规 则形状。 图 3中的 A区域为 4个防潮物 205聚集在一起形成的区域， A区域 的形状为规则的正方形； 图 3中的 B区域为 2个防潮物 205聚集在一起形成 的区域， B区域的形状为规则的圓形； 图 3中的 C区域为 3个防潮物 205聚 集在一起形成的区域， C区域的形状为不规则形状。
例如， 防潮物 205可以混合于全部胶膜 204中， 也可以混合于部分胶膜 204中。
例如， 防潮物 205混合于 OLED结构 202四周的胶膜 204中， 混合于胶 膜 204中的防潮物 205在 OLED基板 201上的投影呈四边形分布。
比如， 如图 4所示， 混合于胶膜 204中的防潮物 205在 OLED基板 201 上的投影呈长方形分布。
例如， 针对 OLED显示面板包括的一个防潮物 205 , 防潮物 205混合于 胶膜 204中的任何一种实施方式都适用于本发明实施例， 下面将列举几种比 较典型的情况进行介绍。
1、 防潮物 205混合于胶膜 204中且与 OLED基板 201接触。
比如， 如图 5A所示， 防潮物 205混合于胶膜 204中， 防潮物 205的 A 端与 OLED基板 201接触， 并且防潮物 205的 B端未与封装盖板 203接触。
2、 防潮物 205混合于胶膜 204中且与封装盖板 203接触。
比如， 如图 5B所示， 防潮物 205混合于胶膜 204中， 防潮物 205的 a 端与封装盖板 203接触， 并且防潮物 205的 b端未与 OLED基板 201接触。
3、 防潮物 205混合于胶膜 204中且与 OLED基板 201和封装盖板 203 接触。
比如， 如图 5C所示， 防潮物 205混合于胶膜 204中， 并且防潮物 205 与 OLED基板 201和封装盖板 203接触。 防潮物 205与封装盖板 203的接触 点为 E点， 防潮物 205与 OLED基板 201的接触点为 F点。
4、防潮物 205混合于胶膜 204中且未与 OLED基板 201和封装盖板 203 接触 （即， 防潮物 205不接触 OLED基板 201且不接触封装盖板 203 ) 。
比如， 如图 5D所示， 防潮物 205混合于胶膜 204中， 防潮物 205不与 OLED基板 201接触且不与封装盖板 203接触。
二、 防潮物 205包括颗粒状干燥剂的物体。
例如， 防潮物 205为对包括颗粒状干燥剂与光感性液态材料的混合物进 行刻蚀处理后得到的第一附着物。
例如，防潮物 205附着于 OLED基板 201和 /或封装盖板 203,且胶膜 204 包覆防潮物 205。
比如， 如图 6所示， 一部分防潮物 205附着于 OLED基板 201 , 另一部 分防潮物 205附着于封装盖板 203, 胶膜 204包覆防潮物 205。
由于颗粒状干燥剂与光感性液态材料的混合物能够固定在 OLED基板 201和 /或封装盖板 203上， 因而对包括颗粒状干燥剂与光感性液态材料的混 合物进行刻蚀处理后得到的第一附着物能够附着于 OLED基板 201和 /或封装 盖板 203。 比如光敏树脂。
防潮物 205的形状可与刻蚀处理时采用的掩膜版的形状有关。 例如， 防 潮物和 /或防氧化物的形状可以为规则形状， 也可以为不规则形状； 较佳地， 防潮物和 /或防氧化物的形状包括圓柱形和 /或圓球
在防潮物 205的形状包括圓柱形和 /或圓球形时，防潮物 205接触空气中 的水汽的面积比较大， OLED显示面板吸收水汽的效果比较好。
在防潮物 205附着于 OLED基板 201和封装盖板 203时， OLED显示面 板吸收水汽的效果比较好。 防氧化物 206; 防氧化物 206设于所述胶膜 204中。
OLED显示面板包括的防氧化物 206可以还原氧气， 避免空气中的氧气 对 OLED结构 202中的有机发光材料产生消极影响。 OLED显示面板包括的防氧化物 206越多， OLED显示面板还原氧气的 效果越好。
例如， 防氧化物 206可以为任何能够还原氧气的物体， 比如， 还原剂或 者包括还原剂的物体。 例如， 防氧化物 206可以为化学还原剂或者物理还原 剂， 比如， 固体还原剂。
例如， 防氧化物 206为颗粒状还原剂 （比如， Fe (铁）微粒）或者对包 括颗粒状还原剂与光感性液态材料的混合物进行刻蚀处理后得到的第二附着 物。
例如， 防氧化物 206的形状和大小的实施方式与防潮物 205的形状和大 小的实施方式类似， 在此不再赘述。
例如， 防氧化物 206设于胶膜 204中的实施方式与防潮物 205设于胶膜 204中的实施方式类似， 在此不再赘述。
例如， 混合于胶膜 204中的防潮物 205和 /或防氧化物 206均匀分布； 或 混合于胶膜 204中的防潮物 205和 /或防氧化物 206聚集在胶膜 204中的 至少一个区域。
例如， 聚集防潮物 205和 /或防氧化物 206的区域的形状包括圓形和 /或 多边形。 例如， 混合于胶膜 204中的防潮物 205和 /或防氧化物 206在 OLED 基板 201上的投影呈四边形分布。
例如， 防潮物 205和 /或防氧化物 206附着于 OLED基板 201和 /或封装 盖板 203, 且胶膜 204包覆防潮物 205和防氧化物 206。
例如， 防潮物 205和 /或防氧化物 206的形状包括圓柱形和 /或圓球形。 例如， 如图 7所示， 胶膜 204设于 OLED基板 201上未被 OLED结构 202覆盖的区域且胶膜 204的厚度等于 OLED结构 202的厚度。
例如，在胶膜 204设于 OLED基板 201上未被 OLED结构 202覆盖的区 域且胶膜 204的厚度等于 OLED结构 202的厚度时，可以减小 OLED显示面 板的厚度， 从而减小 OLED显示面板的体积。
例如， 本发明实施例的显示装置， 包括上述所述的 OLED显示面板。 如图 8所示， 本发明的一个实施例的 OLED显示面板封装方法， 包括如 下步骤：
步骤 801、 在 OLED基板和 /或封装盖板上形成胶膜， 其中， 所述胶膜中 包含有用于吸收水汽的防潮物；
步骤 802、 将所述 OLED基板与封装盖板相对设置， 完成封装。
例如， 所述胶膜中还可以包含有用于还原氧气的防氧化物。
例如， 所述防潮物为颗粒状干燥剂， 所述防氧化物为颗粒状还原剂。 在 OLED基板和 /或封装盖板上形成包含有防潮物和防氧化物的胶膜， 例如， 可 以将防潮物和防氧化物混合到胶膜中， 并将混合有防潮物和防氧化物的所述 胶膜设于 OLED基板和 /或封装盖板上。
例如， 可以采用现有技术中将两个或多个物体混合的方法， 将防潮物和 防氧化物混合到胶膜中， 比如， 可以将防潮物和防氧化物加入到胶膜中， 搅 拌加入防潮物和防氧化物的胶膜， 从而实现将防潮物和防氧化物混合到胶膜 中。
例如， 将防潮物和防氧化物混合到胶膜中之后， 可以将混合有防潮物和 防氧化物的所述胶膜设于 OLED基板和 /或封装盖板上之前， 还可以对防潮 物、 防氧化物和胶膜构成的混合物进行脱泡处理。
对防潮物、 防氧化物和胶膜构成的混合物进行脱泡处理， 能够提高防潮 物和防氧化物与胶膜的密合度。
例如，可以采用现有技术中将胶膜设于 OLED基板和 /或封装盖板上的方 法，将混合有防潮物和防氧化物的胶膜设于 OLED基板和 /或封装盖板上， 比 如， 可以采用涂覆法将混合有防潮物和防氧化物的胶膜设于 OLED基板和 / 或封装盖板上。
例如， 防潮物为对包括颗粒状干燥剂与光感性液态材料的混合物进行刻 蚀处理后得到的第一附着物， 防氧化物为对包括颗粒状还原剂与光感性液态 材料的混合物进行刻蚀处理后得到的第二附着物，在 OLED基板和 /或封装盖 板上形成包含有防潮物和防氧化物的胶膜，例如，可在 OLED基板和 /或封装 盖板上形成附着的防潮物和防氧化物， 并将胶膜包覆住所述防潮物和防氧化 物。
例如，在 OLED基板和 /或封装盖板上形成附着的防潮物和防氧化物，例 如， 可以将防潮物和防氧化物与光感性液态材料混合， 并将防潮物、 防氧化 物和光感性液态材料的混合物设于 OLED基板和 /或封装盖板上；通过光刻工 艺， 在 OLED基板和 /或封装盖板上形成附着的防潮物和防氧化物。
例如，附着在 OLED基板和 /或封装盖板上的防潮物和防氧化物的形状与 光刻工艺中采用的掩膜版有关。
将胶膜包覆住所述防潮物和防氧化物， 例如， 可将胶膜设于附着有防潮 物和防氧化物的 OLED基板和 /或封装盖板上。
由于胶膜为胶体， 因而在将胶膜设于附着有防潮物和防氧化物的 OLED 基板和 /或封装盖板上后， 胶膜会包覆住所述防潮物和防氧化物， 从而实现在 OLED基板和 /或封装盖板上形成包含有防潮物和防氧化物的胶膜。
尽管上面已描述了本发明的优选实施例， 但本领域内的技术人员一旦得 知了基本创造性概念， 则可对这些实施例作出另外的变更和修改。 所以， 所 附权利要求意欲解释为包括优选实施例以及落入本发明范围的所有变更和修 改。

Claims

权利要求书
1、 一种 OLED显示面板， 包括 OLED基板， 与所述 OLED基板相对设 置的封装盖板， 设于所述 OLED基板和封装盖板之间的胶膜， 以及吸收水汽 的防潮物； 其中， 所述防潮物设于所述胶膜中。
2、 如权利要求 1所述的 OLED显示面板， 其中， 所述防潮物为颗粒状 干燥剂。
3、 如权利要求 1或 2所述的 OLED显示面板， 还包括用于还原氧气的 防氧化物； 其中， 所述防氧化物设于所述胶膜中。
4、 如权利要求 3所述的 OLED显示面板， 其中， 所述防氧化物为颗粒 状还原剂。
5、 如权利要求 3或 4所述的 OLED显示面板， 其中， 混合于所述胶膜 中的所述防潮物和 /或防氧化物均匀分布； 或
混合于所述胶膜中的所述防潮物和 /或防氧化物聚集在所述胶膜中的至 少一个区域。
6、 如权利要求 5所述的 OLED显示面板， 其中， 聚集防潮物和 /或防氧 化物的区域的形状包括圓形和 /或多边形。
7、 如权利要求 3或 4所述的 OLED显示面板， 其中， 混合于所述胶膜 中的防潮物和 /或防氧化物在所述 OLED基板上的投影呈四边形分布。
8、 如权利要求 1-7任一所述的 OLED显示面板， 其中， 所述防潮物为 对包括颗粒状干燥剂与光感性液态材料的混合物进行刻蚀处理后得到的第一 附着物。
9、 如权利要求 4-8任一所述的 OLED显示面板， 其中， 所述防氧化物 为对包括颗粒状还原剂与光感性液态材料的混合物进行刻蚀处理后得到的第 二附着物。
10、 如权利要求 1-9任一所述的 OLED显示面板， 其中， 所述防潮物和 /或防氧化物附着于所述 OLED基板和 /或封装盖板， 且所述胶膜包覆所述防 潮物和防氧化物。
11、 如权利要求 4-8任一所述的 OLED显示面板， 其中， 所述防潮物和 /或防氧化物的形状包括圓柱形和 /或圓球形。
12、 如权利要求 1-11所述的 OLED显示面板， 其中， 所述胶膜设于所 述 OLED基板上未被 OLED 结构覆盖的区域且所述胶膜的厚度等于所述 OLED结构的厚度。
13、 一种显示装置， 包括如权利要求 1~12任一所述的 OLED显示面板。
14、 一种 OLED显示面板封装方法， 包括：
在 OLED基板和 /或封装盖板上形成胶膜，其中，所述胶膜中包含有用于 吸收水汽的防潮物；
将所述 OLED基板与封装盖板相对设置， 完成封装。
15、如权利要求 14所述的方法， 其中， 所述胶膜中还包含有用于还原氧 气的防氧化物。
16、 如权利要求 15所述的方法， 其中， 所述防潮物为颗粒状干燥剂， 所 述防氧化物为颗粒状还原剂，在 OLED基板和 /或封装盖板上形成包含有防潮 物和防氧化物的胶膜包括：
将防潮物和防氧化物混合到胶膜中， 并将混合有防潮物和防氧化物的所 述胶膜设于 OLED基板和 /或封装盖板上。
17、如权利要求 15所述的方法， 其中， 所述防潮物为对包括颗粒状干燥 剂与光感性液态材料的混合物进行刻蚀处理后得到的第一附着物， 所述防氧 化物为对包括颗粒状还原剂与光感性液态材料的混合物进行刻蚀处理后得到 的第二附着物，在 OLED基板和 /或封装盖板上形成包含有防潮物和防氧化物 的胶膜包括：
在 OLED基板和 /或封装盖板上形成附着的防潮物和防氧化物，并将胶膜 包覆住所述防潮物和防氧化物。
PCT/CN2013/081460 2013-05-24 2013-08-14 Oled显示面板及其封装方法、显示装置 Ceased WO2014187032A1 (zh)