WO2014153491A1 - Bainitic microalloy steel with enhanced nitriding characteristics - Google Patents
Bainitic microalloy steel with enhanced nitriding characteristics Download PDFInfo
- Publication number
- WO2014153491A1 WO2014153491A1 PCT/US2014/031398 US2014031398W WO2014153491A1 WO 2014153491 A1 WO2014153491 A1 WO 2014153491A1 US 2014031398 W US2014031398 W US 2014031398W WO 2014153491 A1 WO2014153491 A1 WO 2014153491A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- steel part
- degrees
- steel
- approximately
- forged steel
- Prior art date
Abstract
Description
Claims