WO2014106859A2 - Procédé pour enduction de papier et de cartons - Google Patents

Procédé pour enduction de papier et de cartons Download PDF

Info

Publication number
WO2014106859A2
WO2014106859A2 PCT/IN2014/000001 IN2014000001W WO2014106859A2 WO 2014106859 A2 WO2014106859 A2 WO 2014106859A2 IN 2014000001 W IN2014000001 W IN 2014000001W WO 2014106859 A2 WO2014106859 A2 WO 2014106859A2
Authority
WO
WIPO (PCT)
Prior art keywords
surface treatment
film
paper
base paper
treatment formulation
Prior art date
Application number
PCT/IN2014/000001
Other languages
English (en)
Other versions
WO2014106859A3 (fr
Inventor
Ramjee Subramanian
Chidambara Vinayagam CHAVADI ALWARKURICHI SIVASAILAPPAN
Biman Kanti GHOSH
Original Assignee
Itc Limited
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Itc Limited filed Critical Itc Limited
Publication of WO2014106859A2 publication Critical patent/WO2014106859A2/fr
Publication of WO2014106859A3 publication Critical patent/WO2014106859A3/fr

Abstract

La présente invention concerne un procédé pour transférer une formulation d'enduction (210) sur un papier de base. Dans un mode de réalisation, le procédé comprend l'application d'au moins une couche de la formulation d'enduction (210) sur un film non absorbant (204) pour former un substrat traité (218). Le procédé comprend en outre le transfert de la formulation d'enduction (210) du substrat traité (218) au papier de base (220), pour créer un papier de base traité (226). L'énergie de surface de la formulation d'enduction (210) est inférieure à l'énergie de surface du film non absorbant (204) et à l'énergie de surface du papier de base (220).
PCT/IN2014/000001 2013-01-03 2014-01-01 Procédé pour enduction de papier et de cartons WO2014106859A2 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
IN6/KOL/2013 2013-01-03
IN6KO2013 2013-01-03

Publications (2)

Publication Number Publication Date
WO2014106859A2 true WO2014106859A2 (fr) 2014-07-10
WO2014106859A3 WO2014106859A3 (fr) 2014-09-04

Family

ID=51062533

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IN2014/000001 WO2014106859A2 (fr) 2013-01-03 2014-01-01 Procédé pour enduction de papier et de cartons

Country Status (1)

Country Link
WO (1) WO2014106859A2 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020201716A1 (fr) * 2019-04-05 2020-10-08 British American Tobacco (Investments) Limited Article à fumer

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2407549A (en) * 1943-03-11 1946-09-10 Gurwick Irving Method of surface coating tissue paper with thermoresponsive resins
US4489738A (en) * 1983-03-07 1984-12-25 Eli Simon Self-extinguishing cigarettes
EP0532193A1 (fr) * 1991-09-10 1993-03-17 Philip Morris Products Inc. Enveloppe pour articles à fumer pour contrôler la vitesse de combustion et procédé de sa production
WO2002055294A1 (fr) * 2001-01-15 2002-07-18 Rfs Ecusta Nouvelles matieres et procede de fabrication afferent pour produits a faible propension a la combustion
US20040118420A1 (en) * 2002-12-20 2004-06-24 Barnes Vernon Brent Equipment and methods for manufacturing cigarettes
US6854469B1 (en) * 2001-06-27 2005-02-15 Lloyd Harmon Hancock Method for producing a reduced ignition propensity smoking article
US7285182B2 (en) * 2002-03-19 2007-10-23 Ciba Specialty Chemicals Corporation Composition for surface treatment of paper
US20110290436A1 (en) * 2010-05-20 2011-12-01 Jocelyne Dumas Paper for smoking article having low ignition propensity properties
US20120227754A1 (en) * 2011-03-10 2012-09-13 Norman Alan B Smoking articles and wrapping materials therefor

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2407549A (en) * 1943-03-11 1946-09-10 Gurwick Irving Method of surface coating tissue paper with thermoresponsive resins
US4489738A (en) * 1983-03-07 1984-12-25 Eli Simon Self-extinguishing cigarettes
EP0532193A1 (fr) * 1991-09-10 1993-03-17 Philip Morris Products Inc. Enveloppe pour articles à fumer pour contrôler la vitesse de combustion et procédé de sa production
WO2002055294A1 (fr) * 2001-01-15 2002-07-18 Rfs Ecusta Nouvelles matieres et procede de fabrication afferent pour produits a faible propension a la combustion
US6854469B1 (en) * 2001-06-27 2005-02-15 Lloyd Harmon Hancock Method for producing a reduced ignition propensity smoking article
US7285182B2 (en) * 2002-03-19 2007-10-23 Ciba Specialty Chemicals Corporation Composition for surface treatment of paper
US20040118420A1 (en) * 2002-12-20 2004-06-24 Barnes Vernon Brent Equipment and methods for manufacturing cigarettes
US20110290436A1 (en) * 2010-05-20 2011-12-01 Jocelyne Dumas Paper for smoking article having low ignition propensity properties
US20120227754A1 (en) * 2011-03-10 2012-09-13 Norman Alan B Smoking articles and wrapping materials therefor

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020201716A1 (fr) * 2019-04-05 2020-10-08 British American Tobacco (Investments) Limited Article à fumer
JP2022528901A (ja) * 2019-04-05 2022-06-16 ブリティッシュ アメリカン タバコ （インヴェストメンツ） リミテッド 喫煙品
JP7418467B2 (ja) 2019-04-05 2024-01-19 ブリティッシュ アメリカン タバコ （インヴェストメンツ） リミテッド 喫煙品

Also Published As

Publication number Publication date
WO2014106859A3 (fr) 2014-09-04

Similar Documents

Publication Publication Date Title
CA2427830C (fr) Procede de production de produits du tabac permettant de reduire le risque d'allumage, et produits fabriques selon ce procede
JP6193363B2 (ja) 開口領域のあるバンドを有するバンド付シガレットラッパー
JP5214702B2 (ja) 発火傾向特性が低減された喫煙品
JP5334959B2 (ja) 皺防止剤でパターンが付けられた包装紙
JP5876220B2 (ja) 喫煙物品の発火性特性を低減するための巻紙上の処理領域
EP0870437A2 (fr) Enveloppe d'article à fumer pour contrÔler la propension à l'allumage d'un article à fumer sans affecter les caractéristiques de consommation
AU2010278397A1 (en) Banded paper, smoking article and method
PT2155004E (pt) Artigos para fumar com papel com faixas
CN109890881A (zh) 用于形成包含纳米纤维素的膜的方法
WO2014106859A2 (fr) Procédé pour enduction de papier et de cartons
PT2071965E (pt) Artigo de fumar com características melhoradas de extinção
US20230301343A1 (en) Low ignition propensity cigarette paper and manufacture thereof
JP3176539B2 (ja) 調湿性低密度紙及びその製造方法
JP2002019296A5 (fr)
EA025115B1 (ru) Способ изготовления оберточной бумаги для курительных изделий
CZ306256B6 (cs) Zařízení a způsob pro povrchovou aktivaci vrstev celulózových vláken, materiálů na bázi papíru a kartónových desek

Legal Events

Date Code Title Description
122 Ep: pct application non-entry in european phase

Ref document number: 14735262

Country of ref document: EP

Kind code of ref document: A2