WO2014077729A1 - Granulated filler for a toilet for pets and method for manufacturing same - Google Patents

Granulated filler for a toilet for pets and method for manufacturing same Download PDF

Info

Publication number
WO2014077729A1
WO2014077729A1 PCT/RU2013/000198 RU2013000198W WO2014077729A1 WO 2014077729 A1 WO2014077729 A1 WO 2014077729A1 RU 2013000198 W RU2013000198 W RU 2013000198W WO 2014077729 A1 WO2014077729 A1 WO 2014077729A1
Authority
WO
WIPO (PCT)
Prior art keywords
bentonite clay
components
glauconite
enriched glauconite
diatomite
Prior art date
Application number
PCT/RU2013/000198
Other languages
French (fr)
Russian (ru)
Inventor
Виктор Геннадиевич СЕРЖАНТОВ
Original Assignee
Serzhantov Viktor Gennadievich
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Serzhantov Viktor Gennadievich filed Critical Serzhantov Viktor Gennadievich
Publication of WO2014077729A1 publication Critical patent/WO2014077729A1/en

Abstract

The group of inventions relates to means for the care of pets, in particular to toilet fillers for pets. A granulated filler on the basis of natural rocks comprises bentonite clay and natural sorbents, with the natural sorbents used being zeolite, diatomite or a mixture thereof in different ratios. The binder introduced is a magnetic fraction of finely disperse enriched glauconite with a concentration of at least 92%, wherein the finely disperse bentonite clay comprises at least 70% of montmorillonite. The combinations of components of natural sorbents used, in addition are shungite and dolomite. The method for manufacturing a granulated filler comprises preparing the starting material, wherein the starting material used comprises binders, namely a magnetic fraction of finely disperse enriched glauconite with a concentration of at least 92% and finely disperse bentonite clay comprising at least 70% montmorillonite, mixing the binders with combinations of finely disperse components of sorbents (diatomite, shungite, zeolite, dolomite in various ratios), grinding the mixture, mixing the mixture with water to a moisture content of the resultant mass of at least 27%, granulating, drying the granules with hot air at no lower than 60°C to a moisture content of no greater than 10%, crushing, screening, sorting according to granulometric composition, and then packing.

Description

ГРАНУЛИРОВАННЫЙ НАПОЛНИТЕЛЬ ТУАЛЕТА ДЛЯ ДОМАШНИХ ЖИВОТНЫХ И СПОСОБ ЕГО ИЗГОТОВЛЕНИЯ  GRANULATED TOILET FILLER FOR PETS AND METHOD FOR ITS MANUFACTURE
Область техники  Technical field
Группа изобретений относится к области удовлетворения жизненных потребностей, а именно к средствам ухода за домашними животными, в частности к наполнителям туалетов для домашних животных, обитающих в жилище человека, а также способам их изготовления. Новые составы наполнителей могут быть охарактеризованы как сорбенты влаги и неприятных запахов.  The group of inventions relates to the field of satisfying vital needs, and in particular to pet care products, in particular, toilets for toilets for pets living in a person’s home, as well as methods for their manufacture. New compositions of fillers can be characterized as sorbents of moisture and unpleasant odors.
Предшествующий уровень техники  State of the art
Известен гигиенический наполнитель «CATSAN®» для кошачьего туалета, содержащий белые гранулы, состоящие из натурального кварцевого песка, очищенного мела и минеральных добавок, разработанный фирмой "WALTHAM", изготовитель Effet GmbH, 27281 Verden/Allor, Germany. Known for the hygienic filler "CATSAN ® " for cat litter, containing white granules consisting of natural quartz sand, refined chalk and mineral additives, developed by WALTHAM, manufactured by Effet GmbH, 27281 Verden / Allor, Germany.
Недостатками гигиенического наполнителя являются недостаточно высокое поглощение запаха, невысокое водопоглощение - 50-60% и высокая стоимость.  The disadvantages of the hygienic filler are insufficiently high odor absorption, low water absorption - 50-60% and high cost.
Известен наполнитель туалетов для домашних животных на основе вермикулита, перлита с добавлением различных ароматизирующих отдушек (1-3% от массы наполнителя) с запахом апельсина, лимона и т.д. (см. патент США на изобретение JV° 4085704, МПК А01К 29/00, опубл. 25.04.1978 г.).  Known filler for toilets for pets based on vermiculite, perlite with the addition of various flavoring fragrances (1-3% by weight of the filler) with the smell of orange, lemon, etc. (see US patent for the invention JV ° 4085704, IPC A01K 29/00, publ. 04/25/1978).
Недостатком наполнителя туалетов для домашних животных является низкая сорбционная емкость по аммиаку, а для устранения запаха применяются маскирующие отдушки, которые обладают высокой аллергенностью.  The disadvantage of filler toilets for pets is the low sorption capacity for ammonia, and masking fragrances that are highly allergenic are used to eliminate odor.
Известен наполнитель туалета для кошек, содержащий бентонит, при этом он содержит перемешанный с глиной бентонит в количестве 5-50% и выполнен высушенным, обожженным и дробленым до размера гранул (частиц) 1-7 мм (см. патент РФ на изобретение JN° 2125792, МПК АО 1 23/00, опубл. 10.02.1999 г.).  Known cat litter filler containing bentonite, while it contains bentonite mixed with clay in an amount of 5-50% and is dried, calcined and crushed to a particle size of 1-7 mm (see RF patent for the invention JN ° 2125792 , IPC AO 1 23/00, publ. 02/10/1999).
Недостатком наполнителя туалета для кошек является недостаточно высокое поглощение запаха и низкий влагопоглотительный сорбирующий эффект.  The disadvantage of a cat litter is the lack of a high odor absorption and low moisture-absorbing sorbing effect.
Известен гигиенический наполнитель для содержания животных на основе природных сорбентов из опал-кристобалитовых сорбентов типа диатомитов, трепелов, опок, содержащий связующие добавки, при этом наполнитель выполнен в виде гранул, термически обработанных при температурах 150-1200°С, а в качестве природных сорбентов использованы сорбенты, имеющие общую пористость 30- 95%, сорбциоиную емкость 25,0-350 мгэ-экв/100 г, влагопоглощение 200-800%. В качестве связующей добавки использован гипс с содержанием 1-3%, от массы наполнителя, либо жидкое стекло с содержанием 15-20% от массы наполнителя, либо технический желатин с содержанием 10-25% от массы наполнителя. В наполнитель дополнительно введен ароматизатор (см. заявку на вьщачу патента РФ на изобретение Ш 20031 1 1 107, МПК АО 1 К 23/00, опубл. 10.12.2004 г.). Known hygienic filler for keeping animals on the basis of natural sorbents from opal-cristobalite sorbents such as diatomites, tripoli, flasks containing binders, the filler is made in the form of granules, heat-treated at temperatures of 150-1200 ° C, and used as natural sorbents sorbents having a total porosity of 30-95%, sorption capacity 25.0-350 mEq / 100 g, moisture absorption 200-800%. AT gypsum with a content of 1-3% by weight of the filler, or liquid glass with a content of 15-20% by weight of the filler, or technical gelatin with a content of 10-25% by weight of the filler, was used as a binder. A flavoring agent is additionally introduced into the filler (see the application for a patent of the Russian Federation for invention Ш 20031 1 1 107, IPC AO 1 K 23/00, published on December 10, 2004).
Недостатками гигиенического наполнителя для содержания животных является факт резкой потери сорбционной емкости природных сорбентов (диатомита и опоки) при их нагревании свыше температуры 200°С, так как при этом снижается их прочность и, кроме того, резко падает сорбционная емкость по отношению к различным неорганическим и органическим веществам. Введение различных ароматизаторов снижает все преимущества природных сорбентов.  The disadvantages of a hygienic filler for keeping animals is the fact that there is a sharp loss in the sorption capacity of natural sorbents (diatomite and flask) when they are heated above 200 ° C, since this decreases their strength and, in addition, the sorption capacity with respect to various inorganic and organic matter. The introduction of various flavorings reduces all the benefits of natural sorbents.
Известен способ изготовления наполнителя туалетов для кошек, предусматривающий обработку исходного сырья, при этом в качестве исходного сырья используют кремнеземсодержащую породу - опоку с содержанием, мас.%: Fe203 - 1,2-3,7; А1203 - 3,9-11,4; MgO - 0,3-2,1 ; СаО - 1,2-13,1 ; S03 - 0,1-0,8; Si02 - остальное, причем обработку опоки проводят путем ее дробления, измельчения до размера частиц 0,5-7,0 мм и прокаливания при 300-350°С в течение 10-30 с. В опоку дополнительно вводят ароматизаторы и твердые адсорбенты в любом необходимом количестве (см. патент РФ на изобретение J e 2134957, МПК А01К 1/035, А01К 1/015, А01К 23/00, опубл. 27.08.1999 г.). A known method of manufacturing a filler of toilets for cats, involving the processing of feedstock, while the feedstock used is siliceous rock - flask with a content, wt.%: Fe 2 0 3 - 1.2-3.7; A1 2 0 3 - 3.9-11.4; MgO - 0.3-2.1; CaO - 1.2-13.1; S0 3 - 0.1-0.8; Si0 2 - the rest, and the processing of the flask is carried out by crushing it, grinding it to a particle size of 0.5-7.0 mm and calcining at 300-350 ° C for 10-30 s. Fragrances and solid adsorbents are additionally introduced into the flask in any required quantity (see RF patent for invention J e 2134957, IPC А01К 1/035, А01К 1/015, А01К 23/00, published on 08.27.1999).
К недостаткам способа изготовления наполнителя туалетов для кошек следует отнести длительность технологического процесса и получение наполнителя природного происхождения, минерал который имеет редкое происхождение и практически не добывается в качестве сопутствующего компонента при добыче других полезных ископаемых, а поэтому потребуются дополнительные затраты на производство горных работ и индивидуальное нанесение ущерба окружающей природной среде. Кроме того, при прокаливании опок до 300-350°С их сорбционная способность по отношению к различным органическим соединениям, например аминам, меркаптанам и др., резко уменьшается. Введение различных ароматизаторов и наполнителей сводит на нет все преимущества опок как сорбентов.  The disadvantages of the method of manufacturing a filler of toilets for cats should include the duration of the process and the production of filler of natural origin, a mineral which is of rare origin and is practically not mined as an accompanying component in the extraction of other minerals, and therefore additional costs for mining and individual application will be required damage to the environment. In addition, when the flasks are calcined to 300-350 ° С, their sorption ability with respect to various organic compounds, for example amines, mercaptans, etc., sharply decreases. The introduction of various flavors and fillers negates all the advantages of flasks as sorbents.
Наиболее близким по технической сущности к предложенному изобретению является известный гигиенический наполнитель для кошачьего туалета на основе природных пород (см. патент РФ на изобретение N° 2127041 , МПК А01К 1/015, опубл. 10.03.1999 г.), в котором в качестве пород используют природные минеральные сорбенты, обладающие общей пористостью 50 - 90%, сорбционной емкостью 25,0-250 мг-экв/100 г, водопоглощением 50-200%, типа опок или трепелов, в отдельности или в смеси с другими природными минеральными сорбентами, термически обработанными при температуре 90-1200°С, измельченными до фракции 1-7 мм и герметически упакованными. В качестве природных сорбентов используют цеолиты, диатомиты, опоки, трепелы, палыгорскиты, бентониты, перлиты, глаукониты, вермикулиты или их смесь в различных соотношениях. В наполнитель вводят гипс в количестве 1-2% от его массы. The closest in technical essence to the proposed invention is a well-known hygienic filler for a cat toilet based on natural breeds (see RF patent for the invention N ° 2127041, IPC A01K 1/015, publ. March 10, 1999), in which natural mineral sorbents are used as rocks, having a total porosity of 50 - 90%, a sorption capacity of 25.0-250 mEq / 100 g, and water absorption of 50-200%, such as flasks or tripoli, individually or in a mixture with other natural mineral sorbents, thermally treated at a temperature of 90-1200 ° C, crushed to a fraction of 1-7 mm and hermetically packed. As natural sorbents, zeolites, diatomites, flasks, tripoli, palygorskites, bentonites, perlites, glauconites, vermiculites or their mixture in various ratios are used. Gypsum is introduced into the filler in an amount of 1-2% of its mass.
Недостатком гигиенического наполнителя для кошачьего туалета на основе природных пород является факт резкой потери сорбционной емкости цеолита, диатомита и опоки при их нагревании свыше температуры 200°С, так как при этом снижается их прочность и, кроме того, резко падает сорбционная емкость по отношению к различным неорганическим и органическим веществам, что связано с разрушением естественных сорбирующих формирований у названных природных алюмосиликатов, представляющих собой неорганические макроциклические ионофоры. Кроме того, введение в наполнитель гипса приводит к тому, что гипс разносится домашними животными по жилому помещению.  A disadvantage of the hygienic filler for a cat litter based on natural breeds is the fact of a sharp loss of the sorption capacity of zeolite, diatomite and flask when they are heated above 200 ° C, as this reduces their strength and, in addition, the sorption capacity decreases sharply with respect to various inorganic and organic substances, which is associated with the destruction of natural sorbing formations of the named natural aluminosilicates, which are inorganic macrocyclic ionophores. In addition, the introduction of gypsum into the filler leads to the fact that the gypsum is carried by domestic animals in the living room.
Также наиболее близким по технической сущности к предложенному изобретению является известный способ производства гигиенического наполнителя, включающий сушку, обжиг природных сорбентов и расфасовку наполнителя, при этом перед сушкой природных сорбентов производят сначала их дробление, затем их рассеивание до фракции 0,05-1 мм, после чего полученную массу высушивают при температуре 20-50°С, вводят в нее связующую добавку и/или ароматизатор и производят гранулирование наполнителя до фракции 2-10 мм, затем осуществляют его термическую обработку при температурах 150-1200°С с временным интервалом от 30 мин до 24 ч и последующую расфасовку (см. заявку на выдачу патента РФ на изобретение Ш 20031 1 1 107, МПК А01 23/00, опубл. 10.12.2004 г.).  Also the closest in technical essence to the proposed invention is a known method for the production of hygienic filler, including drying, firing of natural sorbents and packaging of the filler, while before drying the natural sorbents, they are first crushed, then dispersed to a fraction of 0.05-1 mm, after whereby the resulting mass is dried at a temperature of 20-50 ° C, a binder additive and / or flavor are introduced into it, and the filler is granulated to a fraction of 2-10 mm, then it is heat treated tissue at temperatures of 150-1200 ° C with a time interval of 30 minutes to 24 hours and subsequent packaging (see application for the grant of a patent of the Russian Federation for invention Ш 20031 1 1 107, IPC A01 23/00, publ. 10.12.2004) .
Недостатками способа производства гигиенического наполнителя является длительность технологического процесса, а также то, что при прокаливании опок до 1200°С их сорбционная способность по отношению к различным органическим соединениям, например аминам, меркаптанам и др., резко уменьшается. Введение различных ароматизаторов и наполнителей сводит на нет все преимущества опок как сорбентов. The disadvantages of the method of production of hygienic filler is the duration of the process, and the fact that when the flasks are calcined to 1200 ° C, their sorption ability with respect to various organic compounds, for example amines, mercaptans, etc., decreases sharply. Introduction various flavors and fillers negates all the advantages of flasks as sorbents.
Раскрытие изобретения  Disclosure of invention
Основной задачей настоящего изобретения является разработка экономичного способа получения гигиенического гранулированного наполнителя на основе обогащенного глауконитового связующего с комбинацией компонент природных сорбентов для сорбции различных газообразных, жидких, пахучих и токсичных веществ.  The main objective of the present invention is to develop an economical method for producing a hygienic granular filler based on an enriched glauconite binder with a combination of components of natural sorbents for sorption of various gaseous, liquid, odorous and toxic substances.
Единым техническим результатом, достигаемым при решении настоящей задачи при осуществлении группы изобретений, является обеспечение максимального запахо-влагопоглотителыюго сорбирующего эффекта наполнителя, адаптированного под различных домашних животных и их привыкание к новому гранулированному гигиеническому наполнителю за счет оптимального качественного и количественного подбора исходных компонентов, а также снижение энергозатрат за счет уменьшения температуры технологического процесса.  The single technical result achieved in solving this problem when implementing the group of inventions is to provide the maximum odor-moisture absorbing sorbing effect of the filler, adapted for various domestic animals and their getting used to the new granular hygienic filler due to the optimal qualitative and quantitative selection of the starting components, as well as reducing energy consumption by reducing the temperature of the process.
Указанный технический результат достигается тем, что в гранулированном наполнителе туалета для домашних животных на основе природных пород, содержащим бентонитовую глину и природные сорбенты, в качестве которых используют цеолит, диатомит или их смесь в различных соотношениях, согласно изобретения, в качестве связующего введена магнитная фракция мелкодисперсного обогащенного глауконита концентрацией не менее 92%, при этом мелкодисперсная бентонитовая глина содержит не менее 70% монтмориллонита, а в качестве комбинаций компонент природных сорбентов дополнительно используют шунгит, доломит.  The specified technical result is achieved by the fact that in the granular filler of the toilet for pets based on natural breeds containing bentonite clay and natural sorbents, which are used as zeolite, diatomite or a mixture thereof in various proportions, according to the invention, a finely divided magnetic fraction is introduced as a binder enriched glauconite with a concentration of not less than 92%, while finely dispersed bentonite clay contains at least 70% montmorillonite, and as a combination of natural components GOVERNMENTAL sorbent additionally used shungite dolomite.
Целесообразно, чтобы наполнитель содержал обогащенный глауконит, бентонитовую глину и диатомит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 10-50;  It is advisable that the filler contains enriched glauconite, bentonite clay and diatomite in the following ratio of components, wt.%: Enriched glauconite - 10-50;
бентонитовая глина - 10-50;  bentonite clay - 10-50;
диатомит - 10-40.  diatomite - 10-40.
Целесообразно, чтобы наполнитель содержал обогащенный глауконит, бентонитовую глину и шунгит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 10-50;  It is advisable that the filler contains enriched glauconite, bentonite clay and shungite in the following ratio of components, wt.%: Enriched glauconite - 10-50;
бентонитовая глина - 10-50; шунгит - 10-40. bentonite clay - 10-50; shungite - 10-40.
Целесообразно, чтобы наполнитель содержал обогащенный глауконит, бентонитовую глину и цеолит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 10-50;  It is advisable that the filler contains enriched glauconite, bentonite clay and zeolite in the following ratio of components, wt.%: Enriched glauconite - 10-50;
бентонитовая глина - 10-50;  bentonite clay - 10-50;
цеолит - 10-40.  zeolite - 10-40.
Целесообразно, чтобы наполнитель содержал обогащенный глауконит, бентонитовую глину и доломит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 10-50;  It is advisable that the filler contains enriched glauconite, bentonite clay and dolomite in the following ratio of components, wt.%: Enriched glauconite - 10-50;
бентонитовая глина - 10-50;  bentonite clay - 10-50;
доломит - 10-40.  dolomite - 10-40.
Целесообразно, чтобы наполнитель содержал обогащенный глауконит, бентонитовую глину, диатомит и шунгит при следующем соотношении компонентов, мас.%:  It is advisable that the filler contains enriched glauconite, bentonite clay, diatomite and shungite in the following ratio of components, wt.%:
обогащенный глауконит - 10-50;  enriched glauconite - 10-50;
бентонитовая глина - 10-50;  bentonite clay - 10-50;
диатомит - 10-20;  diatomite - 10-20;
шунгит - 10-20.  shungite - 10-20.
Целесообразно, чтобы наполнитель содержал обогащенный глауконит, бентонитовую глину, диатомит и цеолит при следующем соотношении компонентов, мас.%:  It is advisable that the filler contains enriched glauconite, bentonite clay, diatomite and zeolite in the following ratio of components, wt.%:
обогащенный глауконит - 10-50;  enriched glauconite - 10-50;
бентонитовая глина - 10-50;  bentonite clay - 10-50;
диатомит - 10-20;  diatomite - 10-20;
цеолит - 10-20.  zeolite - 10-20.
Целесообразно, чтобы наполнитель содержал обогащенный глауконит, бентонитовую глину, диатомит и доломит при следующем соотношении компонентов, мас.%:  It is advisable that the filler contains enriched glauconite, bentonite clay, diatomite and dolomite in the following ratio of components, wt.%:
обогащенный глауконит - 10-50;  enriched glauconite - 10-50;
бентонитовая глина - 10-50;  bentonite clay - 10-50;
диатомит - 10-20;  diatomite - 10-20;
доломит - 10-20. Целесообразно, чтобы наполнитель содержал обогащенный глауконит, бентонитовую глину, шунгит и цеолит при следующем соотношении компонентов, мас.%: dolomite - 10-20. It is advisable that the filler contains enriched glauconite, bentonite clay, shungite and zeolite in the following ratio of components, wt.%:
обогащенный глауконит - 10-50;  enriched glauconite - 10-50;
бентонитовая глина - 10-50;  bentonite clay - 10-50;
шунгит - 10-20;  shungite - 10-20;
цеолит - 10-20.  zeolite - 10-20.
Целесообразно, чтобы наполнитель содержал обогащенный глауконит, бентонитовую глину, шунгит и доломит при следующем соотношении компонентов, мас.%:  It is advisable that the filler contains enriched glauconite, bentonite clay, shungite and dolomite in the following ratio of components, wt.%:
обогащенный глауконит - 10-50;  enriched glauconite - 10-50;
бентонитовая глина - 10-50;  bentonite clay - 10-50;
шунгит - 10-20;  shungite - 10-20;
доломит - 10-20.  dolomite - 10-20.
Целесообразно также, чтобы наполнитель содержал обогащенный глауконит, бентонитовую глину, цеолит и доломит при следующем соотношении компонентов, мас.%:  It is also advisable that the filler contains enriched glauconite, bentonite clay, zeolite and dolomite in the following ratio of components, wt.%:
обогащенный глауконит - 10-50;  enriched glauconite - 10-50;
бентонитовая глина - 10-50;  bentonite clay - 10-50;
цеолит - 10-20;  zeolite - 10-20;
доломит - 10-20.  dolomite - 10-20.
Указанный технический результат достигается также тем, что способ изготовления гранулированного наполнителя туалета для домашних животных на основе природных пород включает подготовку исходного сырья, при этом в качестве исходного сырья используют связующие магнитную фракцию мелкодисперсного обогащенного глауконита, концентрацией не менее 92%, и мелкодисперсную бентонитовую глину, содержащую не менее 70% монтмориллонита, перемешивание связующих с комбинациями мелкодисперсных компонент сорбентов диатомит, шунгит, цеолит, доломит в различных соотношениях, измельчение смеси, перемешивание с водой до влажности полученной массы не менее 27%, гранулирование, подсушивание гранул горячим воздухом не ниже 60°С до влажности не более 10%, дробление, просеивание, сортировку по гранулометрическому составу и последующую расфасовку. Целесообразно, чтобы измельчение смеси осуществлялось до фракции не более 60 мкм. The specified technical result is also achieved by the fact that the method of manufacturing a granular toilet filler for pets on the basis of natural breeds involves preparing the feedstock, using binder magnetic fraction of finely divided enriched glauconite with a concentration of at least 92% and finely dispersed bentonite clay containing at least 70% montmorillonite, mixing binders with combinations of finely divided components of the sorbents diatomite, shungite, zeolite, dolomite in in excellent ratios, grinding the mixture, mixing with water to a moisture content of not less than 27%, granulating, drying granules with hot air at least 60 ° C to a moisture content of not more than 10%, crushing, sieving, sorting according to particle size distribution and subsequent packaging. It is advisable that the grinding mixture was carried out to a fraction of not more than 60 microns.
Целесообразно, чтобы гранулирование осуществлялось до получения гранул диаметром от 2 до 7 мм, длиной от 30 до 110 мм.  It is advisable that the granulation was carried out to obtain granules with a diameter of 2 to 7 mm, a length of 30 to 110 mm.
Целесообразно, чтобы дробление полученных гранул осуществлялось до получения гранул неправильной формы, имеющих размер в поперечнике от 2 до 7 мм и длину от 2 до 7 мм.  It is advisable that the crushing of the obtained granules is carried out to obtain granules of irregular shape, having a size across from 2 to 7 mm and a length from 2 to 7 mm.
Целесообразно также, чтобы просеивание осуществлялось до размера частиц 2-7 мм.  It is also advisable that the sieving was carried out to a particle size of 2-7 mm
Введение в наполнитель в качестве связующего магнитной фракции мелкодисперсного обогащенного глауконита концентрацией не менее 92%, позволяет эффективнее использовать сорбционные свойства обогащенного глауконита. Если концентрация обогащенного глауконита более 92%, то использование бентонитовой глины в комбинации, как дополнительного связующего уменьшается, а сорбционная глауконитовая составляющая увеличивается. Глауконит по своим структурно-геохимическим свойствам является минеральным сырьем многоцелевого назначения. Однако применение необработанного глауконитового песка в качестве связующего, при всех его повышенных сорбционных свойствах, представляется невозможным из-за наличия в глауконитовом песке балласта (кварц, полевой шпат и т.д.) от 50 до 70%. Использование отсепарированной магнитной фракции обогащенного глауконита из глауконитового песка в качестве связующего при изготовлении гранул позволяет получить гранулированный сорбент, обладающий повышенными сорбционными способностями и ёмкостью.  The introduction into the filler as a magnetic binder fraction of finely divided enriched glauconite with a concentration of not less than 92% allows more efficient use of the sorption properties of enriched glauconite. If the concentration of enriched glauconite is more than 92%, then the use of bentonite clay in combination as an additional binder decreases, and the sorption glauconite component increases. Glauconite in its structural and geochemical properties is a mineral raw material for multipurpose use. However, the use of untreated glauconite sand as a binder, with all its enhanced sorption properties, seems impossible due to the presence of ballast (quartz, feldspar, etc.) in glauconite sand from 50 to 70%. The use of the separated magnetic fraction of enriched glauconite from glauconite sand as a binder in the manufacture of granules makes it possible to obtain a granular sorbent with enhanced sorption capabilities and capacity.
Обогащенный глауконит является связующим при изготовлении гранул, поэтому его соотношение мас.% к другим сорбционным компонентам должна быть больше, чтобы гранулы обладали хорошей прочностью и не разваливались, так как они не обжигаются при высоких температурах.  Enriched glauconite is a binder in the manufacture of granules, therefore, its ratio of wt.% To other sorption components should be greater so that the granules have good strength and do not fall apart, since they do not burn at high temperatures.
Введение в наполнитель дополнительного связующего мелкодисперсную бентонитовую глину, содержащую не менее 70% монтмориллонита, позволяет придать материалу перед гранулированием большую эластичность, что в свою очередь увеличивает прочностные качества гранулированного наполнителя. Если содержание монтмориллонита более 70%, то использование бентонитовой глины в комбинации, как дополнительного связующего уменьшается, а соотношение глауконитовой составляющей увеличивается. The introduction of an additional binder into the filler finely dispersed bentonite clay containing at least 70% montmorillonite allows the material to be given greater elasticity before granulation, which in turn increases the strength properties of the granular filler. If the content of montmorillonite is more than 70%, then the use of bentonite clay in combination, as an additional binder decreases, and the ratio of the glauconite component increases.
Бентонитовая глина с большой концентрацией монтмориллонита вводится в наполнитель, как дополнительное связующее для дублирования (страховки) обогащенного глауконита, чтобы гранулы обладали хорошей прочностью и не разваливались, если возникает необходимость использовать другие сорбирующие компоненты наполнителя в максимальных соотношениях, для усиления сорбционных, запахо-влагопоглощающих свойств наполнителя.  Bentonite clay with a high concentration of montmorillonite is introduced into the filler as an additional binder for duplication (insurance) of enriched glauconite, so that the granules have good strength and do not fall apart if it becomes necessary to use other sorbent components of the filler in maximum proportions, to enhance the sorption, odor-moisture-absorbing properties filler.
Использование в качестве комбинаций компонент природных мелкодисперсных сорбентов диатомита, шунгита, цеолита, доломита в различных соотношениях позволяет усилить запахо-влагопоглотительные сорбирующие эффекты наполнителя. Если используется один из перечисленных сорбентов, то он вводится в наполнитель в пределах 10-40 мас.%; если используются два из перечисленных сорбентов, то каждый из них вводится в наполнитель в пределах 10- 20 мас.%. Если в наполнитель вводить сорбенты в количестве более 40 мас.%, то их большее количество повлияет на твёрдость гранул, так как компоненты природных мелкодисперсных сорбентов не обладают связующими свойствами.  The use of components of natural finely dispersed sorbents of diatomite, shungite, zeolite, dolomite in various proportions allows you to enhance the odor-moisture-absorbing sorbing effects of the filler. If one of the listed sorbents is used, then it is introduced into the filler in the range of 10-40 wt.%; if two of the listed sorbents are used, then each of them is introduced into the filler in the range of 10-20 wt.%. If sorbents in an amount of more than 40 wt.% Are introduced into the filler, then their greater amount will affect the hardness of the granules, since the components of natural finely dispersed sorbents do not have binding properties.
Использование компонент природных сорбентов (диатомита, шунгита, цеолита, доломита) в различных комбинационных соотношениях позволяет получать гранулированные наполнители, адаптированные под различных домашних животных и быстрое их привыкание к новому гигиеническому наполнителю.  The use of components of natural sorbents (diatomite, shungite, zeolite, dolomite) in various combination ratios allows to obtain granular fillers adapted for various domestic animals and quickly get used to the new hygienic filler.
Разные комбинации компонент выбранных сорбентов связаны со способностью удерживать продолжительное время комплексные запахи, а также быстрого привыкания к новому гранулированному гигиеническому наполнителю различных домашних животных (кошки, собаки и т.д.).  Different combinations of the components of the selected sorbents are associated with the ability to retain complex odors for a long time, as well as quickly getting used to the new granular hygienic filler of various domestic animals (cats, dogs, etc.).
Исходным связующим сорбирующим компонентом для гранулирования гигиенического наполнителя туалета для домашних животных является:  The initial sorbent binder component for granulating a sanitary toilet pet filler is:
- магнитная фракция мелкодисперсного обогащенного глауконита, концентрацией не менее 92%;  - magnetic fraction of finely divided enriched glauconite, with a concentration of at least 92%;
- мелкодисперсная бентонитовая глина, содержащая не менее 70% монтмориллонита. Бентониты - это коллоидные глины, состоящие в основном из минералов группы монтмориллонита, которые обладают ярко выраженными сорбционными свойствами. В качестве сорбционных компонент используются комбинации природных мелкодисперсных сорбентов диатомит, шунгит, цеолит, доломит или их смесь в различных соотношениях. - finely dispersed bentonite clay containing at least 70% montmorillonite. Bentonites are colloidal clays, consisting mainly of the minerals of the montmorillonite group, which have pronounced sorption properties. As sorption components, combinations of natural finely dispersed sorbents diatomite, shungite, zeolite, dolomite, or a mixture thereof in various ratios are used.
Гранулированный гигиенический наполнитель туалета для домашних животных на основе природных пород содержит мелкодисперсную бентонитовую глину, в которой не менее 70% монтмориллонита, а в качестве связующего сорбента введена магнитная фракция мелкодисперсного обогащенного глауконита, концентрацией не менее 92%, и комбинации компонент природных сорбентов диатомит, шунгит, цеолит, доломит в различных соотношениях.  The granular hygienic filler of a toilet for pets based on natural breeds contains finely dispersed bentonite clay, in which at least 70% montmorillonite, and a magnetic fraction of finely divided enriched glauconite, at a concentration of not less than 92%, and a combination of components of natural sorbents diatomite, shungite, are introduced , zeolite, dolomite in various proportions.
Перемешивание измельченной смеси с водой до влажности полученной массы не менее 27% проводится для получения гомогенезированной массы направляемой в гранулятор для изготовления гранул.  Mixing the crushed mixture with water to a moisture content of not less than 27% is carried out to obtain a homogenized mass sent to the granulator for the manufacture of granules.
Подсушивание гранул горячим воздухом не ниже 60°С до влажности не более 10% проводится для достижения гранулами необходимой жёсткости перед проведением их дробления.  Drying the granules with hot air at least 60 ° C to a moisture content of not more than 10% is carried out to achieve the necessary hardness of the granules before crushing them.
В гранулированном гигиеническом наполнителе туалета для домашних животных могут быть следующие варианты составов связующих компонент и сорбционных компонент, содержащихся в разных комбинациях и в различных соотношениях:  In the granular hygienic filler of a toilet for pets there can be the following options for the compositions of the binder components and sorption components contained in different combinations and in different ratios:
1) обогащенный глауконит, бентонитовая глина и диатомит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 10-50, бентонитовая глина - 10-50, диатомит - 10-40;  1) enriched glauconite, bentonite clay and diatomite in the following ratio of components, wt.%: Enriched glauconite - 10-50, bentonite clay - 10-50, diatomite - 10-40;
2) обогащенный глауконит, бентонитовая глина и шунгит при следующем соотношении компонентов, обогащенный глауконит - 10-50, бентонитовая глина - 10-50, шунгит - 10-40;  2) enriched glauconite, bentonite clay and shungite in the following ratio of components, enriched glauconite - 10-50, bentonite clay - 10-50, shungite - 10-40;
3) обогащенный глауконит, бентонитовая глина и цеолит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 10-50, бентонитовая глина - 10-50, цеолит - 10-40;  3) enriched glauconite, bentonite clay and zeolite in the following ratio of components, wt.%: Enriched glauconite - 10-50, bentonite clay - 10-50, zeolite - 10-40;
4) обогащенный глауконит, бентонитовая глина и доломит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 10-50, бентонитовая глина - 10-50, доломит - 10-40;  4) enriched glauconite, bentonite clay and dolomite in the following ratio of components, wt.%: Enriched glauconite - 10-50, bentonite clay - 10-50, dolomite - 10-40;
5) обогащенный глауконит, бентонитовая глина, диатомит и шунгит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 10-50, бентонитовая глина - 10-50, диатомит - 10-20, шунгит - 10-20; 6) обогащенный глауконит, бентонитовая глина, диатомит и цеолит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 10-50, бентонитовая глина - 10-50, диатомит - 10-20, цеолит - 10-20; 5) enriched glauconite, bentonite clay, diatomite and shungite in the following ratio of components, wt.%: Enriched glauconite - 10-50, bentonite clay - 10-50, diatomite - 10-20, shungite - 10-20; 6) enriched glauconite, bentonite clay, diatomite and zeolite in the following ratio of components, wt.%: Enriched glauconite - 10-50, bentonite clay - 10-50, diatomite - 10-20, zeolite - 10-20;
7) обогащенный глауконит, бентонитовая глина, диатомит и доломит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 10-50, бентонитовая глина - 10-50, диатомит - 10-20, доломит - 10-20;  7) enriched glauconite, bentonite clay, diatomite and dolomite in the following ratio of components, wt.%: Enriched glauconite - 10-50, bentonite clay - 10-50, diatomite - 10-20, dolomite - 10-20;
8) обогащенный глауконит, бентонитовая глина, шунгит и цеолит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 10-50, бентонитовая глина - 10-50, шунгит - 10-20, цеолит - 10-20;  8) enriched glauconite, bentonite clay, shungite and zeolite in the following ratio of components, wt.%: Enriched glauconite - 10-50, bentonite clay - 10-50, shungite - 10-20, zeolite - 10-20;
9) обогащенный глауконит, бентонитовая глина, шунгит и доломит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 10-50, бентонитовая глина - 10-50, шунгит - 10-20, доломит - 10-20;  9) enriched glauconite, bentonite clay, shungite and dolomite in the following ratio of components, wt.%: Enriched glauconite - 10-50, bentonite clay - 10-50, shungite - 10-20, dolomite - 10-20;
10) обогащенный глауконит, бентонитовая глина, цеолит и доломит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 10-50, бентонитовая глина - 10-50, цеолит - 10-20, доломит— 10-20.  10) enriched glauconite, bentonite clay, zeolite and dolomite in the following ratio of components, wt.%: Enriched glauconite - 10-50, bentonite clay - 10-50, zeolite - 10-20, dolomite - 10-20.
Предложенный способ изготовления гранулированного гигиенического наполнителя туалета для домашних животных на основе природных пород осуществляют следующим образом.  The proposed method for the manufacture of granular hygienic filler toilet for pets based on natural breeds is as follows.
Подготавливают исходное сырье, при этом в качестве исходного сырья используют связующие магнитную фракцию мелкодисперсного обогащенного глауконита, концентрацией не менее 92%, и мелкодисперсную бентонитовую глину, содержащую не менее 70% монтмориллонита. Перемешивают связующие компоненты с комбинациями мелкодисперсных компонент сорбентов (диатомит, шунгит, цеолит, доломит) или их смеси в различных соотношениях. Перемешанный состав направляется в мелющее устройство, где происходит помол до фракции не более 60 мкм, полученная многокомпонентная мука перемешивается с водой в гомогенезаторе до влажности полученной массы не менее 27%. Полученная масса направляется в экструзионный гранулятор, из которого получаются гранулы диаметром от 2 до 7 мм, длиной от 30 до 1 10 мм (в виде лапши), которые после выхода из гранулятора подсушиваются горячим воздухом не ниже 60°С до влажности не более 10%. Подсушенные гранулы подаются в дробилку, где превращаются в гранулы неправильной формы, имеющие размер в поперечнике от 2 до 7 мм, и в длину также от 2 до 7 мм. В результате дробления образуется различный гранулометрический состав. Гранулы просеиваются через сита, имеющие размер от 2 до 7 мм. Просеянные гранулы сортируются по гранулометрическому составу. Затем осуществляют расфасовку полученного гигиенического гранулированного наполнителя туалетов для домашних животных в различную потребительскую тару. The feedstock is prepared, while the binder magnetic fraction of finely divided enriched glauconite with a concentration of not less than 92% and finely dispersed bentonite clay containing at least 70% montmorillonite are used as the starting material. Mix the binder components with combinations of finely divided components of the sorbents (diatomite, shungite, zeolite, dolomite) or mixtures thereof in various ratios. The mixed composition is sent to a grinding device, where grinding to a fraction of not more than 60 microns takes place, the obtained multicomponent flour is mixed with water in a homogenizer to a moisture content of not less than 27%. The resulting mass is sent to an extrusion granulator, from which granules with a diameter of 2 to 7 mm, a length of 30 to 1 10 mm (in the form of noodles) are obtained, which, after leaving the granulator, are dried with hot air at least 60 ° C to a moisture content of not more than 10% . The dried granules are fed to a crusher, where they are transformed into irregularly shaped granules, having a size across from 2 to 7 mm, and also from 2 to 7 mm in length. As a result of crushing, various particle size distribution is formed. Granules are sifted through sieves, having a size of 2 to 7 mm. Sifted granules are sorted by particle size distribution. Then carry out the packaging of the obtained hygienic granular filler for toilets for pets in various consumer containers.
Лучший вариант осуществления изобретения  The best embodiment of the invention
Изобретение иллюстрируется следующими примерами.  The invention is illustrated by the following examples.
Пример 1. Подготовленное исходное сырье, связующие, магнитную фракцию мелкодисперсного обогащенного глауконита, концентрацией не менее 92%, и мелкодисперсную бентонитовую глину, содержащую не менее 70% монтмориллонита, перемешивают с мелкодисперсным наполнителем (сорбционным компонентом), в качестве которого используют диатомит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 40, бентонитовая глина - 30, диатомит - 30. Перемешанный состав направляется в мелющее устройство, где происходит помол до фракции не более 60 мкм, полученная многокомпонентная мука перемешивается с водой в гомогенезаторе до влажности полученной массы не менее 27%. Полученная масса направляется в экструзионный гранулятор, из которого получаются гранулы диаметром от 3 мм, длиной 50 мм (лапша), которые после выхода из гранулятора подсушиваются горячим воздухом не ниже 60°С до влажности 8%. Подсушенные гранулы подаются в дробилку, где превращаются в гранулы неправильной формы, имеющие размер в поперечнике от 2 до 7 мм, и в длину также от 2 до 7 мм. В результате дробления образуется различный гранулометрический состав. Гранулы просеиваются через сита, имеющие размер от 2 до 7 мм. Просеянные гранулы сортируются по гранулометрическому составу. Затем осуществляют расфасовку полученного гигиенического наполнителя туалетов для домашних животных в различную потребительскую тару.  Example 1. Prepared feedstock, binders, magnetic fraction of finely divided enriched glauconite, with a concentration of at least 92%, and finely dispersed bentonite clay containing at least 70% montmorillonite, mixed with finely divided filler (sorption component), which is used diatomite in the following ratio components, wt.%: enriched glauconite - 40, bentonite clay - 30, diatomite - 30. The mixed composition is sent to a grinding device, where grinding to a fraction of not more than 60 microns occurs, floor Chennai multicomponent flour is mixed with water to a moisture gomogenezatore resulting mass at least 27%. The resulting mass is sent to an extrusion granulator, from which granules with a diameter of 3 mm, length 50 mm (noodles) are obtained, which, after leaving the granulator, are dried with hot air at least 60 ° C to a moisture content of 8%. The dried granules are fed to a crusher, where they are transformed into irregularly shaped granules, having a size across from 2 to 7 mm, and also from 2 to 7 mm in length. As a result of crushing, various particle size distribution is formed. Granules are sieved through sieves having a size of 2 to 7 mm. Sifted granules are sorted by particle size distribution. Then carry out the packaging of the obtained hygienic filler of toilets for pets in various consumer containers.
Пример 2. Подготовленное исходное сырье, связующие магнитную фракцию мелкодисперсного обогащенного глауконита, концентрацией не менее 92%, и мелкодисперсную бентонитовую глину, содержащую не менее 70% монтмориллонита, перемешивают с мелкодисперсным наполнителем (сорбционным компонентом) шунгит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 50, бентонитовая глина - 20, шунгит - 30. Перемешанный состав направляется в мелющее устройство, где происходит помол до фракции не более 60 мкм, полученная многокомпонентная мука перемешивается в гомогенезаторе с водой до влажности полученной массы не менее 27%. Полученная масса направляется в экструзионный гранулятор, из которого получаются гранулы диаметром от 3 мм, длиной 50 мм (лапша), которые после выхода из гранулятора подсушиваются горячим воздухом не ниже 60°С до влажности 5%. Подсушенные гранулы подаются в дробилку, где превращаются в гранулы неправильной формы, имеющие размер в поперечнике от 2 до 7 мм, и в длину также от 2 до 7 мм. В результате дробления образуется различный гранулометрический состав. Гранулы просеиваются через сита, имеющие размер от 2 до 7 мм. Просеянные гранулы сортируются по гранулометрическому составу. Затем осуществляют расфасовку полученного гигиенического наполнителя туалетов для домашних животных в различную потребительскую тару. Example 2. Prepared feedstock, binding the magnetic fraction of finely divided enriched glauconite with a concentration of not less than 92%, and finely dispersed bentonite clay containing at least 70% montmorillonite, mixed with finely divided filler (sorption component) shungite in the following ratio of components, wt.%: enriched glauconite - 50, bentonite clay - 20, shungite - 30. The mixed composition is sent to a grinding device, where grinding to a fraction of not more than 60 microns takes place, the obtained multicomponent flour flies in homogenizer with water to a moisture content of not less than 27%. The resulting mass is sent to an extrusion granulator, from which granules with a diameter of 3 mm, length 50 mm (noodles) are obtained, which, after leaving the granulator, are dried with hot air at least 60 ° C to a moisture content of 5%. The dried granules are fed to the crusher, where they are transformed into granules of irregular shape, having a size across from 2 to 7 mm, and also from 2 to 7 mm in length. As a result of crushing, various particle size distribution is formed. Granules are sieved through sieves having a size of 2 to 7 mm. Sifted granules are sorted by particle size distribution. Then carry out the packaging of the obtained hygienic filler of toilets for pets in various consumer containers.
Пример 3. Подготовленное исходное сырье, связующие магнитную фракцию мелкодисперсного обогащенного глауконита, концентрацией не менее 92%, и мелкодисперсную бентонитовую глину, содержащую не менее 70% монтмориллонита, перемешивают с мелкодисперсным наполнителем (сорбционным компонентом), цеолит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 40, бентонитовая глина - 30, цеолит - 30. Перемешанный состав направляется в мелющее устройство, где происходит помол до фракции не более 60 мкм, полученная многокомпонентная мука перемешивается в гомогенезаторе с водой до влажности полученной массы не менее 27%. Полученная масса направляется в экструзионный гранулятор, из которого получаются гранулы диаметром от 3 мм, длиной 50 мм (лапша), которые после выхода из гранулятора подсушиваются горячим воздухом не ниже 60°С до влажности 8%. Подсушенные гранулы подаются в дробилку, где превращаются в гранулы неправильной формы, имеющие размер в поперечнике от 2 до 7 мм, и в длину также от 2 до 7 мм. В результате дробления образуется различный гранулометрический состав. Гранулы просеиваются через сита, имеющие размер от 2 до 7 мм. Просеянные гранулы сортируются по гранулометрическому составу. Затем осуществляют расфасовку полученного гигиенического наполнителя туалетов для домашних животных в различную потребительскую тару.  Example 3. Prepared feedstock, binding the magnetic fraction of finely divided enriched glauconite with a concentration of not less than 92%, and finely dispersed bentonite clay containing at least 70% montmorillonite, mixed with finely divided filler (sorption component), zeolite in the following ratio of components, wt.% : enriched glauconite - 40, bentonite clay - 30, zeolite - 30. The mixed composition is sent to a grinding device, where grinding to a fraction of not more than 60 microns occurs, the obtained multicomponent flour eshivaetsya in gomogenezatore with water to a moisture content of the mix at least 27%. The resulting mass is sent to an extrusion granulator, from which granules with a diameter of 3 mm, length 50 mm (noodles) are obtained, which, after leaving the granulator, are dried with hot air at least 60 ° C to a moisture content of 8%. The dried granules are fed to a crusher, where they are transformed into irregularly shaped granules, having a size across from 2 to 7 mm, and also from 2 to 7 mm in length. As a result of crushing, various particle size distribution is formed. Granules are sieved through sieves having a size of 2 to 7 mm. Sifted granules are sorted by particle size distribution. Then carry out the packaging of the obtained hygienic filler of toilets for pets in various consumer containers.
Пример 4. Подготовленное исходное сырье, связующие магнитную фракцию мелкодисперсного обогащенного глауконита, концентрацией не менее 92%, и мелкодисперсную бентонитовую глину, содержащую не менее 70% монтмориллонита, перемешивают с мелкодисперсным наполнителем (сорбционным компонентом), доломит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 50, бентонитовая глина - 20, доломит - 30. Перемешанный состав направляется в мелющее устройство, где происходит помол до фракции не более 60 мкм, полученная многокомпонентная мука перемешивается в гомогенезаторе с водой до влажности полученной массы не менее 27%. Полученная масса направляется в экструзионный гранулятор, из которого получаются гранулы диаметром от 3 мм, длиной 50 мм (лапша), которые после выхода из гранулятора подсушиваются горячим воздухом не ниже 60°С до влажности 8%. Подсушенные гранулы подаются в дробилку, где превращаются в гранулы неправильной формы, имеющие размер в поперечнике от 2 до 7 мм, и в длину также от 2 до 7 мм. В результате дробления образуется различный гранулометрический состав. Гранулы просеиваются через сита, имеющие размер от 2 до 7 мм. Просеянные гранулы сортируются по гранулометрическому составу. Затем осуществляют расфасовку полученного гигиенического наполнителя туалетов для домашних животных в различную потребительскую тару. Example 4. Prepared feedstock, binding the magnetic fraction of finely divided enriched glauconite with a concentration of not less than 92%, and finely dispersed bentonite clay containing at least 70% montmorillonite, mixed with finely divided filler (sorption component), dolomite in the following ratio of components, wt.%: enriched glauconite - 50, bentonite clay - 20, dolomite - 30. The mixed composition is sent to a grinding device, where grinding to a fraction of not more than 60 microns takes place, the obtained multicomponent flour is mixed in a homogenizer with water to a moisture content of not less than 27%. The resulting mass is sent to an extrusion granulator, from which granules with a diameter of 3 mm, length 50 mm (noodles) are obtained, which, after leaving the granulator, are dried with hot air at least 60 ° C to a moisture content of 8%. The dried granules are fed to a crusher, where they are transformed into irregularly shaped granules, having a size across from 2 to 7 mm, and also from 2 to 7 mm in length. As a result of crushing, various particle size distribution is formed. Granules are sieved through sieves having a size of 2 to 7 mm. Sifted granules are sorted by particle size distribution. Then carry out the packaging of the obtained hygienic filler of toilets for pets in various consumer containers.
Пример 5. Подготовленное исходное сырье, связующие магнитную фракцию мелкодисперсного обогащенного глауконита, концентрацией не менее 92%, и мелкодисперсную бентонитовую глину, содержащую не менее 70% монтмориллонита, перемешивают с мелкодисперсным наполнителем (сорбционным компонентом), диатомит и шунгит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 30, бентонитовая глина - 30, диатомит - 20, шунгит - 20. Перемешанный состав направляется в мелющее устройство, где происходит помол до фракции не более 60 мкм, полученная многокомпонентная мука перемешивается в гомогенезаторе с водой до влажности полученной массы не менее 27%. Полученная масса направляется в экструзионный гранулятор, из которого получаются гранулы диаметром от 3 мм, длиной 50 мм (лапша), которые после выхода из гранулятора подсушиваются горячим воздухом не ниже 60°С до влажности 5%. Подсушенные гранулы подаются в дробилку, где превращаются в гранулы неправильной формы, имеющие размер в поперечнике от 2 до 7 мм, и в длину также от 2 до 7 мм. В результате дробления образуется различный гранулометрический состав. Гранулы просеиваются через сита, имеющие размер от 2 до 7 мм. Просеянные гранулы сортируются по гранулометрическому составу. Затем осуществляют расфасовку полученного гигиенического наполнителя туалетов для домашних животных в различную потребительскую тару. Пример 6. Подготовленное исходное сырье, связующие магнитную фракцию мелкодисперсного обогащенного глауконита, концентрацией не менее 92%, и мелкодисперсную бентонитовую глину, содержащую не менее 70% монтмориллонита, перемешивают с мелкодисперсным наполнителем (сорбционным компонентом), диатомит и цеолит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 40, бентонитовая глина - 20, диатомит - 20, цеолит - 20. Перемешанный состав направляется в мелющее устройство, где происходит помол до фракции не более 60 мкм, полученная многокомпонентная мука перемешивается в гомогенезаторе с водой до влажности полученной массы не менее 27%. Полученная масса направляется в экструзионный гранулятор, из которого получаются гранулы диаметром от 3 мм, длиной 50 мм (лапша), которые после выхода из гранулятора подсушиваются горячим воздухом не ниже 60°С до влажности 6%. Подсушенные гранулы подаются в дробилку, где превращаются в гранулы неправильной формы, имеющие размер в поперечнике от 2 до 7 мм, и в длину также от 2 до 7 мм. В результате дробления образуется различный гранулометрический состав. Гранулы просеиваются через сита, имеющие размер от 2 до 7 мм. Просеянные гранулы сортируются по гранулометрическому составу. Затем осуществляют расфасовку полученного гигиенического наполнителя туалетов для домашних животных в различную потребительскую тару. Example 5. Prepared feedstock, binding the magnetic fraction of finely divided enriched glauconite with a concentration of not less than 92%, and finely dispersed bentonite clay containing at least 70% montmorillonite, mixed with finely divided filler (sorption component), diatomite and shungite in the following ratio of components, wt .%: enriched glauconite - 30, bentonite clay - 30, diatomite - 20, shungite - 20. The mixed composition is sent to a grinding device, where grinding to a fraction of not more than 60 microns takes place, a lot component flour is mixed in a homogenizer with water to a moisture content of not less than 27%. The resulting mass is sent to an extrusion granulator, from which granules with a diameter of 3 mm, length 50 mm (noodles) are obtained, which, after leaving the granulator, are dried with hot air at least 60 ° C to a moisture content of 5%. The dried granules are fed to a crusher, where they are transformed into irregularly shaped granules, having a size across from 2 to 7 mm, and also from 2 to 7 mm in length. As a result of crushing, various particle size distribution is formed. Granules are sieved through sieves having a size of 2 to 7 mm. Sifted granules are sorted by particle size distribution. Then carry out the packaging of the obtained hygienic filler of toilets for pets in various consumer containers. Example 6. Prepared feedstock, binding the magnetic fraction of finely divided enriched glauconite with a concentration of at least 92%, and finely dispersed bentonite clay containing at least 70% montmorillonite, mixed with finely divided filler (sorption component), diatomite and zeolite in the following ratio of components, wt. .%: enriched glauconite - 40, bentonite clay - 20, diatomite - 20, zeolite - 20. The mixed composition is sent to a grinding device, where grinding to a fraction of not more than 60 microns takes place, a lot component flour is mixed in a homogenizer with water to a moisture content of not less than 27%. The resulting mass is sent to an extrusion granulator, from which granules with a diameter of 3 mm, length 50 mm (noodles) are obtained, which, after leaving the granulator, are dried with hot air at least 60 ° C to a moisture content of 6%. The dried granules are fed to a crusher, where they are transformed into irregularly shaped granules, having a size across from 2 to 7 mm, and also from 2 to 7 mm in length. As a result of crushing, various particle size distribution is formed. Granules are sieved through sieves having a size of 2 to 7 mm. Sifted granules are sorted by particle size distribution. Then carry out the packaging of the obtained hygienic filler of toilets for pets in various consumer containers.
Пример 7. Подготовленное исходное сырье, связующие магнитную фракцию мелкодисперсного обогащенного глауконита, концентрацией не менее 92%, и мелкодисперсную бентонитовую глину, содержащую не менее 70% монтмориллонита, перемешивают с мелкодисперсным наполнителем (сорбционным компонентом), диатомит и доломит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 30, бентонитовая глина - 30, диатомит - 20, доломит - 20. Перемешанный состав направляется в мелющее устройство, где происходит помол до фракции не более 60 мкм, полученная многокомпонентная мука перемешивается в гомогенезаторе с водой до влажности полученной массы не менее 27%. Полученная масса направляется в экструзионный гранулятор, из которого получаются гранулы диаметром от 3 мм, длиной 50 мм (лапша), которые после выхода из гранулятора подсушиваются горячим воздухом не ниже 60°С до влажности 8%. Подсушенные гранулы подаются в дробилку, где превращаются в гранулы неправильной формы, имеющие размер в поперечнике от 2 до 7 мм, и в длину также от 2 до 7 мм. В результате дробления образуется различный гранулометрический состав. Гранулы просеиваются через сита, имеющие размер от 2 до 7 мм. Просеянные гранулы сортируются по гранулометрическому составу. Затем осуществляют расфасовку полученного гигиенического наполнителя туалетов для домашних животных в различную потребительскую тару. Example 7. Prepared feedstock, binding the magnetic fraction of finely divided enriched glauconite, with a concentration of at least 92%, and finely dispersed bentonite clay containing at least 70% montmorillonite, mixed with finely divided filler (sorption component), diatomite and dolomite in the following ratio of components, wt .%: enriched glauconite - 30, bentonite clay - 30, diatomite - 20, dolomite - 20. The mixed composition is sent to a grinding device, where grinding to a fraction of not more than 60 microns, obtained the component flour is mixed in a homogenizer with water to a moisture content of at least 27%. The resulting mass is sent to an extrusion granulator, from which granules with a diameter of 3 mm, length 50 mm (noodles) are obtained, which, after leaving the granulator, are dried with hot air at least 60 ° C to a moisture content of 8%. The dried granules are fed to a crusher, where they are transformed into irregularly shaped granules, having a size across from 2 to 7 mm, and also from 2 to 7 mm in length. As a result of crushing, various grading. Granules are sieved through sieves having a size of 2 to 7 mm. Sifted granules are sorted by particle size distribution. Then carry out the packaging of the obtained hygienic filler of toilets for pets in various consumer containers.
Пример 8. Подготовленное исходное сырье, связующие магнитную фракцию мелкодисперсного обогащенного глауконита, концентрацией не менее 92%, и мелкодисперсную бентонитовую глину, содержащую не менее 70% монтмориллонита, перемешивают с мелкодисперсным наполнителем (сорбционным компонентом), шунгит и цеолит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 40, бентонитовая глина - 30, шунгит - 15, цеолит - 15. Перемешанный состав направляется в мелющее устройство, где происходит помол до фракции не более 60 мкм, полученная многокомпонентная мука перемешивается в гомогенезаторе с водой до влажности полученной массы не менее 27%. Полученная масса направляется в экструзионный гранулятор, из которого получаются гранулы диаметром от 3 мм, длиной 50 мм (лапша), которые после выхода из гранулятора подсушиваются горячим воздухом не ниже 60°С до влажности 7%. Подсушенные гранулы подаются в дробилку, где превращаются в гранулы неправильной формы, имеющие размер в поперечнике от 2 до 7 мм, и в длину также от 2 до 7 мм. В результате дробления образуется различный гранулометрический состав. Гранулы просеиваются через сита, имеющие размер от 2 до 7 мм. Просеянные гранулы сортируются по гранулометрическому составу. Затем осуществляют расфасовку полученного гигиенического наполнителя туалетов для домашних животных в различную потребительскую тару.  Example 8. Prepared feedstock, binding the magnetic fraction of finely divided enriched glauconite, with a concentration of not less than 92%, and finely dispersed bentonite clay containing at least 70% montmorillonite, mixed with finely divided filler (sorption component), shungite and zeolite in the following ratio of components, wt .%: enriched glauconite - 40, bentonite clay - 30, shungite - 15, zeolite - 15. The mixed composition is sent to a grinding device, where grinding to a fraction of not more than 60 microns occurs, the multicompound Onion flour is mixed in a homogenizer with water to a moisture content of at least 27%. The resulting mass is sent to an extrusion granulator, from which granules with a diameter of 3 mm, length 50 mm (noodles) are obtained, which, after leaving the granulator, are dried with hot air at least 60 ° C to a moisture content of 7%. The dried granules are fed to a crusher, where they are transformed into irregularly shaped granules, having a size across from 2 to 7 mm, and also from 2 to 7 mm in length. As a result of crushing, various particle size distribution is formed. Granules are sieved through sieves having a size of 2 to 7 mm. Sifted granules are sorted by particle size distribution. Then carry out the packaging of the obtained hygienic filler of toilets for pets in various consumer containers.
Пример 9. Подготовленное исходное сырье, связующие магнитную фракцию мелкодисперсного обогащенного глауконита, концентрацией не менее 92%, и мелкодисперсную бентонитовую глину, содержащую не менее 70% монтмориллонита, перемешивают с мелкодисперсным наполнителем (сорбционным компонентом), шунгит и доломит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 40, бентонитовая глина - 30, шунгит - 15, доломит - 15. Перемешанный состав направляется в мелющее устройство, где происходит помол до фракции не более 60 мкм, полученная многокомпонентная мука перемешивается в гомогенезаторе с водой до влажности полученной массы не менее 27%. Полученная масса направляется в экструзионный гранулятор, из которого получаются гранулы диаметром от 3 мм, длиной 50 мм (лапша), которые после выхода из гранулятора подсушиваются горячим воздухом не ниже 60°С до влажности 5%. Подсушенные гранулы подаются в дробилку, где превращаются в гранулы неправильной формы, имеющие размер в поперечнике от 2 до 7 мм, и в длину также от 2 до 7 мм. В результате дробления образуется различный гранулометрический состав. Гранулы просеиваются через сита, имеющие размер от 2 до 7 мм. Просеянные гранулы сортируются по гранулометрическому составу. Затем осуществляют расфасовку полученного гигиенического наполнителя туалетов для домашних животных в различную потребительскую тару. Example 9. Prepared feedstock, binding the magnetic fraction of finely divided enriched glauconite with a concentration of not less than 92%, and finely dispersed bentonite clay containing at least 70% montmorillonite, mixed with finely divided filler (sorption component), shungite and dolomite in the following ratio of components, wt .%: enriched glauconite - 40, bentonite clay - 30, shungite - 15, dolomite - 15. The mixed composition is sent to a grinding device, where grinding to a fraction of not more than 60 microns, obtained many component flour is mixed in a homogenizer with water to a moisture content of not less than 27%. The resulting mass is sent to an extrusion granulator, from which granules with a diameter of 3 mm, length 50 mm (noodles) are obtained, which after exits from the granulator are dried with hot air at least 60 ° C to a moisture content of 5%. The dried granules are fed to a crusher, where they are transformed into irregularly shaped granules, having a size across from 2 to 7 mm, and also from 2 to 7 mm in length. As a result of crushing, various particle size distribution is formed. Granules are sieved through sieves having a size of 2 to 7 mm. Sifted granules are sorted by particle size distribution. Then carry out the packaging of the obtained hygienic filler of toilets for pets in various consumer containers.
Пример 10. Подготовленное исходное сырье, связующие магнитную фракцию мелкодисперсного обогащенного глауконита, концентрацией не менее 92%, и мелкодисперсную бентонитовую глину, содержащую не менее 70% монтмориллонита, перемешивают с мелкодисперсным наполнителем (сорбционным компонентом), цеолит и доломит при следующем соотношении компонентов, мас.%: обогащенный глауконит - 30, бентонитовая глина - 30, цеолит - 20, доломит - 20. Перемешанный состав направляется в мелющее устройство, где происходит помол до фракции не более 60 мкм, полученная многокомпонентная мука перемешивается в гомогенезаторе с водой до влажности полученной массы не менее 27%. Полученная масса направляется в экструзионный гранулятор, из которого получаются гранулы диаметром от 3 мм, длиной 50 мм (лапша), которые после выхода из гранулятора подсушиваются горячим воздухом не ниже 60°С до влажности 10%. Подсушенные гранулы подаются в дробилку, где превращаются в гранулы неправильной формы, имеющие размер в поперечнике от 2 до 7 мм, и в длину также от 2 до 7 мм. В результате дробления образуется различный гранулометрический состав. Гранулы просеиваются через сита, имеющие размер от 2 до 7 мм. Просеянные гранулы сортируются по гранулометрическому составу. Затем осуществляют расфасовку полученного гигиенического наполнителя туалетов для домашних животных в различную потребительскую тару.  Example 10. Prepared feedstock, binding the magnetic fraction of finely divided enriched glauconite with a concentration of not less than 92%, and finely dispersed bentonite clay containing at least 70% montmorillonite, mixed with finely divided filler (sorption component), zeolite and dolomite in the following ratio of components, wt .%: enriched glauconite - 30, bentonite clay - 30, zeolite - 20, dolomite - 20. The mixed composition is sent to a grinding device, where grinding to a fraction of not more than 60 microns, obtained by many mponentnaya gomogenezatore flour is stirred with water to a moisture content of the mix at least 27%. The resulting mass is sent to an extrusion granulator, from which granules with a diameter of 3 mm and a length of 50 mm (noodles) are obtained, which, after leaving the granulator, are dried with hot air at least 60 ° C to a moisture content of 10%. The dried granules are fed to a crusher, where they are transformed into irregularly shaped granules, having a size across from 2 to 7 mm, and also from 2 to 7 mm in length. As a result of crushing, various particle size distribution is formed. Granules are sieved through sieves having a size of 2 to 7 mm. Sifted granules are sorted by particle size distribution. Then carry out the packaging of the obtained hygienic filler of toilets for pets in various consumer containers.
Настоящее изобретение не ограничено описанными выше примерами, приведенными лишь в качестве иллюстрации конкретных вариантов его осуществления.  The present invention is not limited to the examples described above, given only as an illustration of specific options for its implementation.
Эффективность гранулированного наполнителя оценивали по его влагопоглощению и сорбционным дезодорирующим свойствам (таблица). Из таблицы видно, что влагопоглощение разных композиций сорбционных компонент в среднем составляет около 300%, т.е. один килограмм гранулированного наполнителя удерживает не менее 1,5 литра жидкости. The effectiveness of the granular filler was evaluated by its moisture absorption and sorption deodorizing properties (table). The table shows that the moisture absorption of different compositions of the sorption components an average of about 300%, i.e. one kilogram of granular filler holds at least 1.5 liters of fluid.
Таблица Table
Figure imgf000018_0001
Figure imgf000018_0001
Применение обогащенного глауконита значительно увеличивает сорбционную способность удерживать запах, как отдельно, так и в комбинации с другими сорбирующими компонентами. The use of enriched glauconite significantly increases the sorption ability to retain odor, both separately and in combination with other sorbent components.
Предложенная технология изготовления гигиенического гранулированного наполнителя туалетов для домашних животных позволяет получить продукт улучшенного качества за счет повышения реагентной, сорбционной и адсорбционной способностей, а также создать комфортные условия для домашних животных и их владельцев.  The proposed technology for the production of hygienic granular filler of toilets for pets allows to obtain a product of improved quality by increasing reagent, sorption and adsorption abilities, as well as create comfortable conditions for pets and their owners.

Claims

Формула изобретения Claim
1. Гранулированный наполнитель туалета для домашних животных на основе природных пород, содержащий бентонитовую глину и природные сорбенты, в качестве которых используют цеолит, диатомит или их смесь в различных соотношениях, отличающийся тем, что в качестве связующего введена магнитная фракция мелкодисперсного обогащенного глауконита, концентрацией не менее 92%, при этом мелкодисперсная бентонитовая глина содержит не менее 70% монтмориллонита, а в качестве комбинаций компонент природных сорбентов дополнительно используют шунгит, доломит.  1. A granular filler of a toilet for pets based on natural breeds, containing bentonite clay and natural sorbents, which are used as zeolite, diatomite, or a mixture thereof in various proportions, characterized in that a magnetic fraction of finely divided enriched glauconite is introduced as a binder, the concentration is not less than 92%, while finely dispersed bentonite clay contains at least 70% montmorillonite, and shungite is additionally used as combinations of components of natural sorbents with dolom it.
2. Наполнитель по п. 1, отличающийся тем, что содержит обогащенный глауконит, бентонитовую глину и диатомит при следующем соотношении компонентов, мас.%:  2. A filler according to claim 1, characterized in that it contains enriched glauconite, bentonite clay and diatomite in the following ratio of components, wt.%:
обогащенный глауконит - 10-50;  enriched glauconite - 10-50;
бентонитовая глина - 10-50;  bentonite clay - 10-50;
диатомит - 10-40.  diatomite - 10-40.
3. Наполнитель по п. 1, отличающийся тем, что содержит обогащенный глауконит, бентонитовую глину и шунгит при следующем соотношении компонентов, мас.%:  3. The filler according to claim 1, characterized in that it contains enriched glauconite, bentonite clay and shungite in the following ratio of components, wt.%:
обогащенный глауконит - 10-50;  enriched glauconite - 10-50;
бентонитовая глина - 10-50;  bentonite clay - 10-50;
шунгит - 10-40.  shungite - 10-40.
4. Наполнитель по п. 1 , отличающийся тем, что содержит обогащенный глауконит, бентонитовую глину и цеолит при следующем соотношении компонентов, мас.%:  4. The filler according to claim 1, characterized in that it contains enriched glauconite, bentonite clay and zeolite in the following ratio of components, wt.%:
обогащенный глауконит - 10-50;  enriched glauconite - 10-50;
бентонитовая глина - 10-50;  bentonite clay - 10-50;
цеолит - 10-40.  zeolite - 10-40.
5. Наполнитель по п. 1, отличающийся тем, что содержит обогащенный глауконит, бентонитовую глину и доломит при следующем соотношении компонентов, мас.%:  5. The filler according to claim 1, characterized in that it contains enriched glauconite, bentonite clay and dolomite in the following ratio of components, wt.%:
обогащенный глауконит - 10-50;  enriched glauconite - 10-50;
бентонитовая глина - 10-50;  bentonite clay - 10-50;
доломит - 10-40. dolomite - 10-40.
6. Наполнитель по п. 1, отличающийся тем, что содержит обогащенный глауконит, бентонитовую глину, диатомит и шунгит при следующем соотношении компонентов, мас.%: 6. The filler according to claim 1, characterized in that it contains enriched glauconite, bentonite clay, diatomite and shungite in the following ratio of components, wt.%:
обогащенный глауконит - 10-50;  enriched glauconite - 10-50;
бентонитовая глина - 10-50;  bentonite clay - 10-50;
диатомит - 10-20;  diatomite - 10-20;
шунгит - 10-20.  shungite - 10-20.
7. Наполнитель по п. 1, отличающийся тем, что содержит обогащенный глауконит, бентонитовую глину, диатомит и цеолит при следующем соотношении компонентов, мас.%:  7. The filler according to claim 1, characterized in that it contains enriched glauconite, bentonite clay, diatomite and zeolite in the following ratio of components, wt.%:
обогащенный глауконит - 10-50;  enriched glauconite - 10-50;
бентонитовая глина - 10-50;  bentonite clay - 10-50;
диатомит - 10-20;  diatomite - 10-20;
цеолит - 10-20.  zeolite - 10-20.
8. Наполнитель по п. 1, отличающийся тем, что содержит обогащенный глауконит, бентонитовую глину, диатомит и доломит при следующем соотношении компонентов, мас.%:  8. The filler according to claim 1, characterized in that it contains enriched glauconite, bentonite clay, diatomite and dolomite in the following ratio of components, wt.%:
обогащенный глауконит - 10-50;  enriched glauconite - 10-50;
бентонитовая глина - 10-50;  bentonite clay - 10-50;
диатомит - 10-20;  diatomite - 10-20;
доломит - 10-20.  dolomite - 10-20.
9. Наполнитель по п. 1, отличающийся тем, что содержит обогащенный глауконит, бентонитовую глину, шунгит и цеолит при следующем соотношении компонентов, мас.%:  9. The filler according to claim 1, characterized in that it contains enriched glauconite, bentonite clay, shungite and zeolite in the following ratio of components, wt.%:
обогащенный глауконит - 10-50;  enriched glauconite - 10-50;
бентонитовая глина - 10-50;  bentonite clay - 10-50;
шунгит - 10-20;  shungite - 10-20;
цеолит - 10-20.  zeolite - 10-20.
10. Наполнитель по п. 1 , отличающийся тем, что содержит обогащенный глауконит, бентонитовую глину, шунгит и доломит при следующем соотношении компонентов, мас.%:  10. The filler according to claim 1, characterized in that it contains enriched glauconite, bentonite clay, shungite and dolomite in the following ratio of components, wt.%:
обогащенный глауконит - 10-50;  enriched glauconite - 10-50;
бентонитовая глина - 10-50;  bentonite clay - 10-50;
шунгит - 10-20; доломит - 10-20. shungite - 10-20; dolomite - 10-20.
1 1. Наполнитель по п. 1 , отличающийся тем, что содержит обогащенный глауконит, бентонитовую глину, цеолит и доломит при следующем соотношении компонентов, мас.%:  1 1. The filler according to claim 1, characterized in that it contains enriched glauconite, bentonite clay, zeolite and dolomite in the following ratio of components, wt.%:
обогащенный глауконит - 10-50;  enriched glauconite - 10-50;
бентонитовая глина - 10-50;  bentonite clay - 10-50;
цеолит - 10-20;  zeolite - 10-20;
доломит - 10-20.  dolomite - 10-20.
12. Способ изготовления гранулированного наполнителя туалета для домашних животных на основе природных пород, охарактеризованного в пп. 1-1 1 , включающий подготовку исходного сырья, при этом в качестве исходного сырья используют связующие магнитную фракцию мелкодисперсного обогащенного глауконита, концентрацией не менее 92%, и мелкодисперсную бентонитовую глину, содержащую не менее 70% монтмориллонита, перемешивание связующих с комбинациями мелкодисперсных компонент сорбентов диатомит, шунгит, цеолит, доломит в различных соотношениях, измельчение смеси, перемешивание с водой до влажности полученной массы не менее 27%, гранулирование, подсушивание гранул горячим воздухом не ниже 60°С до влажности не более 10%, дробление, просеивание, сортировку по гранулометрическому составу и последующую расфасовку.  12. A method of manufacturing a granular filler of a toilet for pets based on natural rocks, described in paragraphs. 1-1 1, including the preparation of the feedstock, using binder magnetic fraction of finely divided enriched glauconite with a concentration of not less than 92% and finely dispersed bentonite clay containing at least 70% montmorillonite, mixing binders with combinations of finely dispersed components of sorbents diatomite , schungite, zeolite, dolomite in various proportions, grinding the mixture, mixing with water to a moisture content of at least 27%, granulating, drying granules with hot air e below 60 ° C to a moisture content of not more than 10%, crushing, sifting, sorting by particle size distribution and subsequent packaging.
13. Способ по п. 12, отличающийся тем, что измельчение смеси осуществляют до фракции не более 60 мкм.  13. The method according to p. 12, characterized in that the grinding of the mixture is carried out to a fraction of not more than 60 microns.
14. Способ по п. 12, отличающийся тем, что гранулирование осуществляют до получения гранул диаметром от 2 до 7 мм, длиной от 30 до 1 10 мм.  14. The method according to p. 12, characterized in that the granulation is carried out to obtain granules with a diameter of 2 to 7 mm, a length of 30 to 1 10 mm.
15. Способ по п. 12, отличающийся тем, что дробление полученных гранул осуществляют до получения гранул неправильной формы, имеющих размер в поперечнике от 2 до 7 мм и длину от 2 до 7 мм.  15. The method according to p. 12, characterized in that the crushing of the obtained granules is carried out to obtain granules of irregular shape, having a size across from 2 to 7 mm and a length of from 2 to 7 mm.
16. Способ по п. 12, отличающийся тем, что просеивание осуществляют до размера частиц 2-7 мм.  16. The method according to p. 12, characterized in that the sieving is carried out to a particle size of 2-7 mm
PCT/RU2013/000198 2012-11-13 2013-03-15 Granulated filler for a toilet for pets and method for manufacturing same WO2014077729A1 (en)