WO2013173625A1 - Compositions containing purified non-hevea rubber and related purification methods

Info

Publication number: WO2013173625A1
Application number: PCT/US2013/041422
Authority: WO
Inventors: Amy Randall; Arif Omer GOZEN
Original assignee: Bridgestone Corporation
Priority date: 2012-05-16
Filing date: 2013-05-16
Publication date: 2013-11-21
Also published as: AU2017200069B2; ES2638943T3; US20150126673A1; CN107254007B; RU2014150798A; AU2017200069A1; CN104395349A; US10023660B2; AU2013262725A1; CA2873783C; EP2850110B1; MX362581B; CN107254007A; RU2017140651A3; EP2850110A1; CA2873783A1; MX2014013961A; AU2013262725B2; EP2850110A4; RU2017140651A

Abstract

Provided herein are organic solvent-based processes for the isolation of purified natural rubber from non-Hevea plants. The processes are particularly useful with plant matter that comprises at least 90% by weight roots sourced from Taraxacum kok-saghyz (Russian dandelion), Scorzonera tau-saghyz (Tau-Saghyz), Scorzonera uzbekistanica, and combinations thereof. Also provided herein is a purified non-Hevea rubber product containing 100 phr of rubber sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof, having a specified purity level. Additionally provided are sulfur-vulcanizable rubber compounds and sulfur-vulcanized rubber compounds that incorporate 10-100 phr of purified non-Hevea rubber product sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof, having a specified purity level.

Description

COMPOSITIONS CONTAINING PURIFIED NON-HEVEA RUBBER AND RELATED

PURIFICATION METHODS

CROSS-REFERENCE TO RELATED APPLICATION

[0001] This application claims priority to and any other benefit of U.S. Provisional Patent Application Serial No. 61/647,778, filed May 16, 2012, and entitled "COMPOSITIONS CONTAINING PURIFIED NON-HE VE A RUBBER AND RELATED PURIFICATION METHODS," the entire disclosure of which is incorporated by reference herein;

BACKGROUND

[0002] The Hevea plant or tree (also called Hevea brasiliensis or a rubber tree) is a well- known source of natural rubber (also called polyisoprene). Rubber sources such as Hevea brasiliensis, Ficus elastic (India rubber tree) and Cryptostegia grandiflora (Madagascar rubbervine) produce natural rubber in the form of a sap where the rubber is suspended in an aqueous solution that flows freely and can be recovered by tapping of the plant. Various non- Hevea plants are also known to contain natural rubber, but their rubber is stored within the individual cells of the plant (e.g., stems, roots or leaves) and cannot be accessed by tapping but can only be accessed by breaking down the cell walls by physical or other means. Thus, processes for the removal of rubber from non-Hevea plants are generally more complicated and entailed than processes for harvesting rubber from Hevea trees.

SUMMARY

[0003] Provided herein are organic solvent-based processes for the isolation of purified natural rubber from non-Hevea plants. The processes are particularly useful with plant matter that comprises at least 90% by weight roots sourced from Taraxacum kok-saghyz (Russian dandelion), Scorzonera tau-saghyz (Tau-Saghyz), Scorzonera uzbekistanica, and combinations thereof. The processes are also useful in further purifying semi-purified non-Hevea plant matter (i.e., plant matter that has had a majority of the cellulose-type plant material removed but that still contains some amount of cellulose-type plant material in addition to other impurities along with non-Hevea rubber).

[0004] Also provided herein is a purified non-Hevea rubber product containing 100 phr of rubber sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof, having a specified purity level. Additionally provided are sulfur-vulcanizable rubber compounds and sulfur-vulcanized rubber compounds that incorporate 10-100 phr of non-Hevea rubber sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof, having a specified purity level. The purified non-Hevea rubber product, sulfur-vulcanizable rubber compounds and sulfur- vulcanized rubber compounds all make use of the discovery that up to 3.5% of total impurities can be present in the non-Hevea rubber and its use as a total or partial replacement for Hevea natural rubber will result in comparable or even improved mechanical properties.

[0005] The process for isolating purified natural rubber from non-Hevea plant matter comprises providing harvested plant matter comprising at least 90%> by weight of roots sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof. This harvested plant matter is mixed with at least one rubber-soluble organic solvent at a weight ratio of from 2: 100 to 20:100 thereby producing a quantity of dissolved rubber and a quantity of solids. The solids represent insoluble cellulose-based plant matter in addition to impurities that are not soluble in the at least one rubber-soluble organic solvent. After mixing, the dissolved rubber is isolated from the solids to produce a dissolved rubber fraction that contains no more than 2% by weight solids based on the total weight of the dissolved rubber fraction. The at least one rubber-soluble solvent is then removed from the dissolved rubber fraction to produce a solid rubber mass. The solid rubber mass is mixed with at least one rubber-insoluble organic solvent at a weight ratio of 2: 100 to 20: 100 thereby dissolving a quantity of impurities from the solid rubber mass and thereafter the remaining solid rubber mass is isolated from the at least one rubber-insoluble organic solvent to produce a purified natural rubber. The purified natural rubber contains no more than 3.5% by weight total impurities based upon the total weight of the purified natural rubber that is obtained.

[0006] The purified non-Hevea rubber product provided herein contains 100 phr of rubber sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof with no more than 3.5% by weight of total impurities (based upon the total weight of the purified non-Hevea rubber). Of the no more than 3.5% by weight total impurities, no more than 2% by weight are volatiles, no more than 1% by weight are residues and no more than 0.5%> by weight are combustibles. In other words, the purified non-Hevea rubber contains up to 2% by weight volatile impurities, up to 1% by weight residue impurities and up to 0.5%> by weight combustible impurities. The purified non-Hevea rubber may be purified according to the previously-described organic-solvent purification processes or by other methods as long as the impurities content falls within the specified range.

[0007] The sulfur- vulcanizable rubber compound provided herein contains 10-100 phr of purified non-Hevea natural rubber sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof wherein said purified non-Hevea natural rubber contains no more than 3.5% by weight total impurities with no more than 2% by weight volatiles, no more than 1% by weight residue and no more than 0.5%> by weight combustibles; 0- 90 phr of at least one synthetic conjugated-diene containing polymer or copolymer; and 20-200 phr of at least one reinforcing filler selected from the group consisting of carbon black, silica, calcium carbonate, clay, talc, barite, wollastonite, mica, precipitated silicates, and diatomite. The purified non-Hevea natural rubber that is utilized in the sulfur-vulcanizable rubber compound may be purified according to the previously-described organic-solvent purification processes or by other methods so long as the impurities content falls within the specified range.

[0008] The sulfur- vulcanized rubber compound provided herein contains 10-100 phr of purified non-Hevea natural rubber sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof wherein said purified non-Hevea natural rubber contains no more than 3.5% by weight total impurities with no more than 2% by weight volatiles, no more than 1% by weight residue and no more than 0.5% by weight combustibles; 0- 90 phr of at least one synthetic conjugated-diene containing polymer or copolymer; 20-200 phr of at least one reinforcing filler selected from the group consisting of carbon black, silica, calcium carbonate, clay, talc, barite, wollastonite, mica, precipitated silicates, and diatomite; 0.5- 6 phr sulfur; and at least one accelerator. The purified non-Hevea natural rubber that is utilized in the sulfur-vulcanized rubber compound may be purified according to the previously-described organic-solvent purification processes or by other methods as long as the impurities content falls within the specified range. DETAILED DESCRIPTION

[0009] The process for isolating purified natural rubber from non-Hevea plant matter comprises providing harvested plant matter comprising at least 90% by weight of roots sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof. This harvested plant matter is mixed with at least one rubber-soluble organic solvent at a weight ratio of from 2: 100 to 20:100 thereby producing a quantity of dissolved rubber and a quantity of solids. The solids represent insoluble cellulose-based plant matter in addition to impurities that are not soluble in the at least one rubber-soluble organic solvent. After mixing, the dissolved rubber is isolated from the solids to produce a dissolved rubber fraction that contains no more than 2% by weight solids based on the total weight of the dissolved rubber fraction. The at least one rubber-soluble solvent is then removed from the dissolved rubber fraction to produce a solid rubber mass. The solid rubber mass is mixed with at least one rubber-insoluble organic solvent at a weight ratio of 2: 100 to 20: 100 thereby dissolving a quantity of impurities from the solid rubber mass and thereafter the remaining solid rubber mass is isolated from the at least one rubber-insoluble organic solvent to produce a purified natural rubber. The purified natural rubber contains no more than 3.5% by weight total impurities based upon the total weight of the purified natural rubber that is obtained.

[00010] The purified non-Hevea rubber product provided herein contains 100 phr of rubber sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof with no more than 3.5% by weight of total impurities (based upon the total weight of the purified non-Hevea rubber). Of the no more than 3.5% by weight total impurities, no more than 2% by weight are volatiles, no more than 1% by weight are residues and no more than 0.5%> by weight are combustibles. In other words, the purified non- Hevea rubber contains up to 2% by weight volatile impurities, up to 1% by weight residue impurities and up to 0.5%> by weight combustible impurities. The purified non-Hevea rubber may be purified according to the previously-described organic-solvent purification processes or by other methods as long as the impurities content falls within the specified range.

[00011] The sulfur- vulcanizable rubber compound provided herein contains 10-

100 phr of purified non-Hevea natural rubber sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof wherein said purified non- Hevea natural rubber contains no more than 3.5% by weight total impurities with no more than 2% by weight volatiles, no more than 1% by weight residue and no more than 0.5% by weight combustibles; 0-90 phr of at least one synthetic conjugated-diene containing polymer or copolymer; and 20-200 phr of at least one reinforcing filler selected from the group consisting of carbon black, silica, calcium carbonate, clay, talc, barite, wollastonite, mica, precipitated silicates, and diatomite. The purified non-Hevea natural rubber that is utilized in the sulfur- vulcanizable rubber compound may be purified according to the previously-described organic- solvent purification processes or by other methods so long as the impurities content falls within the specified range.

[00012] The sulfur- vulcanized rubber compound provided herein contains 10-100 phr of purified non-Hevea natural rubber sourced from Taraxacum kok-saghyz, Scorzonera tau- saghyz, Scorzonera uzbekistanica, and combinations thereof wherein said purified non-Hevea natural rubber contains no more than 3.5% by weight total impurities with no more than 2% by weight volatiles, no more than 1% by weight residue and no more than 0.5% by weight combustibles; 0-90 phr of at least one synthetic conjugated-diene containing polymer or copolymer; 20-200 phr of at least one reinforcing filler selected from the group consisting of carbon black, silica, calcium carbonate, clay, talc, barite, wollastonite, mica, precipitated silicates, and diatomite; 0.5-6 phr sulfur; and at least one accelerator. The purified non-Hevea natural rubber that is utilized in the sulfur-vulcanized rubber compound may be purified according to the previously-described organic-solvent purification processes or by other methods as long as the impurities content falls within the specified range.

Definitions

[00013] As used herein, the term "combustibles" or "combustible impurities" means those impurities that will burn-off during a thermogravimetric analysis at a temperature range of 600-750 °C.

[00014] As used herein, the term "non Hevea" or "non-Hevea plant" is intended to encompass plants that contain natural rubber within the individual cells of the plant.

[00015] As used herein, the term "plant matter" means material obtained from a non-Hevea plant.

[00016] As used herein, the term "residues" or "residue impurities" means those impurities that will burn during a thermogravimetric analysis at a temperature range of greater than 750 °C; these impurities will remain as ash-like material at the conclusion of the 850 °C heating cycle.

[00017] As used herein, the term "rubber-soluble organic solvent" means an organic solvent with a solubility parameter that is similar enough to the solubility parameter of natural rubber that the natural rubber contained within the non-Hevea plant matter will be dissolved therein. More specifically, a rubber-soluble solvent will have a solubility parameter of

3 1/2

7.3-9.2 (cal/cm ) . Some rubber-soluble solvents will be non-polar organic solvents.

[00018] As used herein, the term "rubber-insoluble organic solvent" means an organic solvent with a solubility parameter that is dissimilar enough to the solubility parameter of natural rubber that the natural rubber from the non-Hevea plant matter will not dissolve therein. More specifically, a rubber-insoluble solvent will have a solubility parameter of 9.3-24

3 1/2

(cal/cm ) . Some rubber-insoluble solvents will be polar organic solvents.

[00019] As used herein, the term "total impurities" means the sum of volatiles, combustibles and residues.

[00020] As used herein, the term "volatiles" or "volatile impurities" means those impurities that will burn-off during a thermogravimetric analysis at a temperature of less than 250/275 °C; such impurities include substances like resins, terpenes and low-mass organics. Processes

[00021] In certain embodiments, the processes disclosed herein yield a purified natural rubber that contains no more than 3% by weight total impurities. In other embodiments, the processes disclosed herein yield a purified natural rubber that contains no more than 2.5% by weight total impurities.

[00022] As previously discussed, according to the processes disclosed herein, the harvested plant matter is mixed with the at least one rubber-soluble organic solvent at a weight to volume ratio of 2: 100 to 20: 100. In other words, 2 grams of harvested plant matter to 100 mL of total rubber-soluble organic solvent and 20 grams of harvested plant matter to 100 mL of total rubber-soluble organic solvent. These ratios can also be represented as weight to volume ratios of 1 :50 to 10:50. In certain embodiments, the harvested plant matter is mixed with the at least one rubber- soluble organic solvent at a weight to volume ratio of 3:100 to 10:100. In other words, 3 grams of harvested plant matter to 100 mL of total rubber-soluble organic solvent and 10 grams of harvested plant matter to 100 mL of total rubber-soluble organic solvent. The relative amounts of harvested plant matter and total rubber-soluble solvent that are utilized in a particular process can be dependent upon the amount of mixing that may be applied to the mixture of harvested plant matter and at least one rubber-soluble organic solvent, the affinity of the solvent(s) for natural rubber and the amount of time that the mixture is allowed to remain in contact prior to isolating the dissolved rubber from the solids.

[00023] In certain embodiments of the processes disclosed herein, the at least one rubber-soluble organic solvent comprises one or more rubber-soluble organic solvents.

[00024] In certain embodiments of the processes disclosed herein, when the harvested plant matter and at least one rubber-soluble solvent are mixed together, it can be advantageous to apply some type of agitation to the mixture in order to assist in dissolution of the rubber from the plant matter. Various types of agitation can be utilized including continuous or intermittent mixing using various types of apparatus, including, but not limited to, magnetic stir bars, propellers, baffles, sonication and the like.

[00025] According to the processes disclosed herein, the mixture of harvested plant matter and at least one rubber-soluble organic solvent are allowed to remain in contact for various amounts of time, as may be required to dissolve the desired amount of rubber from the harvest plant matter. The actual amount of time that the mixture is allowed to remain in contact can be influenced by various factors including the presence and amount of agitation and the relative amounts of harvested plant matter and solvent. In certain embodiments of the processes disclosed herein, the mixture of harvested plant matter and at least one rubber soluble organic solvent are allowed to remain in contact for 4-24 hours. In other embodiments of the processes disclosed herein, a shorter contact time such as 30 minutes up to 12 hours or even 30 minutes to 6 hours may be achieved based upon use of a solvent or solvents that exhibit particular affinity for natural rubber, agitation and/or relatively more solvent(s). In preferred embodiments of the processes disclosed herein, the mixture of harvested plant matter and at least one rubber-soluble organic solvent are allowed to remain in contact for 6-12 hours.

[00026] According to the processes disclosed herein, after the mixture of harvested plant matter and at least one rubber-soluble organic solvent have been allowed to remain in contact for a sufficient amount of time to dissolve the desired amount of rubber, the at least one rubber-soluble solvent is removed from the dissolved rubber fraction to produce a solid rubber mass that contains no more than 2% by weight solids based upon the total weight of the dissolved rubber fraction. In other embodiments, the solid rubber mass contains no more than 1% by weight solids based upon the total weight of the dissolved rubber fraction. Solids refers to all material that is not soluble in the at least one non-soluble organic solvent and may include cellulose, dirt, ash and other plant material. Various methods may be utilized to separate the dissolved rubber fraction from the solids. These methods include, but are not limited to flotation, filtering and centrifuging. In preferred embodiments of the processes disclosed herein, the dissolved rubber fraction is removed from the solids using a centrifuging process.

[00027] As previously discussed, the at least one rubber-soluble solvent is removed from the dissolved rubber fraction to produce a solid rubber mass. The removal of the at least one rubber-soluble solvent may be effected using various types of apparatus, including, but not limited to evaporating of solvent under vacuum, evaporating of solvent by mild heating, by causing coagulation of the rubber based upon addition of other solvents, and coagulation by freezing. The term solid rubber mass should be understood to include both solid and semi-solid rubber masses, that contain some small amount of residual solvent (e.g., up to 5% by weight, preferably 2% by weight or less, based upon the total weight of the solid rubber mass).

[00028] As previously discussed, the processes disclosed herein make use of at least one rubber-insoluble organic solvent that is mixed with the solid rubber mass in order to dissolve soluble impurities and remove them from the solid rubber mass. The solid rubber mass is mixed with the at least one rubber-insoluble organic solvent at a weight to volume ratio of 2: 100 to 20: 100. In other words, 2 grams of solid rubber mass to 100 mL of total rubber- insoluble organic solvent and 20 grams of solid rubber mass to 100 mL of total rubber-insoluble organic solvent. These ratios can also be represented as weight to volume ratios of 1 :50 to 1 :5. In certain embodiments, the solid rubber mass is mixed with the at least one rubber-insoluble organic solvent at a weight to volume ratio of 5:100 to 10:100. In other words, 5 grams of harvested plant matter to 100 mL of total rubber-insoluble organic solvent and 10 grams of harvested plant matter to 100 mL of total rubber-insoluble organic solvent. The relative amounts of harvested plant matter and total rubber-insoluble solvent that are utilized in a particular embodiment of the processes disclosed herein can be dependent upon the amount of mixing that may be applied to the mixture of solid rubber mass and at least one rubber-insoluble organic solvent as well as the amount of time that the mixture is allowed to remain in contact prior to isolating the reduced solid rubber mass from the at least one rubber-insoluble organic solvent. [00029] In certain embodiments of the processes disclosed herein, the at least one rubber-insoluble organic solvent comprises one or more rubber-insoluble organic solvents.

[00030] In certain embodiments of the processes disclosed herein, when the solid rubber mass and at least one rubber-insoluble organic solvent are mixed together, it can be advantageous to apply some type of agitation to the mixture in order to increase assist in dissolution of the rubber from the plant matter. Various types of agitation can be utilized including continuous or intermittent mixing using various types of apparatus, including, but not limited to, magnetic stir bars, propellers, baffles, sonication and the like.

[00031] According to the processes disclosed herein, the mixture of solid rubber mass and at least one rubber-insoluble organic solvent are allowed to remain in contact for various amounts of time, as may be required to dissolve the desired amount of soluble impurities from the solid rubber mass. The actual amount of time that the mixture is allowed to remain in contact can be influenced by various factors including the presence and amount of agitation and the relative amounts of solid rubber mass and solvent. In certain embodiments of the processes disclosed herein, the mixture of solid rubber mass and at least one rubber-insoluble organic solvent are allowed to remain in contact for 8-12 hours. In other embodiments of the processes disclosed herein, a shorter contact time such as 30 minutes up to 12 hours or even 30 minutes to 6 hours may be achieved based upon use of a solvent or solvents that exhibit particular affinity for natural rubber, agitation and/or relatively more solvent(s). In preferred embodiments of the processes disclosed herein, the mixture of harvested plant matter and at least one rubber- insoluble organic solvent are allowed to remain in contact for 4-6 hours.

[00032] As previously discussed, the processes disclosed herein make use of non- Hevea plant matter comprising at least 90% by weight of roots that are sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof. In other words, the harvested plant matter contains 10% or less of plant matter from sources other than the roots of Taraxacum kok-saghyz, Scorzonera tau-saghyz and Scorzonera uzbekistanicai plant (or combinations thereof). This other matter may include crowns from the same plant sources. The plant matter that is utilized may take various physical forms as described further herein. In certain embodiments, the plant matter comprises chopped roots from Taraxacum kok- saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof. In certain embodiments, the plant matter also includes crown material in addition to root material, all of which has been mechanically reduced in size. In preferred embodiments, all or almost all (i.e., 98% by weight or more or even 99% by weight or more of the dirt) of the residual dirt that may have been attached to the roots has been removed. Various methods for removing the dirt may be utilized including one or more of water washing, shaking, forced air and vacuum. When any type of water washing is used to remove dirt, it is preferably followed by drying of the roots to remove residual water.

[00033] In certain embodiments, the plant matter has been chopped into pieces.

The chipping or chopping make take place in one or more than one step. Rough chopping may take place before or after the optional removal of leaves and soil (such as by shaking the plant or subjecting it to strong air currents), but is preferably after the removal of a large majority of leaves and soil from the harvested plant matter. Chipping or chopping into pieces with an average size of 1.5" or less or 1" or less may be achieved using various physical means. One exemplary way of obtaining chopped plant matter with an average size of 1.5" or less or 1" or less is to feed raw plant material (or optionally rough chopped plant matter) into a shredder, a granulator, a hammer mill or a roller mill. A granulator is a well-known machine designed for chopping or grinding material into various sizes. Most granulators contain multiple knives (often steel knives) and one or more screens (sometimes interchangeable) with various diameter holes to determine the size of the final product. Various size granulators exist and may be useful in chopping the plant matter such as those containing openings of 3/8", ¼" and 1/8". A hammer mill can generally be described as a steel drum containing a vertical or horizontal rotating shaft or drum on which hammers are mounted; the hammers "pound" the material that is passed through the mill. Various size hammer mills exist and may be useful in chopping the plant matter such as those containing openings of 3/8", ¼" and 1/8". A roller mill/cracker mill can generally be described as a device with two or more rolls each containing longitudinal grooves which assist in further size reduction of material fed through the mill. Various size roller mills exist and may be useful in chopping the plant matter such as those containing openings of 3/8", ¼" and 1/8". In certain embodiments according to the processes disclosed herein, the plant matter is subjected to at least one of a shredder, a granulator, a hammer mill, a roller mill and a flaker mill to produce chopped plant matter having an average size of 1" or less". In other embodiments according to the processes disclosed herein, the plant matter is subjected to at least two of a shredder, a granulator, a hammer mill, a roller mill and a flaker mill to produce chopped plant matter having an average size of 1" or less.

[00034] In certain embodiments of the processes disclosed herein, the plant matter has not only been chopped or shredded (such as by treatment in a shredder, roller mill, hammer mill and/or granulator) but has also been subjected to a flaker mill/flaker and/or other mechanical treatment capable of rupturing the cell walls of the cells that contain the natural rubber. A flaker mill or flaker can generally be described as a device with two or more rolls each having a smooth surface, usually operated at different speeds, with a defined and adjustable clearance between rolls which primarily assist in providing further rupturing of plant cell walls. Such types of mechanical treatment tend to increase the amount of natural rubber that can ultimately be recovered from the plant matter. In certain embodiments of the processes disclosed herein, chopped plant matter is subjected to both roll milling and flake milling. In those embodiments where at least one of roll milling, or hammer milling, a shredder, a granulator and flake milling is used upon the chopped plant matter, the chopped plant matter is preferably treated with at least one antioxidant (the amount of the antioxidant being in accordance with the antioxidant discussion herein).

[00035] In certain preferred embodiments of the processes disclosed herein, the plant matter that is subjected to the organic-based purification process in order to isolate purified natural rubber has been semi-purified in order to remove a majority of the cellulose-type plant material. Such semi-purified plant material will still contain some amount of cellulose-type plant material in addition to other impurities along with non-Hevea rubber. In certain embodiments, at least 50% by weight of the cellulose-type plant material has been removed to form the semi- purified plant material. In other embodiments, at least 75% or even at least 80% of the cellulose- type plant material has been removed to form the semi-purified plant material.

[00036] In certain preferred embodiments of the processes disclosed herein, the harvested plant matter comprises at least 90%> by weight of roots sourced from Taraxacum kok- saghyz. It should be understood that when the weight percentage of plant matter is specified that it is intended to include any residual dirt or other matter associated with the plant matter that is added along with the plant matter to the solvent. In other preferred embodiments of the processes disclosed herein, the harvested plant matter comprises at least 95 %> by weight of roots sourced from Taraxacum kok-saghyz. [00037] In any of the foregoing embodiments of the processes described herein, the at least one rubber-soluble organic solvent may comprise non-polar organic solvent. Suitable non-polar organic solvents may be selected from the group consisting of alkanes having from 4 to 9 carbon atoms (e.g., pentane, hexane, heptanes, nonane and the like); cycloalkanes and alkyl cycloalkanes having from 5 to 10 carbon atoms (e.g., cyclohexane, cyclopentane and the like); aromatics and alkyl substituted aromatics having from 6 to 12 carbon atoms (e.g., benzene, toluene, xylene and the like); and combinations thereof. In certain preferred embodiments of the processes disclosed herein, the at least rubber-soluble solvent or the at least one non-polar organic solvent is toluene. In any of the embodiments of the processes disclosed herein, mixtures of two or more non-polar organic solvents may be utilized.

[00038] In any of the foregoing embodiments of the processes disclosed herein, the at least one rubber-insoluble organic solvent may comprise polar organic solvent. Suitable polar organic solvents may be selected from the group consisting of alcohols having 1 to 8 carbon atoms (e.g., ethanol, isopropanol, ethanol and the like); ethers and esters having from 2 to 8 carbon atoms; cyclic ethers having from 4 to 8 carbon atoms; and ketones having from 3 to 8 carbon atoms (e.g., acetone, methyl ethyl ketone and the like); and combinations thereof. In certain preferred embodiments of the processes disclosed herein, the at least one rubber-insoluble organic solvent or at least one polar organic solvent is acetone. In any of the embodiments of the processes disclosed herein, mixtures of two or more polar organic solvents may be utilized.

Purified Non-Hevea Rubber Product

[00039] As previously discussed, the non-Hevea rubber that is present at 100 phr in the purified non-Hevea rubber product contains non-Hevea rubber containing no more than 3.5% by weight total impurities.

[00040] In certain embodiments, the non-Hevea rubber that is present at 100 phr in the purified non-Hevea rubber product contains no more than 3% by weight total impurities. In other embodiments, the purified non-Hevea rubber that is present at 100 phr in the purified non- Hevea rubber product contains no more than 2.5% by weight total impurities.

[00041] It is contemplated that the purified non-Hevea rubber product (whether containing no more than 3.5% by weight total impurities, no more than 3% by weight total impurities or no more than 2.5% by weight total impurities) may be sold in a pure form (i.e., with no additional additives). It is also contemplated that it may be formulated with one or more other rubbers or rubber additives and sold in such a formulated form. In certain embodiments, the one or more rubbers may be selected from the group consisting of Hevea-natural rubber, synthetic conjugated-diene containing polymers and copolymers. Non-limiting examples of such rubbers include, but are not limited to, polybutadiene, polyisoprene, and styrene -butadiene copolymer. The rubber additives may be selected from one or more of conventional rubber additives. Examples include, but are not limited to, fillers, process oils, plasticizers, antidegradants (e.g., antioxidants and antioxonants), curing agents and the like.

Sulfur- Vulcanizable Rubber Compound

[00042] As previously discussed, the sulfur-vulcanizable rubber compound contains 10-100 phr of non-Hevea rubber sourced from Taraxacum kok-saghyz, Scorzonera tau- saghyz, Scorzonera uzbekistanica, and combinations that contains no more than 3.5% by weight total impurities, with no more than 2% by weight volatiles, no more than 1% by weight residue and no more than 0.5% by weight combustibles.

[00043] In certain embodiments of the sulfur-vulcanizable rubber compound, the non-Hevea rubber sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof utilizes purified rubber that contains no more than 3% by weight total impurities. In other embodiments of the sulfur-vulcanizable rubber compound, the rubber sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof utilizes purified rubber that contains no more than 2.5% by weight total impurities.

[00044] In certain preferred embodiments of the sulfur-vulcanizable rubber compound, the rubber is sourced from Taraxacum kok-saghyz. In certain of these embodiments, the source is plant matter that comprises at least 90% or at least 95% by weight roots from Taraxacum kok-saghyz.

[00045] As previously discussed, the sulfur-vulcanizable rubber compound contains 0-90 phr of at least one synthetic conjugated-diene containing polymer or copolymer. In certain embodiments, the sulfur-vulcanizable rubber compound contains 10-90 phr of at least one synthetic conjugated-diene containing polymer or copolymer. In yet other embodiments, the sulfur-vulcanizable rubber compound contains 40-90 phr of at least one synthetic conjugated- diene containing polymer or copolymer. Non-limiting examples of the synthetic conjugated diene containing polymer or copolymer include polybutadiene, polyisoprene and styrene- butadiene copolymer. In certain embodiments, the sulfur-vulcanizable compound contains 0-90 phr of Hevea-natural rubber. In other embodiments, the sulfur-vulcanizable compound contains 10-60 phr of Hevea-natural rubber. In certain embodiments, the 0-90 phr of Hevea natural rubber together with the rubber sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof, comprises 100 phr of the sulfur- vulcanizable rubber compound; in some such embodiments the non-Hevea rubber may be viewed as a partial replacement for Hevea rubber. Alternatively, in other embodiments, the sulfur-vulcanizable rubber compound may comprise 10-100 phr of purified rubber sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof (with a no more than 3% by weight total impurities, or no more than 2.5% by weight total impurities); 0-90 phr of at least one synthetic conjugated-diene containing polymer or copolymer; and 0-90 phr of at Hevea natural rubber.

[00046] As previously discussed, the sulfur-vulcanizable rubber compound contains 20-200 phr of at least one reinforcing filler selected from the group consisting of carbon black, silica, calcium carbonate, clay, talc, barite, wollastonite, mica, precipitated silicates, and diatomite. Various combinations of reinforcing fillers may be utilized. In preferred embodiments, the sulfur-vulcanizable rubber compound contains at least one of silica and carbon black. In preferred embodiments, the at least one reinforcing filler is present in an amount of 5- 100 phr.

[00047] The silica utilized (silicon dioxide) may include wet-process, hydrated silica produced by a chemical reaction in water, and precipitated as ultra-fine spherical particles. In certain of the foregoing embodiments, the silica has a surface area of about 32 to about 400 m 2 /g, in another embodiment about 100 to about 250 m 2 /g, and in yet another embodiment, about 150 to about 220 m /g. The pH of the silica filler in certain of the foregoing embodiments is about 5.5 to about 7 and in another embodiment about 5.5 to about 6.8. Commercially available silicas include Hi-Sil™ 215, Hi-Sil™ 233, Hi-Sil™ 255LD, and Hi-Sil™ 190 (PPG Industries; Pittsburgh, Pennsylvania), Zeosil™ 1165MP and 175GRPlus (Rhodia), Vulkasil™ (Bary AG), Ultrasil™ VN2, VN3 (Degussa), and HuberSil™ 8745 (Huber).

[00048] If silica is used as a filler, it may be desirable to use a coupling agent to couple the silica to the polymer. Numerous coupling agents are known, including but not limited to organosulfide polysulfides and organoalkoxymercaptosilanes. Generally, any organosilane polysulfide may be used. Suitable organosilane polysulfides include, but are not limited to, 3,3'- bis(trimethoxysilylpropyl)disulfide, 3,3'-bis(triethoxysilylpropyl)disulfide, 3,3'- bis(triethoxysilylpropyl)tetrasulfide, 3 ,3 '-bis(triethoxysilylpropyl)octasulfide, 3,3'- bis(trimethoxysilylpropyl)tetrasulfide, 2,2'-bis(triethoxysilylethyl)tetrasulfide, 3,3'- bis(trimethoxysilylpropyl)trisulfide, 3,3'-bis(triethoxysilylpropyl)trisulfide, 3,3'- bis(tributoxysilylpropyl)disulfide, 3,3'-bis(trimethoxysilylpropyl)hexasulfide, 3,3'- bis(trimethoxysilylpropyl)octasulfide, 3,3'-bis(trioctoxysilylpropyl)tetrasulfide, 3,3'- bis(trihexoxysilylpropyl)disulfide, 3,3'-bis(tri-2"-ethylhexoxysilylpropyl)trisulfide, 3,3'- bis(triisooctoxysilylpropyl)tetrasulfide, 3,3'-bis(tri-t-butoxysilylpropyl)disulfide, 2,2'- bis(methoxydiethoxysilylethyl)tetrasulfide, 2,2'-bis(tripropoxysilylethyl)pentasulfide, 3,3'- bis(tricycloneoxysilylpropyl)tetrasulfide, 3,3'-bis(tricyclopentoxysilylpropyl)trisulfide, 2,2'- bis(tri-2"-methylcyclohexoxysilylethyl)tetrasulfide, bis(trimethoxysilylmethyl)tetrasulfide, 3- methoxyethoxypropoxysilyl 3'-diethoxybutoxy-silylpropyl tetrasulfide, 2,2'- bis(dimethylmethoxysilylethyl)disulfide, 2,2'-bis(dimethylsecbutoxysilylethyl) trisulfide, 3,3'- bis(methylbutylethoxysilylpropyl)tetrasulfide, 3,3'-bis(di t-butylmethoxysilylpropyl) tetrasulfide, 2,2'-bis(phenylmethylmethoxysilylethyl)trisulfide, 3,3'-bis(diphenyl isopropoxysilylpropyl)tetrasulfide, 3,3'-bis(diphenylcyclohexoxysilylpropyl)disulfide, 3,3'- bis(dimethylethylmercaptosilylpropyl)tetrasulfide, 2,2'-bis(methyldimethoxysilylethyl)trisulfide, 2,2'-bis(methyl ethoxypropoxysilylethyl)tetrasulfide, 3,3'- bis(diethylmethoxysilylpropyl)tetrasulfide, 3,3'-bis(ethyldi-secbutoxysilylpropyl)disulfide, 3,3'- bis(propyldiethoxysilylpropyl) disulfide, 3,3'-bis(butyldimethoxysilylpropyl)trisulfide, 3,3'- bis(phenyldimethoxysilylpropyl)tetrasulfide, 3'-trimethoxysilylpropyl tetrasulfide, 4,4'- bis(trimethoxysilylbutyl)tetrasulfide, 6,6'-bis(triethoxysilylhexyl)tetrasulfide, 12, 12'- bis(triisopropoxysilyl dodecyl)disulfide, 18,18'-bis(trimethoxysilyloctadecyl)tetrasulfide, 18,18'- bis(tripropoxysilyloctadecenyl)tetrasulfide, 4,4'-bis(trimethoxysilyl-buten-2-yl)tetrasulfide, 4,4'- bis(trimethoxysilylcyclohexylene)tetrasulfide, 5 ,5 '-bis(dimethoxymethylsilylpentyl)trisulfide, 3,3'-bis(trimethoxysilyl -2-methylpropyl)tetrasulfide and 3,3'-bis(dimethoxyphenylsilyl-2- methylpropyl)disulfide .

[00049] Suitable organoalkoxymercaptosilanes include, but are not limited to, triethoxy mercaptopropyl silane, trimethoxy mercaptopropyl silane, methyl dimethoxy mercaptopropyl silane, methyl diethoxy mercaptopropyl silane, dimethyl methoxy mercaptopropyl silane, triethoxy mercaptoethyl silane, tripropoxy mercaptopropyl silane, ethoxy dimethoxy mercaptopropylsilane, ethoxy diisopropoxy mercaptopropylsilane, ethoxy didodecyloxy mercaptopropylsilane and ethoxy dihexadecyloxy mercaptopropylsilane. Such organoalkoxymercaptosilanes may be capped with a blocking group, i.e., the mercapto hydrogen atom is replaced with another group. A representative example of a capped organoalkoxymercaptosilane coupling agent is a liquid 3-octanoylthio-l-propyltriethoxysilane, commercially available as NXTTM Silane from Momentive Performance Materials Inc.

[00050] Mixtures of various organosilane polysulfide compounds and organoalkoxymercaptosilanes can be used.

[00051] The carbon black(s) utilized may include any of the commonly available, commercially-produced carbon blacks. These include those having a surface area (EMSA) of at least 20 m 2 /gram and in other embodiments at least 35 m 2 /gram up to 200 m 2 /gram or higher. Surface area values include those determined by ASTM test D-1765 using the cetyltrimethyl- ammonium bromide (CTAB) technique. Among the useful carbon blacks are furnace black, channel blacks and lamp blacks. More specifically, examples of the carbon blacks include super abrasion furnace (SAF) blacks, high abrasion furnace (HAF) blacks, fast extrusion furnace (FEF) blacks, fine furnace (FF) blacks, intermediate super abrasion furnace (ISAF) blacks, semi- reinforcing furnace (SRF) blacks, medium processing channel blacks, hard processing channel blacks and conducting channel blacks. Other carbon blacks that may be utilized include acetylene blacks. Mixtures of two or more of the above blacks can be used. Exemplary carbon blacks include those bearing ASTM designation (D-1765-82a) N-110, N-220, N-339, N-330, N- 351, N-550, and N-660. In one or more embodiments, the carbon black may include oxidized carbon black.

[00052] In certain embodiments of the sulfur-vulcanizable rubber compound, other conventional rubber additives may also be added to the rubber compositions. These include, for example, process oils, plasticizers, anti-degradants such as antioxidants and anti-ozonants, curing agents and the like.

[00053] Typically, process oils are added to tread rubber compositions as a softener. Non-limiting examples of process oils used in the tread rubber compositions disclosed herein include paraffinic, naphthenic, and aromatic process oils, and the like. In one or more embodiments according to the first-sixth embodiments disclosed herein, the process oil is an aromatic process oil. In other embodiments, the process oil is a low polycyclic aromatic content ("low PCA") oil containing less than 2%. Other useful oils include those containing less than 3 wt%, less than 2 wt% or less than 1 wt% of polycyclic aromatic compounds (as measured by IP346) ("low PCA oils"). Such low PCA oils are increasingly used in an effort to reduce the amount of polycyclic aromatic compounds present in rubbers used in tires. Commercially available low PCA oils include various naphthenic oils, mild extraction solvates (MES) and treated distillate aromatic extracts (TDAE).

[00054] In certain embodiments, the sulfur-vulcanizable rubber compound, especially when used for tire treads, preferably contains between 1 and 100 phr process oil. In one or more embodiments, the amount of process oil is between 2 and 100 phr; in other embodiments, between 1 and 50 phr; in others, between 2 and 50 phr. In still other embodiments, the amount of process oil is between 1 and 20 phr; in others, between 2 and 20 phr; in others, between 1 and 10 phr; in still others, between 2 and 10 phr.

[00055] When forming a tread rubber composition, generally all ingredients may be mixed with standard equipment such as, e.g., Banbury or Brabender mixers. Typically, mixing occurs in two or more stages. During the first stage (also known as the masterbatch stage), mixing typically is begun at temperatures of about 100 °C to about 130 °C and increases until a so-called drop temperature, typically about 165 °C, is reached.

[00056] Where a rubber composition includes fillers other than (or in addition to) carbon black, a separate re-mill stage often is employed for separate addition of the other fillers. This stage often is performed at temperatures similar to, although often slightly lower than, those employed in the masterbatch stage, i.e., ramping from about 90 °C to a drop temperature of about 150 °C. For purposes of this application, the term "masterbatch" means the composition that is present during the masterbatch stage or the composition as it exists during any re -mill stage, or both.

[00057] Curatives, accelerators, etc., are generally added at a final mixing stage.

To avoid undesirable scorching and/or premature onset of vulcanization, this mixing step often is done at lower temperatures, e.g., starting at about 60 °C to about 65 °C and not going higher than about 105° to about 110 °C. For purposes of this application, the term "final batch" means the composition that is present during the final mixing stage. [00058] Subsequently, the compounded mixture is processed (e.g., milled) into sheets prior to being formed into any of a variety of components and then vulcanized, which typically occurs at about 5° to about 15 °C higher than the highest temperatures employed during the mixing stages, most commonly about 170 °C.

[00059] In certain embodiments of the sulfur-vulcanizable rubber compound, the compound will exhibit a tan δ at 60 °C, 10 Hz and 2% strain of less than 0.2 after curing with 0.5-2 phr of sulfur at 135-165 °C for 5-40 minutes. In certain preferred embodiments, the compound will exhibit a tan δ at 60 °C, 10 Hz and 2% strain of less than 0.15 after curing with 0.5-2 phr of sulfur at 135-165 °C for 5-40 minutes. While the sulfur-vulcanizable rubber compound may be sold in a vulcanized or non-vulcanized form, the tan δ can only be measured upon a cured compound and, thus, exemplary cure conditions that should be employed when measuring the tan δ of a compound in question have been specified. Thus, the phrase sulfur- vulcanizable compound as used herein should be understood to mean a compound that is capable of being sulfur- vulcanized but that has not necessarily been vulcanized. A compound that has already been sulfur-vulcanized (i.e., cured) should be understood to be a sulfur-vulcanizable compound since it was capable of being vulcanized.

[00060] In certain embodiments of the sulfur-vulcanizable rubber compound, the compound will exhibit an elongation at break at room temperature (i.e., 23 °C) of at least 450 MPa after curing with 0.5-2 phr of sulfur at 135-165 °C for 5-40 minutes. In certain preferred embodiments, the compound will exhibit an elongation at break at room temperature of at least 500 MPa after curing with 0.5-2 phr of sulfur at 135-165 °C for 5-40 minutes. While the sulfur- vulcanizable rubber compound may be sold in a vulcanized or non-vulcanized form, the elongation at break can only be measured upon a cured compound and, thus, exemplary cure conditions that should be employed when measuring the elongation at break of a compound in question have been specified.

Sulfur-vulcanized Rubber Compound

[00061] As previously discussed, the sulfur-vulcanized rubber compound contains 10-100 phr of non-Hevea rubber sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations that contains no more than 3.5% by weight total impurities, with no more than 2% by weight volatiles, no more than 1% by weight residue and no more than 0.5% by weight combustibles.

[00062] In certain embodiments of the sulfur-vulcanized rubber compound, the non-Hevea rubber sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof utilizes purified rubber that contains no more than 3% by weight total impurities. In other embodiments of the sulfur-vulcanized rubber compound, the rubber sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof utilizes purified rubber that contains no more than 2.5% by weight total impurities.

[00063] In certain preferred embodiments of the sulfur- vulcanized rubber compound, the rubber is sourced from Taraxacum kok-saghyz. In certain of these embodiments, the source is plant matter that comprises at least 90% or at least 95% by weight roots from Taraxacum kok-saghyz.

[00064] As previously discussed, the sulfur-vulcanized rubber compound contains

0.5-6 phr of sulfur. In preferred embodiments, the sulfur- vulcanized rubber compound contains 1.2-4 phr of sulfur. Sulfur may be added in the form of elemental sulfur, via a sulfur donor or by a combination of both.

[00065] As previously discussed, the sulfur-vulcanized rubber compound contains at least one accelerator. The particular vulcanization accelerator or accelerators is not particularly limited. In preferred embodiments, the at least one accelerator is amine-containing. Non- limiting examples of the at least one accelerator include: diphenyl guanidine (DPG), tetramethylthiuram disulfide (TMTD), 4,4'-dithiodimorpholine (DTDM), tetrabutylthiuram disulfide (TBTD), benzothiazyl disulfide (MBTS), 2-(morpholinothio) benzothiazole (MBS), N- tert-butyl-2-benzothiazole sulfonamide (TBBS), N-cyclohexyl-2-benzothiazole sulfonamide (CBS), and mixtures thereof. The amount of vulcanization accelerator(s) used in the sulfur- vulcanized rubber compound may be from about 0.1 to about 10 phr or from about 1 to about 5 phr.

[00066] In certain embodiments of the sulfur-vulcanized rubber compound, the non-Hevea rubber sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof utilizes purified rubber that contains no more than 3% by weight total impurities. In other embodiments of the sulfur-vulcanized rubber compound, the rubber sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof utilizes purified rubber that contains no more than 2.5% by weight total impurities.

[00067] In certain preferred embodiments of the sulfur-vulcanized rubber compound, the rubber is sourced from Taraxacum kok-saghyz. In certain of these embodiments, the source is plant matter that comprises at least 90% or at least 95% by weight roots from Taraxacum kok-saghyz.

[00068] As previously discussed, the sulfur-vulcanized rubber compound contains

0-90 phr of at least one synthetic conjugated-diene containing polymer or copolymer. In certain embodiments, the sulfur- vulcanized rubber compound contains 10-90 phr of at least one synthetic conjugated-diene containing polymer or copolymer. In yet other embodiments, the sulfur-vulcanized rubber compound contains 40-90 phr of at least one synthetic conjugated-diene containing polymer or copolymer. Non-limiting examples of the synthetic conjugated diene containing polymer or copolymer include polybutadiene, polyisoprene and styrene -butadiene copolymer. In certain embodiments, the sulfur-vulcanized compound contains 0-90 phr of Hevea -natural rubber. In other embodiments, the sulfur- vulcanizable compound contains 10-60 phr of Hevea-natural rubber. In certain embodiments, the 0-90 phr of Hevea natural rubber together with the rubber sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof, comprises 100 phr of the sulfur- vulcanized rubber compound; in some such embodiments the non-Hevea rubber may be viewed as a partial replacement for Hevea rubber. Alternatively, in other embodiments, the sulfur-vulcanized rubber compound may comprise 10-100 phr of purified rubber sourced from Taraxacum kok- saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof (with a no more than 3% by weight total impurities, or no more than 2.5% by weight total impurities); 0-90 phr of at least one synthetic conjugated-diene containing polymer or copolymer; and 0-90 phr of at Hevea natural rubber.

[00069] As previously discussed, the sulfur-vulcanized rubber compound contains

20-200 phr of at least one reinforcing filler selected from the group consisting of carbon black, silica, calcium carbonate, clay, talc, barite, wollastonite, mica, precipitated silicates, and diatomite. Various combinations of reinforcing fillers may be utilized. In preferred embodiments, the sulfur-vulcanized rubber compound contains at least one of silica and carbon black. In preferred embodiments, the at least one reinforcing filler is present in an amount of 5- 100 phr.

[00070] The silica utilized (silicon dioxide) may include wet-process, hydrated silica produced by a chemical reaction in water, and precipitated as ultra-fine spherical particles. In certain of the foregoing embodiments, the silica has a surface area of about 32 to about 400 m 2 /g, in another embodiment about 100 to about 250 m 2 /g, and in yet another embodiment, about 150 to about 220 m /g. The pH of the silica filler in certain of the foregoing embodiments is about 5.5 to about 7 and in another embodiment about 5.5 to about 6.8. Commercially available silicas include Hi-Sil™ 215, Hi-Sil™ 233, Hi-Sil™ 255LD, and Hi-Sil™ 190 (PPG Industries; Pittsburgh, Pennsylvania), Zeosil™ 1165MP and 175GRPlus (Rhodia), Vulkasil™ (Bary AG), Ultrasil™ VN2, VN3 (Degussa), and HuberSil™ 8745 (Huber).

[00071] If silica is used as a filler, it may be desirable to use a coupling agent to couple the silica to the polymer. Numerous coupling agents are known, including but not limited to organosulfide polysulfides and organoalkoxymercaptosilanes. Generally, any organosilane polysulfide may be used. Suitable organosilane polysulfides include, but are not limited to, 3,3'- bis(trimethoxysilylpropyl)disulfide, 3,3'-bis(triethoxysilylpropyl)disulfide, 3,3'- bis(triethoxysilylpropyl)tetrasulfide, 3 ,3 '-bis(triethoxysilylpropyl)octasulfide, 3,3'- bis(trimethoxysilylpropyl)tetrasulfide, 2,2'-bis(triethoxysilylethyl)tetrasulfide, 3,3'- bis(trimethoxysilylpropyl)trisulfide, 3,3'-bis(triethoxysilylpropyl)trisulfide, 3,3'- bis(tributoxysilylpropyl)disulfide, 3,3'-bis(trimethoxysilylpropyl)hexasulfide, 3,3'- bis(trimethoxysilylpropyl)octasulfide, 3,3'-bis(trioctoxysilylpropyl)tetrasulfide, 3,3'- bis(trihexoxysilylpropyl)disulfide, 3,3'-bis(tri-2"-ethylhexoxysilylpropyl)trisulfide, 3,3'- bis(triisooctoxysilylpropyl)tetrasulfide, 3,3'-bis(tri-t-butoxysilylpropyl)disulfide, 2,2'- bis(methoxydiethoxysilylethyl)tetrasulfide, 2,2'-bis(tripropoxysilylethyl)pentasulfide, 3,3'- bis(tricycloneoxysilylpropyl)tetrasulfide, 3,3'-bis(tricyclopentoxysilylpropyl)trisulfide, 2,2'- bis(tri-2"-methylcyclohexoxysilylethyl)tetrasulfide, bis(trimethoxysilylmethyl)tetrasulfide, 3- methoxyethoxypropoxysilyl 3'-diethoxybutoxy-silylpropyl tetrasulfide, 2,2'- bis(dimethylmethoxysilylethyl)disulfide, 2,2'-bis(dimethylsecbutoxysilylethyl) trisulfide, 3,3'- bis(methylbutylethoxysilylpropyl)tetrasulfide, 3,3'-bis(di t-butylmethoxysilylpropyl) tetrasulfide, 2,2'-bis(phenylmethylmethoxysilylethyl)trisulfide, 3,3'-bis(diphenyl isopropoxysilylpropyl)tetrasulfide, 3,3'-bis(diphenylcyclohexoxysilylpropyl)disulfide, 3,3'- bis(dimethylethylmercaptosilylpropyl)tetrasulfide, 2,2'-bis(methyldimethoxysilylethyl)trisulfide, 2,2'-bis(methyl ethoxypropoxysilylethyl)tetrasulfide, 3,3'- bis(diethylmethoxysilylpropyl)tetrasulfide, 3,3'-bis(ethyldi-secbutoxysilylpropyl)disulfide, 3,3'- bis(propyldiethoxysilylpropyl) disulfide, 3,3'-bis(butyldimethoxysilylpropyl)trisulfide, 3,3'- bis(phenyldimethoxysilylpropyl)tetrasulfide, 3'-trimethoxysilylpropyl tetrasulfide, 4,4'- bis(trimethoxysilylbutyl)tetrasulfide, 6,6'-bis(triethoxysilylhexyl)tetrasulfide, 12, 12'- bis(triisopropoxysilyl dodecyl)disulfide, 18,18'-bis(trimethoxysilyloctadecyl)tetrasulfide, 18,18'- bis(tripropoxysilyloctadecenyl)tetrasulfide, 4,4'-bis(trimethoxysilyl-buten-2-yl)tetrasulfide, 4,4'- bis(trimethoxysilylcyclohexylene)tetrasulfide, 5 ,5 '-bis(dimethoxyrnethylsilylpentyl)trisulfide, 3,3'-bis(trimethoxysilyl -2-methylpropyl)tetrasulfide and 3,3'-bis(dimethoxyphenylsilyl-2- methylpropyl)disulfide .

[00072] Suitable organoalkoxymercaptosilanes include, but are not limited to, triethoxy mercaptopropyl silane, trimethoxy mercaptopropyl silane, methyl dimethoxy mercaptopropyl silane, methyl diethoxy mercaptopropyl silane, dimethyl methoxy mercaptopropyl silane, triethoxy mercaptoethyl silane, tripropoxy mercaptopropyl silane, ethoxy dimethoxy mercaptopropylsilane, ethoxy diisopropoxy mercaptopropylsilane, ethoxy didodecyloxy mercaptopropylsilane and ethoxy dihexadecyloxy mercaptopropylsilane. Such organoalkoxymercaptosilanes may be capped with a blocking group, i.e., the mercapto hydrogen atom is replaced with another group. A representative example of a capped organoalkoxymercaptosilane coupling agent is a liquid 3-octanoylthio-l-propyltriethoxysilane, commercially available as NXTTM Silane from Momentive Performance Materials Inc.

[00073] Mixtures of various organosilane polysulfide compounds and organoalkoxymercaptosilanes can be used.

[00074] The carbon black(s) utilized may include any of the commonly available, commercially-produced carbon blacks. These include those having a surface area (EMSA) of at least 20 m 2 /gram and in other embodiments at least 35 m 2 /gram up to 200 m 2 /gram or higher. Surface area values include those determined by ASTM test D-1765 using the cetyltrimethyl- ammonium bromide (CTAB) technique. Among the useful carbon blacks are furnace black, channel blacks and lamp blacks. More specifically, examples of the carbon blacks include super abrasion furnace (SAF) blacks, high abrasion furnace (HAF) blacks, fast extrusion furnace (FEF) blacks, fine furnace (FF) blacks, intermediate super abrasion furnace (ISAF) blacks, semi- reinforcing furnace (SRF) blacks, medium processing channel blacks, hard processing channel blacks and conducting channel blacks. Other carbon blacks that may be utilized include acetylene blacks. Mixtures of two or more of the above blacks can be used. Exemplary carbon blacks include those bearing ASTM designation (D-1765-82a) N-110, N-220, N-339, N-330, N- 351, N-550, and N-660. In one or more embodiments, the carbon black may include oxidized carbon black.

[00075] In certain embodiments of the sulfur- vulcanized rubber compound, other conventional rubber additives may also be added to the rubber compositions. These include, for example, process oils, plasticizers, anti-degradants such as antioxidants and anti-ozonants, curing agents and the like.

[00076] Typically, process oils are added to tread rubber compositions as a softener. Non-limiting examples of process oils used in the tread rubber compositions disclosed herein include paraffinic, naphthenic, and aromatic process oils, and the like. In one or more embodiments according to the first-sixth embodiments disclosed herein, the process oil is an aromatic process oil. In other embodiments, the process oil is a low polycyclic aromatic content ("low PCA") oil containing less than 2%. Other useful oils include those containing less than 3 wt%, less than 2 wt% or less than 1 wt% of polycyclic aromatic compounds (as measured by IP346) ("low PCA oils"). Such low PCA oils are increasingly used in an effort to reduce the amount of polycyclic aromatic compounds present in rubbers used in tires. Commercially available low PCA oils include various naphthenic oils, mild extraction solvates (MES) and treated distillate aromatic extracts (TDAE).

[00077] In certain embodiments, the sulfur-vulcanized rubber compound, especially when used for tire treads, preferably contains between 1 and 100 phr process oil. In one or more embodiments, the amount of process oil is between 2 and 100 phr; in other embodiments, between 1 and 50 phr; in others, between 2 and 50 phr. In still other embodiments, the amount of process oil is between 1 and 20 phr; in others, between 2 and 20 phr; in others, between 1 and 10 phr; in still others, between 2 and 10 phr.

[00078] When forming a tread rubber composition, generally all ingredients may be mixed with standard equipment such as, e.g., Banbury or Brabender mixers. Typically, mixing occurs in two or more stages. During the first stage (also known as the masterbatch stage), mixing typically is begun at temperatures of about 100 °C to about 130 °C and increases until a so-called drop temperature, typically about 165 °C, is reached.

[00079] Where a rubber composition includes fillers other than (or in addition to) carbon black, a separate re-mill stage often is employed for separate addition of the other fillers. This stage often is performed at temperatures similar to, although often slightly lower than, those employed in the masterbatch stage, i.e., ramping from about 90 °C to a drop temperature of about 150 °C. For purposes of this application, the term "masterbatch" means the composition that is present during the masterbatch stage or the composition as it exists during any re -mill stage, or both.

[00080] Curatives, accelerators, etc., are generally added at a final mixing stage.

To avoid undesirable scorching and/or premature onset of vulcanization, this mixing step often is done at lower temperatures, e.g., starting at about 60 °C to about 65 °C and not going higher than about 105 °C to about 110 °C. For purposes of this application, the term "final batch" means the composition that is present during the final mixing stage.

[00081] Subsequently, the compounded mixture is processed (e.g., milled) into sheets prior to being formed into any of a variety of components and then vulcanized, which typically occurs at about 5°C to about 15 °C higher than the highest temperatures employed during the mixing stages, most commonly about 170 °C.

[00082] In certain embodiments of the sulfur-vulcanized rubber compound, the compound will exhibit a tan δ at 60 °C, 10 Hz and 2% strain of less than 0.2 after curing with 0.5-2 phr of sulfur at 135-165 °C for 5-40 minutes. In certain preferred embodiments, the compound will exhibit a tan δ at 60 °C, 10 Hz and 2% strain of less than 0.15 after curing with 0.5-2 phr of sulfur at 135-165 °C for 5-40 minutes. The phrase sulfur-vulcanized rubber compound should be understood to refer to a compound that has been vulcanized. However, the method of vulcanization is not particularly limited and the cure conditions for tan δ have been provided only in an effort to identify the conditions that should be used during testing to determining whether a particular compound has the specified properties.

[00083] In certain embodiments of the sulfur-vulcanized rubber compound, the compound will exhibit an elongation at break at room temperature (i.e., 23 °C) of at least 450 MPa after curing with 0.5-2 phr of sulfur at 135-165 °C for 5-40 minutes. In certain preferred embodiments, the compound will exhibit an elongation at break at room temperature of at least 500 MPa after curing with 0.5-2 phr of sulfur at 135-165 °C for 5-40 minutes. Again, the phrase sulfur-vulcanized rubber compound should be understood to refer to a compound that has been vulcanized. However, the method of vulcanization is not particularly limited and the cure conditions for elongation at break have been provided only in an effort to identify the conditions that should be used during testing to determining whether a particular compound has the specified properties.

Example 1 (Purification of Rubber from T S Plant Matter)

[00084] As described in more detail herein, rubber was isolated from a sample of

TKS harvested plant matter and purified according to the following procedure. Raw TKS harvested plant matter was added to toluene at room temperature (the plant matter was added in a weight to volume ratio of 1 :20 or 100 grams harvested plant matter to 2000 mL toluene) by adding both harvested plant matter and toluene to an Erlenmeyer flask with stirring (the flask was corked after addition of the materials in order to minimize any evaporation of solvent). The TKS harvested plant matter consisted of primarily root material from Taraxacum kok-saghyz plants (the plants were approximately 2-3 years old at the time of harvest) that had been harvested, washed thoroughly with water to remove all visible dirt and dried. (Prior to mixing with the toluene, the washed and dried roots had been pebble -milled, screened and separated through a water-based flotation process in order to separate a majority of the cellulose plant material from the rubber. However, a certain amount of cellulose plant material and other impurities remained in the TKS harvested plant matter and the purpose of the purification was to isolate the rubber from the cellulose plant material and other impurities.) The TKS harvested plant matter was allowed to soak in the toluene for 6-12 hours.

[00085] An antioxidant (Santoflex 13) was added to the toluene solution in an amount of 1% by weight (based on the total weight of plant matter). After soaking for 6-12 hours, the solution (including both toluene and harvested plant matter) was centrifuged using a IEC/EXD centrifuge by Damon IEC at 4000 rpm for 2 hours. After the centrifuge was stopped, it was observed that solids had precipitated at the bottom of the containers. The viscous toluene phase was decanted from the solids and poured into aluminum pans (about 15-17% of solids based on the original weight of the harvested TKS plant material remained as precipitates/solids in the bottom of the flask). The aluminum pans were placed into a fume hood and allowed to dry overnight (approximately 8-10 hours) at room temperature. The next morning the toluene had evaporated leaving behind rubber sheets in the pans. These sheets were collected by lifting them from the pan and cut into small pieces (of approximately l x l cm in size) and added to acetone. The rubber and acetone were present in an amount of 5% by weight rubber based upon the total volume of the acetone solvent (i.e., at a ratio of 5 g rubber to 100 mL acetone). The mixture of rubber pieces and acetone was allowed to soak overnight (approximately 8-10 hours) at 50 °C (the mixture was contained within a closed container that allowed for recondensation of any evaporated solvent). The next morning the acetone (containing impurities such as terpenes, resins and fatty acids) was decanted from the rubber pieces.

[00086] The rubber pieces that remained after the acetone had been decanted were dried under vacuum at 23 °C. Analysis of the "purified" rubber was performed using thermogravimetric analysis ("TGA") and microscopy in order to determine the relative amounts of rubber and various impurities. For the TGA, a Q5000 model from TA Instruments was used with a standard heating protocol from room temperature to 850 °C. Results are reported below in Table 1.

Example 2 - Preparation of Rubber Compounds Using T S-Sourced Natural Rubber

[00087] In order to evaluate the effect of impurity levels on rubber compounds, rubber compounds were prepared using purified TKS-sourced natural rubber with varying impurity levels. (The abbreviation "TKS" is used to refer to Taraxacum kok-saghyz.) A rubber compound containing commercial Hevea-sourced natural rubber was used as a control. The TKS-sourced natural rubber indicated below as "Compounded TKS" was obtained from a sample of Harvested TKS that was purified using the procedure described in Example 1, above. The TKS-sourced natural rubber indicated below as "Harvested TKS" was a sample provided by the Ohio State University Agricultural Research and Development Center; the method used to purify the Harvested TKS included pebble-milling, screening and separation by water-flotation (more precise details were not available). Each natural rubber source was found to contain impurities in the amounts listed in Table 1 below. The rubber compounds were prepared using the formulation provided in Table 2.

Residue weight % 1.39 0.75 0.225

Total impurity weight % 4.26 2.09 2.59

microcrystalline wax blend (55% paraffin) by Hallstar

2 Santofiex 13

Hydrocarbon resin C5-C9 blend by Resinall

⁴ 2,2,4-trimethyl 1,2-hydroquinoline ("TMQ")

⁵ N-cyclohexyl benzothiazole sulfenamide ("CBS")

[00088] First, a master batch was prepared in a 65-gram Brabender mixer using the ingredients listed in Table 2 under "Master Batch." At time = 0, all polymer (i.e, the strips of rubber) was added into the mixer at 110 °C. The mixer was set to 70 rpm. At time = 30 sec. all the carbon black and the master batch ingredients were added into the batch. Once a total mixing time of 4 min. or a drop temperature of 145-150 °C was reached mixing was stopped and the batch was removed from the mixer. Compounded rubber was then rolled through a mill and cut into small strips for feeding for the final mix. Then, the additional ingredients listed in Table 5 under "Final Batch" were added. At time = 0, all polymer (i.e., the strips of rubber) and the final batch ingredients were consecutively added into the mixer at 80 °C. The mixer was set to 50 rpm. Once a total mixing time of 1 min. or a drop temperature of 110 °C was reached mixing was stopped and the batch was removed from the mixer. Compounded rubber was then rolled through a mill and sheeted out for curing.

[00089] Sample 1 was a control that contained 100 phr commercially available

Hevea natural rubber. Samples 2-5 contained 100 phr of Compounded TKS. Samples 3-5 also contained an additional ingredient at amounts of 5, 10 and 15 phr, respectively, that constituted TKS Impurities. The TKS Impurities were a combination of ash, cellulose, resins and other plant matter that are typically found in TKS-sourced natural rubber. The TKS Impurities, which had been extracted from the TKS harvested plant matter during the first purification stage and precipitated in the bottom of the beaker/flask (and then dried at room temperature to remove toluene solvent) were added to Samples 3-5 during the master batch stage.

[00090] The rubber compounds prepared as Samples 1-5 were analyzed by TGA and results are shown in Table 3 below. The results show that the total impurity levels (volatiles + residue) are comparable for the control Sample 1 and the Compounded TKS Sample 2. The total impurity levels are noticeably higher for Samples 3-5 due to the addition of TSK Impurities into the rubber compounds. The percent combustibles were omitted from the total impurity calculation because they are primarily due to the presence of carbon black in the rubber compound.

[00091] After curing at 145 °C for t90 x 1.5 minutes (t90 is the optimum vulcanization time obtained from Monsanto Rheometer for rubber), Samples 1-5 were subjected to physical testing for various dynamic and tensile properties and results are reported in Table 4 below. The value reported as t90 is a measure of the time (in minutes) required to reach 90% completion in curing. The viscoelastic properties of the cured rubber compounds were measured using the following methods. The first method is a temperature sweep test conducted with an Advanced Rheometric Expansion System (ARES) from TA Instruments. The test specimen has a rectangular geometry having a length of 47 mm, a thickness of 2 mm, and a width of 12.7 mm. The length of specimen between the grips on the test machine, i.e., the gap, is approximately 27 mm. The test is conducted using a frequency of 3.14 rad/sec. The temperature is started at -100 °C and increased to 100 °C. The strain is 0.5% for the temperature range of -100 °C to -21 °C, and 2% for the temperature range of -20 °C to 100 °C. The second viscoelastic test is a strain sweep conducted with an Advanced Rheometric Expansion System (ARES) from TA Instruments. The test specimen has a cylindrical button geometry having a diameter of 9.27 mm and a 15.6 mm length. The test is conducted using a frequency of 3.14 rad/sec. The temperature is held constant at the desired temperature, i.e., 60 °C. The strain is swept from 0.03% to 15%. The third viscoelastic test is a dynamic compression test done with a Dynastat™ mechanical spectrometer (Dynastatics Instruments Corp.; Albany, New York) using a cylindrical test specimen (9.27 mm diameter x 15.6 mm height). The sample is compressed under a static load of 2 kg before testing. After it reached an equilibrium state, the test started with a dynamic compression load of 1.25 kg at a frequency of 1 Hz. The sample was then dynamically compressed and then extended and the resultant hysteresis (tangent delta) was then recorded.

[00092] Tensile mechanical properties were determined following the guidelines, but not restricted to, the standard procedure described in ASTM-D412, using ring samples with a dimension of 1.27 mm in width and 1.91 mm in thickness. A specific gauge length of 25.4 mm was used for the tensile test. Specimens are strained at a constant rate and the resulting force is recorded as a function of extension (strain). Force readings are expressed as engineering stresses by reference to the original cross-sectional area of the test piece. The specimens are tested at 23 °C. Breaking strength/tensile strength (Tb), elongation at break/elongation performance (Eb), Tb x Eb and modulus at 23 °C are also reported. The same tensile mechanical properties were also tested at 100 °C.

200% Modulus @ 100 °C (MPa) 4.95 5.29 4.21 4.07 5.00

Tb @ 100 °C (MPa) 22.0 20.5 16.8 14.9 14.00

Eb @ 100 °C (MPa) 640 576 593 563 480

Tb x Eb @ 100 °C (MPa) 14080 11808 9962 8389 6720

[00093] From a review of the data, it can be concluded that the control Sample 1 and the Compounded TKS without any additional impurities (Sample 2) exhibit similar physical properties. The time required to reach 90% completion in curing (t90) is very similar in both Sample 1 and Sample 2. Addition of the impurities (i.e., Samples 3-5) caused cure times to slightly increase. The overall dynamic and tensile properties of Samples 1 and 2 were similar showing that the Compounded TKS without any additional impurities performs comparably to commercial Hevea natural rubber. Elastic modulus values (C) of Sample 1 and Sample 2 were almost identical within the temperature range evaluated. However, Compounded TKS showed better (i.e., lower) hysteresis loss (tan δ) at 60 °C which is generally understood to be a predictor of better rolling resistance. While the tensile strength (Eb) of the Hevea natural rubber of Sample 1 was similar to that of Compounded TKS without any additional impurities in Sample 2, Sample 2 displayed better elongation performance (Eb) at room temperature. Elongation performance is generally understood to be a predictor of flexibility and high-temperature performance. Once the additional amounts of TSK Impurities were added into Samples 3, 4 and 5, the physical performance of the rubber compounds was adversely affected as shown by the reduction in Tb x Eb and increased AG' values. Overall, samples 3 and 4 showed decreased elastic properties (i.e., both 50 and 100 °C, Tb and Eb values which are an indication of strength in the TKS compound. Sample 5 (containing Compounded TKS with 15 phr impurities) showed substantially decreased mechanical performance as compared to Sample 1 and Sample 2, especially in terms of elongation and tensile strength.

[00094] To the extent that the term "includes" or "including" is used in the specification or the claims, it is intended to be inclusive in a manner similar to the term "comprising" as that term is interpreted when employed as a transitional word in a claim. Furthermore, to the extent that the term "or" is employed {e.g., A or B) it is intended to mean "A or B or both." When the applicants intend to indicate "only A or B but not both" then the term "only A or B but not both" will be employed. Thus, use of the term "or" herein is the inclusive, and not the exclusive use. See Bryan A. Garner, A Dictionary of Modern Legal Usage 624 (2d. Ed. 1995). Also, to the extent that the terms "in" or "into" are used in the specification or the claims, it is intended to additionally mean "on" or "onto." Furthermore, to the extent the term "connect" is used in the specification or claims, it is intended to mean not only "directly connected to," but also "indirectly connected to" such as connected through another component or components.

[00095] While the present application has been illustrated by the description of embodiments thereof, and while the embodiments have been described in considerable detail, it is not the intention of the applicants to restrict or in any way limit the scope of the appended claims to such detail. Additional advantages and modifications will readily appear to those skilled in the art. Therefore, the application, in its broader aspects, is not limited to the specific details, the representative apparatus, and illustrative examples shown and described. Accordingly, departures may be made from such details without departing from the spirit or scope of the applicant's general inventive concept.

Claims

What is claimed is:

1. A method for isolating purified natural rubber from non-Hevea plant matter comprising:

a. providing harvested plant matter comprising at least 90% by weight of roots sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof;

b. mixing the harvested plant matter with at least rubber- soluble organic solvent at a weight ratio of from 2:100 to 20: 100 thereby producing a quantity of dissolved rubber and a quantity of solids;

c. isolating the dissolved rubber from the solids to produce a dissolved rubber fraction that contains no more than 2% by weight solids based on the total weight of the dissolved rubber fraction;

d. removing the at least one rubber-soluble organic solvent from the dissolved rubber fraction to produce a solid rubber mass;

e. mixing the solid rubber mass with at least one rubber-insoluble organic solvent at a weight ratio of 2:100 to 20:100 thereby dissolving a quantity of impurities from the solid rubber mass; and

f. isolating the remaining solid rubber mass from the at least one rubber- insoluble organic solvent to produce a purified natural rubber

wherein said purified natural rubber contains no more than 3.5% by weight total impurities based upon the total weight of the purified natural rubber.

2. A method according to claim 1 wherein the harvested plant matter comprises at least 95%) by weight of root material sourced from Taraxacum kok-saghyz.

3. A method according to claim 1 wherein the total impurities present in the purified natural rubber comprises no more than 2% by weight volatiles, no more than 1% by weight residue and no more than 0.5%> by weight combustibles.

4. A method according to any of claims 1-3 wherein the at least one rubber-soluble organic solvent is a non-polar organic solvent and the at least one rubber-insoluble organic solvent is a polar organic solvent.

5. A method according to any of claims 1-3 wherein the dissolved rubber is isolated from the solids by use of a centrifuge.

6. A method according to any of claims 1-3 wherein the harvested plant matter and the at least one rubber-soluble organic solvent are allowed to remain in contact for 4-24 hours prior to isolating the dissolved rubber from the solids.

7. A method according to any of claims 1-3 wherein the harvested plant matter is subjected to at least one of chopping, chipping, grinding, milling and masticating prior to being mixed with the at least one rubber-soluble organic solvent.

8. A method according to any of claims 1-3 wherein the at least one rubber-insoluble organic solvent is selected from the group consisting of alcohols, having 1 to 8 carbon atoms; ethers and esters having from 2 to 8 carbon atoms; cyclic ethers having from 4 to 8 carbon atoms; ketones having from 3 to 8 carbon atoms; and combinations thereof; and

the at least one rubber-soluble organic solvent is selected from the group consisting of alkanes having from 4 to 9 carbon atoms; cycloalkanes and alkyl cycloalkanes having from 5 to 10 carbon atoms; aromatics and alkyl substituted aromatics having from 6 to 12 carbon atoms, and combinations thereof.

9. A method according to any of claims 1-3 wherein the at least one rubber-soluble organic solvent is toluene and the at least rubber-insoluble organic solvent is acetone.

10. The purified non-Hevea rubber resulting from any of claims 1-3.

11. A purified non-Hevea rubber product containing 100 phr of rubber sourced from Taraxacum kok-saghyz, Scorzonera tau-saghyz, Scorzonera uzbekistanica, and combinations thereof wherein said purified non-Hevea rubber product contains no more than 3.5% by weight total impurities based upon the total weight of the purified non-Hevea rubber product with no more than 2% by weight volatiles, no more than 1% by weight residue and no more than 0.5% by weight combustibles.

12. A purified non-Hevea rubber product according to claim 11 wherein the total amount of impurities is no more than 3% by weight.

13. A purified non-Hevea rubber product according to claim 11 wherein the total amount of impurities is no more than 2.5% by weight.

14. A purified non-Hevea rubber product according to any of claims 11-13 further comprising 0-90 phr of at least one synthetic conjugated-diene containing polymer or copolymer; and 0-90 hr of Hevea natural rubber.

15. A sulfur- vulcanizable rubber compound containing 10-100 phr of purified non-Hevea product according to any one of claims 11-13; 0-90 phr of at least one synthetic conjugated-diene containing polymer or copolymer;

0-90 phr of Hevea natural rubber; and

20-200 phr of at least one reinforcing filler selected from the group consisting of carbon black, silica, calcium carbonate, clay, talc, barite, wollastonite, mica, precipitated silicates, and diatomite.

16. A sulfur- vulcanizable rubber compound according to claim 15 exhibiting a tan δ at 60 °C, 10 Hz and 2% strain of less than 0.2 after curing with 0.5-2 phr of sulfur at 135-165 °C for 5-40 minutes.

17. A sulfur- vulcanizable rubber compound according to claim 15 exhibiting a elongation at break at room temperature of at least 450 MPa after curing with 0.5-2 phr of sulfur at 135-165 °C for 5-40 minutes.

18. A sulfur- vulcanized rubber compound obtained by curing the sulfur- vulcanizable rubber compound according to claim 15 with 0.5-6 phr sulfur and at least one accelerator.

19. A sulfur- vulcanized rubber compound according to claim 18 exhibiting a tan δ at 60 °C, 10 Hz and 2% strain of less than 0.2 after curing with 0.5-2 phr of sulfur at 135-165 °C for 5-40 minutes.

20. A sulfur- vulcanized rubber compound according to claim 18 exhibiting a elongation at break at room temperature of at least 450 MPa after curing with 0.5-2 phr of sulfur at 135-165 °C for 5-40 minutes.