WO2013107818A1 - Copolymères d'éthylène-acide(méth)acrylique destinés à des stratifiés de cellule solaires - Google Patents

Copolymères d'éthylène-acide(méth)acrylique destinés à des stratifiés de cellule solaires Download PDF

Info

Publication number
WO2013107818A1
WO2013107818A1 PCT/EP2013/050843 EP2013050843W WO2013107818A1 WO 2013107818 A1 WO2013107818 A1 WO 2013107818A1 EP 2013050843 W EP2013050843 W EP 2013050843W WO 2013107818 A1 WO2013107818 A1 WO 2013107818A1
Authority
WO
WIPO (PCT)
Prior art keywords
polymer
solar cell
copolymer
din
ethylene
Prior art date
Application number
PCT/EP2013/050843
Other languages
English (en)
Inventor
Szilard Csihony
Ivette Garcia Castro
Sven Fleischmann
Bernd DÜTTRA
Original Assignee
Basf Se
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Basf Se filed Critical Basf Se
Publication of WO2013107818A1 publication Critical patent/WO2013107818A1/fr

Abstract

La présente invention a trait à des modules de cellule solaire, à des stratifiés qui sont constitués d'éléments de cellule solaire encapsulés à l'intérieur d'une composition polymère d'un copolymère d'éthylène et d'un acide carboxylique éthyléniquement insaturé et de compositions qui comprennent des semi-conducteurs choisis dans le groupe constitué par du silicium, des éléments III-V, II-VI et I-III-VI.
PCT/EP2013/050843 2012-01-19 2013-01-17 Copolymères d'éthylène-acide(méth)acrylique destinés à des stratifiés de cellule solaires WO2013107818A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US201261588193P 2012-01-19 2012-01-19
EP12151690.0 2012-01-19
EP12151690 2012-01-19
US61/588193 2012-01-19

Publications (1)

Publication Number Publication Date
WO2013107818A1 true WO2013107818A1 (fr) 2013-07-25

Family

ID=48798694

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2013/050843 WO2013107818A1 (fr) 2012-01-19 2013-01-17 Copolymères d'éthylène-acide(méth)acrylique destinés à des stratifiés de cellule solaires

Country Status (1)

Country Link
WO (1) WO2013107818A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2016187010A (ja) * 2015-03-27 2016-10-27 三菱化学株式会社 薄膜太陽電池モジュール

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000186114A (ja) * 1998-10-16 2000-07-04 Du Pont Mitsui Polychem Co Ltd 太陽電池封止材料及び太陽電池モジュ―ル
JP2001144313A (ja) * 1999-11-11 2001-05-25 Du Pont Mitsui Polychem Co Ltd 太陽電池封止材料及び太陽電池モジュール
US20050279401A1 (en) * 2004-06-17 2005-12-22 Arhart Richard J Multilayer ionomer films for use as encapsulant layers for photovoltaic cell modules
EP1863098A1 (fr) * 2005-03-08 2007-12-05 Du Pont-Mitsui Polychemicals Co., Ltd. Materiau etancheifiant pour pile solaire
US20100126557A1 (en) * 2008-11-24 2010-05-27 E. I. Du Pont De Nemours And Company Solar cell modules comprising an encapsulant sheet of a blend of ethylene copolymers
US20110108094A1 (en) * 2008-06-26 2011-05-12 Du Pont-Mitsui Polychemicals Co., Ltd. Laminated sheet for solar cell and solar cell module using the same

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000186114A (ja) * 1998-10-16 2000-07-04 Du Pont Mitsui Polychem Co Ltd 太陽電池封止材料及び太陽電池モジュ―ル
JP2001144313A (ja) * 1999-11-11 2001-05-25 Du Pont Mitsui Polychem Co Ltd 太陽電池封止材料及び太陽電池モジュール
US20050279401A1 (en) * 2004-06-17 2005-12-22 Arhart Richard J Multilayer ionomer films for use as encapsulant layers for photovoltaic cell modules
EP1863098A1 (fr) * 2005-03-08 2007-12-05 Du Pont-Mitsui Polychemicals Co., Ltd. Materiau etancheifiant pour pile solaire
US20110108094A1 (en) * 2008-06-26 2011-05-12 Du Pont-Mitsui Polychemicals Co., Ltd. Laminated sheet for solar cell and solar cell module using the same
US20100126557A1 (en) * 2008-11-24 2010-05-27 E. I. Du Pont De Nemours And Company Solar cell modules comprising an encapsulant sheet of a blend of ethylene copolymers

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
THE DOW CHEMICAL COMPANY: "PRIMACOR Copolymers for Hot Melt Applications", November 2002 (2002-11-01), pages 1 - 4, XP002693016, Retrieved from the Internet <URL:http://www.dow.com/PublishedLiterature/dh_0031/0901b80380031e0f.pdf> [retrieved on 20130228] *

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2016187010A (ja) * 2015-03-27 2016-10-27 三菱化学株式会社 薄膜太陽電池モジュール

Similar Documents

Publication Publication Date Title
KR101903197B1 (ko) 태양 전지 봉지재 및 그것을 이용하여 제작된 태양 전지 모듈
US20100295091A1 (en) Encapsulant compositions, methods of manufacture and uses thereof
JP6090865B2 (ja) 低ヘイズ性および高耐湿性を有する封入材シートを含む太陽電池モジュール
US9368663B2 (en) Solar cell sealing film and solar cell using the sealing film
US20100269890A1 (en) Polymeric Encapsulants for Photovoltaic Modules and Methods of Manufacture
KR20080078816A (ko) 태양 전지 모듈용 충전재, 및 그것을 이용한 태양 전지모듈, 및 태양 전지 모듈용 충전재의 제조 방법
EP2613362A1 (fr) Film de revêtement de batterie solaire et module de batterie solaire fabriqué à l&#39;aide de celui-ci
KR20130069639A (ko) 광반도체 보호재 및 그 전구체 및 광반도체 보호재의 제조 방법
US20230103244A1 (en) Film and electronic device comprising same
EP2913358B1 (fr) Composition de résine pour matériaux d&#39;encapsulation pour cellules solaires
CN113801584B (zh) 一种光伏封装胶膜及光伏组件
JP2015162498A (ja) 太陽電池封止材用積層体、太陽電池封止材及び太陽電池モジュール
US8338699B2 (en) Poly(vinyl butyral) encapsulant comprising chelating agents for solar cell modules
KR20110124235A (ko) 태양 전지 모듈에 대한 힌더드 아민을 포함하는 폴리(비닐 부티랄) 밀봉제
WO2011041653A2 (fr) Matériau encapsulant pour cellules photovoltaïques
WO2013107818A1 (fr) Copolymères d&#39;éthylène-acide(méth)acrylique destinés à des stratifiés de cellule solaires
KR20110035246A (ko) 태양전지 봉지용 에틸렌 ― 비닐아세테이트 공중합체 조성물, 태양전지 봉지용 접착필름 및 태양전지 모듈
US20120190766A1 (en) EVM Granulated Materials As Embedding Material For Solar Modules, Method For Its Production, Adhesive Foil As Well As A Solar Module, Method For Its Production And Production Device
KR101603842B1 (ko) 봉지재 시트
TW201333048A (zh) 用於太陽能電池層合物之乙烯－（甲基）丙烯酸共聚物
SG178281A1 (en) Method for producing solar modules
WO2011108434A1 (fr) Feuille de matériau d&#39;étanchéité pour module de cellule solaire et module de cellule solaire
KR20140015940A (ko) 이종의 원료로 제조된 봉지재를 함께 사용한 태양전지 모듈 및 그 제조 방법
JP2014037127A (ja) 積層防湿フィルム
JP2012019135A (ja) 太陽電池モジュール用封止材シートおよび太陽電池モジュール

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13700726

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 13700726

Country of ref document: EP

Kind code of ref document: A1