WO2013073821A1 - Alloy cast iron and manufacturing method of rolling piston using the same - Google Patents
Alloy cast iron and manufacturing method of rolling piston using the same Download PDFInfo
- Publication number
- WO2013073821A1 WO2013073821A1 PCT/KR2012/009576 KR2012009576W WO2013073821A1 WO 2013073821 A1 WO2013073821 A1 WO 2013073821A1 KR 2012009576 W KR2012009576 W KR 2012009576W WO 2013073821 A1 WO2013073821 A1 WO 2013073821A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- cast iron
- alloy cast
- rolling piston
- maintaining
- hardness
- Prior art date
Abstract
Description
No. | C | Si | Mn | P | S | Cr | Cu |
1 | 3.0 | 2.25 | 0.5 | 0.1 | 0.06 | 0.7 | 0.6 |
2 | 3.1 | 2.4 | 0.6 | 0.15 | 0.06 | 0.7 | 0.7 |
3 | 3.2 | 2.3 | 0.7 | 0.2 | 0.07 | 0.8 | 0.8 |
4 | 3.3 | 2.4 | 0.8 | 0.25 | 0.07 | 0.8 | 0.9 |
5 | 3.4 | 2.2 | 0.9 | 0.25 | 0.08 | 0.9 | 0.9 |
6 | 3.5 | 2.35 | 1.0 | 0.3 | 0.08 | 1.0 | 1.0 |
No. | 1 | 2 | 3 | 4 | 5 | 6 |
Hardness after casting (HRB) | 98 | 99 | 100 | 101 | 102 | 103 |
Hardness after thermal processing (HRC) | 49 | 50 | 51 | 52 | 52 | 53 |
Tensile Strength(Mpa) | 293 | 298 | 300 | 305 | 310 | 308 |
Matrix Structure | Martensite | Martensite | Martensite | Martensite | Martensite | Martensite |
Content of Steadite (%) | 3 | 3.5 | 4 | 4.5 | 5 | 6 |
Type of Graphite (A-type) (%) | 85 | 90 | 95 | 85 | 90 | 95 |
Claims (9)
- An alloy cast iron comprising, by weight:3.0 ~ 3.5 % carbon (C);2.2 ~ 2.4% silicon (Si);0.5 ~ 1.0% manganese (Mn);0.1 ~ 0.3% phosphorus (P);0.06 ~ 0.08% sulfur (S);0.7 ~ 1.0% chrome (Cr);0.6 ~ 1.0% copper (Cu); anda residue formed of Fe and inevitable impurities,wherein 3~8vol% steadite structure is formed.
- The alloy cast iron of claim 1, wherein the alloy cast iron undergoes a thermal processing including quenching and tempering.
- The alloy cast iron of claim 2, wherein the quenching is performed by maintaining the alloy cast iron at 900±10℃ for 90 ~ 150 minutes, then by oil-cooling the alloy cast iron to 50 ~ 90℃, and then by maintaining the alloy cast iron at 50 ~ 90℃ for 5 ~ 7 hours.
- The alloy cast iron of claim 3, wherein the tempering is performed by maintaining the alloy cast iron at 250±10℃ for 150 ~ 210 minutes, and then by cooling the alloy cast iron to room temperature in air.
- The alloy cast iron of claim 4, wherein the tempered alloy cast iron has a Rockwell hardness of 45~55.
- A method of manufacturing a rolling piston for a rotary compressor, the method comprising:a melting step of preparing a molten metal comprising, by weight, 3.0 ~ 3.5% carbon (C), 2.2 ~ 2.4% silicon (Si), 0.5 ~ 1.0% manganese (Mn), 0.1 ~ 0.3% phosphorus (P), 0.06 ~ 0.08% sulfur (S), 0.7 ~ 1.0% chrome (Cr), 0.6 ~ 1.0% copper (Cu), and a residue formed of Fe and inevitable impurities;a casting step of pouring the molten metal in a mold and cooling thereby preparing a semi-product in which 3~8vol% steadite structure is formed;a grinding step of grinding the cooled semi-product to a prescribed shape; anda thermal-processing step of thermally-processing the ground semi-product for a Rockwell hardness of 45~55.
- The method of claim 6, wherein the thermal-processing step includes quenching and tempering.
- The method of claim 7, wherein the quenching is performed by maintaining the alloy cast iron at 900±10℃ for 90 ~ 150 minutes, then by oil-cooling the alloy cast iron to 50 ~ 90℃, and then by maintaining the alloy cast iron at 50 ~ 90℃ for 5 ~ 7 hours.
- The method of claim 7, wherein the tempering is performed by maintaining the alloy cast iron at 250±10℃ for 150 ~ 210 minutes, and then by cooling the alloy cast iron to room temperature in air.