WO2013025330A2 - Optically clear conductive adhesive and articles therefrom - Google Patents
Optically clear conductive adhesive and articles therefrom Download PDFInfo
- Publication number
- WO2013025330A2 WO2013025330A2 PCT/US2012/048769 US2012048769W WO2013025330A2 WO 2013025330 A2 WO2013025330 A2 WO 2013025330A2 US 2012048769 W US2012048769 W US 2012048769W WO 2013025330 A2 WO2013025330 A2 WO 2013025330A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- electrically conductive
- optically clear
- clear adhesive
- layer
- adhesive
- Prior art date
Abstract
Description
Claims