WO2012115218A1 - Procédé de fabrication de dianthra[2,3-b:2',3'-f]thiéno[3,2-b]thiophène et son utilisation - Google Patents

Procédé de fabrication de dianthra[2,3-b:2',3'-f]thiéno[3,2-b]thiophène et son utilisation Download PDF

Info

Publication number
WO2012115218A1
WO2012115218A1 PCT/JP2012/054528 JP2012054528W WO2012115218A1 WO 2012115218 A1 WO2012115218 A1 WO 2012115218A1 JP 2012054528 W JP2012054528 W JP 2012054528W WO 2012115218 A1 WO2012115218 A1 WO 2012115218A1
Authority
WO
WIPO (PCT)
Prior art keywords
organic
layer
thieno
thiophene
compound
Prior art date
Application number
PCT/JP2012/054528
Other languages
English (en)
Japanese (ja)
Inventor
和男 瀧宮
一樹 新見
博一 桑原
雄一 貞光
英成 狩野
Original Assignee
国立大学法人広島大学
日本化薬株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 国立大学法人広島大学, 日本化薬株式会社 filed Critical 国立大学法人広島大学
Priority to JP2012539130A priority Critical patent/JPWO2012115218A1/ja
Publication of WO2012115218A1 publication Critical patent/WO2012115218A1/fr

Abstract

Selon l'invention, on obtient un dianthra[2,3-b:2',3'-f]thiéno[3,2-b]thiophène en soumettant un dérivé spécifique d'anthracène à une sulfométhylation, en faisant réagir le dérivé d'anthracène avec un composé spécifique de l'étain, puis en soumettant l'anthracène et le composé de l'étain ayant réagi à une cyclisation.
PCT/JP2012/054528 2011-02-25 2012-02-24 Procédé de fabrication de dianthra[2,3-b:2',3'-f]thiéno[3,2-b]thiophène et son utilisation WO2012115218A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2012539130A JPWO2012115218A1 (ja) 2011-02-25 2012-02-24 ジアントラ［２，３−ｂ：２’，３’−ｆ］チエノ［３，２−ｂ］チオフェンの製造方法並びにその用途

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2011039404 2011-02-25
JP2011-039404 2011-02-25

Publications (1)

Publication Number Publication Date
WO2012115218A1 true WO2012115218A1 (fr) 2012-08-30

Family

ID=46720992

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2012/054528 WO2012115218A1 (fr) 2011-02-25 2012-02-24 Procédé de fabrication de dianthra[2,3-b:2',3'-f]thiéno[3,2-b]thiophène et son utilisation

Country Status (3)

Country Link
JP (1) JPWO2012115218A1 (fr)
TW (1) TW201247676A (fr)
WO (1) WO2012115218A1 (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018043763A1 (fr) * 2016-09-02 2018-03-08 Kyushu University, National University Corporation Laser à rétroaction distribuée à couche mince organique à onde continue et diode laser à semi-conducteur organique à commande électrique
KR20180026320A (ko) * 2016-09-02 2018-03-12 고쿠리쓰다이가쿠호진 규슈다이가쿠 연속파 유기 박막 분산형 피드백 레이저 및 전기적으로 구동되는 유기 반도체 레이저 다이오드
WO2020039708A1 (fr) 2018-08-23 2020-02-27 国立大学法人九州大学 Élément électroluminescent organique
US11183815B2 (en) 2017-02-07 2021-11-23 Koala Tech Inc. Current-injection organic semiconductor laser diode, meihod for producing same and program
WO2023189381A1 (fr) * 2022-03-30 2023-10-05 ソニーグループ株式会社 Élément électroluminescent et dispositif électronique
JP7512917B2 (ja) 2021-01-29 2024-07-09 コニカミノルタ株式会社 有機エレクトロルミネッセンス素子及びその製造方法、並びにそれを具備した照明装置、表示装置及び印刷造形物

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE112013005942T5 (de) * 2012-12-12 2015-09-24 Daicel Corporation Lösungsmittel oder Lösungsmittelzusammensetzung zur Herstellung organischer Transistoren

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2009009790A1 (fr) * 2007-07-12 2009-01-15 President And Fellows Of Harvard College Dérivés thiéno-thiophène stables à l'air présentant une mobilité de trous élevée
JP2011003852A (ja) * 2009-06-22 2011-01-06 Asahi Kasei Corp 硫黄原子を含有する縮合多環芳香族化合物のシート状結晶が基板上に積層された有機半導体薄膜、及びその製法

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2009009790A1 (fr) * 2007-07-12 2009-01-15 President And Fellows Of Harvard College Dérivés thiéno-thiophène stables à l'air présentant une mobilité de trous élevée
JP2011003852A (ja) * 2009-06-22 2011-01-06 Asahi Kasei Corp 硫黄原子を含有する縮合多環芳香族化合物のシート状結晶が基板上に積層された有機半導体薄膜、及びその製法

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
RICHARD A.H. ET AL.: "Palladium(0) catalyzed coupling of trans-1,2-Bis(tri-n-butylstannyl) ethylene with aromatic halides: A convenient synthesis of substituted trans-§-bromostyrenes.", TETRAHEDRON LETTERS, vol. 29, no. 23, 1988, pages 2783 - 2786 *

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11909177B2 (en) 2016-09-02 2024-02-20 Kyushu University, National University Corporation Continuous-wave organic thin-film distributed feedback laser and electrically driven organic semiconductor laser diode
KR20180026320A (ko) * 2016-09-02 2018-03-12 고쿠리쓰다이가쿠호진 규슈다이가쿠 연속파 유기 박막 분산형 피드백 레이저 및 전기적으로 구동되는 유기 반도체 레이저 다이오드
JP2019526937A (ja) * 2016-09-02 2019-09-19 国立大学法人九州大学 連続波有機薄膜分布帰還型レーザ及び電気駆動有機半導体レーザダイオード
KR102402133B1 (ko) * 2016-09-02 2022-05-26 고쿠리쓰다이가쿠호진 규슈다이가쿠 연속파 유기 박막 분산형 피드백 레이저 및 전기적으로 구동되는 유기 반도체 레이저 다이오드
US11539190B2 (en) 2016-09-02 2022-12-27 Kyushu University, National University Corporation Continuous-wave organic thin-film distributed feedback laser and electrically driven organic semiconductor laser diode
WO2018043763A1 (fr) * 2016-09-02 2018-03-08 Kyushu University, National University Corporation Laser à rétroaction distribuée à couche mince organique à onde continue et diode laser à semi-conducteur organique à commande électrique
US12015248B2 (en) 2016-09-02 2024-06-18 Kyushu University, National University Corporation Continuous-wave organic thin-film distributed feedback laser and electrically driven organic semiconductor laser diode
US11183815B2 (en) 2017-02-07 2021-11-23 Koala Tech Inc. Current-injection organic semiconductor laser diode, meihod for producing same and program
US11626710B2 (en) 2017-02-07 2023-04-11 Kyushu University, National University Corporation Current-injection organic semiconductor laser diode, method for producing same and program
US11955776B2 (en) 2017-02-07 2024-04-09 Kyushu University, National University Corporation Current-injection organic semiconductor laser diode, method for producing same and program
WO2020039708A1 (fr) 2018-08-23 2020-02-27 国立大学法人九州大学 Élément électroluminescent organique
JP7512917B2 (ja) 2021-01-29 2024-07-09 コニカミノルタ株式会社 有機エレクトロルミネッセンス素子及びその製造方法、並びにそれを具備した照明装置、表示装置及び印刷造形物
WO2023189381A1 (fr) * 2022-03-30 2023-10-05 ソニーグループ株式会社 Élément électroluminescent et dispositif électronique

Also Published As

Publication number Publication date
JPWO2012115218A1 (ja) 2014-07-07
TW201247676A (en) 2012-12-01

Similar Documents

Publication Publication Date Title
JP5622585B2 (ja) 新規な複素環式化合物及びその利用
JP6208133B2 (ja) 複素環化合物及びその利用
WO2012115218A1 (fr) Procédé de fabrication de dianthra[2,3-b:2',3'-f]thiéno[3,2-b]thiophène et son utilisation
WO2014061745A1 (fr) Nouveau composé aromatique polycyclique condensé et son utilisation
JP6558777B2 (ja) 有機化合物及びその用途
JP2016166284A (ja) 新規な有機化合物およびその利用
JP6436590B2 (ja) 新規な有機多環芳香族化合物、およびその利用
JP6425646B2 (ja) 新規縮合多環芳香族化合物及びその用途
WO2013031468A1 (fr) Composé hétérocyclique et son utilisation
JP6478278B2 (ja) 有機多環芳香族化合物、およびその利用
JP6572473B2 (ja) 有機化合物及びその用途
JP5600267B2 (ja) 新規な化合物及びその利用
WO2012165612A1 (fr) Matériau semi-conducteur organique et dispositif électronique organique
JP6497560B2 (ja) 新規縮合多環芳香族化合物及びその用途
JP6592863B2 (ja) 有機化合物及びその用途
JP6478279B2 (ja) 有機多環芳香族化合物、およびその利用
JP6478277B2 (ja) 有機多環芳香族化合物、およびその利用

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 2012539130

Country of ref document: JP

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 12749714

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 12749714

Country of ref document: EP

Kind code of ref document: A1