WO2012089807A1 - Iron based powders for powder injection molding - Google Patents
Iron based powders for powder injection molding Download PDFInfo
- Publication number
- WO2012089807A1 WO2012089807A1 PCT/EP2011/074230 EP2011074230W WO2012089807A1 WO 2012089807 A1 WO2012089807 A1 WO 2012089807A1 EP 2011074230 W EP2011074230 W EP 2011074230W WO 2012089807 A1 WO2012089807 A1 WO 2012089807A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- iron
- powder composition
- based powder
- powder
- content
- Prior art date
Abstract
Description
Claims