WO2012087671A1 - Compositions de revêtement - Google Patents

Compositions de revêtement Download PDF

Info

Publication number
WO2012087671A1
WO2012087671A1 PCT/US2011/064642 US2011064642W WO2012087671A1 WO 2012087671 A1 WO2012087671 A1 WO 2012087671A1 US 2011064642 W US2011064642 W US 2011064642W WO 2012087671 A1 WO2012087671 A1 WO 2012087671A1
Authority
WO
WIPO (PCT)
Prior art keywords
composition
present
coating
polymeric binder
test
Prior art date
Application number
PCT/US2011/064642
Other languages
English (en)
Inventor
Samir H. SONI
Original Assignee
3M Innovative Properties Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 3M Innovative Properties Company filed Critical 3M Innovative Properties Company
Publication of WO2012087671A1 publication Critical patent/WO2012087671A1/fr

Abstract

L'invention concerne une composition de revêtement, plus particulièrement une composition de revêtement de soubassement, celle-ci comportant un liant polymère, une charge et un pigment anti-corrosion. Le liant polymère est fait d'une résine alkyde modifiée par de la colophane, d'une résine maléique et d'une matière siccative. Les liants de la présente invention permettent une formulation de compositions de revêtement qui est supérieure aux compositions formulées à partir de liants classiques. La présente invention concerne également un procédé de préparation de ladite composition de revêtement.
PCT/US2011/064642 2010-12-20 2011-12-13 Compositions de revêtement WO2012087671A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
IN3889/CHE/2010 2010-12-20
IN3889CH2010 2010-12-20

Publications (1)

Publication Number Publication Date
WO2012087671A1 true WO2012087671A1 (fr) 2012-06-28

Family

ID=46314356

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2011/064642 WO2012087671A1 (fr) 2010-12-20 2011-12-13 Compositions de revêtement

Country Status (1)

Country Link
WO (1) WO2012087671A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2023281320A1 (fr) * 2021-07-08 2023-01-12 Kansai Nerolac Paints Limited Composition de revêtement et son procédé de préparation

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2181054A (en) * 1936-08-21 1939-11-21 Modified alkyd resin
US2272057A (en) * 1937-11-02 1942-02-03 Resinous Prod & Chemical Co Resin emulsion
US2978424A (en) * 1958-12-23 1961-04-04 Glidden Co Metal primers and coating compositions modified with lower alkyl esters of unsaturated aliphatic acids
US5093463A (en) * 1991-01-14 1992-03-03 Westvaco Corporation Maleinized rosin containing solvent-borne alkyd resin compositions
EP0379746B1 (fr) * 1988-11-30 1994-09-28 Nippon Paint Co., Ltd. Composition de revêtement contenant des trichites d'oxyde de zinc de type tétrapode
WO2004033567A1 (fr) * 2002-10-10 2004-04-22 Mansoor Khorasani Revetements a isolation thermique
US20090318612A1 (en) * 2006-07-04 2009-12-24 Ppg B.V. Paint composition
WO2010112605A1 (fr) * 2009-04-03 2010-10-07 Akzo Nobel Coatings International B.V. Composition de revêtement anticorrosion

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2181054A (en) * 1936-08-21 1939-11-21 Modified alkyd resin
US2272057A (en) * 1937-11-02 1942-02-03 Resinous Prod & Chemical Co Resin emulsion
US2978424A (en) * 1958-12-23 1961-04-04 Glidden Co Metal primers and coating compositions modified with lower alkyl esters of unsaturated aliphatic acids
EP0379746B1 (fr) * 1988-11-30 1994-09-28 Nippon Paint Co., Ltd. Composition de revêtement contenant des trichites d'oxyde de zinc de type tétrapode
US5093463A (en) * 1991-01-14 1992-03-03 Westvaco Corporation Maleinized rosin containing solvent-borne alkyd resin compositions
WO2004033567A1 (fr) * 2002-10-10 2004-04-22 Mansoor Khorasani Revetements a isolation thermique
US20090318612A1 (en) * 2006-07-04 2009-12-24 Ppg B.V. Paint composition
WO2010112605A1 (fr) * 2009-04-03 2010-10-07 Akzo Nobel Coatings International B.V. Composition de revêtement anticorrosion

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
PIGMENTAN CC: "Technical Data Sheet", November 2010 (2010-11-01), Retrieved from the Internet <URL:http://www.pigmentan.com/Pigmentan/Templates/showpage.asp?DBID=1&LNGID=1&TMID=108&FID=684&1ID=1132> [retrieved on 20120201] *
PIGMENTAN EM: "Starting Formulation SB0807-13", March 2010 (2010-03-01), Retrieved from the Internet <URL:http://www.pigmentan.com/Pigmentan/Templates/showpage.asp?DBID=1&LNGID=1&TMID=108&FID=684&1ID=926> [retrieved on 20120201] *

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2023281320A1 (fr) * 2021-07-08 2023-01-12 Kansai Nerolac Paints Limited Composition de revêtement et son procédé de préparation

Similar Documents

Publication Publication Date Title
AU2012328817B2 (en) Corrosion, chip and fuel resistant coating composition
CN103703067B (zh) 包含氢氧化镁的涂料组合物及相关的经涂覆的基材
CN106232737B (zh) 耐腐蚀性涂料组合物
WO2009084849A2 (fr) Compositions de revêtement sans chrome pour le traitement de surface de tôles d&#39;acier, comprenant des nanotubes de carbone, procédés de traitement de surface de tôles d&#39;acier et tôles d&#39;acier traitées en surface au moyen dudit procédé
CN1625588A (zh) 不含铬酸盐的免底涂层防腐涂料组合物及其制备方法
JP5995846B2 (ja) リン含有ポリエステルを使用した、金属表面の腐食防止コーティング方法
WO2012087671A1 (fr) Compositions de revêtement
JP7506990B2 (ja) 一液型水性塗料組成物
KR101611062B1 (ko) 고내식성 방식도료 조성물에 의한 판스프링의 도장방법
RU2378305C1 (ru) Антикоррозионный состав для покрытий
US8911542B2 (en) Anti-corrosive compositions
KR20170046923A (ko) Cr-free 에폭시 워시 프라이머 고접착력 방식도료 조성물 및 그 제조방법
JPS60197773A (ja) 金属表面処理組成物及びこのものを用いた金属の表面処理方法
JP2009191245A (ja) 水性コーティング材
RU2436820C1 (ru) Антикоррозионная грунтовка
CN105950017B (zh) 特种集装箱底部防锈沥青漆
EP2214841A1 (fr) Agent pour le traitement de films de peinture de couche de finition pour conférer une résistance aux taches et procédé de traitement de films de peinture de couche de finition pour conférer une résistance aux taches
Vikhareva et al. Modern strategies for the creation of polymer coatings. Part II1
JP2017101146A (ja) Ｓｎイオンを利用した１液型高耐食性塗料組成物
JPS621476A (ja) 塗装法
JP4268382B2 (ja) 防食性に優れた鉄鋼製品
RU2378304C1 (ru) Покрывной состав для защиты металла от коррозии
JPH01316474A (ja) 防錆剤組成物
Ahmed Modified zinc oxide‐phosphate core‐shell pigments in solvent‐based paints
Serban et al. Anticorrosive film-forming nonpolluting products achieved in Romania

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 11852142

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 11852142

Country of ref document: EP

Kind code of ref document: A1