WO2012016185A2 - Niobium oxide compositions and methods for using same - Google Patents
Niobium oxide compositions and methods for using same Download PDFInfo
- Publication number
- WO2012016185A2 WO2012016185A2 PCT/US2011/045964 US2011045964W WO2012016185A2 WO 2012016185 A2 WO2012016185 A2 WO 2012016185A2 US 2011045964 W US2011045964 W US 2011045964W WO 2012016185 A2 WO2012016185 A2 WO 2012016185A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- anode
- tno
- niobium oxide
- charge
- active material
- Prior art date
Abstract
Description
Claims