WO2011069942A1 - Matières à mouler constituées de copolyamide partiellement aromatique à base d'octaméthylène diamine - Google Patents

Matières à mouler constituées de copolyamide partiellement aromatique à base d'octaméthylène diamine Download PDF

Info

Publication number
WO2011069942A1
WO2011069942A1 PCT/EP2010/068930 EP2010068930W WO2011069942A1 WO 2011069942 A1 WO2011069942 A1 WO 2011069942A1 EP 2010068930 W EP2010068930 W EP 2010068930W WO 2011069942 A1 WO2011069942 A1 WO 2011069942A1
Authority
WO
WIPO (PCT)
Prior art keywords
acid
copolyamide
molding compositions
units
compositions according
Prior art date
Application number
PCT/EP2010/068930
Other languages
German (de)
English (en)
Inventor
Christian Schmidt
Philippe Desbois
Original Assignee
Basf Se
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Basf Se filed Critical Basf Se
Publication of WO2011069942A1 publication Critical patent/WO2011069942A1/fr

Abstract

L'invention concerne des matières à mouler constituées de copolyamide partiellement aromatique, contenant A) 35 à 100 % en poids d'un copolyamide partiellement aromatique, partiellement cristallin, constitué de a1) 60 à 95 % en moles de motifs qui sont dérivés de la 1,8-octaméthylène diamine et de l'acide téréphtalique, a2) 5 à 40 % en moles de motifs qui sont dérivés d'autres monomères constitutifs du polyamide, différents de a1) la combinaison d'octaméthylène diamine et d'acide subérique étant exclue dans les motifs a2), B) 0 à 65 % en poids d'autres additifs, la somme des pourcentages en poids de A) et de B) étant égale à 100 %.
PCT/EP2010/068930 2009-12-08 2010-12-06 Matières à mouler constituées de copolyamide partiellement aromatique à base d'octaméthylène diamine WO2011069942A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP09178361.3 2009-12-08
EP09178361 2009-12-08

Publications (1)

Publication Number Publication Date
WO2011069942A1 true WO2011069942A1 (fr) 2011-06-16

Family

ID=43466440

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2010/068930 WO2011069942A1 (fr) 2009-12-08 2010-12-06 Matières à mouler constituées de copolyamide partiellement aromatique à base d'octaméthylène diamine

Country Status (1)

Country Link
WO (1) WO2011069942A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8957180B2 (en) 2011-08-23 2015-02-17 Basf Se Process for producing moldings
WO2015197124A1 (fr) * 2014-06-26 2015-12-30 Dsm Ip Assets B.V. Procédé de préparation d'un polyamide semi-aromatique semi-cristallin
US9315626B2 (en) 2009-12-08 2016-04-19 Basf Se Process for preparing polyamides
TWI651369B (zh) * 2014-06-26 2019-02-21 Ｄｓｍ智慧財產有限公司 用於製備半晶質半芳香聚醯胺之方法

Citations (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3843611A (en) 1972-05-22 1974-10-22 Phillips Petroleum Co Copolyamide from terephthalic acid,dodecanedioic acid and dodecane diamine
US3948862A (en) 1974-05-06 1976-04-06 E. I. Du Pont De Nemours And Company Continuous process for preparing aliphatic polycarbonamides
DE2702661A1 (de) 1976-02-05 1977-08-11 Ciba Geigy Ag Stabilisatorsysteme aus triarylphosphiten und phenolen
US4148846A (en) 1970-09-10 1979-04-10 Rohm And Haas Company Acrylic modifiers for polycarbonamides
EP0050265A1 (fr) 1980-10-16 1982-04-28 Bayer Ag Compositions de polyesters thermoplastiques
EP0129195A2 (fr) 1983-06-15 1984-12-27 BASF Aktiengesellschaft Procédé pour la production continue de polyamides
US4607073A (en) * 1984-01-27 1986-08-19 Mitsui Petrochemical Industries, Ltd. Molding polyamide composition
EP0208187A2 (fr) 1985-07-06 1987-01-14 Bayer Ag Polymères greffés et leurs mélanges avec des polyamides
EP0235690A2 (fr) 1986-03-04 1987-09-09 Bayer Ag Polymères greffés sur des polymères caoutchouteux à structure séquencée
EP0299444A2 (fr) 1987-07-17 1989-01-18 BASF Aktiengesellschaft Copolyamides partiellement aromatiques avec un taux de triamine abaissé
DE3725576A1 (de) 1987-08-01 1989-02-09 Bayer Ag Formmassen aus aromatischem polyester und gepfropftem silikonkautschuk
EP0319290A2 (fr) 1987-12-04 1989-06-07 Polyplastics Co. Ltd. Composition de résines
DE3800603A1 (de) 1988-01-12 1989-07-20 Bayer Ag Formmassen aus aromatischen polyestern, vinyl-copolymerisaten und gepfropftem siliconkautschuk
JPH0453870A (ja) * 1990-06-20 1992-02-21 Toray Ind Inc 自動車用アンダーフード部品
JPH07126381A (ja) * 1993-11-02 1995-05-16 Toray Ind Inc ポリアミドの製造方法
EP0922065A2 (fr) 1996-08-30 1999-06-16 Basf Aktiengesellschaft Procede pour la preparation de polyamides a partir d'aminonitriles
EP1198491A1 (fr) 1999-07-30 2002-04-24 Basf Aktiengesellschaft Procede de production de polyamides a partir de dinitriles et de diamines
DE10313681A1 (de) 2003-03-26 2004-10-07 Basf Ag Verfahren zur Herstellung von Polyamiden
CN1537881A (zh) * 2003-04-18 2004-10-20 上海杰事杰新材料股份有限公司 高韧性半芳香族尼龙及其制备方法
WO2007023108A1 (fr) 2005-08-26 2007-03-01 Basf Aktiengesellschaft Procede pour preparer des polyamides
EP1994075A2 (fr) 2006-03-08 2008-11-26 Basf Se Copolyamides partiellement aromatiques à haute cristallinité

Patent Citations (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4148846A (en) 1970-09-10 1979-04-10 Rohm And Haas Company Acrylic modifiers for polycarbonamides
US3843611A (en) 1972-05-22 1974-10-22 Phillips Petroleum Co Copolyamide from terephthalic acid,dodecanedioic acid and dodecane diamine
US3948862A (en) 1974-05-06 1976-04-06 E. I. Du Pont De Nemours And Company Continuous process for preparing aliphatic polycarbonamides
DE2702661A1 (de) 1976-02-05 1977-08-11 Ciba Geigy Ag Stabilisatorsysteme aus triarylphosphiten und phenolen
US4360617A (en) 1976-02-05 1982-11-23 Ciba-Geigy Corporation Stabilizer systems of triarylphosphites and phenols
EP0050265A1 (fr) 1980-10-16 1982-04-28 Bayer Ag Compositions de polyesters thermoplastiques
EP0129195A2 (fr) 1983-06-15 1984-12-27 BASF Aktiengesellschaft Procédé pour la production continue de polyamides
US4607073A (en) * 1984-01-27 1986-08-19 Mitsui Petrochemical Industries, Ltd. Molding polyamide composition
EP0208187A2 (fr) 1985-07-06 1987-01-14 Bayer Ag Polymères greffés et leurs mélanges avec des polyamides
EP0235690A2 (fr) 1986-03-04 1987-09-09 Bayer Ag Polymères greffés sur des polymères caoutchouteux à structure séquencée
EP0299444A2 (fr) 1987-07-17 1989-01-18 BASF Aktiengesellschaft Copolyamides partiellement aromatiques avec un taux de triamine abaissé
DE3725576A1 (de) 1987-08-01 1989-02-09 Bayer Ag Formmassen aus aromatischem polyester und gepfropftem silikonkautschuk
EP0319290A2 (fr) 1987-12-04 1989-06-07 Polyplastics Co. Ltd. Composition de résines
DE3800603A1 (de) 1988-01-12 1989-07-20 Bayer Ag Formmassen aus aromatischen polyestern, vinyl-copolymerisaten und gepfropftem siliconkautschuk
JPH0453870A (ja) * 1990-06-20 1992-02-21 Toray Ind Inc 自動車用アンダーフード部品
JPH07126381A (ja) * 1993-11-02 1995-05-16 Toray Ind Inc ポリアミドの製造方法
EP0922065A2 (fr) 1996-08-30 1999-06-16 Basf Aktiengesellschaft Procede pour la preparation de polyamides a partir d'aminonitriles
EP1198491A1 (fr) 1999-07-30 2002-04-24 Basf Aktiengesellschaft Procede de production de polyamides a partir de dinitriles et de diamines
DE10313681A1 (de) 2003-03-26 2004-10-07 Basf Ag Verfahren zur Herstellung von Polyamiden
CN1537881A (zh) * 2003-04-18 2004-10-20 上海杰事杰新材料股份有限公司 高韧性半芳香族尼龙及其制备方法
WO2007023108A1 (fr) 2005-08-26 2007-03-01 Basf Aktiengesellschaft Procede pour preparer des polyamides
EP1994075A2 (fr) 2006-03-08 2008-11-26 Basf Se Copolyamides partiellement aromatiques à haute cristallinité

Non-Patent Citations (6)

* Cited by examiner, † Cited by third party
Title
AJROLDI, G.; STEA, A.; MATTIUSSI, F., J. APPL. POLY. SEI., vol. 17, 1973, pages 3187 - 3197
C.B. BUCKNALL: "Toughened Plastics", 1977, APPLIED SCIENCE PUBLISHERS
DATABASE EPODOC [online] EUROPEAN PATENT OFFICE, THE HAGUE, NL; 2004, SHANGHAI JIESHIJIE NEW MATERIAL CO LTD [CN], XP002630803, Database accession no. CN-03116483-A *
GAYMANS ET AL., J. POLYM. SEI. A, CHEM., vol. 27, 1989, pages 423 - 430
H. LUDEWIG, FASERFORSCHUNG UND TEXTILCHEMIE, vol. 7, 27 June 1955 (1955-06-27)
HOUBEN-WEYL: "Methoden der organischen Chemie", 1961, GEORG-THIEME-VERLAG, pages: 392 - 406

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9315626B2 (en) 2009-12-08 2016-04-19 Basf Se Process for preparing polyamides
US8957180B2 (en) 2011-08-23 2015-02-17 Basf Se Process for producing moldings
WO2015197124A1 (fr) * 2014-06-26 2015-12-30 Dsm Ip Assets B.V. Procédé de préparation d'un polyamide semi-aromatique semi-cristallin
TWI651369B (zh) * 2014-06-26 2019-02-21 Ｄｓｍ智慧財產有限公司 用於製備半晶質半芳香聚醯胺之方法
US10577500B2 (en) 2014-06-26 2020-03-03 Dsm Ip Assets B.V. Process for the preparation of a semi-crystalline semi-aromatic polyamide

Similar Documents

Publication Publication Date Title
EP2510056B1 (fr) Copolyamide semi-aromatique, semi-cristallin
EP1851265B1 (fr) Polyamides resistants au vieillissement thermique
EP2001951B1 (fr) Polyamides thermoconducteurs
EP2379644B1 (fr) Polyamides résistants au vieillissement thermique
EP2356174B1 (fr) Polyamide stabilisé
EP2652032B1 (fr) Polyamides résistants au fil incandescent
EP2493968A1 (fr) Polyamides résistant au vieillissement thermique
WO2009156342A1 (fr) Polyamide thermoconducteur avec terre de diatomées
WO2011069942A1 (fr) Matières à mouler constituées de copolyamide partiellement aromatique à base d'octaméthylène diamine
WO2006010543A1 (fr) Polyamides thermostabilises
WO2013189676A1 (fr) Polyamides ignifugés comprenant des homopolymères polyacrylonitrile
WO2013139827A1 (fr) Polyamides ignifuges de couleur claire
EP2665777B1 (fr) Polyamides stables à l'hydrolyse
EP3322753A1 (fr) Compositions de polyamide présentant des propriétés optiques améliorées
EP2817363B1 (fr) Mélanges cuo/zno servant de stabilisants pour des polyamides ignifugés
EP3283562B1 (fr) Polyamide présentant des caractéristiques optiques améliorées
EP2756033B1 (fr) Mélanges d'argent et d'oxyde de zinc en tant que stabilisant pour des polyamides ignifugés contenant du phosphore rouge
WO2012146624A1 (fr) Matières à mouler ignifugées
DE102015215118A1 (de) Polyamide mit 2,6-BAMP-Derivaten
EP2415827A1 (fr) Polyamides ignifuges dotés de silicate en couche
WO2012062594A1 (fr) Polyamides résistant au vieillissement thermique
DE102008058246A1 (de) Hochmolekulare Polyamide
WO2013083508A1 (fr) Polyamides ignifugés comprenant des polyesters à cristaux liquides

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 10793193

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 10793193

Country of ref document: EP

Kind code of ref document: A1