WO2011062775A2 - Matériaux de réacteur de pyrolyse poreux et procédés - Google Patents

Matériaux de réacteur de pyrolyse poreux et procédés Download PDF

Info

Publication number
WO2011062775A2
WO2011062775A2 PCT/US2010/055423 US2010055423W WO2011062775A2 WO 2011062775 A2 WO2011062775 A2 WO 2011062775A2 US 2010055423 W US2010055423 W US 2010055423W WO 2011062775 A2 WO2011062775 A2 WO 2011062775A2
Authority
WO
WIPO (PCT)
Prior art keywords
refractory material
reactor
porosity
grain
less
Prior art date
Application number
PCT/US2010/055423
Other languages
English (en)
Other versions
WO2011062775A3 (fr
Inventor
Changmin Chun
Frank Hershkowitz
Paul F. Keusenkothen
Shiun Ling
Gary David Mohr
Original Assignee
Exxonmobil Chemical Patents Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US12/623,046 external-priority patent/US8932534B2/en
Application filed by Exxonmobil Chemical Patents Inc. filed Critical Exxonmobil Chemical Patents Inc.
Priority to JP2012539936A priority Critical patent/JP2013511592A/ja
Priority to EP10774410A priority patent/EP2501783A2/fr
Priority to CN2010800599198A priority patent/CN103025849A/zh
Priority to CA2781026A priority patent/CA2781026A1/fr
Publication of WO2011062775A2 publication Critical patent/WO2011062775A2/fr
Publication of WO2011062775A3 publication Critical patent/WO2011062775A3/fr

Abstract

Dans un aspect, la présente invention concerne un appareil de réacteur pour la pyrolyse d'une matière première d'hydrocarbures, ledit appareil comprenant : un composant de réacteur comprenant un matériau réfractaire sous forme d'oxyde, le matériau réfractaire ayant un point de fusion de pas moins de 2060 °C, et qui reste sous forme d'oxyde lorsqu'il est exposé à un gaz ayant une pression partielle de carbone de 10-22 bar et une pression partielle d'oxygène de 10-10 bar, à une température de 1200 °C; où ledit matériau réfractaire a pas moins de 4 % de porosité formée, mesurée à 20 °C, sur la base du volume en vrac dudit matériau réfractaire. Dans un autre mode de réalisation, le matériau réfractaire a une porosité totale dans la plage de 4 à 60 % en volume.
PCT/US2010/055423 2009-11-20 2010-11-04 Matériaux de réacteur de pyrolyse poreux et procédés WO2011062775A2 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
JP2012539936A JP2013511592A (ja) 2009-11-20 2010-11-04 多孔性の熱分解反応器材料および方法
EP10774410A EP2501783A2 (fr) 2009-11-20 2010-11-04 Matériaux de réacteur de pyrolyse poreux et procédés
CN2010800599198A CN103025849A (zh) 2009-11-20 2010-11-04 多孔热解反应器材料和方法
CA2781026A CA2781026A1 (fr) 2009-11-20 2010-11-04 Materiaux de reacteur de pyrolyse poreux et procedes

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US12/623,046 2009-11-20
US12/623,046 US8932534B2 (en) 2009-11-20 2009-11-20 Porous pyrolysis reactor materials and methods
EP10150598.0 2010-01-13
EP10150598 2010-01-13

Publications (2)

Publication Number Publication Date
WO2011062775A2 true WO2011062775A2 (fr) 2011-05-26
WO2011062775A3 WO2011062775A3 (fr) 2012-05-03

Family

ID=44060270

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2010/055423 WO2011062775A2 (fr) 2009-11-20 2010-11-04 Matériaux de réacteur de pyrolyse poreux et procédés

Country Status (3)

Country Link
EP (1) EP2501783A2 (fr)
JP (1) JP2013511592A (fr)
WO (1) WO2011062775A2 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2013141950A1 (fr) * 2012-03-20 2013-09-26 Exxonmobil Chemical Patents Inc. Composant isolant thermique pour réacteur à pyrolyse
WO2015055950A1 (fr) * 2013-10-17 2015-04-23 Saint-Gobain Centre De Recherches Et D'etudes Europeen Mélange particulaire pour l'obtention d'un produit en zircone yttriee
CN117169002A (zh) * 2023-11-03 2023-12-05 山东一路交通科技有限公司 一种汽车零部件抗弯折强度检测装置

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11976208B2 (en) 2018-08-08 2024-05-07 Mitsubishi Gas Chemical Company, Inc. Hard-coat composition, laminate film, and curable film

Family Cites Families (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
NL6709949A (fr) * 1966-07-22 1968-01-23
US4402746A (en) * 1982-03-31 1983-09-06 Exxon Research And Engineering Co. Alumina-yttria mixed oxides in dispersion strengthened high temperature alloys
JP2844100B2 (ja) * 1989-12-26 1999-01-06 東海カーボン株式会社 ジルコニア耐火物とその製造方法
SE469754B (sv) * 1990-05-14 1993-09-06 Kanthal Ab Ugn foer krackning av kolvaeten
JP2976209B2 (ja) * 1990-08-23 1999-11-10 東海カーボン株式会社 カーボンブラック製造炉
TW548334B (en) * 1997-08-20 2003-08-21 Jgc Corp Heating furnace and method of manufacturing the same
US6830676B2 (en) * 2001-06-11 2004-12-14 Chrysalis Technologies Incorporated Coking and carburization resistant iron aluminides for hydrocarbon cracking
US7482502B2 (en) * 2003-01-24 2009-01-27 Stone & Webster Process Technology, Inc. Process for cracking hydrocarbons using improved furnace reactor tubes
JP4580729B2 (ja) * 2004-10-29 2010-11-17 株式会社ノリタケカンパニーリミテド ジルコニア多孔質体およびその製造方法
US20080138630A1 (en) * 2006-12-08 2008-06-12 Ngk Spark Plug Co., Ltd. Assembly including polytetrafluoroethylene porous body
US8450552B2 (en) * 2009-05-18 2013-05-28 Exxonmobil Chemical Patents Inc. Pyrolysis reactor materials and methods

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11976208B2 (en) 2018-08-08 2024-05-07 Mitsubishi Gas Chemical Company, Inc. Hard-coat composition, laminate film, and curable film

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2013141950A1 (fr) * 2012-03-20 2013-09-26 Exxonmobil Chemical Patents Inc. Composant isolant thermique pour réacteur à pyrolyse
US9707536B2 (en) 2012-03-20 2017-07-18 Exxonmobil Chemical Patents Inc. Reactor components
WO2015055950A1 (fr) * 2013-10-17 2015-04-23 Saint-Gobain Centre De Recherches Et D'etudes Europeen Mélange particulaire pour l'obtention d'un produit en zircone yttriee
FR3012135A1 (fr) * 2013-10-17 2015-04-24 Saint Gobain Ct Recherches Melange particulaire pour l'obtention d'un produit en zircone yttriee
CN117169002A (zh) * 2023-11-03 2023-12-05 山东一路交通科技有限公司 一种汽车零部件抗弯折强度检测装置
CN117169002B (zh) * 2023-11-03 2024-02-13 山东一路交通科技有限公司 一种汽车零部件抗弯折强度检测装置

Also Published As

Publication number Publication date
JP2013511592A (ja) 2013-04-04
WO2011062775A3 (fr) 2012-05-03
EP2501783A2 (fr) 2012-09-26

Similar Documents

Publication Publication Date Title
US10053390B2 (en) Pyrolysis reactor materials and methods
US8932534B2 (en) Porous pyrolysis reactor materials and methods
US8512663B2 (en) Pyrolysis reactor materials and methods
CA2744023C (fr) Ceramique formee stable a la chaleur, appareil et son procede d'utilisation
US8734729B2 (en) Stabilized ceramic composition, apparatus and methods of using the same
WO2011062775A2 (fr) Matériaux de réacteur de pyrolyse poreux et procédés

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 201080059919.8

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 10774410

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase in:

Ref document number: 2781026

Country of ref document: CA

WWE Wipo information: entry into national phase

Ref document number: 2012539936

Country of ref document: JP

ENP Entry into the national phase in:

Ref document number: 20127013120

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase in:

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 2010774410

Country of ref document: EP