Classifications

• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01P—WAVEGUIDES; RESONATORS, LINES, OR OTHER DEVICES OF THE WAVEGUIDE TYPE
  • H01P1/00—Auxiliary devices
  • H01P1/20—Frequency-selective devices, e.g. filters
  • H01P1/201—Filters for transverse electromagnetic waves
  • H01P1/203—Strip line filters
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B15/00—Layered products comprising a layer of metal
  • B32B15/04—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material
  • B32B15/08—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material of synthetic resin
  • B32B15/09—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material of synthetic resin comprising polyesters
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
  • B32B17/02—Layered products essentially comprising sheet glass, or glass, slag, or like fibres in the form of fibres or filaments
  • B32B17/04—Layered products essentially comprising sheet glass, or glass, slag, or like fibres in the form of fibres or filaments bonded with or embedded in a plastic substance
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K7/00—Use of ingredients characterised by shape
  • C08K7/02—Fibres or whiskers
  • C08K7/04—Fibres or whiskers inorganic
  • C08K7/14—Glass
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L67/00—Compositions of polyesters obtained by reactions forming a carboxylic ester link in the main chain; Compositions of derivatives of such polymers
  • C08L67/02—Polyesters derived from dicarboxylic acids and dihydroxy compounds
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01P—WAVEGUIDES; RESONATORS, LINES, OR OTHER DEVICES OF THE WAVEGUIDE TYPE
  • H01P1/00—Auxiliary devices
  • H01P1/20—Frequency-selective devices, e.g. filters
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01P—WAVEGUIDES; RESONATORS, LINES, OR OTHER DEVICES OF THE WAVEGUIDE TYPE
  • H01P11/00—Apparatus or processes specially adapted for manufacturing waveguides or resonators, lines, or other devices of the waveguide type
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01P—WAVEGUIDES; RESONATORS, LINES, OR OTHER DEVICES OF THE WAVEGUIDE TYPE
  • H01P11/00—Apparatus or processes specially adapted for manufacturing waveguides or resonators, lines, or other devices of the waveguide type
  • H01P11/007—Manufacturing frequency-selective devices

Definitions

• the invention relates to a component of an electronic installation, more particular a component of an electronic installation for outdoor use, which component has been manufactured of a polymer composition and has been plated with an electrical conductive material.
• Radio frequency (RF) filters represent a class of electronic filters, designed to operate on signals in the megahertz to gigahertz frequency ranges (medium frequency to extremely high frequency). This frequency range is the range used by most broadcast radio, television, wireless communication (mobile telephones also called cell phones, Wi-Fi, etc), and thus most RF devices will include some kind of filtering on the signals transmitted or received.
• RF filters used in base stations for mobile telephone.
• EMI electro-magnetic interferences
• the inferences cause a disturbance that affects the electrical circuit due to for example electromagnetic conduction or electromagnetic radiation from an external source.
• the disturbance may interrupt, obstruct or otherwise degrade or limit the effective performance of the circuit.
• Examples of external sources causing the disturbance include electric or electronic equipment or even natural sources, for example the sun or the Northern Lights.
• Housings for RF filters are traditionally made of metal such as alumina.
• a problem of such housings is that their fabrication process is complicated and laborious.
• the housing must be cast at high temperature and processed to remove flash and to drill in holes for taps etc and it must be cut and sanded to produce flat locking surfaces. In some occasions it is even necessary to drill the housing from a solid block of material, for example if housings of barium oxide or zirconium oxide have to be produced. Examples of RF filters and housings of RF filters are given in US-4,278,957, EP-A-1544938-A and EP-A-1544940.
• the housing In US-5,329,687 it was proposed to produce the housing from a glass fibre reinforced polyetherimide resin, sold under the trade name Ultem ®.
• the housing is produced by injection molding and is plated with an electrically conductive material, using vacuum metallization processes or chemical plating processes, which processes comprise chemical and/or electrochemical treatment steps, to apply often 2 or more layers of metal.
• the housing is plated to provide shielding against electro-magnetic interferences. Therefore it is important that the plated metal layer covers the entire surface of the housing, so it has no openings to let pass electromagnetic radiation. It is therefore also very important that the plated metal layer keeps its integrity during the service life of the housing.
• the housing fulfills severe demands posed to the housing, for example by outdoor use, even in aerospace, under which conditions among others large temperature fluctuations may occur.
• outdoor use is the use of the RF filters in outdoor placed cabinets for mobile telephone base stations.
• polyetherimide is difficult to process, especially if it is glass fibre reinforced. Both melting point and viscosity of the polymer composition containing the
• polyetherimide and the glass fibres are very high, resulting in a complicated injection molding process. It is also difficult to obtain the right dimensions for the housings, which must be within narrow tolerances, in view of its application. Furthermore it is necessary to use chromium ions in the plating process of polyetherimide. This induces the risk of health problems.
• Object of the present invention is to provide a component of an electronic installation, more particular a component of an electronic installation for outdoor use, which component has been manufactured of a polymer composition and has been plated with an electrical conductive material that is easier to produce than the housing of the polymer composition containing the polyetherimide, and which component keeps functioning under severe outdoor use conditions.
• the polymer composition contains:
• PET polyethylene terephthalate
• the housing shows no ultimate failure of the metal layer disposed on the housing, even not after a long period, so that a housing is provided with a long service life.
• the RF filter functions very well within a well defined range of frequencies.
• the component is an antenna, for example a dipole antenna.
• the antenna keeps functioning well after a long period of use.
• Prior art antenna's often have been produced of pure metal or of heavy metal foils that have been adhered to a substrate. These antenna's are complicated and therefore costly to produce.
• the polyethylene terephthalate polymer is a polyester based on terephthalic acid and ethylene glycol as main monomeric units.
• the polyethylene terephthalate can also contain small amounts of other diacids, like isophtalic acid, or diols, like diethylene glycol as comonomers.
• the composition contains at least a polyethylene terephthalate homopolymer.
• a polyethylene terephthalate homopolymer is herein understood to contain less than 5 mol% of monomer units other than those of terephthalic acid and ethylene glycol. The advantage of such a homopolymer is a higher melting point and better crystallisation behaviour.
• the polyethylene terephthalate homopolymer contains less than 4 mol%, even more preferably less than 3 mol% and most preferably less than 2 mol% of monomer units other than those of terephthalic acid and ethylene glycol.
• at least 50 weight (wt) % of polyethylene terephthalate in the composition is the homopolymer, more preferably at least 90 wt. %, most preferably at least 95 wt. %.
• the polyethylene terephthalate may have a relative solution viscosity
• RSV determined on a solution of 1 gram polymer in 125 grams of a 7/10 (m/m) trichlorophenol/phenol mixture at 25°C; method based on ISO 1628-5) of from 1.50 to 2.00, preferably 1.60-1.85, and most preferably 1 .65-1.80.
• a higher RSV will result in improved strength and toughness of a composition, whereas a lower RSV promotes melt flow and crystallisation speed.
• the present RSV range an optimum in performance is reached, without the need for adding impact-modifiers or flow- promoters, which is favourable for even further extending the service life of the component.
• the polyethylene terephthalate may have been post-condensed in the solid state, for example by exposing the composition in granular form to an elevated temperature of up to about 10°C below its melting point, in an inert atmosphere during several hours.
• Another advantage of such a solid state post-condensation is that any volatiles present in the composition, and that may affect processing behaviour of the composition or properties of a part moulded thereof, are substantially removed.
• the polymer composition preferably contains a nucleating agent to enhance the crystallisation of the polyethylene terephthalate.
• a nucleating agent any known nucleating agents may be used.
• inorganic additives like micro- talcum, or a metal-carboxylate, especially an alkalimetal-carboxylate like sodium benzoate is used. More preferably sodium benzoate is used in an amount of from about 0.05 to 0.5 mass% (based on polyethylene terephthalate).
• the polymer composition that is used in component according to the invention is preferably substantially free of plasticizers, i.e. it preferably contains no additives that lower the temperature range in which crystallisation from the melt occurs.
• plasticizers i.e. it preferably contains no additives that lower the temperature range in which crystallisation from the melt occurs.
• Suitable glass fibres for use in the polymer composition may have a fibre diameter of from 5 to 20 ⁇ , preferably 8-15 ⁇ , and most preferably 9-1 1 ⁇ for optimal balance of mechanical properties and processability.
• the glass fibres preferably have a sizing on their surface that is compatible with polyethylene terephthalate and contains an epoxy- or amino-functional compound.
• the sizing contains an epoxy-functional compound. The advantage thereof is a good dispersability in polyethylene terephthalate and improved long-term mechanical properties of the polymer composition, especially fatigue behaviour.
• the polymer composition may contain between 10 and 60 wt. % of glass fibres.
• the polymer composition contains between 30 and 50 wt. % of glass fibres.
• the composition is very well processable by the injection moulding process and the components according to the invention keep functioning very well for an extended period of time. Most preferably between 35 and 45 wt.%.
• the polyethylene terephthalate composition that is used in the process according to the invention may also contain 0-20 mass% of other fibrous or particulate mineral fillers.
• filler particles are used, for example talcum or kaolin, because they contribute to the stiffness of the composition without undesirably enhancing anisotropy in properties of the composition.
• the polymer composition that is used in the component according to the invention may also contain the usual additives, like stabilisers, anti-oxidants, colorants, processing aids like a mould-release agent, viscosity-modifiers like a chain extension agent, impact-modifiers, etcetera.
• additives like stabilisers, anti-oxidants, colorants, processing aids like a mould-release agent, viscosity-modifiers like a chain extension agent, impact-modifiers, etcetera.
• the polymer composition contains less than 5 wt. % of the usual additives, more preferably less than 3 wt. %, most preferably less than 1 wt. %.
• the composition consists of the PET, the glass fibres and less than 5 wt. % of the usual additives, more preferably less than 3 wt. %, most preferably less than 1 wt. %.
• the polymer composition of the component according to the invention comprising a PET and a reinforcing fibre may be obtained by mixing or blending the various components applying known techniques. This mixing may be a 'dry' blending operation, wherein the various components are mixed below the melt processing temperatures of the PET, or a melt blending process wherein the components, optionally pre-blended, are mixed at suitable melt processing
• temperatures e.g. in a single or twin screw extruder. Also a combination of dry blending and melt blending may be applied.
• the component according to the invention is suitably manufactured by an injection molding process, followed by metal plating of the component obtained in that process with an electrically conductive material.
• This plating process may be carried out by using a vacuum metallization processes or a chemical plating process, for example a process comprising chemical and/or electrochemical treatment steps, to apply often 2 or more layers of metal.
• the plating process is a so-called electroless chemical plating process, which means that for the application of the first layer or layers chemical steps are used in the plating process.
• Such process preferably contains the steps of:
• step 5 it is also possible to replace step 5 by simply electroless deposition of a 2 - 10 micron layer of Ni or Ag.
• the component of the electronic installation according to the invention preferably is such a component suitable for outdoor use.
• the component may be a housing or an antenna. Even more preferably the component is a housing of an RF filter, most preferably a housing of an RF filter for use in a base station for mobile telephone.
• the housing of the RF-filter is plated at the inside of the housing. Often the housing exists of 2 or more parts.
• the housing may exist of a body and a cover plate or of a body and both a bottom and a cover plate.
• PET composition containing 50 wt. % of glass fibers (PET, 50% glass). Delivered by DSM the Netherlands.
• PET -Arnite AV2-370/B
• PET glass fibers
• test sample a box was used being in its shape representative for a RF filter housing.
• the size of the box was 1 10 x 1 10 x 32 mm.
• test sample was produced by using an Arburg Allrounder 320 S injection moulding machine, to which machine a mould for the test sample was mounted.
• test sample was plated by a process consisting of the following steps:
• Test samples were produced from Arnite AV2-390XT and Arnite AV2-370/B (examples 1 and 2) and PA-6 and PC (comparative experiments A and B). The test samples were subjected to a thermal shock test by heating the samples at 200 °C for 30 minutes, followed by a rapid immersion in water of 20 °C.
• the samples were subjected to a humidity test by keeping the samples for 640 hours at 85 °C and 85 % of relative humidity.
• Example 1 PET, 50 % glass pass pass
• Example 2 PET, 30 % glass pass pass Comp. exp. A. PA, 30 % glass fail fail Comp. exp. B. PC fail pass

Landscapes

• Chemical & Material Sciences (AREA)
• Manufacturing & Machinery (AREA)
• Physics & Mathematics (AREA)
• Electromagnetism (AREA)
• Engineering & Computer Science (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Health & Medical Sciences (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Organic Chemistry (AREA)
• Compositions Of Macromolecular Compounds (AREA)
• Shielding Devices Or Components To Electric Or Magnetic Fields (AREA)
• Injection Moulding Of Plastics Or The Like (AREA)

Priority Applications (5)

Applications Claiming Priority (2)

Publications (1)

Family

ID=41818655

Family Applications (1)

Country Status (7)

Cited By (2)

Families Citing this family (3)

Citations (6)

Family Cites Families (12)

• 2010
  • 2010-11-07 US US13/504,267 patent/US9203130B2/en not_active Expired - Fee Related
  • 2010-11-17 KR KR1020127015457A patent/KR20120097518A/ko not_active Ceased
  • 2010-11-17 EP EP10777024A patent/EP2502307A1/en not_active Withdrawn
  • 2010-11-17 CN CN201510856216.2A patent/CN105348752A/zh active Pending
  • 2010-11-17 CN CN201510856218.1A patent/CN105462189A/zh active Pending
  • 2010-11-17 CN CN2010800525616A patent/CN102668234A/zh active Pending
  • 2010-11-17 JP JP2012539311A patent/JP5987214B2/ja not_active Expired - Fee Related
  • 2010-11-17 WO PCT/EP2010/067639 patent/WO2011061211A1/en not_active Ceased
• 2012
  • 2012-04-20 IN IN3477DEN2012 patent/IN2012DN03477A/en unknown
• 2015
  • 2015-10-20 JP JP2015206046A patent/JP2016029734A/ja active Pending

Patent Citations (6)

Also Published As

Similar Documents

Legal Events