WO2011029781A1 - Polymers having terminal amino groups and use thereof as additives for zinc and zinc alloy electrodeposition baths - Google Patents
Polymers having terminal amino groups and use thereof as additives for zinc and zinc alloy electrodeposition baths Download PDFInfo
- Publication number
- WO2011029781A1 WO2011029781A1 PCT/EP2010/062954 EP2010062954W WO2011029781A1 WO 2011029781 A1 WO2011029781 A1 WO 2011029781A1 EP 2010062954 W EP2010062954 W EP 2010062954W WO 2011029781 A1 WO2011029781 A1 WO 2011029781A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- zinc
- electrolyte bath
- polymer
- formula
- bath according
- Prior art date
Abstract
Description
Claims