WO2011019287A2 - Method and device for manufacturing titanium objects - Google Patents
Method and device for manufacturing titanium objects Download PDFInfo
- Publication number
- WO2011019287A2 WO2011019287A2 PCT/NO2010/000303 NO2010000303W WO2011019287A2 WO 2011019287 A2 WO2011019287 A2 WO 2011019287A2 NO 2010000303 W NO2010000303 W NO 2010000303W WO 2011019287 A2 WO2011019287 A2 WO 2011019287A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- reactor
- reactor chamber
- virtual
- chamber
- actuator
- Prior art date
Abstract
Description
Claims