WO2010135806A1 - Derivatives of native lignin from softwood feedstocks - Google Patents
Derivatives of native lignin from softwood feedstocks Download PDFInfo
- Publication number
- WO2010135806A1 WO2010135806A1 PCT/CA2010/000210 CA2010000210W WO2010135806A1 WO 2010135806 A1 WO2010135806 A1 WO 2010135806A1 CA 2010000210 W CA2010000210 W CA 2010000210W WO 2010135806 A1 WO2010135806 A1 WO 2010135806A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- lignin
- mmol
- derivatives
- derivative according
- pulping
- Prior art date
Abstract
Description
Claims