WO2010070202A1 - Ferritic-austenitic stainless steel - Google Patents
Ferritic-austenitic stainless steel Download PDFInfo
- Publication number
- WO2010070202A1 WO2010070202A1 PCT/FI2009/051005 FI2009051005W WO2010070202A1 WO 2010070202 A1 WO2010070202 A1 WO 2010070202A1 FI 2009051005 W FI2009051005 W FI 2009051005W WO 2010070202 A1 WO2010070202 A1 WO 2010070202A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- weight
- stainless steel
- duplex stainless
- steel
- less
- Prior art date
Abstract
Description
Claims