WO2010065319A2 - Processus utilisant un tamis moléculaire ssz-83 - Google Patents

Processus utilisant un tamis moléculaire ssz-83 Download PDF

Info

Publication number
WO2010065319A2
WO2010065319A2 PCT/US2009/065069 US2009065069W WO2010065319A2 WO 2010065319 A2 WO2010065319 A2 WO 2010065319A2 US 2009065069 W US2009065069 W US 2009065069W WO 2010065319 A2 WO2010065319 A2 WO 2010065319A2
Authority
WO
WIPO (PCT)
Prior art keywords
molecular sieve
oxide
catalyst
ssz
tetravalent element
Prior art date
Application number
PCT/US2009/065069
Other languages
English (en)
Other versions
WO2010065319A3 (fr
Inventor
Allen W. Burton Jr.
Stacey I. Zones
Original Assignee
Chevron U.S.A. Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chevron U.S.A. Inc. filed Critical Chevron U.S.A. Inc.
Publication of WO2010065319A2 publication Critical patent/WO2010065319A2/fr
Publication of WO2010065319A3 publication Critical patent/WO2010065319A3/fr

Abstract

La présente invention concerne un nouveau tamis moléculaire cristallin désigné SSZ-83 synthétisé qui utilise un dication 1,4-bis(N-butylpiperidinium)butane ou un dication 1,4-bis(N-butylpyrrolidinium)butane comme agent d'orientation de structure.
PCT/US2009/065069 2008-11-25 2009-11-19 Processus utilisant un tamis moléculaire ssz-83 WO2010065319A2 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US11778308P 2008-11-25 2008-11-25
US61/117,783 2008-11-25

Publications (2)

Publication Number Publication Date
WO2010065319A2 true WO2010065319A2 (fr) 2010-06-10
WO2010065319A3 WO2010065319A3 (fr) 2010-08-26

Family

ID=42233793

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2009/065069 WO2010065319A2 (fr) 2008-11-25 2009-11-19 Processus utilisant un tamis moléculaire ssz-83

Country Status (1)

Country Link
WO (1) WO2010065319A2 (fr)

Cited By (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011163009A2 (fr) * 2010-06-25 2011-12-29 Chevron U.S.A. Inc. Procédé d'hydroisomérisation utilisant le tamis moléculaire ssz-81
WO2011163016A2 (fr) * 2010-06-25 2011-12-29 Chevron U.S.A. Inc. Procédés utilisant tamis moléculaire ssz-81
WO2014099261A1 (fr) * 2012-12-21 2014-06-26 Exxonbobil Chemical Patents Inc. Synthèse de zsm-5
US8900548B2 (en) 2011-10-12 2014-12-02 Exxonmobil Research And Engineering Company Synthesis of MSE-framework type molecular sieves
US8916130B2 (en) 2011-10-12 2014-12-23 Exxonmobil Research And Engineering Company Synthesis of MSE-framework type molecular sieves
US9192924B1 (en) 2014-06-04 2015-11-24 Chevron U.S.A. Inc. Molecular sieve SSZ-99
US9193600B1 (en) 2014-06-04 2015-11-24 Chevron U. S. A. Inc. Method for making molecular sieve SSZ-99
WO2015187215A1 (fr) * 2014-06-04 2015-12-10 Chevron U.S.A. Inc. Procédé pour fabriquer un tamis moléculaire ssz-100
WO2015187214A1 (fr) * 2014-06-04 2015-12-10 Chevron U.S.A. Inc. Tamis moléculaire ssz-100
WO2015187216A1 (fr) * 2014-06-04 2015-12-10 Chevron U.S.A. Inc. Procédés utilisant un tamis moléculaire ssz-100
WO2015187213A1 (fr) * 2014-06-04 2015-12-10 Chevron U.S.A. Inc. Procédés utilisant un tamis moléculaire ssz-99
US20160001273A1 (en) * 2014-07-03 2016-01-07 Chevron U.S.A. Inc Processes using molecular sieve ssz-98
WO2016039807A1 (fr) * 2014-09-09 2016-03-17 Chevron U.S.A. Inc. Procédé de fabrication d'un tamis moléculaire ssz-101
WO2016039808A1 (fr) * 2014-09-09 2016-03-17 Chevron U.S.A. Inc. Procédés utilisant un tamis moléculaire ssz-101
US9522896B2 (en) 2014-12-04 2016-12-20 Uop Llc Organo-1-oxa-4-azonium cyclohexane compounds
US9751772B2 (en) 2014-12-04 2017-09-05 Uop Llc Aluminophosphate molecular sieves using an organo-1-oxa-4-azoniumcyclohexane compound
US9815706B2 (en) 2014-12-04 2017-11-14 Uop Llc Zeolites using an organo-1-oxa-4-azoniumcyclohexane compound
US9901911B2 (en) 2014-12-18 2018-02-27 Uop Llc Coherently grown composite aluminophosphate and silicoaluminophosphate molecular sieves
US10046975B2 (en) 2016-10-11 2018-08-14 Chevron U.S.A. Inc. Synthesis of molecular sieve SSZ-83
CN110655090A (zh) * 2019-11-07 2020-01-07 中国石油化工股份有限公司 毫米级微球状分子筛及其制备方法
US10800718B2 (en) 2016-10-04 2020-10-13 Exxonmobil Chemical Patents Inc. Disproportionation and transalkylation of heavy aromatic hydrocarbons

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5007997A (en) * 1988-03-23 1991-04-16 Chevron Research Company Zeolite SSZ-26
US6468485B1 (en) * 2001-07-13 2002-10-22 Chevron U.S.A. Inc. Using zeolite SSZ-60 for reduction of oxides of nitrogen in a gas stream
US6555089B1 (en) * 2001-07-13 2003-04-29 Chevron U.S.A. Inc. Zeolite SSZ-58 composition of matter and synthesis thereof
US7022308B1 (en) * 2004-09-22 2006-04-04 Chevron U.S.A. Inc. Preparation of molecular sieve SSZ-33

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5007997A (en) * 1988-03-23 1991-04-16 Chevron Research Company Zeolite SSZ-26
US6468485B1 (en) * 2001-07-13 2002-10-22 Chevron U.S.A. Inc. Using zeolite SSZ-60 for reduction of oxides of nitrogen in a gas stream
US6555089B1 (en) * 2001-07-13 2003-04-29 Chevron U.S.A. Inc. Zeolite SSZ-58 composition of matter and synthesis thereof
US7022308B1 (en) * 2004-09-22 2006-04-04 Chevron U.S.A. Inc. Preparation of molecular sieve SSZ-33

Cited By (42)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011163016A2 (fr) * 2010-06-25 2011-12-29 Chevron U.S.A. Inc. Procédés utilisant tamis moléculaire ssz-81
WO2011163009A3 (fr) * 2010-06-25 2012-03-29 Chevron U.S.A. Inc. Procédé d'hydroisomérisation utilisant le tamis moléculaire ssz-81
WO2011163016A3 (fr) * 2010-06-25 2012-04-05 Chevron U.S.A. Inc. Procédés utilisant tamis moléculaire ssz-81
US8546628B2 (en) 2010-06-25 2013-10-01 Chevron U.S.A. Inc. Hydroisomerization process using molecular sieve SSZ-81
WO2011163009A2 (fr) * 2010-06-25 2011-12-29 Chevron U.S.A. Inc. Procédé d'hydroisomérisation utilisant le tamis moléculaire ssz-81
US9035058B2 (en) 2011-10-12 2015-05-19 Exxonmobil Research And Engineering Company Synthesis of MSE-framework type molecular sieves
US8900548B2 (en) 2011-10-12 2014-12-02 Exxonmobil Research And Engineering Company Synthesis of MSE-framework type molecular sieves
US8916130B2 (en) 2011-10-12 2014-12-23 Exxonmobil Research And Engineering Company Synthesis of MSE-framework type molecular sieves
US10293334B2 (en) 2012-12-21 2019-05-21 Exxonmobil Chemical Patents Inc. Synthesis of ZSM-5
WO2014099261A1 (fr) * 2012-12-21 2014-06-26 Exxonbobil Chemical Patents Inc. Synthèse de zsm-5
US9757716B2 (en) 2012-12-21 2017-09-12 Exxonmobil Chemical Patents Inc. Synthesis of ZSM-5
CN106457232A (zh) * 2014-06-04 2017-02-22 雪佛龙美国公司 制备分子筛ssz‑99的方法
WO2015187215A1 (fr) * 2014-06-04 2015-12-10 Chevron U.S.A. Inc. Procédé pour fabriquer un tamis moléculaire ssz-100
WO2015187212A1 (fr) * 2014-06-04 2015-12-10 Chevron U.S.A. Inc. Procédé de fabrication d'un tamis moléculaire ssz-99
WO2015187211A1 (fr) * 2014-06-04 2015-12-10 Chevron U.S.A. Inc. Tamis moléculaire ssz-99
WO2015187216A1 (fr) * 2014-06-04 2015-12-10 Chevron U.S.A. Inc. Procédés utilisant un tamis moléculaire ssz-100
WO2015187213A1 (fr) * 2014-06-04 2015-12-10 Chevron U.S.A. Inc. Procédés utilisant un tamis moléculaire ssz-99
CN106413889A (zh) * 2014-06-04 2017-02-15 雪佛龙美国公司 分子筛ssz‑99
US9259720B2 (en) 2014-06-04 2016-02-16 Chevron U.S.A. Inc. Method for making molecular sieve SSZ-100
US9272270B2 (en) 2014-06-04 2016-03-01 Chevron U.S.A. Inc. Molecular sieve SSZ-100
WO2015187214A1 (fr) * 2014-06-04 2015-12-10 Chevron U.S.A. Inc. Tamis moléculaire ssz-100
US9192924B1 (en) 2014-06-04 2015-11-24 Chevron U.S.A. Inc. Molecular sieve SSZ-99
US9468917B2 (en) 2014-06-04 2016-10-18 Chevron U.S.A. Inc. Processes using molecular sieve SSZ-100
US9475038B2 (en) 2014-06-04 2016-10-25 Chevron U.S.A. Inc. Processes using molecular sieve SSZ-99
CN106413889B (zh) * 2014-06-04 2018-09-18 雪佛龙美国公司 分子筛ssz-99
US9193600B1 (en) 2014-06-04 2015-11-24 Chevron U. S. A. Inc. Method for making molecular sieve SSZ-99
US9700878B2 (en) * 2014-07-03 2017-07-11 Chevron U.S.A. Inc. Processes using molecular sieve SSZ-98
US20160001273A1 (en) * 2014-07-03 2016-01-07 Chevron U.S.A. Inc Processes using molecular sieve ssz-98
WO2016039807A1 (fr) * 2014-09-09 2016-03-17 Chevron U.S.A. Inc. Procédé de fabrication d'un tamis moléculaire ssz-101
US9550177B2 (en) 2014-09-09 2017-01-24 Chevron U.S.A. Inc. Processes using molecular sieve SSZ-101
WO2016039808A1 (fr) * 2014-09-09 2016-03-17 Chevron U.S.A. Inc. Procédés utilisant un tamis moléculaire ssz-101
US9512010B2 (en) 2014-09-09 2016-12-06 Chevron U.S.A. Inc. Method for making molecular sieve SSZ-101
US9815706B2 (en) 2014-12-04 2017-11-14 Uop Llc Zeolites using an organo-1-oxa-4-azoniumcyclohexane compound
US9522896B2 (en) 2014-12-04 2016-12-20 Uop Llc Organo-1-oxa-4-azonium cyclohexane compounds
US9751772B2 (en) 2014-12-04 2017-09-05 Uop Llc Aluminophosphate molecular sieves using an organo-1-oxa-4-azoniumcyclohexane compound
US9901911B2 (en) 2014-12-18 2018-02-27 Uop Llc Coherently grown composite aluminophosphate and silicoaluminophosphate molecular sieves
US10800718B2 (en) 2016-10-04 2020-10-13 Exxonmobil Chemical Patents Inc. Disproportionation and transalkylation of heavy aromatic hydrocarbons
US10046975B2 (en) 2016-10-11 2018-08-14 Chevron U.S.A. Inc. Synthesis of molecular sieve SSZ-83
KR20190062559A (ko) * 2016-10-11 2019-06-05 셰브런 유.에스.에이.인크. 분자체 ssz-83의 합성
KR102338494B1 (ko) 2016-10-11 2021-12-14 셰브런 유.에스.에이.인크. 분자체 ssz-83의 합성
CN110655090A (zh) * 2019-11-07 2020-01-07 中国石油化工股份有限公司 毫米级微球状分子筛及其制备方法
CN110655090B (zh) * 2019-11-07 2021-04-27 中国石油化工股份有限公司 毫米级微球状分子筛及其制备方法

Also Published As

Publication number Publication date
WO2010065319A3 (fr) 2010-08-26

Similar Documents

Publication Publication Date Title
KR101352250B1 (ko) 분자체 ｓｓｚ-74 조성물 및 이의 합성
WO2010065319A2 (fr) Processus utilisant un tamis moléculaire ssz-83
CA2613399C (fr) Composition de tamis moleculaire ssz-56 et synthese de cette composition
CA2653928C (fr) Composition de tamis moleculaire ssz-75 de matiere et synthese de celle-ci
AU2005322503B2 (en) Molecular sieve SSZ-70 composition of matter and synthesis thereof
US9539545B2 (en) Processes using molecular sieve SSZ-96
WO2010088243A2 (fr) Procédés mettant en oeuvre un tamis moléculaire ssz-79
WO2010059297A2 (fr) Procédés utilisant le tamis moléculaire ssz-82
WO2000000430A2 (fr) Tamis moleculaire cit-6
JP5475289B2 (ja) 分子ふるいｓｓｚ−７４組成物及びその合成
WO2014123610A1 (fr) Procédés utilisant un tamis moléculaire ssz-85
WO2011163016A2 (fr) Procédés utilisant tamis moléculaire ssz-81
EP3145865B1 (fr) Procédés utilisant un tamis moléculaire ssz-95
AU2012200356B2 (en) Molecular sieve SSZ-74 composition of matter and synthesis thereof
WO2013154671A1 (fr) Procédés d'utilisation d'un tamis moléculaire ssz-87
CA2594614A1 (fr) Composition de matiere de tamis moleculaire ssz-71 et synthese de celui-ci

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 09830861

Country of ref document: EP

Kind code of ref document: A2

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 09830861

Country of ref document: EP

Kind code of ref document: A2