WO2010035488A1 - プラズマディスプレイパネル - Google Patents
プラズマディスプレイパネル Download PDFInfo
- Publication number
- WO2010035488A1 WO2010035488A1 PCT/JP2009/004905 JP2009004905W WO2010035488A1 WO 2010035488 A1 WO2010035488 A1 WO 2010035488A1 JP 2009004905 W JP2009004905 W JP 2009004905W WO 2010035488 A1 WO2010035488 A1 WO 2010035488A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- oxide
- protective layer
- dielectric layer
- magnesium oxide
- mgo
- Prior art date
Abstract
Description
図1は本発明の実施の形態におけるPDP1の構造を示す斜視図である。PDP1の基本構造は、一般的な交流面放電型PDPと同様である。図1に示すように、PDP1は前面ガラス基板3などよりなる第1基板(以下、前面板2と呼ぶ)、と、背面ガラス基板11などよりなる第2基板(以下、背面板10と呼ぶ)とが対向して配置され、その外周部をガラスフリットなどからなる封着材によって気密封着されている。封着されたPDP1内部の放電空間16には、キセノン(Xe)とネオン(Ne)などの放電ガスが400Torr(53300Pa)~600Torr(80000Pa)の圧力で封入されている。
2 前面板
3 前面ガラス基板
4 走査電極
4a,5a 透明電極
4b,5b 金属バス電極
5 維持電極
6 表示電極
7 ブラックストライプ(遮光層)
8 誘電体層
9 保護層
10 背面板
11 背面ガラス基板
12 アドレス電極
13 下地誘電体層
14 隔壁
15 蛍光体層
16 放電空間
81 第1誘電体層
82 第2誘電体層
92 凝集粒子
92a 結晶粒子
Claims (1)
- 基板上に形成した表示電極を覆うように誘電体層を形成するとともに前記誘電体層上に保護層を形成した第1基板と、前記第1基板に放電ガスが充填された放電空間を形成するように対向配置され、かつ前記表示電極と交差する方向にアドレス電極を形成するとともに前記放電空間を区画する隔壁を設けた第2基板とを有するプラズマディスプレイパネルであって、
前記保護層は酸化マグネシウムと酸化カルシウムからなる金属酸化物により形成され、前記金属酸化物は、前記保護層面におけるX線回折分析において、前記酸化マグネシウムのピークが発生する回折角と前記ピークと同一方位の前記酸化カルシウムのピークが発生する回折角との間にピークが存在するものであることを特徴とするプラズマディスプレイパネル。