WO2010033960A1 - Produits fibreux et procédés de fabrication - Google Patents

Produits fibreux et procédés de fabrication Download PDF

Info

Publication number
WO2010033960A1
WO2010033960A1 PCT/US2009/057769 US2009057769W WO2010033960A1 WO 2010033960 A1 WO2010033960 A1 WO 2010033960A1 US 2009057769 W US2009057769 W US 2009057769W WO 2010033960 A1 WO2010033960 A1 WO 2010033960A1
Authority
WO
WIPO (PCT)
Prior art keywords
fibers
population
composition
fiber
polycation
Prior art date
Application number
PCT/US2009/057769
Other languages
English (en)
Inventor
Patrick D. Kincaid
Michael C. Berg
David S. Soane
Gangadhar Jogikalmath
Original Assignee
Nanopaper, Llc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanopaper, Llc filed Critical Nanopaper, Llc
Priority to CA2738087A priority Critical patent/CA2738087A1/fr
Publication of WO2010033960A1 publication Critical patent/WO2010033960A1/fr
Priority to US13/069,007 priority patent/US20110247772A1/en

Abstract

La présente invention a pour objet des matières fibreuses fabriquées à partir de populations multiples de fibres, et les compositions associées à leur préparation. Dans certains exemples, les populations de fibres peuvent avoir des surfaces natives différentes, dans lesquelles au moins l’une des populations peut être modifiée en surface, par exemple au moyen d’un polycation (par exemple, une polyamine), de polymères secondaires, de polymères complémentaires, et/ou d’autres agents. Ces populations peuvent être combinées pour former une composition fibreuse, les traitements de surface pouvant améliorer les propriétés du produit final. Les populations de fibres peuvent aussi avoir d’autres caractéristiques physiquement variables (par exemple, les formes et les tailles). Ces compositions peuvent être utilisées dans une variété d’applications telles que les produits de papier, les filtres, les produits fibreux ignifuges, les matières fibreuses adsorbant les protéines, et les feuilles fibreuses ayant des propriétés conductrices. La présente invention a également pour objet des procédés de préparation de certaines parties ou de la totalité de ces matières fibreuses.
PCT/US2009/057769 2008-09-22 2009-09-22 Produits fibreux et procédés de fabrication WO2010033960A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CA2738087A CA2738087A1 (fr) 2008-09-22 2009-09-22 Produits fibreux et procedes de fabrication
US13/069,007 US20110247772A1 (en) 2008-09-22 2011-03-22 Fibrous products and methods of manufacture

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US9890708P 2008-09-22 2008-09-22
US61/098,907 2008-09-22

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US13/069,007 Continuation US20110247772A1 (en) 2008-09-22 2011-03-22 Fibrous products and methods of manufacture

Publications (1)

Publication Number Publication Date
WO2010033960A1 true WO2010033960A1 (fr) 2010-03-25

Family

ID=41571642

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2009/057769 WO2010033960A1 (fr) 2008-09-22 2009-09-22 Produits fibreux et procédés de fabrication

Country Status (3)

Country Link
US (1) US20110247772A1 (fr)
CA (1) CA2738087A1 (fr)
WO (1) WO2010033960A1 (fr)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011147825A1 (fr) * 2010-05-27 2011-12-01 Akzo Nobel Chemicals International B.V. Composition barrière cellulosique
WO2011147823A1 (fr) * 2010-05-27 2011-12-01 Akzo Nobel Chemicals International B.V. Composition barrière cellulosique comprenant un polymère anionique
WO2012162168A1 (fr) * 2011-05-20 2012-11-29 Dreamweaver International, Inc. Séparateur pour batterie lithium-ion à simple couche
KR101229710B1 (ko) 2011-09-30 2013-02-05 한솔제지주식회사 지력증강제용 ｎｆｃ를 이용한 종이 제조 방법
US20140224443A1 (en) * 2011-09-01 2014-08-14 Nanopaper, Llc Additives for papermaking
CN105247136A (zh) * 2013-06-03 2016-01-13 王子控股株式会社 含微细纤维的片材的制造方法
US9587353B2 (en) 2012-06-15 2017-03-07 Nanopaper, Llc Additives for papermaking
US9605383B2 (en) * 2009-08-12 2017-03-28 Nanopaper, Llc High strength paper
US20190300677A1 (en) * 2010-05-27 2019-10-03 Kemira Oyj Cellulosic barrier composition comprising anionic polymer

Families Citing this family (37)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE102007000806B3 (de) * 2007-10-01 2009-04-30 Institut für Holztechnologie Dresden gGmbH Beschichtung für Holzmaterialien und Verfahren zu ihrer Herstellung
FI124724B (fi) * 2009-02-13 2014-12-31 Upm Kymmene Oyj Menetelmä muokatun selluloosan valmistamiseksi
WO2011085038A1 (fr) * 2010-01-06 2011-07-14 Sustainable Health Enterprises (She) Matériau fibreux hautement absorbant et rétentif
WO2014164127A1 (fr) * 2013-03-09 2014-10-09 Donaldson Company, Inc. Matériau filtrant non tissé comprenant des fibres de cellulose microfibrillées
WO2016022758A1 (fr) * 2014-08-06 2016-02-11 Clarcor Engine Mobile Solutions, Llc Couche filtrante hautement efficace composite à capacité améliorée
WO2017175063A1 (fr) 2016-04-04 2017-10-12 Fiberlean Technologies Limited Compositions et procédés conférant une plus grande résistance aux produits pour plafonds, produits de revêtement des sols et autres produits de construction
US20210129110A1 (en) * 2016-12-22 2021-05-06 Duke University Polycationic microfibers and methods of using the same
US11639579B2 (en) 2018-08-23 2023-05-02 Eastman Chemical Company Recycle pulp comprising cellulose acetate
US11408128B2 (en) 2018-08-23 2022-08-09 Eastman Chemical Company Sheet with high sizing acceptance
US11519132B2 (en) 2018-08-23 2022-12-06 Eastman Chemical Company Composition of matter in stock preparation zone of wet laid process
US11420784B2 (en) 2018-08-23 2022-08-23 Eastman Chemical Company Food packaging articles
US11332888B2 (en) 2018-08-23 2022-05-17 Eastman Chemical Company Paper composition cellulose and cellulose ester for improved texturing
US11512433B2 (en) 2018-08-23 2022-11-29 Eastman Chemical Company Composition of matter feed to a head box
US11421385B2 (en) 2018-08-23 2022-08-23 Eastman Chemical Company Soft wipe comprising cellulose acetate
US11286619B2 (en) 2018-08-23 2022-03-29 Eastman Chemical Company Bale of virgin cellulose and cellulose ester
US11339537B2 (en) 2018-08-23 2022-05-24 Eastman Chemical Company Paper bag
US11421387B2 (en) 2018-08-23 2022-08-23 Eastman Chemical Company Tissue product comprising cellulose acetate
US11299854B2 (en) 2018-08-23 2022-04-12 Eastman Chemical Company Paper product articles
US11525215B2 (en) 2018-08-23 2022-12-13 Eastman Chemical Company Cellulose and cellulose ester film
US11414791B2 (en) 2018-08-23 2022-08-16 Eastman Chemical Company Recycled deinked sheet articles
US11306433B2 (en) 2018-08-23 2022-04-19 Eastman Chemical Company Composition of matter effluent from refiner of a wet laid process
US11492756B2 (en) 2018-08-23 2022-11-08 Eastman Chemical Company Paper press process with high hydrolic pressure
US11401659B2 (en) 2018-08-23 2022-08-02 Eastman Chemical Company Process to produce a paper article comprising cellulose fibers and a staple fiber
US11492757B2 (en) 2018-08-23 2022-11-08 Eastman Chemical Company Composition of matter in a post-refiner blend zone
US11390991B2 (en) 2018-08-23 2022-07-19 Eastman Chemical Company Addition of cellulose esters to a paper mill without substantial modifications
US11313081B2 (en) 2018-08-23 2022-04-26 Eastman Chemical Company Beverage filtration article
US11530516B2 (en) * 2018-08-23 2022-12-20 Eastman Chemical Company Composition of matter in a pre-refiner blend zone
US11466408B2 (en) * 2018-08-23 2022-10-11 Eastman Chemical Company Highly absorbent articles
US11441267B2 (en) 2018-08-23 2022-09-13 Eastman Chemical Company Refining to a desirable freeness
US11479919B2 (en) 2018-08-23 2022-10-25 Eastman Chemical Company Molded articles from a fiber slurry
US11492755B2 (en) 2018-08-23 2022-11-08 Eastman Chemical Company Waste recycle composition
US11414818B2 (en) 2018-08-23 2022-08-16 Eastman Chemical Company Dewatering in paper making process
US11230811B2 (en) 2018-08-23 2022-01-25 Eastman Chemical Company Recycle bale comprising cellulose ester
US11332885B2 (en) 2018-08-23 2022-05-17 Eastman Chemical Company Water removal between wire and wet press of a paper mill process
US11390996B2 (en) 2018-08-23 2022-07-19 Eastman Chemical Company Elongated tubular articles from wet-laid webs
US11401660B2 (en) 2018-08-23 2022-08-02 Eastman Chemical Company Broke composition of matter
CN112452052B (zh) * 2020-10-15 2022-04-12 华南理工大学 静电亚导体过滤材料、使用该过滤材料的滤芯及过滤材料的制备方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2190111A (en) * 1986-05-01 1987-11-11 Kimberly Clark Co Absorbent protective nonwoven fabric
US5459912A (en) * 1992-03-31 1995-10-24 E. I. Du Pont De Nemours And Company Patterned spunlaced fabrics containing woodpulp and/or woodpulp-like fibers
EP0729735A1 (fr) * 1995-03-01 1996-09-04 Yhtyneet Paperitehtaat Oy Procédé pour la fabrication d'un composite absorbant pour un article absorbant hygiénique, et un composite absorbant fabriqué selon ce procédé
DE19923344A1 (de) * 1999-05-21 2000-11-23 Corovin Gmbh Verfahren zur Herstellung von Spinnvlies- oder Meltblown-Fasern/Filamenten, Verfahren zur Herstellung von Folien sowie Spinnvlies- oder Metlblown-Fasern/Filamente, Folien, Vliesstoff
WO2007092450A2 (fr) * 2006-02-03 2007-08-16 Nanopaper Llc Fonctionnalisation de composants en papier

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7396584B2 (en) * 2001-11-21 2008-07-08 Basf Aktiengesellschaft Crosslinked polyamine coating on superabsorbent hydrogels
US7018945B2 (en) * 2002-07-02 2006-03-28 Kimberly-Clark Worldwide, Inc. Composition and method for treating fibers and nonwoven substrates
WO2008057312A2 (fr) * 2006-10-27 2008-05-15 Nanopaper, Llc Pigments pour papier coloré

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2190111A (en) * 1986-05-01 1987-11-11 Kimberly Clark Co Absorbent protective nonwoven fabric
US5459912A (en) * 1992-03-31 1995-10-24 E. I. Du Pont De Nemours And Company Patterned spunlaced fabrics containing woodpulp and/or woodpulp-like fibers
EP0729735A1 (fr) * 1995-03-01 1996-09-04 Yhtyneet Paperitehtaat Oy Procédé pour la fabrication d'un composite absorbant pour un article absorbant hygiénique, et un composite absorbant fabriqué selon ce procédé
DE19923344A1 (de) * 1999-05-21 2000-11-23 Corovin Gmbh Verfahren zur Herstellung von Spinnvlies- oder Meltblown-Fasern/Filamenten, Verfahren zur Herstellung von Folien sowie Spinnvlies- oder Metlblown-Fasern/Filamente, Folien, Vliesstoff
WO2007092450A2 (fr) * 2006-02-03 2007-08-16 Nanopaper Llc Fonctionnalisation de composants en papier

Cited By (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9605383B2 (en) * 2009-08-12 2017-03-28 Nanopaper, Llc High strength paper
WO2011147823A1 (fr) * 2010-05-27 2011-12-01 Akzo Nobel Chemicals International B.V. Composition barrière cellulosique comprenant un polymère anionique
WO2011147825A1 (fr) * 2010-05-27 2011-12-01 Akzo Nobel Chemicals International B.V. Composition barrière cellulosique
US20130209772A1 (en) * 2010-05-27 2013-08-15 Akzo Nobel Chemicals International B.V. Cellulosic barrier composition
RU2563478C2 (ru) * 2010-05-27 2015-09-20 Кемира Ойй Целлюлозная барьерная композиция
US20190300677A1 (en) * 2010-05-27 2019-10-03 Kemira Oyj Cellulosic barrier composition comprising anionic polymer
WO2012162168A1 (fr) * 2011-05-20 2012-11-29 Dreamweaver International, Inc. Séparateur pour batterie lithium-ion à simple couche
CN103688387A (zh) * 2011-05-20 2014-03-26 梦想编织者国际股份有限公司 单层锂离子电池隔膜
EA029971B1 (ru) * 2011-05-20 2018-06-29 Дримуивер Интернэшнл, Инк. Однослойный сепаратор литий-ионного аккумулятора
US20140224443A1 (en) * 2011-09-01 2014-08-14 Nanopaper, Llc Additives for papermaking
KR101229710B1 (ko) 2011-09-30 2013-02-05 한솔제지주식회사 지력증강제용 ｎｆｃ를 이용한 종이 제조 방법
US9587353B2 (en) 2012-06-15 2017-03-07 Nanopaper, Llc Additives for papermaking
CN105247136A (zh) * 2013-06-03 2016-01-13 王子控股株式会社 含微细纤维的片材的制造方法
US10697118B2 (en) 2013-06-03 2020-06-30 Oji Holdings Corporation Method for producing sheet containing fine fibers
US11542659B2 (en) 2013-06-03 2023-01-03 Oji Holdings Corporation Method for producing sheet containing fine fibers

Also Published As

Publication number Publication date
US20110247772A1 (en) 2011-10-13
CA2738087A1 (fr) 2010-03-25

Similar Documents

Publication Publication Date Title
US20110247772A1 (en) Fibrous products and methods of manufacture
US10905990B2 (en) Nonwoven filtration media including microfibrillated cellulose fibers
US10315155B2 (en) Highly porous fibrous network materials for gas filtration
JP6861276B2 (ja) セルロース系化学繊維、および該セルロース系繊維を含む不織布製品または不織布
US8123906B2 (en) Functionalization of paper components
CN107921343A (zh) 包含纤维素长丝的过滤介质
FI81842C (fi) Icke-vaevd fiberprodukt.
US20090165976A1 (en) Expansion agents for paper-based materials
EP1716288B1 (fr) Modification de fibres de cellulose a l'aide d'un derive de cellulose amphotere
Delgado-Fornué et al. Adhesion between cellulosic fibers in paper
JP7434369B2 (ja) 染料捕捉不織布及びその製造方法
CN114450450A (zh) 包含粘胶纤维的湿法网
RU2793041C1 (ru) Нетканое полотно, фиксирующее краситель, и способ его изготовления
Chaliewsak et al. FEASIBILITY STUDY ON PREPARATION OF RICE STRAW NONWOVEN COATED WITH CHITOSAN FOR REACTIVE DYE ADSORPTION.
WO2023049527A1 (fr) Milieu filtrant à fibres biodégradables
WO2022207556A1 (fr) Matériau filtrant pour emballage alimentaire

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 09792814

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 2738087

Country of ref document: CA

122 Ep: pct application non-entry in european phase

Ref document number: 09792814

Country of ref document: EP

Kind code of ref document: A1