WO2010030137A2 - 초슬림 터치 스크린 겸용 윈도우 - Google Patents

초슬림 터치 스크린 겸용 윈도우 Download PDF

Info

Publication number
WO2010030137A2
WO2010030137A2 PCT/KR2009/005159 KR2009005159W WO2010030137A2 WO 2010030137 A2 WO2010030137 A2 WO 2010030137A2 KR 2009005159 W KR2009005159 W KR 2009005159W WO 2010030137 A2 WO2010030137 A2 WO 2010030137A2
Authority
WO
WIPO (PCT)
Prior art keywords
touch screen
window
combined
buffer layer
touch
Prior art date
Application number
PCT/KR2009/005159
Other languages
English (en)
French (fr)
Other versions
WO2010030137A3 (ko
Inventor
김종완
Original Assignee
주식회사 모젬
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 모젬 filed Critical 주식회사 모젬
Publication of WO2010030137A2 publication Critical patent/WO2010030137A2/ko
Publication of WO2010030137A3 publication Critical patent/WO2010030137A3/ko

Abstract

본 발명은 윈도우와 터치 스크린를 일체로 구성함으로써 구조를 간단히 하여 공정 자동화 및 공정에서의 불량률을 줄일 수 있고, 터치 신뢰도 및 투과도가 현저히 향상되며, 슬림하고 전극층과 컬러막간의 간섭 및 색조 손상을 방지할 수 있으며, 표면경도가 높아 스크래치 등의 발생을 방지할 수 있는 터치 스크린 겸용 윈도우 및 이를 구비한 터치 패널을 제공하는 것을 목적으로 한다.

Description

초슬림 터치 스크린 겸용 윈도우
본 발명은 터치 스크린 겸용 윈도우 및 이를 구비한 초슬림 터치 패널 및 휴대 단말기에 관한 것이다.
터치 패널은 그 구동방식에 따라 접촉식 정전용량 방식, 적외선 광 감지 방식, 표면 초음파 전도 방식, 압전 방식, 적분식 장력 측정 방식, 압력 저항막 방식 등이 있는데, 기존에는 압력 저항막 방식이 PDA 등의 휴대 단말기에 가장 많이 사용되고 있다.
압력 저항막 방식은 도 1에서와 같이 유리나 투명한 플라스틱 판위에 저항성분의 물질을 입히고, 그 위에 PET필름이나 Glass를 덮어 씌운 형태로 되어 있으며, 두면이 서로 닿지 않도록 일정한 간격으로 절연봉이 설치되어 있는 구조를 가지며, 통상적으로 필름-글래스의 터치패널은 5층 구조를 갖는다.
압력 저항막 방식은 코스트, 정밀도에 관해서는 다른 방식에 비해 뛰어나지만, 필름과 글래스의 2장 구조 및 5층 이상의 구조를 가짐으로써 투과율이 저하되고, 어 다른 방식에 비해 낮고, 유효 화면에 비해 그 이외의 부분(액자)이 넓으며, 필름을 밀착시켜 단락시키는 구조이므로, 동작온도범위가 좁고 경시변화에 약하다는 결점을 가지고 있다. 또한, 빛이 막을 통과할 때, 공기와 막의 경계에서 반사가 일어나는데 이 때문에 투과도가 저하되는 문제점이 있다.
또한, 터치할 때마다 도전막끼리 기계적으로 접촉하는 구조로서 마모되기 쉽기 때문에 도전막을 두껍게 해야 하며 이 두께가 투과율의 약화, 황색 경향을 보이는 요인이 되어 휴대 단말기에 적용하기에는 무리가 있다.
접촉식 정전용량 방식은 터치화면 센서를 구성하는 유리의 양면에 투명한 특수 전도성 금속물질(TCO)을 코팅하는 방법으로 만들어지며, 사람의 몸에 있는 정전용량을 이용하는 방식이다. 이 경우 Parasitic capacitance를 통해 사용자가 터치를 함으로 인해서 사람의 몸에 있는 정전용량을 이용하여 전류의 양이 변경된 부분을 인식하고 크기를 계산하여 위치를 검출하는 원리를 가지고 있다.
도 2는 접촉식 정전용량 방식의 개념도로서, 휴대폰의 window lens부위에 손가락이 접촉하면 터치 스크린를 통해 인체에 전하가 축적되어 capacitance 값이 커지게 되고, 이 값의 변화를 회로에서 sensing하여 회로 내부의 switch를 동작시켜 외부로 신호를 출력하게 된다. 이는 기존 터치패널이 두 개의 전극으로 구성된 것과 비교하여 터치 스크린 제품은 하나의 전극을 가진 하나의 시트로 구성되며 인체의 누르는 압력이 없어도 구동이 가능하게 설계되어 간단한 접촉만으로도 동작이 가능한 구조이다. 인체의 접촉만으로 동작하는 터치 스크린은 사용자로 하여금 제품과 친밀감을 조성하여 사용자와 제품간의 친화력을 키워주게 되어 제품의 감성적인 기능을 부가시켜준다.
종래에는 도 3에서와 같이 터치패널과 윈도우 렌즈를 별도로 제조하여 이들을 합지하는 방법이 사용되어 왔다. 그러나 이러한 구조의 제품은 아래의 여러 문제점들이 발생하여 개선이 요구된다.
1) ITO 필름 적용 공정의 문제점
현재 도전층 재료로써 ITO가 코팅된 PET 필름이 사용되는데, PET 필름은 기본적으로 투과율이 90%미만의 재료로써 중간재로 사용될 시 투과율의 감소가 많아 화면시인성이 저해되고, 전체 공정상에서도 단순 부착공정이 추가되어 많은 공정상의 문제, 즉, 이물, 스크래치등의 문제와 접착제의 신뢰성등에 매우 취약한 구조를 가지게 된다.
2) 많은 공정 단계
제조 공정중에서는 최소 3회 이상의 전면 접착 공정이 진행되므로 이물 혼입등의 문제에 매우 취약한 구조이고 접착불량에 의한 화면왜곡 현상 발생과 휴대폰 등 휴대 단말기의 신뢰성 기준에 부합하기 매우 어려운 구조이다.
3) 제품 신뢰성 취약
최종 제품에서 PET재질의 필름이 표면에 드러나게 되어 스크래치등의 외부 환경에 취약한 구조를 드러내고 있다.
본 발명은 상기의 문제점을 해결하기 위한 것으로서, 윈도우와 터치 스크린을 일체로 구성함으로써 구조를 간단히 하여 공정 자동화 및 공정에서의 불량률을 줄일 수 있고, 터치 신뢰도 및 투과도가 현저히 향상되며, 슬림하고 투명 전극층과 컬러막간의 간섭 및 색조 손상을 방지할 수 있으며, 표면경도가 높아 스크래치 등의 발생을 방지할 수 있는 터치 스크린 겸용 윈도우 및 이를 구비한 터치 패널을 제공하는 것을 목적으로 한다. 특허청구범위의 각 청구항 발명은 상기 목적 중 적어도 하나 이상의 목적을 달성한다.
상기의 목적을 달성하기 위한 수단으로서,
본 발명은 데코레이션층이 상측 및 하측 중 적어도 일측에 구비된 투명수지필름; 상기 투명수지필름 하부에 형성된 폴리머 버퍼층; 상기 폴리머 버퍼층 하부에 형성된 전극 패턴; 및 상기 투명수지필름의 상부에 접착된 유리;를 포함하여 이루어진 터치 스위치 겸용 윈도우를 제공한다.
또한, 상기 폴리머 버퍼층의 두께는 1㎚~100㎛ 범위내인 것을 특징으로 하는 터치 스크린 겸용 윈도우를 제공한다.
또한, 상기 폴리머 버퍼층은 우레탄 아크릴레이트 수지, 실리콘 수지, PMMA, PC, PET, 테프론계열 수지 중에서 적어도 하나 이상 선택되어 증착 또는 코팅 방식으로 형성된 것을 특징으로 하는 터치 스크린 겸용 윈도우를 제공한다.
또한, 광투과도가 90% 이상인 것을 특징으로 하는 터치 스크린 겸용 윈도우를 제공한다.
본 발명은 또한, 상기 터치 스크린 겸용 윈도우를 구비한 터치 패널을 제공한다.
본 발명은 또한, 상기 터치 패널을 구비한 휴대형 단말기를 제공한다.
상기의 수단을 갖는 본 발명은, 윈도우와 터치 스크린을 일체로 구성함으로써 구조를 간단히 하여 공정 자동화 및 공정에서의 불량률을 줄일 수 있고, 터치 신뢰도 및 투과도가 현저히 향상되며, 슬림하고 전극층과 컬러막간의 간섭 및 색조 손상을 방지할 수 있으며, 표면경도가 높아 스크래치 등의 발생을 방지할 수 있다.
도 1은 종래의 압력 저항막 방식의 터치 패널에 관한 도,
도 2는 종래의 접촉식 정전용량 방식의 터치 패널에 관한 도,
도 3은 종래의 윈도우 및 터치 스크린이 별도로 구성된 제품에 관한 도,
도 4 및 도 5는 본 발명의 일실시예에 따른 터치 스크린 겸용 윈도우의 단면 개략도이다.
**도면의 주요부호에 대한 설명**
10: 투명수지필름
20: 데코레이션층
30: 폴리머 버퍼층
40: 전극 패턴
50: 유리
이하 도면 및 실시예를 통해 본 발명을 상세하게 설명한다. 하기의 설명은 본 발명의 일례를 들어 기술하는 것이므로, 비록 한정적, 단정적 표현이 있더라도 특허청구범위로부터 정해지는 권리범위를 제한하는 것이 아니다.
도 4 및 도 5는 본 발명의 일실시예에 따른 터치 스크린 겸용 윈도우의 개략 단면도로서, 데코레이션층(20)이 상측 및 하측 중 적어도 일측에 구비된 투명수지필름(10); 상기 투명수지필름(10) 하부에 형성된 폴리머 버퍼층(30), 상기 폴리머 버퍼층(30) 하부에 형성된 전극 패턴(40), 및 상기 투명수지필름(10)의 상부에 접착된 유리(50)를 포함하여 이루어진 것을 특징으로 한다.
상기 투명수지필름(10)의 재료는 투명한 필름이라면 제한되지 않으며, PC(폴리카보네이트), PET(폴리에틸렌테레프탈레이트), PMMA(폴리메틸메타크릴레이트) 등의 폴리머 수지를 들 수 있으며, 이 중 PC와 PET가 물성 및 광투과도, 데코레이션 용이성 등이 좋아 바람직하다. 또한, 상기 투명수지필름(10)은 편광필름, 시야각을 줄여 사생활을 보호하는 사생활 보호 필름 등과 같은 기능성 필름일 수도 있다.
상기 투명수지필름(10)의 두께는 제한되지 않으나 0.01~0.5mm로 슬림한 것이 좋다.
상기 투명수지필름(10)의 상측 및 하측 중 적어도 일측에는 데코레이션층(20)이 형성된다. 즉, 도 4 및 도 5에 도시된 바와 같이, 투명수지필름(10)의 상측 또는 하측에 데코레이션층(20)이 위치할 수도 있으며 도시되지 않았으나 양쪽에 모두 존재할 수도 있다. 부분적으로 데코레이션층이 위치하는 것도 포함하며, 윈도우의 화상표시영역은 데코레이션을 하지 않을 수도 있으며, 투명 또는 반투명하게 데코레이션하여 표시장치가 꺼졌을 때는 데코레이션한 것이 보이고 켜졌을 때는 화상이 보이도록 할 수도 있다. 또한, 전체적인 칼라 박막 형성 후에 이차적으로 칼라 패턴을 형성하는 등 다층 구조일 수도 있다.
상기 데코레이션 방법은 제한되지 않으며, 메탈 또는/및 산화물을 증착할 수도 있으며, 전도성 증착, 비전도성 증착 등을 통하여 합성수지 기판의 소정 영역에 증착하여 데코레이션할 수 있다.　 또한, 인쇄의 방법으로 색상을 입혀 데코레이션 하는 것도 가능하다.　 또한 증착, 인쇄를 병행하여 데코레이션할 수도 있다.
상기 데코레이션층(20)이 형성된 후에 색상 변형 방지 및 부착력 증대를 위해 폴리머 버퍼층과 접촉하는 면에 표면처리를 한 후, 상기 폴리머 버퍼층(30)을 형성한다. 표면처리 방법으로는 플라즈마 표면처리, 이온빔 처리, 이온주입 등의 방법을 사용할 수 있으며 표면을 깨끗하게 하고 라디칼이 형성되어 버퍼층이 보다 용이하게 부착될 수 있도록 한다.
윈도우와 터치 스위치를 일체로 형성하기 위한 개발 과정에서, 이것이 쉽지 않은 것을 발견하였다. 즉, 데코레이션층(20)을 형성한 후 직접 전극 패턴(40)을 형성하여 제조하였더니 전극 패턴과 데코레이션층간의 간섭이 발생하는 문제가 생겼다. 이를 해결하기 위해 무단히 노력하던 중 두 층간에 폴리머 버퍼층(30)을 형성할 경우 간섭 문제가 해결되는 것을 알게 되었다. 더 나아가 뜻하지 않게 터치 신뢰성이 현저하게 향상되는 효과도 얻게 되었다. 이는 폴리머 버퍼층(30)의 유전율이 좋기 때문에 얻어진 것이 아닌가 생각된다.
폴리머 버퍼층(30)의 재료는 투명재료로서, 우레탄 아크릴레이트나 실리콘 계열 도료나, PMMA, PC, PET, 테프론 계열 등의 재료 중에서 적어도 하나를 선택하는 것이 좋다.
폴리머 버퍼층(30)은 증착방식이나 습식 코팅의 방식으로 형성되는 것이 좋으며, 증착방식으로는 진공증착, 전자빔 증착, 스퍼터, CVD(Chemical vapor deposition)등의 방법을 들 수 있다. 폴리머 버퍼층(30)의 두께는 제한되지 않으나 1nm~100㎛ 범위내가 바람직하다. 1nm 미만에서는 폴리머 버퍼층의 기능이 현저히 떨어지는 것을 발견하였으며, 100㎛를 초과할 경우에는 투과도 및 제조단가에서 문제될 수 있다.
상기 전극 패턴(40)은 제한되지 않으며 종래의 접촉식 정전용량 방식의 터치 패널에 적용되어온 전극 패턴 방식을 채용할 수 있다. 접촉식 정전용량 방식의 터치 패널에 적용되어온 전극 패턴 방식은 본 기술분야에서 잘 알려져 있으므로 자세한 설명을 생략하며, 국내공개특허공보 10-2007-108077, 10-2007-29161 등을 참고할 수 있다.
상기 전극 패턴(40)의 재료는 주로 ITO, IZO, ZnO등의 전도성 산화물을 이용할 수 있으며, 외부와의 연결을 위해 버스전극이 추가로 형성될 수 있다.
전극 패턴(40)이 형성된 후에 투명수지필름(10)의 상부에 유리(50)를 접착한다. 유리(50)를 접착함으로써 표면 스크래치를 방지하며 표면경도를 향상시킬 수 있다. 유리(50)는 특별히 제한되지 않으며 일반 유리 사용할 수 있다. 더 좋기로는 강화유리를 사용하는 것이 좋다. 강화유리는 시중에서 쉽게 구입할 수 있으므로 자세한 설명은 생략한다.　 두께는 제한되지 않으나 0.2~1.2mm의 유리를 사용하는 것이 좋다.
유리(50)와 투명수지필름(10)의 접착은 접착 테이프나 UV-접착제를 이용할 수 있다. 바람직하기로는 UV-접착제가 좋다. 상기 UV-접착제의 일례로는 아크릴, 우레탄 또는 에폭시 UV-접착제를 들 수 있다. 접착 완료 후의 UV-접착제의 두께는 제한되지 않으나 0.005~0.1mm 범위내인 것이 좋다.
유리(50)와 투명수지필름(10)을 UV-접착제로 접착시에는 에어 버블의 제거가 매우 중요하며 에어 버블이 발생할 경우 화상이 일그러지는 등 제품 신뢰성에 타격을 입게 된다. 좋은 방법으로는 압착하여 접착하는 과정에서 동시에 압착하는 것이 아니라 롤프레스에 의해 점진적으로 압착하는 경우 압착함에 따라 가스가 압착 방향 및 측면으로 효과적으로 방출, 제거되도록 하는 것이 좋다.
본 발명에 따른 터치 스위치 겸용 윈도우는 기존에 비하여 구조를 단순화하여 광투과도 측정 결과 80%를 초과하였으며, 특히 대부분 90% 이상의 우수한 결과를 얻었으며, 이는 기존 제품의 광투과도 80%에 비하여 현저히 향상된 결과이다. 또한, 기존에는 접착공정을 3회 이상 실시하였는데 반하여 본 발명의 경우 접착공정이 1회로 현저히 줄어들었으며 따라서 오염의 문제나 접착 공정시 에어버블의 문제 등으로 인한 제품 수율 하락을 방지할 수 있게 되었다.
본 발명은 또한, 전술한 터치 스크린 겸용 윈도우를 구비한 터치 패널 및 휴대 단말기를 제공한다. 윈도우 및 터치 스크린이 일체로 구비된 것을 제외하면 기존의 터치 패널의 구성을 채용할 수 있으며 본 기술분야에서 잘 알려져 있으므로 설명을 생략한다. 휴대 단말기는 일례로 휴대폰, PDA 등을 들 수 있다.
또한, 전술한 터치 스크린 겸용 윈도우를 구비한 일체형 키패드 및 휴대 단말기를 제공한다. 즉, 기존의 윈도우 일체형 키패드의 구성에서 윈도우를 전술한 터치 스크린 겸용 윈도우로 구성할 수 있다. 윈도우 일체형 키패드는 제한되지 않으나 일례로서 본 출원인이 한국에 출원한 10-2006-119380, 10-2006-114783을 예시할 수 있다.
본 발명의 터치 스크린 겸용 윈도우는 윈도우와 터치 스크린을 일체로 구성함으로써 구조를 간단히 하여 공정 자동화 및 공정에서의 불량률을 줄일 수 있고, 터치 신뢰도 및 투과도가 현저히 향상되며, 슬림하고 전극층과 컬러막간의 간섭 및 색조 손상을 방지할 수 있으며, 표면경도가 높아 스크래치 등의 발생을 방지할 수 있어 산업적으로 유용하다.

Claims (8)

  1. 데코레이션층이 상측 및 하측 중 적어도 일측에 구비된 투명수지필름;
    상기 투명수지필름 하부에 형성된 폴리머 버퍼층;
    상기 폴리머 버퍼층 하부에 형성된 전극 패턴; 및
    상기 투명수지필름의 상부에 접착된 유리;를 포함하여 이루어진 터치 스크린 겸용 윈도우.
  2. 제1항에 있어서, 상기 폴리머 버퍼층의 두께는 1㎚~100㎛ 범위내인 것을 특징으로 하는 터치 스크린 겸용 윈도우.
  3. 제1항에 있어서, 상기 폴리머 버퍼층은 우레탄 아크릴레이트 수지, 실리콘 수지, PMMA, PC, PET, 테프론 계열 중에서 적어도 하나 이상 선택되어 증착 또는 코팅 방식으로 형성된 것을 특징으로 하는 터치 스크린 겸용 윈도우.
  4. 제1항 내지 제3항에 있어서, 광투과도가 80% 이상인 것을 특징으로 하는 터치 스크린 겸용 윈도우.
  5. 제1항 내지 제3항 중 어느 한 항의 터치 스크린 겸용 윈도우를 구비한 터치 패널.
  6. 제1항 내지 제3항 중 어느 한 항의 터치 스크린 겸용 윈도우를 구비한 일체형 키패드 .
  7. 제5항의 터치 패널을 구비한 휴대형 단말기.
  8. 제6항의 일체형 키패드를 구비한 휴대형 단말기.
PCT/KR2009/005159 2008-09-12 2009-09-11 초슬림 터치 스크린 겸용 윈도우 WO2010030137A2 (ko)