WO2009106933A1 - Système de pile à combustible désensibilisée - Google Patents

Système de pile à combustible désensibilisée Download PDF

Info

Publication number
WO2009106933A1
WO2009106933A1 PCT/IB2008/050729 IB2008050729W WO2009106933A1 WO 2009106933 A1 WO2009106933 A1 WO 2009106933A1 IB 2008050729 W IB2008050729 W IB 2008050729W WO 2009106933 A1 WO2009106933 A1 WO 2009106933A1
Authority
WO
WIPO (PCT)
Prior art keywords
fuel
additive
fuel cell
stabilising
stabilising additive
Prior art date
Application number
PCT/IB2008/050729
Other languages
English (en)
Inventor
K. Ravindranathan Thampi
Augustin J. Mcevoy
Bahaa El Roustom
Original Assignee
Ecole Polytechnique Federale De Lausanne (Epfl)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ecole Polytechnique Federale De Lausanne (Epfl) filed Critical Ecole Polytechnique Federale De Lausanne (Epfl)
Priority to PCT/IB2008/050729 priority Critical patent/WO2009106933A1/fr
Publication of WO2009106933A1 publication Critical patent/WO2009106933A1/fr

Abstract

La présente invention se rapporte à un système qui utilise et/ou qui traite un carburant, un élément actif de manière catalytique étant désensibilisé vis-à-vis des impuretés présentes dans le carburant. Les inventeurs ont ainsi constaté avec surprise qu'un système de traitement de carburant, qui peut être un système de pile à combustible ou un sous-ensemble d'un système de pile à combustible, pouvait être protégé avec succès des impuretés, en particulier du soufre élémentaire et des composés qui contiennent du soufre. L'effet de protection est obtenu par le biais de l'utilisation d'un additif, de préférence un halogène, dans la préparation de l'élément actif de manière catalytique.
PCT/IB2008/050729 2008-02-28 2008-02-28 Système de pile à combustible désensibilisée WO2009106933A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/IB2008/050729 WO2009106933A1 (fr) 2008-02-28 2008-02-28 Système de pile à combustible désensibilisée

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/IB2008/050729 WO2009106933A1 (fr) 2008-02-28 2008-02-28 Système de pile à combustible désensibilisée

Publications (1)

Publication Number Publication Date
WO2009106933A1 true WO2009106933A1 (fr) 2009-09-03

Family

ID=39689328

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IB2008/050729 WO2009106933A1 (fr) 2008-02-28 2008-02-28 Système de pile à combustible désensibilisée

Country Status (1)

Country Link
WO (1) WO2009106933A1 (fr)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001279268A (ja) * 2000-03-30 2001-10-10 Idemitsu Kosan Co Ltd 燃料電池用燃料油及び燃料電池用水素の製造方法
WO2006125177A2 (fr) * 2005-05-19 2006-11-23 Massachusetts Institute Of Technology Electrode et matieres catalytiques
WO2007015391A1 (fr) * 2005-08-01 2007-02-08 Japan Energy Corporation Procede de desulfuration d'une huile hydrocarbonee
WO2008008409A2 (fr) * 2006-07-12 2008-01-17 The Trustees Of The University Of Pennsylvania anodes céramiques hautes performances À utilisER avec DES combustibles stratégiques et autres combustibles hydrocarbures

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001279268A (ja) * 2000-03-30 2001-10-10 Idemitsu Kosan Co Ltd 燃料電池用燃料油及び燃料電池用水素の製造方法
WO2006125177A2 (fr) * 2005-05-19 2006-11-23 Massachusetts Institute Of Technology Electrode et matieres catalytiques
WO2007015391A1 (fr) * 2005-08-01 2007-02-08 Japan Energy Corporation Procede de desulfuration d'une huile hydrocarbonee
EP1923451A1 (fr) * 2005-08-01 2008-05-21 Japan Energy Corporation Procede de desulfuration d'une huile hydrocarbonee
WO2008008409A2 (fr) * 2006-07-12 2008-01-17 The Trustees Of The University Of Pennsylvania anodes céramiques hautes performances À utilisER avec DES combustibles stratégiques et autres combustibles hydrocarbures

Similar Documents

Publication Publication Date Title
Li et al. The CO poisoning effect in PEMFCs operational at temperatures up to 200 C
Mitzel et al. Review on mechanisms and recovery procedures for reversible performance losses in polymer electrolyte membrane fuel cells
Mukerjee et al. Investigation of enhanced CO tolerance in proton exchange membrane fuel cells by carbon supported PtMo alloy catalyst
Yousfi-Steiner et al. A review on polymer electrolyte membrane fuel cell catalyst degradation and starvation issues: Causes, consequences and diagnostic for mitigation
Haile Materials for fuel cells
Matsutani et al. Effect of particle size of platinum and platinum-cobalt catalysts on stability against load cycling
Yuan et al. Diagnosis of contamination introduced by ammonia at the cathode in a polymer electrolyte membrane fuel cell
Li et al. Recent advances in the anode catalyst layer for proton exchange membrane fuel cells
EP2426763B1 (fr) Composition de catalyseur côté anode pour pile à combustible et ensemble membrane-électrode (mea) pour pile à combustible de type polymère solide
EP2954586B1 (fr) Utilisation d'une couche anode de catalyseur
KR20040038824A (ko) 연료전지시스템의 운전방법 및 연료전지시스템
Jiang et al. Influence of temperature and relative humidity on performance and CO tolerance of PEM fuel cells with Nafion®–Teflon®–Zr (HPO4) 2 higher temperature composite membranes
Zhou et al. Solving Nafion poisoning of ORR catalysts with an accessible layer: designing a nanostructured core‐shell Pt/C catalyst via a one‐step self‐assembly for PEMFC
Zhu et al. N‐hexadecane fuel for a phosphoric acid direct hydrocarbon fuel cell
JP4336182B2 (ja) 燃料電池システムの運転方法および燃料電池システム
Yoshimi et al. Temperature and humidity dependence of the electrode polarization in intermediate-temperature fuel cells employing CsH2PO4/SiP2O7-based composite electrolytes
JP4661055B2 (ja) 燃料電池システムおよび運転方法
EP2639869B1 (fr) Procédé permettant de faire fonctionner un système de pile à combustible à electrolyte polymère et système de piles à combustible à électrolyte polymère
Li et al. Effect of Co2+ on oxygen reduction reaction catalyzed by Pt catalyst, and its implications for fuel cell contamination
Cheng et al. Propane fuel cells using phosphoric-acid-doped polybenzimidazole membranes
Wang et al. CO-tolerance behaviors of proton exchange membrane fuel cell stacks with impure hydrogen fuel
Madden et al. Proton exchange membrane fuel cell degradation: mechanisms and recent progress
Yang et al. Investigation of an electrode reversal method and degradation recovery mechanisms of PEM fuel cell
Du et al. Performance and durability of a polymer electrolyte fuel cell operating with reformate: effects of CO, CO2, and other trace impurities
WO2009106933A1 (fr) Système de pile à combustible désensibilisée

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 08719509

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 08719509

Country of ref document: EP

Kind code of ref document: A1