WO2009103850A1 - Method for separating zinc, iron, calcium, copper and manganese from the aqueous solutions of cobalt and/or nickel - Google Patents
Method for separating zinc, iron, calcium, copper and manganese from the aqueous solutions of cobalt and/or nickel Download PDFInfo
- Publication number
- WO2009103850A1 WO2009103850A1 PCT/FI2009/050134 FI2009050134W WO2009103850A1 WO 2009103850 A1 WO2009103850 A1 WO 2009103850A1 FI 2009050134 W FI2009050134 W FI 2009050134W WO 2009103850 A1 WO2009103850 A1 WO 2009103850A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- extraction
- solution
- cobalt
- nickel
- aqueous solution
- Prior art date
Abstract
Description
Claims