WO2008153950A1 - Composition d'enrobage protectrice pour substrat en métal et procédé d'enrobage correspondant - Google Patents

Composition d'enrobage protectrice pour substrat en métal et procédé d'enrobage correspondant Download PDF

Info

Publication number
WO2008153950A1
WO2008153950A1 PCT/US2008/007136 US2008007136W WO2008153950A1 WO 2008153950 A1 WO2008153950 A1 WO 2008153950A1 US 2008007136 W US2008007136 W US 2008007136W WO 2008153950 A1 WO2008153950 A1 WO 2008153950A1
Authority
WO
WIPO (PCT)
Prior art keywords
weight
percent
meth
acrylate
monomer mixture
Prior art date
Application number
PCT/US2008/007136
Other languages
English (en)
Inventor
Peter William Uhlianuk
Daniel Lee Neumann
Original Assignee
E. I. Du Pont De Nemours And Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by E. I. Du Pont De Nemours And Company filed Critical E. I. Du Pont De Nemours And Company
Priority to MX2009013111A priority Critical patent/MX2009013111A/es
Priority to EP08768209A priority patent/EP2150593A1/fr
Publication of WO2008153950A1 publication Critical patent/WO2008153950A1/fr

Abstract

Cette invention concerne une composition d'enrobage conçue pour protéger un substrat contre l'abrasion. La composition d'enrobage comprend une polyoléfine chlorsulfonée, un mélange monomère et un catalyseur. Le mélange monomère est constitué de monomères de (méth)acrylate. La composition d'enrobage sert également d'agent d'insonorisation, de revêtement anti-glisse et de revêtement anti-usure. Elle peut être appliquée à une large gamme de substrats plus particulièrement sur une plate-forme en tant que doublure de caisse.
PCT/US2008/007136 2007-06-06 2008-06-06 Composition d'enrobage protectrice pour substrat en métal et procédé d'enrobage correspondant WO2008153950A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
MX2009013111A MX2009013111A (es) 2007-06-06 2008-06-06 Composicion de un revestimiento protector para un sustrato de metal y proceso para aplicarlo.
EP08768209A EP2150593A1 (fr) 2007-06-06 2008-06-06 Composition d'enrobage protectrice pour substrat en métal et procédé d'enrobage correspondant

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US93335107P 2007-06-06 2007-06-06
US60/933,351 2007-06-06

Publications (1)

Publication Number Publication Date
WO2008153950A1 true WO2008153950A1 (fr) 2008-12-18

Family

ID=39683599

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2008/007136 WO2008153950A1 (fr) 2007-06-06 2008-06-06 Composition d'enrobage protectrice pour substrat en métal et procédé d'enrobage correspondant

Country Status (3)

Country Link
EP (1) EP2150593A1 (fr)
MX (1) MX2009013111A (fr)
WO (1) WO2008153950A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN107207895A (zh) * 2014-12-15 2017-09-26 Ppg工业俄亥俄公司 用于声音和振荡阻尼以及防水的涂料组合物、涂层和方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3890407A (en) * 1972-07-20 1975-06-17 Du Pont Novel adhesive compositions
EP0549076A1 (fr) * 1991-12-23 1993-06-30 Ministero Dell' Universita' E Della Ricerca Scientifica E Tecnologica Adhésifs de structure à base d'acrylates
US6497078B1 (en) * 1999-12-13 2002-12-24 Forty Ten L.L.C. Adhesive composition for chemically inert substrate

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3890407A (en) * 1972-07-20 1975-06-17 Du Pont Novel adhesive compositions
EP0549076A1 (fr) * 1991-12-23 1993-06-30 Ministero Dell' Universita' E Della Ricerca Scientifica E Tecnologica Adhésifs de structure à base d'acrylates
US6497078B1 (en) * 1999-12-13 2002-12-24 Forty Ten L.L.C. Adhesive composition for chemically inert substrate

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN107207895A (zh) * 2014-12-15 2017-09-26 Ppg工业俄亥俄公司 用于声音和振荡阻尼以及防水的涂料组合物、涂层和方法
CN107207895B (zh) * 2014-12-15 2023-01-13 Ppg工业俄亥俄公司 用于声音和振荡阻尼以及防水的涂料组合物、涂层和方法

Also Published As

Publication number Publication date
EP2150593A1 (fr) 2010-02-10
MX2009013111A (es) 2010-01-15

Similar Documents

Publication Publication Date Title
US20080305270A1 (en) Protective coating composition and a process for applying same
RU2618730C2 (ru) Способы и композиции для нанесения покрытия на подложку
US5439969A (en) Substrate-reactive coating composition
CN106794486B (zh) 用于涂覆基材的方法和组合物
JP4368395B2 (ja) 塗料組成物、塗装仕上げ方法及び塗装物品
RU2617490C2 (ru) Способы и композиции для нанесения покрытия на подложку
US20080305345A1 (en) Protective coating composition for a metal substrate and a process for coating same
KR101201575B1 (ko) 올리고머성 거대단량체를 함유하는 중합체를 포함하는 코팅 조성물
EP3380561B1 (fr) Composition aqueuse à deux composants pour revêtement de substrats de toiture et procédé de fabrication de revêtements de toiture
US20080305347A1 (en) Protective coating and a coated substrate obtained therefrom
WO2008153950A1 (fr) Composition d'enrobage protectrice pour substrat en métal et procédé d'enrobage correspondant
JP2007284480A (ja) ２液型水性塗料
CN114174361B (zh) 丙烯酸类聚合物、由其制备的水性聚合物分散体和由其制备的可固化成膜组合物
CN113227182B (zh) 含有酸官能多元醇聚合物的涂料组合物和由其形成的涂层
US20080306206A1 (en) Saturant and fiber composite structure
WO2009108495A1 (fr) Polymères contenant un macromonomère oligomère
JPH04300791A (ja) 自動車用マッドガード

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 08768209

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2008768209

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: MX/A/2009/013111

Country of ref document: MX

NENP Non-entry into the national phase

Ref country code: DE