WO2008079563A2 - Dispositif de stockage d'énergie à base de cuivre et procédé associé - Google Patents

Dispositif de stockage d'énergie à base de cuivre et procédé associé Download PDF

Info

Publication number
WO2008079563A2
WO2008079563A2 PCT/US2007/085243 US2007085243W WO2008079563A2 WO 2008079563 A2 WO2008079563 A2 WO 2008079563A2 US 2007085243 W US2007085243 W US 2007085243W WO 2008079563 A2 WO2008079563 A2 WO 2008079563A2
Authority
WO
WIPO (PCT)
Prior art keywords
energy storage
storage device
separator
cathodic material
cathodic
Prior art date
Application number
PCT/US2007/085243
Other languages
English (en)
Other versions
WO2008079563A3 (fr
Inventor
Guillermo Daniel Zappi
Charles Dominic Iacovangelo
David Charles Bogdan, Jr.
Steven Alfred Tysoe
Michael Alan Vallance
Karthick Vilapakkam Gourishankar
Hari Nadathur Seshadri
Guruprasad Sundararajan
Original Assignee
General Electric Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US11/763,787 external-priority patent/US20080145746A1/en
Priority claimed from US11/769,752 external-priority patent/US7632604B2/en
Application filed by General Electric Company filed Critical General Electric Company
Priority to AU2007338533A priority Critical patent/AU2007338533B2/en
Priority to CH00925/09A priority patent/CH698359B1/de
Priority to JP2009543005A priority patent/JP2010514142A/ja
Publication of WO2008079563A2 publication Critical patent/WO2008079563A2/fr
Publication of WO2008079563A3 publication Critical patent/WO2008079563A3/fr

Abstract

L'invention concerne un dispositif de stockage d'énergie qui comprend une matière cathodique en communication électrique avec un séparateur. Cette matière cathodique comprend du cuivre. Le séparateur présente une première surface qui délimite au moins une partie d'une première chambre, ainsi qu'une seconde surface qui délimite une seconde chambre. La première chambre est en communication ionique avec la seconde chambre par l'intermédiaire du séparateur. Ce séparateur présente au moins un des attributs suivants : le séparateur est un composite d'alumine et d'un oxyde de terres rares, ou le séparateur est un composite d'alumine et d'un oxyde de métal de transition, ou le séparateur comprend une pluralité de grains, ces grains délimitant des joints de grains qui délimitent des espaces interstitiels et ces espaces interstitiels délimités par les joints de grains étant exempts d'aluminate de sodium avant un chargement électrique initial du dispositif de stockage d'énergie ou exempts de la matière cathodique après le chargement électrique initial du dispositif de stockage d'énergie, ou le séparateur comprend une phase continue d'un conducteur d'ions de métaux alcalins et une phase continue d'un conducteur d'ions d'oxygène céramique. L'invention concerne également divers systèmes et procédés associés.
PCT/US2007/085243 2006-12-19 2007-11-20 Dispositif de stockage d'énergie à base de cuivre et procédé associé WO2008079563A2 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
AU2007338533A AU2007338533B2 (en) 2006-12-19 2007-11-20 Copper-based energy storage device and method
CH00925/09A CH698359B1 (de) 2006-12-19 2007-11-20 Energiespeichervorrichtung.
JP2009543005A JP2010514142A (ja) 2006-12-19 2007-11-20 銅を主体とするエネルギー蓄積装置及び方法

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
US87084306P 2006-12-19 2006-12-19
US60/870,843 2006-12-19
US11/763,787 2007-06-15
US11/763,787 US20080145746A1 (en) 2006-12-19 2007-06-15 Copper-based energy storage device and method
US11/769,752 US7632604B2 (en) 2006-12-19 2007-06-28 Energy storage device and method
US11/769,752 2007-06-28

Publications (2)

Publication Number Publication Date
WO2008079563A2 true WO2008079563A2 (fr) 2008-07-03
WO2008079563A3 WO2008079563A3 (fr) 2008-10-23

Family

ID=39326042

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2007/085243 WO2008079563A2 (fr) 2006-12-19 2007-11-20 Dispositif de stockage d'énergie à base de cuivre et procédé associé

Country Status (5)

Country Link
JP (1) JP2010514142A (fr)
CN (1) CN102244304A (fr)
AU (1) AU2007338533B2 (fr)
CH (2) CH704630B1 (fr)
WO (1) WO2008079563A2 (fr)

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2008156927A2 (fr) * 2007-06-14 2008-12-24 General Electric Company Dispositif de stockage d'énergie et configuration de cellule destinée à celui-ci
WO2010030510A1 (fr) * 2008-09-09 2010-03-18 General Electric Company Composition, dispositif de stockage d'énergie, et procédé
EP2178150A1 (fr) * 2008-10-07 2010-04-21 General Electric Company Dispositif de stockage d'énergie et procédé associé
EP2541646A1 (fr) * 2011-06-30 2013-01-02 General Electric Company Cellules électrochimiques et dispositifs associés
WO2014108291A1 (fr) * 2013-01-08 2014-07-17 Siemens Aktiengesellschaft Dispositif de stockage électrochimique de forme adaptée pour une distribution de température uniforme
WO2016028348A1 (fr) * 2014-08-21 2016-02-25 Battelle Memorial Institute Procédé de fabrication d'électrolytes solides de β"-alumine améliorés pour dispositifs de stockage d'énergie et applications énergétiques
US9362537B2 (en) 2011-06-30 2016-06-07 General Electric Company Electrochemical cells, and related energy storage devices
CN114843702A (zh) * 2022-05-09 2022-08-02 上海恩捷新材料科技有限公司 金属化合物隔膜及其制备方法与应用

Families Citing this family (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9257698B2 (en) * 2007-01-25 2016-02-09 General Electric Company Composition, energy storage device, and related process
US7993768B2 (en) * 2007-12-20 2011-08-09 General Electric Company Energy storage device and method
US20120219843A1 (en) * 2011-02-24 2012-08-30 General Electric Company Composition, energy storage device, and related processes
JP6217974B2 (ja) * 2013-12-11 2017-10-25 トヨタ自動車株式会社 非水電解質二次電池
KR101586194B1 (ko) * 2014-09-16 2016-01-20 전자부품연구원 금속염화물과 알칼리금속염화물을 함유하는 양극 및 그를 포함하는 알칼리금속이온 이차 전지
JP2018510464A (ja) * 2015-02-27 2018-04-12 マサチューセッツ インスティテュート オブ テクノロジー 双極ファラデー膜を備えた電気化学セル
KR101941655B1 (ko) * 2015-07-13 2019-01-24 제네럴 일렉트릭 컴퍼니 전도성 매트릭스를 포함하는 전기 화학 전지
CN105609761B (zh) * 2015-09-10 2018-05-11 昆明理工大学 一种CuCl/Cu复合材料的应用
CN106711462B (zh) * 2015-11-12 2020-05-12 上海奥能瑞拉能源科技有限公司 一种钠-卤化物电池集流体及含该集流体的钠-卤化物电池
CN112086695B (zh) * 2019-06-13 2021-11-02 中国科学院物理研究所 Sn(AlCl4)2熔盐的应用以及熔盐电池
US11527756B2 (en) * 2020-06-14 2022-12-13 George Clayton Hansen Resistance reduction in a battery and battery materials
CN111653836B (zh) * 2020-06-18 2021-08-13 中国科学院上海应用物理研究所 一种具有功能层的高温熔盐电池及其制备方法

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3773558A (en) * 1971-03-09 1973-11-20 Battelle Memorial Institute Electric accumulator with beta alumina separator and electrolyte consisting of a salt in an organic solvent
JPS5696464A (en) * 1979-12-28 1981-08-04 Toyo Soda Mfg Co Ltd Molten sodium-salt battery
GB2164786A (en) * 1984-09-21 1986-03-26 Lilliwyte Sa Sodium aluminium halide cell
US4945012A (en) * 1989-09-11 1990-07-31 The United States Of America As Represented By The Administrator, National Aeronautics And Space Administration Copper chloride cathode for a secondary battery
US5476733A (en) * 1993-04-02 1995-12-19 Programme 3 Patent Holdings Electrochemical cell
US5763117A (en) * 1995-06-26 1998-06-09 Electro Chemical Holdings Societe Anonyme Electrochemical cell
US20020172871A1 (en) * 2001-05-18 2002-11-21 Trans Ionics Corporation Thin film composite electrolytes, sodium-sulfur cells including same, processes of making same, and vehicles including same

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB8613800D0 (en) * 1986-06-06 1986-07-09 Lilliwyte Sa Electrochemical cell
GB8828829D0 (en) * 1988-12-09 1989-01-18 Lilliwyte Sa Electrochemical cell
US5476732A (en) * 1993-04-02 1995-12-19 Programme 3 Patent Holdings Electrochemical cell
US6117807A (en) * 1998-01-02 2000-09-12 Materials And Systems Research, Inc. Alkali-metal-β- and β"-alumina and gallate polycrystalline ceramics and fabrication by a vapor phase method
US7067208B2 (en) * 2002-02-20 2006-06-27 Ion America Corporation Load matched power generation system including a solid oxide fuel cell and a heat pump and an optional turbine

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3773558A (en) * 1971-03-09 1973-11-20 Battelle Memorial Institute Electric accumulator with beta alumina separator and electrolyte consisting of a salt in an organic solvent
JPS5696464A (en) * 1979-12-28 1981-08-04 Toyo Soda Mfg Co Ltd Molten sodium-salt battery
GB2164786A (en) * 1984-09-21 1986-03-26 Lilliwyte Sa Sodium aluminium halide cell
US4945012A (en) * 1989-09-11 1990-07-31 The United States Of America As Represented By The Administrator, National Aeronautics And Space Administration Copper chloride cathode for a secondary battery
US5476733A (en) * 1993-04-02 1995-12-19 Programme 3 Patent Holdings Electrochemical cell
US5763117A (en) * 1995-06-26 1998-06-09 Electro Chemical Holdings Societe Anonyme Electrochemical cell
US20020172871A1 (en) * 2001-05-18 2002-11-21 Trans Ionics Corporation Thin film composite electrolytes, sodium-sulfur cells including same, processes of making same, and vehicles including same

Cited By (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8110301B2 (en) 2006-12-19 2012-02-07 General Electric Company Energy storage device and cell configuration therefor
WO2008156927A2 (fr) * 2007-06-14 2008-12-24 General Electric Company Dispositif de stockage d'énergie et configuration de cellule destinée à celui-ci
WO2008156927A3 (fr) * 2007-06-14 2009-02-12 Gen Electric Dispositif de stockage d'énergie et configuration de cellule destinée à celui-ci
WO2010030510A1 (fr) * 2008-09-09 2010-03-18 General Electric Company Composition, dispositif de stockage d'énergie, et procédé
EP2178150A1 (fr) * 2008-10-07 2010-04-21 General Electric Company Dispositif de stockage d'énergie et procédé associé
JP2010092856A (ja) * 2008-10-07 2010-04-22 General Electric Co <Ge> エネルギ蓄積装置及び関連方法
EP2541646A1 (fr) * 2011-06-30 2013-01-02 General Electric Company Cellules électrochimiques et dispositifs associés
US9362537B2 (en) 2011-06-30 2016-06-07 General Electric Company Electrochemical cells, and related energy storage devices
WO2014108291A1 (fr) * 2013-01-08 2014-07-17 Siemens Aktiengesellschaft Dispositif de stockage électrochimique de forme adaptée pour une distribution de température uniforme
EP2770552A1 (fr) * 2013-01-08 2014-08-27 Siemens Aktiengesellschaft Dispositif de stockage électrochimique à forme adaptée
US10084160B2 (en) 2013-01-08 2018-09-25 Siemens Aktiengesellschaft Shape-adapted electrochemical storage device for uniform temperature distribution
WO2016028348A1 (fr) * 2014-08-21 2016-02-25 Battelle Memorial Institute Procédé de fabrication d'électrolytes solides de β"-alumine améliorés pour dispositifs de stockage d'énergie et applications énergétiques
US11145894B2 (en) 2014-08-21 2021-10-12 Battelle Memorial Institute Process for fabrication of enhanced β″-alumina solid electrolytes for energy storage devices and energy applications
CN114843702A (zh) * 2022-05-09 2022-08-02 上海恩捷新材料科技有限公司 金属化合物隔膜及其制备方法与应用

Also Published As

Publication number Publication date
WO2008079563A3 (fr) 2008-10-23
AU2007338533A1 (en) 2008-07-03
CH698359B1 (de) 2012-05-31
AU2007338533B2 (en) 2012-05-03
CH704630B1 (de) 2012-09-28
JP2010514142A (ja) 2010-04-30
CN102244304A (zh) 2011-11-16

Similar Documents

Publication Publication Date Title
US7632604B2 (en) Energy storage device and method
AU2007338533B2 (en) Copper-based energy storage device and method
EP2227837B1 (fr) Procédé et dispositif de stockage d&#39;énergie utilisant un électrolyte ternaire
US20080145746A1 (en) Copper-based energy storage device and method
AU2008266715B2 (en) Energy storage device and cell configuration therefor
US8304110B2 (en) Composition and energy storage device
US8178231B2 (en) Composition and energy storage device
US8329336B2 (en) Composition and energy storage device
US20090233170A1 (en) Energy storage device and method
WO2012087495A1 (fr) Batterie à l&#39;halogénure de métal, composition, dispositif d&#39;accumulation d&#39;énergie, et procédés associés
US20090291365A1 (en) Energy storage device and method
WO2017059416A1 (fr) Batteries au sodium-métal à cathode intercalaire
EP3090457B1 (fr) Batteries secondaires au chalcogénure de métal
US20110151289A1 (en) Energy storage device and associated method
CN101563797A (zh) 铜基储能装置和方法
KR20160060693A (ko) 중온 나트륨-금속 할라이드 배터리

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 200780047222.7

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 07854717

Country of ref document: EP

Kind code of ref document: A2

WWE Wipo information: entry into national phase

Ref document number: 2007338533

Country of ref document: AU

WWE Wipo information: entry into national phase

Ref document number: 10200900000925

Country of ref document: CH

ENP Entry into the national phase

Ref document number: 2009543005

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2007338533

Country of ref document: AU

Date of ref document: 20071120

Kind code of ref document: A

122 Ep: pct application non-entry in european phase

Ref document number: 07854717

Country of ref document: EP

Kind code of ref document: A2