WO2008043660A1 - Hitzeaktivierbares klebeband insbesondere für die verklebung von elektronischen bauteilen und leiterbahnen - Google Patents
Hitzeaktivierbares klebeband insbesondere für die verklebung von elektronischen bauteilen und leiterbahnen Download PDFInfo
- Publication number
- WO2008043660A1 WO2008043660A1 PCT/EP2007/060096 EP2007060096W WO2008043660A1 WO 2008043660 A1 WO2008043660 A1 WO 2008043660A1 EP 2007060096 W EP2007060096 W EP 2007060096W WO 2008043660 A1 WO2008043660 A1 WO 2008043660A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- adhesive tape
- heat
- activatable adhesive
- acid
- tape according
- Prior art date
Abstract
Description
Claims