WO2008008715A1 - Compositions désoxygénantes - Google Patents

Compositions désoxygénantes Download PDF

Info

Publication number
WO2008008715A1
WO2008008715A1 PCT/US2007/073007 US2007073007W WO2008008715A1 WO 2008008715 A1 WO2008008715 A1 WO 2008008715A1 US 2007073007 W US2007073007 W US 2007073007W WO 2008008715 A1 WO2008008715 A1 WO 2008008715A1
Authority
WO
WIPO (PCT)
Prior art keywords
composition
surface area
large surface
acidic
oxygen
Prior art date
Application number
PCT/US2007/073007
Other languages
English (en)
Inventor
Alexander Mehlmann
Original Assignee
Freshsafe, Llc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Freshsafe, Llc filed Critical Freshsafe, Llc
Publication of WO2008008715A1 publication Critical patent/WO2008008715A1/fr

Abstract

L'invention concerne des compositions désoxygénantes contenant un composant métallique, ledit composant étant capable de se corroder en présence d'humidité, au moins un matériau acide de grande aire de surface et au moins un sel. Ces compositions peuvent être utilisées dans des sachets et des étiquettes ou incorporées dans des polymères pour former des dispositifs et des emballages désoxygénants.
PCT/US2007/073007 2006-07-11 2007-07-09 Compositions désoxygénantes WO2008008715A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US81992206P 2006-07-11 2006-07-11
US60/819,922 2006-07-11

Publications (1)

Publication Number Publication Date
WO2008008715A1 true WO2008008715A1 (fr) 2008-01-17

Family

ID=38923554

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2007/073007 WO2008008715A1 (fr) 2006-07-11 2007-07-09 Compositions désoxygénantes

Country Status (1)

Country Link
WO (1) WO2008008715A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011020777A1 (fr) * 2009-08-17 2011-02-24 Basf Se Utilisation de tensioactifs non ioniques pour accroître l'activité désoxygénante de films polyoléfiniques fonctionnalisés
WO2012007422A1 (fr) * 2010-07-14 2012-01-19 Chemische Fabrik Budenheim Kg Composition contenant un composant métallique pouvant être activé par un acide
EP2734296A2 (fr) * 2011-07-19 2014-05-28 Multisorb Technologies, Inc. Absorbeur d'oxygène contenant du charbon actif à teneur élevée en eau
WO2019022969A1 (fr) * 2017-07-24 2019-01-31 Performance Managing And Consulting, Inc. Procédé de fabrication d'additifs incorporés à l'état fondu à élimination d'oxygène dans des plastiques pour emballages

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6057013A (en) * 1996-03-07 2000-05-02 Chevron Chemical Company Oxygen scavenging system including a by-product neutralizing material
US6586514B2 (en) * 1993-07-16 2003-07-01 Ciba Specialty Chemicals Corporation Oxygen-scavenging compositions and articles

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6586514B2 (en) * 1993-07-16 2003-07-01 Ciba Specialty Chemicals Corporation Oxygen-scavenging compositions and articles
US6057013A (en) * 1996-03-07 2000-05-02 Chevron Chemical Company Oxygen scavenging system including a by-product neutralizing material

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011020777A1 (fr) * 2009-08-17 2011-02-24 Basf Se Utilisation de tensioactifs non ioniques pour accroître l'activité désoxygénante de films polyoléfiniques fonctionnalisés
JP2015193843A (ja) * 2009-08-17 2015-11-05 アルビス・プラスチック・ゲーエムベーハー 官能化されたポリオレフィンフィルムの酸素捕捉剤活性を増加するための非イオン界面活性剤の使用
US9359485B2 (en) 2009-08-17 2016-06-07 Albis Plastic Gmbh Use of non-ionic surfactants to increase oxygen scavenger activity of functionalized polyolefin films
WO2012007422A1 (fr) * 2010-07-14 2012-01-19 Chemische Fabrik Budenheim Kg Composition contenant un composant métallique pouvant être activé par un acide
US9080028B2 (en) 2010-07-14 2015-07-14 Chemische Fabrik Budenheim Kg Composition with acid-activatable metal component
EP2734296A2 (fr) * 2011-07-19 2014-05-28 Multisorb Technologies, Inc. Absorbeur d'oxygène contenant du charbon actif à teneur élevée en eau
EP2734296A4 (fr) * 2011-07-19 2015-03-25 Multisorb Tech Inc Absorbeur d'oxygène contenant du charbon actif à teneur élevée en eau
WO2019022969A1 (fr) * 2017-07-24 2019-01-31 Performance Managing And Consulting, Inc. Procédé de fabrication d'additifs incorporés à l'état fondu à élimination d'oxygène dans des plastiques pour emballages

Similar Documents

Publication Publication Date Title
TW344676B (en) Oxygen-scavenging composition
EP1952882B1 (fr) Desoxydant resistant a l humidite
EP1550506B1 (fr) Composition absorbant l'oxygene
EP1062267A1 (fr) Compositions et articles piegeant l'oxygene
US20070241309A1 (en) Composition for controlling exposure to oxygen
EP0965381B1 (fr) Absorbant d'oxygène
EP1689826B1 (fr) Desactiveur des especes oxydantes pour un environnement faiblement humide et ses procedes d'utilisation
JP2002511375A (ja) 酸素を掃去するハイドロタルク石およびそれを含有する組成物
JP3877047B2 (ja) 酸素捕獲組成物およびその製造方法
WO2022004740A1 (fr) Composition désoxygénante et son procédé de production
DE112006000198T5 (de) Sauerstoffabsorbiermittel
EP0547761A1 (fr) Absorbeur d'oxgène et méthode pour sa production
WO2008008715A1 (fr) Compositions désoxygénantes
JP2001525449A (ja) 酸素捕捉性組成物
JP4453797B2 (ja) 脱酸素剤組成物
JP3541859B2 (ja) 脱酸素剤及びその包装体
JP3252866B2 (ja) 酸素吸収剤
JPS6218217B2 (fr)
JP2658640B2 (ja) 脱酸素剤
JP7263989B2 (ja) 脱酸素剤、脱酸素剤包装体及び食品包装体
JP2018043216A (ja) 脱酸素剤、脱酸素剤の製造方法、脱酸素剤包装体および食品包装体
CN101415343A (zh) 用于控制暴露于氧的组合物
WO2024070891A1 (fr) Composition d'agent de désoxygénation, son procédé de production, et emballage d'agent de désoxygénation
CN104590750A (zh) 高湿度用脱氧剂包装体及脱氧方法
EP4299161A1 (fr) Poudre désoxygénante

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 07812702

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

NENP Non-entry into the national phase

Ref country code: RU

32PN Ep: public notification in the ep bulletin as address of the adressee cannot be established

Free format text: NOTING OF LOSS OF RIGHTS PURSUANT TO RULE 112(1) EPC, EPA FORM 1205A DATED 09-06-2009

122 Ep: pct application non-entry in european phase

Ref document number: 07812702

Country of ref document: EP

Kind code of ref document: A1