WO2008006858A1 - A method and apparatus for manufacturing a transversely oriented film of thermoplastic polymer material and products obtainable by the same method - Google Patents
A method and apparatus for manufacturing a transversely oriented film of thermoplastic polymer material and products obtainable by the same method Download PDFInfo
- Publication number
- WO2008006858A1 WO2008006858A1 PCT/EP2007/057119 EP2007057119W WO2008006858A1 WO 2008006858 A1 WO2008006858 A1 WO 2008006858A1 EP 2007057119 W EP2007057119 W EP 2007057119W WO 2008006858 A1 WO2008006858 A1 WO 2008006858A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- film
- bosses
- stretching
- orientation
- webs
- Prior art date
Abstract
Description
Claims