WO2007101807A1 - Procede de fabrication de prepolymeres presentant des groupements isocyanate - Google Patents

Procede de fabrication de prepolymeres presentant des groupements isocyanate Download PDF

Info

Publication number
WO2007101807A1
WO2007101807A1 PCT/EP2007/051863 EP2007051863W WO2007101807A1 WO 2007101807 A1 WO2007101807 A1 WO 2007101807A1 EP 2007051863 W EP2007051863 W EP 2007051863W WO 2007101807 A1 WO2007101807 A1 WO 2007101807A1
Authority
WO
WIPO (PCT)
Prior art keywords
extruder
prepolymer
isocyanate
reaction
preparation
Prior art date
Application number
PCT/EP2007/051863
Other languages
German (de)
English (en)
Inventor
Frank Prissok
Rüdiger Krech
Original Assignee
Basf Se
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Basf Se filed Critical Basf Se
Publication of WO2007101807A1 publication Critical patent/WO2007101807A1/fr

Abstract

L'invention concerne un procédé de fabrication en continu de prépolymères présentant des groupements isocyanate, caractérisé en ce que la fabrication est réalisée dans une extrudeuse.
PCT/EP2007/051863 2006-03-06 2007-02-28 Procede de fabrication de prepolymeres presentant des groupements isocyanate WO2007101807A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP06110727.2 2006-03-06
EP06110727 2006-03-06

Publications (1)

Publication Number Publication Date
WO2007101807A1 true WO2007101807A1 (fr) 2007-09-13

Family

ID=38055448

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2007/051863 WO2007101807A1 (fr) 2006-03-06 2007-02-28 Procede de fabrication de prepolymeres presentant des groupements isocyanate

Country Status (1)

Country Link
WO (1) WO2007101807A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020109566A1 (fr) 2018-11-29 2020-06-04 Basf Se Préparation en continu d'un tpus à base de ppg
EP4386025A1 (fr) 2022-12-15 2024-06-19 Aurotec GmbH Procédé et réacteur modulaire pour produire un prépolymère

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3642964A (en) * 1969-12-03 1972-02-15 Upjohn Co Continuous process for the one-shot preparation of a thermoplastic noncellular polyurethane
US4209605A (en) * 1978-10-19 1980-06-24 Union Carbide Corporation Process for producing shaped polyurethane hydrogel articles
US4261946A (en) * 1978-12-16 1981-04-14 Bayer Aktiengesellschaft Process for the production of thermoplastic polymer by introducing thermoplastic polymer into an extruder and adding organic polyisocyanate and chain lengthening agent
EP0617066A2 (fr) * 1987-11-11 1994-09-28 Nippon Polyurethane Industry Co. Ltd. Elastomère d'uréthane thermodurcissable

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3642964A (en) * 1969-12-03 1972-02-15 Upjohn Co Continuous process for the one-shot preparation of a thermoplastic noncellular polyurethane
US4209605A (en) * 1978-10-19 1980-06-24 Union Carbide Corporation Process for producing shaped polyurethane hydrogel articles
US4261946A (en) * 1978-12-16 1981-04-14 Bayer Aktiengesellschaft Process for the production of thermoplastic polymer by introducing thermoplastic polymer into an extruder and adding organic polyisocyanate and chain lengthening agent
EP0617066A2 (fr) * 1987-11-11 1994-09-28 Nippon Polyurethane Industry Co. Ltd. Elastomère d'uréthane thermodurcissable

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020109566A1 (fr) 2018-11-29 2020-06-04 Basf Se Préparation en continu d'un tpus à base de ppg
EP4386025A1 (fr) 2022-12-15 2024-06-19 Aurotec GmbH Procédé et réacteur modulaire pour produire un prépolymère
WO2024126796A1 (fr) 2022-12-15 2024-06-20 Aurotec Gmbh Réacteur modulaire utilisé à des fins de synthèse

Similar Documents

Publication Publication Date Title
EP1777252B1 (fr) Procédé de fabrication de mousses de polyuréthane durcies à froid
DE3850496T2 (de) Polyurethanschaumstoffherstellung.
EP0135111B1 (fr) Polyuréthanes thermoplastiques à haute stabilité contre la chaleur à base de diisocyanate de naphthylène, procédé de leur préparation et leur utilisation
EP2276813B1 (fr) Procédé de production de dispersions de polyol
DE2622951C3 (fr)
DE2850610A1 (de) Verfahren zur herstellung von verstaerkten geschaeumten kunststoffen
DE3850730T3 (de) Polyurethanschaumherstellung.
EP1293524A1 (fr) Procédé de préparation de mousses de polyuréthanne dures ayant une réactivité retardée
DE19924090C1 (de) Verfahren zur kontinuierlichen Herstellung von thermoplastisch verarbeitbaren Polyurethanen mit verbessertem Erweichungsverhalten
EP0747408B1 (fr) Procédé pour la préparation en continu d'élastomères de polyuréthane urée
DE4412677A1 (de) Verfahren zur Herstellung von Polyurethan-Schaumstoffen in Gegenwart von Aminoalkyl- oder Aminophenyl-imidazolen als Katalysator sowie die Verwendung dieser Katalysatoren zur Herstellung von Polyisocyanat-polyadditionsprodukten
EP0095116B1 (fr) Compositions de polyol stables en monophase au stockage possédant de l'éthylène glycol en grande quantité et leur utilisation pour la préparation de polyuréthannes
DE4205934A1 (de) Verfahren zur herstellung von fluorchlorkohlenwasserstoff freien, niedrigdichten polyurethan-weichschaumstoffen und weichelastischen polyurethan-formschaumstoffen sowie hierfuer verwendbare, mit urethangruppen modifizierte polyisocyanatmischungen auf diphenylmethan-diisocyanatbasis
DE3405680A1 (de) Verfahren zur herstellung von gegebenenfalls zelligen polyurethan-polyharnstoff-formkoerpern mit verbessertem entformungsverhalten
DE102004062476A1 (de) Aliphatische sinterfähige thermoplastische Polyurethane und deren Verwendung
DE2913458A1 (de) Dispersionen von hochschmelzenden polyestern in polyhydroxylverbindungen, verfahren zu deren herstellung und deren verwendung bei der herstellung von polyurethankunststoffen
EP0835905B1 (fr) Procédé pour la production d'une dispersion stabile de mélamine en composants polyoliques
DE19907987A1 (de) Weiche, thermoplastische Formmassen
WO2007101807A1 (fr) Procede de fabrication de prepolymeres presentant des groupements isocyanate
DE19811471A1 (de) Verfahren zur Herstellung von Polyharnstoffdispersionen in Polyolen
DE19816525A1 (de) Verfahren zur Herstellung von thermoplastischen Polyurethanen
DE3138422A1 (de) Verfahren zur herstellung von zelligen polyurethan-elastomeren auf basis von 4,4'-diisocyanato-diphenylethan-1,2
EP3024868B1 (fr) Pièces moulées en élastomères en urée de polyuréthane renforcés et leur utilisation
DE19917934A1 (de) Verfahren zur Herstellung von Polyurethanen
DE10047024A1 (de) Verfahren zur Herstellung von flammgeschützten Polyurethanweichschaumstoffen

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application
NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 07712352

Country of ref document: EP

Kind code of ref document: A1