WO2007061928A2 - Hybrid thin-film battery - Google Patents
Hybrid thin-film battery Download PDFInfo
- Publication number
- WO2007061928A2 WO2007061928A2 PCT/US2006/044827 US2006044827W WO2007061928A2 WO 2007061928 A2 WO2007061928 A2 WO 2007061928A2 US 2006044827 W US2006044827 W US 2006044827W WO 2007061928 A2 WO2007061928 A2 WO 2007061928A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- cathode
- electrochemical device
- electrolyte
- depositing
- thick
- Prior art date
Abstract
An electrochemical device is claimed and disclosed wherein certain embodiments have a cathode greater than about 4µm and less than about 200µm thick; a thin electrolyte less than about 10µm thick; and an anode less than about 30µm thick. Another claimed and disclosed electrochemical device includes a cathode greater than about 0.5µm and less than about 200µm thick; a thin electrolyte less than about 10µm thick; and an anode less than about 30µm thick, wherein the cathode is fabricated by a non-vapor phase deposition method. The electrochemical device may also include a substrate, a current collector, an anode current collector, encapsulation and a moderating layer.
Description
HYBRID THIN-FILM BATTERY
RELATED APPLICATIONS
[001] The present application claims the benefit under 35 U.S.C. § 119 of U.S. Patent Application Serial No. 60/737,613, filed November 17, 2005, U.S. Patent Application Serial No. 60/759,479 filed January 17, 2006, and U.S. Patent Application Serial No. 60/782,792, filed March 16, 2006; and is a continuation-in-part, and claims the benefit under 35 U.S.C. § 120, of U.S. patent application Serial No. 11/209,536, entitled "Electrochemical Apparatus with Barrier Layer Protected Substrate," filed 23 August 2005, which is a continuation, and claims the benefit under 35 U.S.C. § 120, of U.S. Patent Application Serial No. 11/374,282, converted from 119(e) of U.S. provisional application Serial No. 60/690,697, and filed on June 15, 2005, entitled "Electrochemical Apparatus with Barrier Layer Protected Substrate," which is a continuation-in-part, and claims the benefit under 35 U.S.C. § 120, of U.S. Patent Application Serial No. 10/215,190, filed 9 August 2002, entitled "Methods of and device for encapsulation and termination of electronic devices," now U.S. Patent No. 6,916,679, issued 12 July 2005, which are all incorporated herein by reference in their entirety.
FIELD OF THE INVENTION
[002] The field of this invention relates to electrochemical devices and methods of manufacturing thereof, and more particularly, the composition, method of depositing, and fabrication of solid-state, thin-film, secondary and primary electrochemical devices, including batteries.
BACKGROUND
[003] Thick positive cathodes are good for creating energy-rich thin-fihn batteries. A thick positive cathode substantially increases the active cathode mass per unit area. Unfortunately, producing such cathodes with typical vacuum vapor phase processes has been problematic.
[004] Cathodes made with a typical vacuum vapor phase method have a number of limitations. For instance, vacuum vapor phase deposited materials typically grow in columns
as schematically shown in FIG. 1. This figure depicts schematically and in cross-sectional view three microscopic columns, grown by a vacuum vapor phase deposition method, of the positive cathode layer of an electrochemical device. As the columns grow through the process, the bases of these columns remain anchored to the substrate surface and the cross sectional area of these bases remains virtually fixed as the height of the columns grows. As the height of the columns increases, the aspect ratio (height of column / width of column) increases and the cathode film consisting of these columns and thus the entire device becomes mechanically unstable, typically around an aspect ratio of 15. Thus, there are limitations to the height, and therefore the thickness, of columns grown with a vacuum deposition processes. Limitations on the height directly correspond to the thickness of the cathode and the energy of an electrochemical device per unit area that can be produced using a vacuum vapor phase deposition method. Furthermore, thick cathodes take a relatively long time to grow using a vacuum vapor phase process and are, therefore, quite expensive. For instance, LiCoO2 positive cathodes grown in a vacuum vapor phase deposition method above about 3μm become overly expensive because of their long deposition time.
[005] Thus, there is demand for electrochemical devices whose cathodes can be produced thick and reliably while being fabricated quickly and inexpensively. Further, it would be desirable to accomplish these demands using any of the many well-known non- vapor phase deposition techniques and processes, such as slurry coating, Meyer rod coating, direct and reverse roll coating, doctor blade coating, spin coating, electrophoretic deposition, sol-gel deposition, spray coating, dip coating, and ink-jetting, to name a few.
[006] Depositing a thicker cathode in order to increase the energy of an electrochemical device per unit area results in an increased, overall thickness of the device. Because an overall thickness increase of a milli, micro, or nano device is typically undesirable, the device manufacturer has to explore options of how to compensate for or offset such a thickness increase. A generally valid and desirable approach is to minimize the thickness and volume of all of the non-energy providing components inside an electrochemical device.
[007] One of the options is to reduce the non-energy providing packaging of an electrochemical device. Both the encapsulation and the substrate are inherent and usually large, fractional parts of the packaging.
[008] For instance, the reduction of an encapsulation thickness from 100 micrometers, which is a typical thickness for a laminate encapsulation, to a true thin-film
encapsulation in the range of 1-10 micrometers would allow the electrochemical device manufacturer, for example, to increase the thickness of the energy bearing cathode by almost 100 micrometers without any discernible overall thickness change of the device. This design approach substantially improves the volumetric quantities of energy, capacity, and power of the electrochemical device. Because these physical performance quantities are required to be delivered in the smallest volume possible for most any milli, micro, or nano electrochemical device, the reduction of the non-energy providing components inside an electrochemical device is critically important for its acceptance in the marketplace.
[009] The other option is to fabricate an electrochemical device onto the thinnest possible substrate, if used, traded or sold as a standalone device. This is different from the non-standalone case wherein the device manufacturer may exploit an existing, free surface in an electronic device (chip surface, printed circuit board surface, etc.) and then directly integrate, fabricate or deposit the electrochemical device onto that free surface. This surface then serves as the electrochemical device's substrate as well. One may consider such an electrochemical device being configured with a zero-thickness substrate because no further substrate thickness was introduced by the electrochemical device into the final electronic device. In the more common, standalone case, however, the limits of substrate thinness are reached when it does not provide adequate chemical and physical, mainly mechanical, protection or functionality anymore to support the electrochemical device. Because most vacuum deposited cathode materials require high-temperature processing to fully develop all of their physical properties, which in turn creates film stresses that are translated into the substrate, the mechanical properties of these vacuum vapor deposited cathode materials may challenge any substrate in terms of mechanical deformation.
[0010] The typical result of vacuum vapor phase deposited films in conjunction with high-temperature processing is a bending, warping, or general deformation of the substrate and thus the entire electrochemical device. If this situation occurs, then completing the fabrication of the electrochemical device becomes difficult, in addition to the mere fact that a deformed electrochemical device is not well suited for device integration. In contrast, non- vapor phase deposited cathode materials may be fabricated with most or even all of their important physical properties already developed at the time of deposition, so that any high- temperature processing becomes redundant. Hence, non- vapor phase deposited cathode materials and other components of an electrochemical device create less stress in the
substrate and. allow the use of a thinner substrate without the risk of substantially deforming it.
[0011] Accordingly, there is also a need for capsulation that exhibits fairly high- temperature characteristics.
[0012] Thus, there is demand for an electrochemical device (i) whose cathode can be produced thick and reliably while being fabricated quickly and inexpensively, (ii) whose substrate thickness is as thin as possible while not being deformed by the component layers of the electrochemical device, (iii) whose encapsulation is fabricated as thin as possible while still providing adequate protection against the ambient in which these devices are operated, and/or (iv) whose encapsulation is composed of high-temperature materials that provide the entire electrochemical device with increased thermal resilience.
SUMMARY
[0013] Various aspects and embodiments of the present invention, as described in more detail and by example below, address certain of the shortfalls of the background technology and emerging needs in the relevant industries.
[0014] One aspect of the invention is an electrochemical device comprising a positive cathode greater than about 0.5μm and less than about 200μm thick; a thin electrolyte less than about lOμm thick; and an anode less than about 30μm thick. The device may also comprise a substrate, current collectors, terminals, a moisture protection layer, and an encapsulation, m an embodiment of the invention, the cathode may be greater than about 5μm and less than about lOOμm thick. The cathode may also be greater than about 30μm and less than about 80μm thick.
[0015] Another aspect of the invention is an electrochemical device comprising a non- vapor phase deposited cathode, an anode, and an electrolyte that is less than lOμm thick. In an embodiment of the invention, the cathode maybe greater than about 0.5μm and less than about 200μm thick, and the anode may be less than about 30μm thick.
[0016] A cathode in accordance with an aspect of an embodiment of the invention may be non- vapor phase deposited. The cathode may be deposited by one of the following methods: slurry coating, Meyer rod coating, direct and reverse roll coating, doctor blade coating, spin coating, electrophoretic deposition or ink-jetting.
[0017] The cathode may comprise LiCoO2, LiMn2O4, LiMnO2, LiNiO2, LiFePO4, LiVO2, and any mixture or chemical derivative thereof. Alternatively these cathode materials may be doped with elements from the groups 1 through 17 of the periodic table.
[0018] In an embodiment, the electrolyte may comprise lithium phosphorus oxynitride (LiPON). The electrolyte may comprise a thin-film electrolyte. The electrolyte may be deposited by a vacuum vapor phase growth method;- or non- vapor phase method.
[0019] The anode may comprise lithium, a lithium alloy or a metal, which can form a solid solution or a chemical compound with lithium, or a so-called lithium-ion compound suitable for use as a negative anode material in lithium based batteries, such as, for example, Li4Ti5O12.
[0020] In a further aspect of an embodiment of the invention, an electrochemical device may also be encapsulated with an encapsulation process selected from the group consisting of vacuum vapor phase grown thin-film encapsulation, pressure — heat lamination as described by Snyder et al. in U.S. Patent No. 6,916,679, the contents of which are hereby incorporated herein by reference in its entirety, metal foil attachment, and metal canning.
[0021] The device may further comprise a cathode current collector and an optional anode current collector on top or underneath of the thin electrolyte layer. The electrolyte immediately underneath the optional anode current collector may be protected by a moisture barrier, such as ZrO2, if the encapsulation has an opening that allows the optional anode current collector to be in direct contact with ambient atmosphere.
[0022] According to an aspect of an embodiment of the present invention, non- vapor phase fabrication methods may be used to form a positive cathode, and the cathode combined with cell components of an electrochemical device that are all, or in part fabricated by vacuum vapor phase methods. Exemplary embodiments that utilize such a combination of different methods are viewed as hybrid fabrication methods and resulting devices, for example, a "hybrid thin-film battery."
[0023] In another aspect of an embodiment of the invention, the non- vapor phase fabrication of the positive cathode does not require a high-temperature fabrication step, which limits the stress development inside the component layer stack of an electrochemical device. This in turn allows use of a thinner substrate. Although thinner substrates may be prone to undesirable deformation under a given magnitude of stress, tradeoffs from using a thin substrate include a thinner electrochemical device for a given energy, capacity, and power
performance. In other words, the use of a thinner substrate allows for increases in the volumetric quantities of energy, capacity, and power of an electrochemical device.
[0024] In another aspect, the cathode may be vacuum vapor phase grown, or fabricated by a non- vapor phase method, and then may be mechanically embossed or otherwise formed into structures that increase its surface area within the same previously coated footprint, but with resulting increased maximum thickness and decreased minimum thickness. This structure or architecture minimizes the average distance of any volume element inside the cathode relative to the neighboring solid state thin-film electrolyte layer, which, unlike in electrochemical devices with gel or liquid type electrolytes, typically does not intimately penetrate the cathode bulk. Therefore, minimizing the average distance of any volume element inside the cathode relative to the solid state thin-film electrolyte reduces the ionic diffusion lengths during operation of the electrochemical device, which in turn improves its power capability.
[0025] A further aspect of an embodiment of the invention involves mixing electronic conducting material such as carbon into an embossed or other surface-increased cathode structure to minimize electronic diffusion lengths inside the cathode bulk to improve the power capability of an electrochemical device.
[0026] In another aspect of an embodiment of the invention, an electrochemical device includes a thin-film encapsulation comprising or consisting of inorganic material that exhibits fairly good high-temperature characteristics.
[0027] In another aspect of an embodiment of the invention, a thin-film encapsulation is used to minimize the thickness contribution of the encapsulation to the overall thickness of the electrochemical device.
[0028] In another aspect, a thin encapsulation, such as a thin-film encapsulation, can overcompensate or at least compensate in full, or in part for any thickness increase of the cathode relative to the overall thickness of the electrochemical device. In addition, and compared with, for example, a pressure-heat laminate, the use of a thinner encapsulation directly increases the volumetric quantities of energy, capacity, and power of a given electrochemical device.
[0029] In yet another aspect of an embodiment of the invention, a thin-film encapsulation consists of multiple inorganic layers that all exhibit intrinsic, high-temperature stability, a characteristic that raises to some extent the temperature stability and resilience of the entire electrochemical device.
BRIEF DESCRIPTION OF THE FIGURES
[0030] The accompanying drawings, which are included to provide a further understanding of the invention and are incorporated in and constitute a part of this specification, illustrate exemplary embodiments of the invention that together with the description serve to explain the principles of the invention. In the drawings:
[0031] FIG. 1 schematically shows a cathode with columns grown according to methods used in the prior art.
[0032] FIG. 2 illustrates a hybrid thin-film electrochemical device according to an exemplary embodiment of the present invention.
[0033] FIG. 3 shows a cross-sectional view of a scanning electron micrograph of a composite LiCoO2 cathode deposited by slurry coating and then coated with a LiPON thin- film electrolyte according to an exemplary embodiment of the invention.
[0034] FIG. 4 illustrates the electrochemical cycle behavior of an electrochemical device using the composite LiCoO2 cathode and the LiPON thin-film from FIG. 3 according to an exemplary embodiment of the invention. )
[0035] FIG. 5 depicts a scanning electron micrograph of a 9μm thick, fully crystalline LiCoO2 positive cathode film fabricated by electrophoretic deposition according to an exemplary embodiment of the invention.
[0036] FIG. 6 shows the current-discharge voltage performance of a thin-film electrochemical device whose LiCoO2 positive cathode was fabricated by electrophoretic deposition according to an exemplary embodiment of the invention.
[0037] FIG. 7 shows the reversible discharge capacity as a function of cycle number of a thin-film electrochemical device whose LiCoO2 positive cathode was fabricated by electrophoretic deposition according to an exemplary embodiment of the invention.
[0038] FIG. 8 shows a scanning electron micrograph of an about 15μm thick, fully crystalline LiCoO2 positive cathode film deposited by ink-jetting according to an exemplary embodiment of the invention.
[0039] FIG. 9 shows a hybrid thin-film electrochemical device without a substrate according to an exemplary embodiment of the present invention.
[0040] FIG. 10 shows a multi-layer thin-film used to encapsulate an electrochemical device according to an exemplary embodiment of the present invention.
[0041] FIG. 11 shows the electrochemical device shown in FIG. 2, including a modulating LiPON layer and a multi-layer thin-film encapsulation layer according to an exemplary embodiment of the present invention.
[0042] FIG. 12 shows an inverted thin-film battery configuration according to an exemplary embodiment of the present invention.
[0043] FIG. 13 shows an exemplary embodiment of an inverted thin-film battery.
[0044] FIG. 14 shows an exemplary embodiment of an embossed cathode layer.
DETAILED DESCRIPTION
[0045] FIG. 1 illustrates a schematic cross-sectional view of a typical cathode layer 120 fabricated onto a metal current collector 101 over a substrate 100. In electrochemical devices produced by vacuum vapor phase deposition processes, the cathode may grow, for example, in columns 120 with inter-columnar void space 111. Also shown in FIG. 1 is a next layer in the fabrication process sequence of the thin-film electrochemical device, the electrolyte 110 with a typical bridging structure over the inter-columnar void space 111.
[0046] FIG. 2 shows a hybrid thin-film electrochemical device with a cathode 210 deposited without using a vacuum vapor phase process according to an exemplary embodiment of the present invention. In this embodiment, a cathode 210 is directly deposited onto a substrate 200. If metallically conducting, for example, the substrate 200 in this embodiment may also serve as the cathode current collector. Otherwise, a metallically conducting current collector (not shown) may be interposed between the substrate 200 and the cathode 210. The cathode 210, for example, may comprise LiCoO2, LiMn2O4, LiMnO2, LiNiO2, LiFePO4, LiVO2, or any mixture or chemical derivative thereof. The cathode 210, for example, in one embodiment, may be between about 0.5μm and about 200μm thick. In a preferred embodiment, the cathode 210, for example, may be between about 5 and about lOOμm thick, hi a most preferred embodiment, for example, the cathode 210 may be between about 30 to about 80μm thick. >
[0047] As shown in FIG. 2, an electrolyte layer 220 may be deposited on the top surface of the cathode layer 210. The electrolyte layer may, for example, comprise lithium phosphorus oxynitride (LiPON) or other solid state thin-film electrolytes such as LiAlF4, as discussed in U.S. Patent No. 4,367,267, or Li3PO4 doped Li4SiS4, as discussed by Yamamura et al. in U.S. Patent No. 5,217,826. Both of these patents are incorporated herein in their
entirety by reference. This electrolyte layer 220 may, for example, be less then about lOμm thick.
[0048] The cathode 210 is thick when compared to the relative sizes of the electrolyte 220, substrate 200, and an anode 230 formed over the electrolyte 220. In other embodiments, the relative size of the cathode 210 is also thick in comparison to the anode current collector 240, as well as a thin-film encapsulation 250.
[0049] The electrolyte 220 may be deposited on the cathode 210 using a variety of methods. These methods may include, for example, vacuum vapor phase growth methods or non- vapor phase methods. Vacuum vapor phase methods may include, for example, reactive or non-reactive RF magnetron sputtering, reactive or non-reactive DC diode sputtering, reactive or non-reactive thermal (resistive) evaporation, reactive or non-reactive electron beam evaporation, ion-beam assisted deposition, plasma enhanced chemical vapor deposition or the like. Non- vapor phase methods may include, for example, spin coating, ink-jetting, thermal spray deposition or dip coating. Spin coating is discussed, for example, by Stetter et al. in U.S. Patent No. 4,795,543; Venkatasetty in U.S. Patent No. 4,948,490; or Schmidt et al. in U.S. Patent No. 6,005,705. One such ink-jetting process is disclosed by Delnick in U.S. Patent No. 5,865,860. A thermal spray deposition process is disclosed by Inda in U.S. Patent Publication No. 2004/0106046. Dip coating is discussed by Kejha in U.S. Patent No. 5,443,602 and U.S. Patent No. 6,134,773. Each of the above patents and patent publications is incorporated herein by reference in its entirety.
[0050] As shown in FIG. 2, the next layer on top of the electrolyte is the thin negative anode layer 230. The thin anode 230 may comprise, for example, lithium, lithium alloys, metals that can form solid solutions or chemical compounds with lithium, or a so-called lithium-ion compound that may be used as a negative anode material in lithium based batteries, such as, for example, Li4Ti5O12. The thin anode layer 230, for example, may be less than about 30μm thick. The thin anode may make contact with the anode current collector 240, which can be accessed electrically through an opening 260 in the encapsulation 250. In one embodiment the anode current collector is less than about 2μm thick. The thin-film encapsulation 250, for example, may be electrically conducting in certain areas and thus may, in some embodiments, serve as an anode current collector. In such embodiments, a separately deposited anode current collector 240 would not be necessary. The thin-film encapsulation 250 may, for example, be less than about 250μm thick.
[0051] The cathode 210 in FIG. 2 may be deposited on the substrate 200 using a variety of deposition methods. In one specific embodiment, the cathode material 210 is deposited using a non- vapor phase deposition method. Non-vapor phase deposition methods are not performed in a vacuum environment. A number of non- vapor phase deposition methods are known in the art. A few exemplary methods include, slurry coating, Meyer rod coating, direct and reverse roll coating, doctor blade coating, spin coating, electrophoretic deposition, sol-gel deposition, spray coating, dip coating, and ink-jetting, to name a few. Any other non-vapor phase deposition methods or methods that do not require deposition in a vacuum may be used without deviating from the spirit, scope or embodiments of the present invention. These non-vapor phase, non- vacuum deposition methods may produce a single phase cathode or a composite cathode. The composite cathode may be deposited either on a nanoscopic, microscopic , or milliscopic scale and may consist of organic and/or inorganic matter which, in addition, may be polymerized, such as poly(vinyl pyrrolidone), sulfur nitride (SN)x, nano-tubed carbon or acetylene black.
[0052] All of the depositions mentioned herein, may, for example, be followed by a drying step with temperatures below about 150°C, and/or a low-temperature drying and adhesion improving step with temperatures between about 150°C to about 400°C, and/or a high temperature anneal step ranging from about 400°C to about 1000°C. These steps may help, for example, in drying, improving adhesion, formation of the correct film phase, and/or crystallization. The cathode deposition material may be used either in pure form or mixed with binder material, with or without carbon-type, metal-type or alloy-type electrical conduction enhancers. When the cathode material comprises a mixed form rather than a pure form, such cathode materials may be composite cathode materials.
[0053] The method of slurry coating has been used in battery fabrication as shown, for example, by Hikaru et al. in U.S. Patent No. 6,114,062, or by Kinsman in U.S. Patent No. 4,125,686, which are incorporated herein in the entirety by reference. Slurry coating may lead to the deposition of a composite electrode consisting of the electrochemical active material, which is in the form of finely dispersed powder particles that are bonded together using a polymeric binder and some form of electrical conduction enhancer, such as carbon black or the like. Also, the slurry contains solvents which need to be evaporated and/or pyrolyzed after film deposition.
[0054] According to an exemplary embodiment, a composite cathode may be deposited from slurry including or consisting of fully crystalline LiCoO2 powder, a polyimide
binder, and a graphite electrical conduction enhancer. This slurry may then be coated onto an Al foil substrate and dried at temperatures below about 150°C in ambient air for less than about 2 days. Subsequently, in this embodiment, the cathode may be coated, for example, with an about 2μm LiPON thin-film electrolyte, an about 3μm thick Li negative anode, and an about 0.3 μm thick Cu anode current collector. Finally, an about lOOμm thick heat and pressure sensitive metal-polymer laminate, which may serve to encapsulate the electrochemical device, may be applied to the electrochemical device so that the electrochemical performance of the device may be tested in the ambient.
[0055] In an exemplary another embodiment, the dried slurry coating may require an additional drying, adhesion, formation, and/or crystallization steps at temperatures up to about 1000°C, as described above, to finalize the structure of the cathode or composite cathode. This method is quick, simple and can produce thick cathodes without using a vacuum vapor phase method. Furthermore, the resulting cathode does not have the mechanical instability as those produced by vacuum vapor phase deposition methods.
[0056] The cathode 210 in FIG. 2 maybe modified as shown, for example, in FIG. 14 through mechanical displacement or removal means including embossing, stamping, abrading, scraping, forming and the like. This layer modification may be performed on either the wet or completely dried cathode. This cathode surface modification improves the ion transfer efficiency between the cathode bulk and the thin-film electrolyte, for example, consisting of a LiPON layer (not shown), and thus improves the power performance of the electrochemical device.
[0057] Further improvement in power capability may be accomplished when cathode 210 comprises a composite material including or consisting of at least the electrochemically active cathode material, for example LiCoO2, and a carbonaceous electronic conduction enhancer, which serves to minimize the electronic diffusion lengths inside the composite cathode bulk.
[0058] FIG. 3 shows a cross-sectional view of a scanning electron micrograph showing an exemplary LiPON coated composite cathode. The dimension calibration bar at the very left side in the left picture is about 9μm long; and the one in the insert picture on the right side represents a length of about 3μm.
[0059] An electrochemical cycling performance of an electrochemical device according to an exemplary embodiment of the present invention is shown in FIG. 4.
[0060] According to an exemplary embodiment of the invention, a composite cathode may be deposited by Meyer rod coating of a viscous suspension or solution containing, for example, LiCoO2 powder, as described by Principe et al. in U.S. Patent No. 6,079,352, which is incorporated herein by reference in its entirety. Alternatively, a polymeric binder, such as, for example, a polyimide, and/or an electrical conduction enhancer, such as graphite, may be admixed. This coating on a substrate, such as an Al foil substrate, may then be dried at temperatures below, for example, about 150°C in jair for less than about 2 days. Subsequently, in this embodiment the cathode may be coated, for example, with an about 2μm LiPON thin-film electrolyte, an about 3μm thick Li negative anode, and an about 0.3 μm thick Cu anode current collector. Finally, an about lOOμm thick heat and pressure sensitive metal-polymer laminate, which may serve to encapsulate the electrochemical device, may be applied to the electrochemical device so that the electrochemical performance of the device may be tested in the ambient.
[0061] In an exemplary embodiment, a dried Meyer rod coating may require an additional drying, adhesion, formation, and/or crystallization steps at temperatures up to, for example, about 1000°C, as described above, to finalize the structure of the cathode or composite cathode. This method is quick, simple and can produce thick cathodes without using a vacuum vapor phase method. Furthermore, the resulting cathode does not have the mechanical instability as those produced by vacuum vapor phase deposition methods.
[0062] According to an exemplary embodiment of the invention, a composite cathode may be deposited by direct and/or reverse roll coating of a viscous suspension or solution, containing, for example, LiCoO2 powder as described by Davis et al. in U.S. Patent No. 3,535,295, which is incorporated herein by reference in its entirety. Alternatively, a polymeric binder, such as, for example, a polyimide, and/or an electrical conduction enhancer, such as graphite, may be admixed. This coating onto a substrate, such as an Al foil substrate, may then be dried at temperatures below about 150°C in ambient air for less than about 2 days. Subsequently, in this embodiment, the cathode may be coated, for example, with an about 2μm LiPON thin-film electrolyte, an about 3μm thick Li negative anode, and an about 0.3 μm thick Cu anode current collector. Finally, an about lOOμm thick heat and pressure sensitive metal-polymer laminate, which may serve to encapsulate the electrochemical device, may be applied to the electrochemical device so that the electrochemical performance of the device may be tested in the ambient.
[0063] In an exemplary embodiment, a dried direct or reverse roll coated deposit may require an additional drying, adhesion, formation, and/or crystallization steps at temperatures up to, for example, about 1000°C, as described above, to finalize the structure of the cathode or composite cathode. This method is quick, simple and can produce thick cathodes without using a vacuum vapor phase method. Furthermore, the resulting cathode does not have the mechanical instability as those produced by vacuum vapor phase deposition methods.
[0064] According to an exemplary embodiment of the invention, a thick cathode may be deposited on a substrate via a doctor blade technique as disclosed by Brown in GB Patent No. 947518, which is incorporated herein in its entirety by reference. This deposition method is analogous to spreading butter. Accordingly, for example, a fine blade slices into some cathode material paste, consisting of the electrochemically active material, in precursor or final form, mixed with solvents, binders, and potentially electrical conduction enhancer materials, and then spreads the cathode material paste under a certain thickness directly onto a substrate. Depending on the formulation of the cathode material paste, additional drying, adhesion, formation and/or crystallization steps at temperatures of up to about 1000°C, as described above, may be used to form the final cathode or composite cathode. This method is quick, simple and can produce thick cathodes without using a vacuum vapor phase method. Furthermore, the resulting cathode does not have the mechanical instability as those produced by vacuum vapor phase deposition methods.
[0065] Spin coating is used in the thin-film coating industry, using a variety of standard spin coaters offered by many well-known manufacturers, such as Hitachi disclosed in JP Patent No. 1320728 and incorporated herein by reference in its entirety. Using a spin coating technique, a cathode powder is suspended or dispersed in a solvent of a low boiling point (high volatility), such as, for example, water, low-molecular mass alcohols, low- molecular mass ethers, low-molecular mass ketones, low-molecular mass esters, low- molecular mass hydrocarbons, etc. This suspension may then be dropped onto a fast spinning substrate (typically about 1000-3000 rpm) and is thus spread out quickly into a thin-film over the substrate due to the high centrifugal forces exerted on the droplets. Because of the extremely low mass or volume per unit area, thin-films of a volatile solvent evaporate quickly leaving the solute or suspended or dispersed material precipitated on the substrate. The spin coating process maybe repeated multiple times so as to increase the thickness of a given film. To further the evaporation process of the solvent and the precipitation of the solute, or suspended or dispersed material, the spinning substrate may be heated. Alternatively, the
spin coating suspension may additionally contain binder material or binder precursor material as well as electrical conduction enhancer material. All of these materials do not and are not intended to evaporate during the spin-coating process, either conducted at ambient conditions or at elevated temperatures, as described above, and/or vacuum. Depending on the spin coating suspension formulations, an additional drying, adhesion, formation, and/or crystallization step at temperatures of up to about 1000°C, as described above, may be required to form the final cathode or composite cathode.
[0066] According to an exemplary embodiment of the present invention, a non- vapor phase LiCoO2 cathode film may be developed using electrophoretic deposition as discussed by Kanamura et al. in 3 Electrochem. Solid State Letters 259-62 (2000) or by Lusk in GB Patent No. 1298746, both of which are incorporated herein by reference in their entirety. For example, micron size, fully crystallized LiCoO2 particles may be suspended in a solution of acetone, isopropanol, and/or iodine and may enable the electrophoretic deposition of, for example, an about 9μm thick, fully crystalline LiCoO2 cathode film onto stainless steel substrate without any columnar structure. This process may be performed, for example, at less than about 120VDC within about 30 minutes at room temperature.
[0067] FIG. 5 depicts a scanning electron micrograph of an exemplary positive cathode film in cross-sectional view deposited with electrophoretic deposition. The potential iodine impurity concentration of the film shown in the figure is below the detection limits (<1 wt%) of the energy dispersive x-ray spectroscopic method employed. Electrochemical cells may also be fabricated with thinner LiCoO2 composite cathodes by electrophoretic deposition, for example, in a solution consisting of about 200ml acetone, about 23mg I2, about 38mg carbon black, and about 53mg poly(tetrafluoroethylene) (PTFE) into which about Ig of fully crystalline LiCoO2 particle powder was suspended. In such an embodiment, the driving voltage of 50VDC for this electrophoretic deposition maybe applied, for example, for about 30 seconds. Following which, the so-deposited LiCoO2 composite film may be annealed at approximately about 377°C in air for about 4 hours to improve adhesion to the conductive substrate. Subsequently, the fabrication of the electrochemical device may be completed by depositing an about 2μm thick LiPON electrolyte using RF magnetron sputter over the LiCoO2 composite cathode, then fabricating approximately about 0.3 μm thick Cu anode current collector film by electron beam evaporation, which may then be followed by a thermal (resistive) vacuum deposition of an about 3μm thick metallic Li anode. The current- discharge voltage performance of such an electrochemical device is presented in FIG. 6,
while its electrochemical cycle stability is shown in FIG. 7. Depending on the formulation of the electrophoretic suspension, an additional drying, adhesion, formation, and/or crystallization step at temperatures of up to about 1000°C, as described above, maybe required to form the final cathode or composite cathode.
[0068] According to an exemplary embodiment, a thick cathode may be deposited using a sol-gel method. In this embodiment, for example, an oxidic cathode film material to be deposited is provided in a precursor state, such as aqueous or alcoholic sols or gels of lithium and cobalt ions that are electrically balanced by anionic counter ions or chelates. These anionic counter ions or chelates may comprise, for example, nitrate, glycolate, hydroxide, citrate, carboxylates, oxalate, alcoholate, or acetylacetonate. Such formulations may be dip coated or sprayed onto the substrate and then dried at elevated temperatures for extended periods of time, for example, less than 2 days. In addition, the so-fabricated films may be subjected to a high-temperature pyrolysis process so as to convert the anionic counter ions or chelates quantitatively into pure oxides. This method is discussed in the Ph.D Thesis of Bernd J. Neudecker, Stuttgart, Germany (1994); by Plichta et al., in 139 J. Electrochem. Soc. 1509-13 (1992); and byNazri, U.S. Patent No. 5,604,057. Alternatively, the sol-gel may additionally contain binder material or binder precursor material, as well as electrical conduction enhancer material. All of these additives do not, and are also not intended to evaporate during the drying process, either done at ambient conditions or at elevated temperatures, as described above, and/or vacuum. Depending on these sol-gel formulations, an additional drying, adhesion, formation, and/or crystallization step at temperatures of up to about 1000°C, as described above, maybe required to form the final cathode or composite cathode.
[0069] In an exemplary embodiment of the present invention, the thick cathode may be deposited using an ink-jet method. Ink-jetting of oxide film electrodes is discussed by Watanabe Kyoichi et al. in JP 2005011656, Speakman in U.S. Patent No. 6,713,389 and Hopkins et al. in U.S. Patent. No. 6,780,208, which are incorporated herein in their entirety by reference. In one embodiment of the present invention, fully crystallized LiCoO2 powder may be milled to about 0.55μm in average particle size, and then dispersed in an aqueous solution of about 0.05vol% iso-octanol, about 5vol% isopropanol, about 10vol% ethylene glycol monobutyl ether, and about 10vol% ethylene glycol. This solution may then be sonicated for about 1 hour to form a suitable ink-jet solution. The LiCoO2 films may then be deposited through a print head and wetted ceramic, for example, about 250μm thick AI2O3
plates, and a stainless steel substrates well, for example, an about 50μm foil. Subsequent to the printing, the as-deposited LiCoO2 films may be dried in air at about 200°C for about 2 hours in order to drive off excess solvent and improve the adhesion of the LiCoO2 film to its substrate. A dried LiCoO2 film thickness of about 15μm may be achieved based on ten print head passes over the same substrate region. A cross-sectional scanning electron micrograph view of such a LiCoO2 film is shown in FIG. 8. Alternatively, the ink-jet solution or suspension may contain binder material, binder precursor material, and/or electrical conduction enhancer material. If used, each of these materials do nots and are also not intended to evaporate during the drying process, whether at ambient conditions or at elevated temperatures, as described above, and/or in a vacuum. Depending on these formulations of the ink-jet solution or suspension, an additional drying, adhesion, formation, and/or crystallization step at temperatures of up to about 1000°C, as described above, maybe required to form the final cathode or composite cathode.
[0070] According to an exemplary embodiment, a cathode fabricated by a non- vapor phase deposition may be coated, in its finished or unfinished state, for example, with an inert, metallically conducting layer, such as gold. Subsequently, a finished or unfinished cathode and an inert, metallically conducting coating may be, for example, heated together for further drying, adhesion, formation, and/or crystallization during which processes the inert, metallically conducting coating may be substantially absorbed into the pores, voids, and crevices of the cathode, thus improving the electrical conduction of the cathode.
[0071] The anode in the exemplary embodiments described above may be deposited using a variety of methods. For example, the anode material may be deposited using a vacuum vapor phase growth method, or a non- vapor phase growth method, such as ink- jetting or dip coating.
[0072] An exemplary embodiment of the present invention includes depositing a negative anode material via a vacuum vapor phase growth method. Typical vapor phase growth methods for negative anodes include, but are not limited to, reactive or non-reactive RF magnetron sputtering, reactive or non-reactive DC diode sputtering, reactive or non- reactive thermal (resistive) evaporation, reactive or non-reactive electron beam evaporation, ion-beam assisted deposition, or plasma enhanced chemical vapor deposition. The negative anode may either be, for example, metallic lithium, a lithium alloy, or a metal that can form a solid solution or a chemical compounds with lithium.
[0073] Other exemplary embodiments may include non-vapor phase growth methods for depositing a negative anode. For example, non-vapor phase growth methods, such as ink- jetting of metallic lithium powder mixtures may be used to deposit a negative anode. Such methods are described by Nelson et al. in U.S. Patent Publication No. 2005/0239917. As well, for example, one could simply dip a sample into molten lithium under a protective atmosphere and allow the resulting film on the sample to cool and solidify. Analogously, one may fabricate a lithium-ion anode, such as metallic tin, by dipping a sample into molten tin under air atmosphere or transfer the molten or hot tin on a flattened face of a, for example, rod and then stamp the tin onto the sample.
[0074] A dip coating technique via sol-gel route may similarly work for depositing negative anode materials as described, for example, by Patrusheva et al. in RU Patent No. 2241281C2, which is incorporated herein by reference in its entirety. For example, SnO2 based Li-ion anodes using suitable anionic formulations of alkoxides may be used, as described by Toki Motoyuki in U.S. Patent. No. 6,235,260, which is also incorporated herein by reference in it entirety.
[0075] FIG. 9 shows an exemplary hybrid thin-film electrochemical device fabricated without a substrate according to an embodiment of the present invention. This device is similar to that shown in FIG. 2, but does not have a substrate. Instead, the device is spatially terminated by a thin metal layer 300 that may be used, for example, as a current collector and electrical terminal. In addition to this thin metal layer 300, the device in FIG. 9 comprises at least a cathode 310, an electrolyte 320, and an anode 330.
[0076] The embodiments described above may be encapsulated using an encapsulation 350 selected from the group consisting of vacuum vapor phase grown thin-film encapsulation, pressure - heat lamination of protective polymer composites as described by Snyder et al. in U.S. Patent No. 6,916,679, pressure - heat lamination of metal foils coated with pressure-heat sensitive adhesive surfaces, and metal canning.
[0077] An anode current collector 340, such as Zr may be interposed between the electrolyte 320, the anode 330, and the encapsulation 350. Furthermore, a moisture barrier may be applied between the anode current collector 340 and the underlying moisture sensitive electrolyte 320 to protect latter from the environment. A material having moisture blocking properties maybe selected: a) from the group of metals, semi-metals, alloys, borides, carbides, diamond, diamond-like carbon, suicides, nitrides, phosphides, oxides, fluorides, chlorides, bromides, iodides; b) from the group of any multinary compounds
composed of borides, carbides, suicides, nitrides, phosphides, oxides, fluorides, chlorides, bromides, and iodides; or c) from the group of high-temperature stable organic polymers and high-temperature stable silicones. This moisture barrier, for example, may comprise ZrO2 or ZrN and may be part of the anode current collector 340 that may be gradiented in terms of its oxide or nitride content thus reaching a stoichiometry of ZrO2 or ZrN near the interface to the electrolyte.
[0078] FIG. 10 shows an embodiment of an electrochemical device with a multilayer thin-film encapsulation material. The multilayer thin-film encapsulation 400 may be comprised, for example, of multiple strong metallic getter layers 410 with alternating amorphous or glassy oxide or nitride layers 420 thereof. The strong metallic getter layers 410 are used to protect the device from moisture and oxygen based on their superior gettering ability for H2O and O2. The strong metallic getter layers may, for example, be comprised of Zr, Y, Ti, Cr, Al, or any alloy thereof. The glassy or amorphous layers 420 may be the oxides or nitrides of the metal or metals used in the getter layers, such as, for example, ZrO2, ZrN, Y2O3, YN, TiO2, TiN, Cr2O3, CrN, Al2O3, AlN, or any multi-element compound thereof. The mechanically dense glassy or amorphous layers being substantially free of grain boundaries may, for example, effectively block any moisture or oxygen diffusion through said oxides or nitrides. As a result, the multilayer thin-film encapsulation may effectively protect the underlying, air sensitive metallic anode.
[0079] In another exemplary embodiment, for example, the multilayer thin-film encapsulation consists of inorganic high-temperature stable or resilient materials. Using such an encapsulation increases the high temperature stability of the electrochemical device as compared with an electrochemical device that employs polymeric components in its encapsulation, such as is the case in the above-mentioned pressure-heat laminated encapsulation described by Snyder et al. in U.S. Patent No. 6,916,679.
[0080] Another exemplary embodiment of inorganic high-temperature stable or resilient materials may include a multilayer thin-film encapsulation having vacuum vapor phase deposited alternating layers. For example, a thin-film encapsulation may comprise or consist of 30 alternating 1000 A thick layers of the sequence ZrO2 /Zr / ZrO2 / Zr /... or ZrN / Zr / ZrN / Zr /..., although it is to be understood that different sized thickness, periods and materials may be used. These alternating layers may be deposited at less than about 1000C substrate temperature in one vacuum chamber pump-down from ambient pressures, for
example. Such an exemplary 30 multilayer thin-film encapsulation may, for example, be only about 3μm thick and high-temperature stable to far above about 300°C.
[0081] As those skilled in the art will appreciate, the mere thinness of such a thin-film encapsulation directly increases the energy, capacity, and power of a given electrochemical device per unit volume (volumetric energy, volumetric capacity, and volumetric power) compared with an electrochemical device that uses a pressure-heat laminated encapsulation, which is typically thicker by at least one order of magnitude than the presented thin-film encapsulation of about 3μm. For example, the volumetric quantities of energy, capacity, and power can increase three-fold when for a given electrochemical device of, for example, 150μm in total packaged thickness, which may comprise an actual electrochemical cell of, for example, lOμm in thickness, a, for example, 35μm thick substrate, and a, for example, lOOμm thick pressure-heat laminate, the encapsulation is replaced by a thin-film encapsulation of, for example, 3μm in thickness, which results in an overall thickness of the electrochemical device of 48μm.
[0082] FIG. 11 shows an electrochemical device according to an exemplary embodiment of the present invention, hi addition to the electrically conductive substrate 500, the positive cathode 510, the electrolyte film 520, the negative anode 530, the anode current collector 540, and the electrical insulation layer 550, this embodiment includes an encapsulation layer 570. This encapsulation may be, for example, a multilayer encapsulation as described above and as shown in FIG. 10. Between the encapsulation layer 570 and the anode 530, for example, a second LiPON layer 560 maybe interposed. The encapsulation layer 570 may be fabricated onto the anode 530, which may comprise metallic lithium. The softness of the anode 530 material may cause the encapsulation layer 570 to crack due to the mechanically weak fundament provided by the soft anode 530 and/or the stress imbalance at the interface of the anode 530 encapsulation 570. Once cracked, the encapsulation 570 may cause exposure of the sensitive anode 530 to the ambient, which may destroy the anode. Using a glassy LiPON (or derivative) modulator layer 560, for example, may mechanically stabilize the soft anode surface while chemically encapsulating it.
[0083] FIG. 11, the cathode 510 may be thick when compared to the relative sizes of the electrolyte 520, substrate 500 (and cathode current collector in some embodiments), anode 530, anode current collector 540, electrical insulation layer 550, modulating LiPON layer 560, and thin-film encapsulation 570.
[0084] The underlying LiPON electrolyte layer 520 together with the overlying LiPON modulator layer 560 confine the interposed anode 530 while protecting it, not only mechanically, but also chemically. In this configuration, a metallic anode 530, such as, for example, metallic Lithium, may be melted when heated above its melting point at about 1810C. Due to its spatial confinement, chemical protection, and inertness towards LiPON well above the melting point of lithium, the metallic lithium anode 530 remains fixed at location and intact as a negative anode material inside of the described electrochemical device. This engineering design also enables the described electrochemical device being used in solder refiow processing or flip chip processing.
[0085] Many materials may be used as the anode, for example, copper lithium alloy or solid solutions, such as, LixCu, LixZr, LixV, LixW, LixBe, LixBeyCu, etc. Those skilled in the art will recognize these and other materials that may be used for the anode. These alloys or solid solutions of lithium may offer stronger mechanical properties compared with soft metallic lithium, and thus may allow the direct deposition of the multilayer thin-film encapsulation 570 without the use of the above -described LiPON modulator layer 560 interposed between the soft negative metallic anode 530 and the multilayer thin-film encapsulation 570. In such case, the LiPON modulator layer 560 may be redundant.
[0086] In an example of the embodiment shown in FIG. 11, an electrochemical device maybe fabricated, for example, onto a 25.4mm x 25.4mm large aluminum substrate of 25μm in thickness (500), coated with a 80μm x 3.3 cm2 large LiCoO2 composite positive cathode consisting of 62 volume % OfLiCoO2 powder and the volume balance of polymeric binder and electronically conducting carbon black powder (510), a 1.5μm thin film of solid state LiPON electrolyte (520), a lOμm thick negative, metallic lithium anode (530), a 0.5μm thick nickel anode current collector (540), a 0.5μm thick ZrO2 electrical insulation layer (550), a 0.5μm thick LiPON modulator layer (560), and a 3μm thick multilayer thin-film encapsulation layer consisting of fifteen 1000 A thick Zr / 1000 A thick ZrO2 bi-stacks (570). In this example., the electrochemical device is 120μm thick at its thickest cross-section and provides 1OmAh of continuous capacity within the voltage range of 4.2 - 3.0V with an average voltage of 4.0V, which results in a volumetric energy of 520 Wh/liter for the fully packaged electrochemical device. When using a lOμm aluminum substrate instead of the 25 μm thick one, then the volumetric energy of this device increases from 520 Wh/liter to 590 Wh/liter.
[0087] In another exemplary embodiment, a barrier layer may be included. This barrier layer may be deposited onto a substrate, such as, for example, a metal foil substrate, wherein the barrier layer chemically separates the battery part (i.e., electrochemically active cell) from the substrate part of an electrochemical apparatus. The barrier may prevent diffusion of any contaminants entering the battery from the substrate as well as, for example, block ions from escaping the battery and diffusing into the substrate during both battery fabrication and during battery operating and storage conditions. Certain potentially suitable materials for a barrier layer may include poor ion conducting materials, for example, such as borides, carbides, diamond, diamond-like carbon, suicides, nitrides, phosphides, oxides, fluorides, chlorides, bromides, iodides, and any multinary compounds thereof. Of those compounds, electrically insulating materials may further prevent possible reactions between the substrate and the battery layers from occurring. For example, if a possible chemical reaction includes the diffusion of ions and electrons, an insulating barrier would provide a way to block the electrons, and thus prevent any such chemical reaction. However, a barrier layer may comprise electrically conducting materials as well, as long as they do not conduct any of the ions of the substrate or battery layer materials. For instance, ZrN is an effective conducting Ia3'er that will prevent ion conduction. In some cases metals, alloys, and/or semi- metals may serve as a sufficient barrier layer depending on the anneal temperatures applied during the battery fabrication process and substrate material used. The diffusion barrier layer may, for example, be single or multi-phase, crystalline, glassy, amorphous or any mixture thereof, although glassy and amorphous structures are preferred in some applications due to their lack of grain boundaries that would otherwise serve as locations for increased, but unwanted, ion and electron conduction.
[0088] A thin-film encapsulation layer, such as the one shown in FIGS. 10 & 11, may, for example, tent over the device. Therefore, a flexible encapsulation may, for example, be used to allow the device to expand and contract. The above-described glass-metal multilayer encapsulation possesses appropriate flexible properties, which can be tailored, for example, by changing the sputter deposition parameters, which then changes the densities of the glass and/or metal. Another approach to tuning the mechanical properties of the constituents of the thin-film encapsulation, and thus also the thin-film encapsulation itself may include changing the stoichiometry of one or more constituents of the thin-film encapsulant. For instance, ZrN can be changed to Zr2N, which is equivalent to depriving the particular composition of this layer of nitride. Alternatively, one can change the metals in the
stack. For example, instead of a Zr, ZrN, Zr, ZrN stack, one could fabricate a multilayer thin- film encapsulation consisting of Zr, AlN, Cr, TiN.
[0089] Some of the embodiments above discuss a thick positive cathode that is inexpensive and reliable. The thick cathode may also be configured with a thin electrolyte, a thin anode, and a thin encapsulation so as to maximize the volumetric densities of capacity, energy, and power of the resulting electrochemical device.
[0090] FIG. 12 shows another embodiment of the present invention, which depicts a configuration variant of the electrochemical device shown in FIG. 2 and termed inverted thin- film battery configuration. The negative anode 610 is chosen from the same materials and fabricated by the same methods as described for FIG. 2, when deposited directly onto substrate 600, which in turn is electrically conducting and chemically inert, such as, for example, Cu foil, to the anode 610. In this particular configuration, the substrate also serves as the anode current collector and negative terminal of a battery. If the substrate 600 is electrically insulating, then an additional anode current collector, consisting of, for example, Cu or Ni, may be interposed between said substrate 600 and the negative anode 610 (not shown). Electrical access to this anode current collector maybe accomplished, for example, by either extending the anode current collector beyond the edge of the encapsulation 650 or providing an opening in the substrate 600. The opening in the substrate may then be filled with a conductive material, such as a Cu paste, in a manner that this material makes electrical contact with the anode current collector. Using the same materials and methods as for the electrolyte in FIG. 2, the electrolyte 620 is deposited over the anode 610. Using the same materials and methods as for the positive cathode in FIG. 2, the positive cathode 630 is deposited over the electrolyte 620. To allow electrical access to the positive cathode 630, a cathode current collector 640, such as Al or Au, is fabricated on top of the positive cathode 630. If encapsulation 650 is used on an electrochemical device, then one may provide an opening 660 in encapsulation 650 to allow electrical access to the positive cathode 630.
[0091] Analogously, an electrochemical device maybe fabricated with inverted thin- film battery configuration using the elements, materials and methods described in regard to FIG. 11. Such an electrochemical device, for example, is shown in FIG. 13. First, a negative anode 710 is directly deposited onto a chemically inert substrate 700. To avoid short- circuiting of an electrochemical device, an electrically insulating layer 750 maybe
which may be partially coated with an electrolyte 720 and may entirely tent over the anode 710. After depositing the electrolyte 720, the positive cathode 730 may be deposited followed
by a cathode current collector 740. To employ a thin-film encapsulation 770 over the existing layers in the fabrication sequence of the electrochemical device, a mechanical and chemical modulation layer 760, for example, may be applied mainly over that area in the battery part of the electrochemical device which is defined by the cathode. Those skilled in the art will appreciate that the invention covers additional inverted configurations, which may be achieved by way of combining constituent parts of the non-inverted batteries described above.
[0092] In another embodiment, a barrier layer may be fabricated between the substrate and the battery part of the electrochemical device as described in U.S. patent application Serial No. 11/209,536, entitled Electrochemical Apparatus with Barrier Layer Protected Substrate, filed 23 August 2005, and incorporated by reference herein in its entirety. Depending on the material and configuration of the barrier layer, one or more additional current collectors may be fabricated onto the barrier layer so as to improve the electrical contact to the positive cathode, the negative anode or both.
[0093] The embodiments described above are exemplary only. One skilled in the art may recognize variations from the embodiments specifically described here, which are intended to be within the scope of this disclosure. As such, the invention is limited only by the following claims. Thus, it is intended that the present invention cover the modifications of this invention provided they come within the scope of the appended claims and their equivalents. Further, specific explanations or theories regarding the formation or performance of electrochemical devices according to the present invention are presented for explanation only and are not to be considered limiting with respect to the scope of the present disclosure or the claims.
Claims
1. An electrochemical device comprising: a positive cathode greater than about 4μm and less than about 200μm thick; an electrolyte less than about lOμm thick; and a negative anode less than about 30μm thick.
2. An electrochemical device comprising: a positive cathode greater than about 0.5μm and less than about 200μm thick; an electrolyte less than about lOμm thick; a negative anode less than about 30μm thick; and wherein said positive cathode is fabricated by a non-vapor phase deposition process.
3. The electrochemical device of claim 2, further comprising a substrate.
4. The electrochemical device of claim 3, wherein the cathode is adjacent to the substrate.
5. The electrochemical device of claim 1, further comprising a substrate, wherein the cathode is adjacent to the substrate.
6. The electrochemical device of claim 3, further comprising said substrate of up to about 50μm in thickness.
7. The electrochemical device of claim 3, further comprising said substrate of up to about lOμm in thickness.
8. The electrochemical device of claim 3, wherein said substrate is selected from the group of aluminum and aluminum alloys.
9. The electrochemical device of claim 3, wherein said substrate comprises a current collector.
10. The electrochemical device of claim 3 , further comprising a barrier layer on said substrate.
11. The electrochemical device of claim 10, wherein said barrier layer is adapted to prevent electrons from migrating between the substrate and either the anode or cathode.
12. The electrochemical device of claim 10, wherein said is barrier layer is adapted to prevent ions from migrating between the substrate and either the anode or cathode
13. The electrochemical device of claim 2, further comprising a current collector.
14. The electrochemical device of claim 2, wherein said cathode is greater than about 5μm and less than about lOOμm thick.
15. The electrochemical device of claim 2, wherein said cathode is greater than about 30μm and less than about 80μm thick.
16. The electrochemical device of claim 2, wherein said electrolyte is a thin-film electrolyte.
17. The electrochemical device of claim 2, wherein said cathode is deposited by slurry coating cathode powder material, binder material, and electrical conduction enhancer material.
18. The electrochemical device of claim 2, wherein said cathode is deposited using a Meyer rod coating technique.
19. The electrochemical device of claim 2, wherein said cathode is deposited using a direct roll coating technique.
20. The electrochemical device of claim 2, wherein said cathode is deposited using a reverse roll coating technique.
21. The electrochemical device of claim 2, wherein said cathode is deposited using a doctor blade technique.
22. The electrochemical device of claim 2, wherein said cathode is deposited by spin coating.
23. The electrochemical device of claim 2, wherein said cathode is deposited by electrophoretic deposition.
24. The electrochemical device of claim 2, wherein said cathode is deposited by an ink-jetting process.
25. The electrochemical device of claim 2, wherein said cathode is substantially absorbed with a material selected from the group of inert metal, inert alloy, and carbonaceous material.
26. The electrochemical device of claim 2, wherein said cathode comprises LiCoO2 or a derivative thereof.
27. The electrochemical device of claim 26, wherein said LiCoO2 or derivative thereof is doped with elements selected from the group of elements from Groups 1 through 17 of the periodic table.
28. The electrochemical device of claim 2, wherein said cathode comprises a material from the group consisting OfLiCoO2, LiMn2O4, LiMnO2, LiNiO2, LiFePO4, LiVO2, and any mixture thereof.
29. The electrochemical device of claim 2, wherein said cathode is formed into a structure with a plurality of vertical structures.
30. The electrochemical device of claim 29, wherein the plurality of vertical structures are formed using mechanical means.
31. The electrochemical device of claim 29, wherein the vertical structures have a height less than a maximum thickness of the cathode material.
32. The electrochemical device of claim 29, wherein said plurality of vertical structures are configured to decrease the average distance between any volume element within said cathode and the closest volume element of said electrolyte layer that is opposite to said cathode.
33. The electrochemical device of claim 2, wherein said cathode is a composite cathode further comprising at least carbonaceous material.
34. The electrochemical device of claim 33, wherein said composite cathode has a shape including a plurality of vertical structures.
35. The electrochemical device of claim 34, wherein said plurality of vertical structures are configured to decrease the average distance between any volume element within said cathode and the closest volume element of said electrolyte layer that is opposite to said cathode.
36. The electrochemical device of claim 2, wherein said electrolyte comprises lithium phosphorus oxynitride (LiPON).
37. The electrochemical device of claim 2, wherein said anode is selected from lithium, lithium alloy, a metal that can form a solid solution or a chemical compound with lithium, and any lithium-ion compound that can serve as a negative anode.
38. The electrochemical device of claim 2, wherein said electrolyte is deposited by a vacuum vapor phase growth method.
39. The electrochemical device of claim 2, wherein said electrolyte is deposited by a non- vapor phase method.
40. The electrochemical device of claim 2, further comprising an encapsulation formed with an encapsulation process selected from vacuum vapor phase grown thin-film encapsulation, pressure - heat lamination of protective polymer composites, pressure - heat lamination of metal foils coated with pressure-heat sensitive adhesive surfaces, and metal canning.
41. The electrochemical device of claim 2, further comprising an encapsulation grown by a vacuum vapor phase process.
42. The electrochemical device of claim 41, wherein said encapsulation consists of a multilayer stack of inorganic compounds and metals.
43. The electrochemical device of claim 41 , wherein said encapsulation is thinner than about lOμm.
44. The electrochemical device of claim 41, wherein said encapsulation is separated from the negative anode by an inteiposed modulation layer.
45. The electrochemical device of claim 44, wherein said modulation layer comprises LiPON.
46. The electrochemical device of claim 44, wherein said modulation layer consists of LiPON.
47. The electrochemical device of claim 2, further comprising an anode current collector.
48. The electrochemical device of claim 47, wherein a moisture barrier is interposed between said anode current collector and said electrolyte.
49. The electrochemical device of claim 48, wherein said moisture barrier comprises a material having moisture blocking properties, and is selected from metals, semi- metals, alloys, borid.es, carbides, diamond, diamond-like carbon, suicides, nitrides, phosphides, oxides, fluorides, chlorides, bromides, and iodides.
50. The electrochemical device of claim 48, wherein said moisture barrier comprises a material having moisture blocking properties, and is selected from any multinary compounds composed of borides, carbides, suicides, nitrides, phosphides, oxides, fluorides, chlorides, bromides, and iodides.
51. The electrochemical device of claim 48, wherein said moisture barrier comprises a material having moisture blocking properties, and is selected from high- temperature stable organic polymers and high-temperature stable silicones.
52. An electrochemical device comprising: a non- vapor phase deposited cathode; an anode; and an electrolyte less than about lOμm thick.
53. The electrochemical device of claim 52, wherein said cathode is greater than about 0.5μm and less than about 200μm thick.
54. The electrochemical device of claim 52, wherein said cathode is greater than about lOμm and less than about lOOμm thick.
55. The electrochemical device of claim 52, wherein said cathode is greater than about 30μm and less than about 80μm thick.
56. The electrochemical device of claim 52, wherein said anode is less than about 30μmthick.
57. The electrochemical device of claim 52, further comprising a substrate.
58. The electrochemical device of claim 57, wherein said substrate has up to about a 50μm thickness.
59. The electrochemical device of claim 57, wherein said substrate has up to about a lOμm thickness.
60. The electrochemical device of claim 57, wherein said substrate is selected from aluminum and aluminum alloys.
61. The electrochemical device of claim 52, wherein said electrolyte is a thin-film electrolyte.
62. The electrochemical device of claim 52, wherein said cathode is deposited by slurry coating cathode powder material, binder, carbonaceous material, carbon-type and electronic enhancer.
63. The electrochemical device of claim 52, wherein said cathode is deposited using a Meyer rod coating technique.
64. The electrochemical device of claim 52, wherein said cathode is deposited using a direct roll coating technique.
65. The electrochemical device of claim 52, wherein said cathode is deposited using a reverse roll coating technique.
66. The electrochemical device of claim 52, wherein said cathode is deposited by a doctor blade technique.
67. The electrochemical device of claim 52, wherein said cathode is deposited by spin coating.
68. The electrochemical device of claim 52, wherein said cathode is deposited by electrόphoretic deposition.
69. The electrochemical device of claim 52, wherein said cathode is deposited by an ink-jetting process.
70. The electrochemical device of claim 52, wherein said cathode is substantially absorbed with a material selected from the group of inert metal, inert alloy, and carbonaceous material.
71. The electrochemical device of claim 52, wherein said cathode comprises LiCoO2.
72. The electrochemical device of claim 52, wherein said cathode comprises a material selected from the group consisting OfLiCoO2, LiMn2O4, LiMnO2, LiNiO2, LiFePO4, LiVO2, and any mixture thereof.
73. The electrochemical device of claim 52, wherein said cathode is formed through mechanical means into a structure with a multitude of smaller vertical structures.
74. The electrochemical device of claim 73, wherein said multitude of smaller vertical structures decrease the average distance between any volume element within said cathode and the closest volume element of said electrolyte layer that is opposite to said cathode.
75. The electrochemical device of claim 52, wherein said cathode is a composite cathode further comprising at least carbonaceous material.
76. The electrochemical device of claim 75, wherein said composite cathode comprises a multitude of vertical structures.
77. The electrochemical device of claim 76, wherein said multitude of vertical structures decrease the average distance between any volume element within said cathode and the closest volume element of said electrolyte layer that is opposite to said cathode.
78. The electrochemical device of claim 52, wherein said electrolyte comprises Lithium Phosphorus Oxynitride (LiPON).
79. The electrochemical device of claim 52, wherein said anode is selected from the group consisting of lithium, lithium alloy, a metal that can form a solid solution or a chemical compound with lithium, and any lithium-ion compound that can serve as a negative anode.
80. The electrochemical device of claim 52, wherein said electrolyte is deposited by a vapor phase growth method.
81. The electrochemical device of claim 52, wherein said electrolyte is deposited by a non-vapor phase method.
82. The electrochemical device of claim 52, wherein said electrochemical device is encapsulated with an encapsulation process selected from vacuum vapor phase grown thin- film encapsulation, pressure - heat lamination of protective polymer composites, pressure - heat lamination of metal foils coated with pressure-heat sensitive adhesive surfaces, and metal canning.
83. The electrochemical device of claim 52, wherein said electrochemical device is encapsulated with an encapsulation grown by a vacuum vapor phase process.
84. The electrochemical device of claim 83, wherein said encapsulation consists of a multilayer stack of inorganic compounds and metals.
85. The electrochemical device of claim 83, wherein said encapsulation is thinner than lOμm.
86. The electrochemical device of claim 83, wherein said encapsulation is separated from the negative anode by an interposed modulation layer.
87. The electrochemical device of claim 86, wherein said modulation layer comprises LiPON.
88. The electrochemical device of claim 86, wherein said modulation layer consists of LiPON.
89. The electrochemical device of claim 52, further comprising a cathode current collector.
90. The electrochemical device of claim 52, further comprising an anode current collector.
91. The electrochemical device of claim 90, wherein said anode current collector covered, at least in part, by a moisture barrier.
92. The electrochemical device of claim 91 , wherein said moisture barrier comprises ZrO2.
93. A method of manufacturing an electrochemical device comprising: depositing a positive cathode that is greater than about 0.5 μm and less than about
200μm thick; depositing an electrolyte that is less than about lOμm thick; depositing a negative anode that is less than about 30μm thick; and depositing said positive cathode by a non- vapor phase deposition process.
94. The method of claim 93, wherein said cathode is deposited on a substrate.
95. The method of claim 94, further comprising depositing said cathode onto said substrate, which is equal or less than about 50μm thick.
96. The method of claim 94, further comprising depositing said cathode onto said substrate, which is equal or less than about lOμm thick.
97. The method of claim 94, further comprising depositing said cathode onto said substrate, and said substrate is selected from the group of aluminum and aluminum alloys.
98. The method of claim 94, wherein said substrate comprises a current collector.
99. The method of claim 93, further comprising depositing a barrier layer.
100. The method of claim 93, wherein said cathode is greater than about 5μm and less than about lOOμm thick.
101. The method of claim 93, wherein said cathode is greater than about 30μm and less than about 80μm thick.
102. The method of claim 93, wherein said electrolyte is a thin-film electrolyte.
103. The method of claim 93 , wherein said step of depositing a cathode comprises slurry coating of cathode powder material, binder material, and electrical conduction enhancer material.
104. The method of claim 93, wherein said step of depositing a cathode comprises a Meyer rod coating technique.
105. The method of claim 93 , wherein said step of depositing a cathode comprises a direct roll coating technique.
106. The method of claim 93, wherein said step of depositing a cathode comprises a reverse roll coating technique.
107. The method of claim 93, wherein said step of depositing a cathode comprises a blade application technique.
108. The method of claim 93, wherein said step of depositing a cathode comprises spin coating.
109. The method of claim 93 , wherein said step of depositing a cathode comprises electrophoretic deposition.
110. The method of claim 93 , wherein said step of depositing a cathode comprises ink-jetting.
111. The method of claim 93, wherein said step of depositing a cathode comprises a) coating said cathode in its finished or unfinished state with a material selected from the group of inert metal and alloy; and b) applying sufficient heat to substantially absorb said material into said cathode.
112. The method of claim 93, wherein said cathode comprises LiCoO2 and doped derivates thereof wherein the doping elements are selected from the group of elements from the Groups 1 through 17 of the periodic table.
113. The method of claim 93, wherein said cathode comprises a material from the group consisting OfLiCoO2, LiMn2O4, LiMnO2, LiNiO2, LiFePO4, LiVO2, and any mixture thereof.
114. The method of claim 93, wherein said cathode is formed through mechanical means into a structure with a multitude of vertical structures.
115. The method of claim 114, wherein said multitude of vertical structures decrease the average distance between any volume element within said cathode and the closest volume element of said electrolyte layer that is opposite to said cathode.
116. The method of claim 114, wherein a height of said multitude of vertical structures is less than the maximum thickness of said cathode.
117. The method of claim 93, wherein said cathode is formed as a composite cathode further comprising at least carbonaceous material.
118. The method of claim 117, wherein said composite cathode is fabricated into a structure with a multitude of vertical structures.
119. The method of claim 118, wherein said multitude of vertical structures decrease the average distance between any volume element within said cathode and the closest volume element of said electrolyte layer that is opposite to said cathode.
120. The method of claim 93, wherein said electrolyte comprises lithium phosphorus oxynitride (LiPON).
121. The method of claim 93 , wherein said anode comprises a material selected from the group consisting of lithium, lithium alloy, a metal that can form a solid solution or a chemical compound with lithium, and any lithium-ion compound that can serve as a negative anode.
122. The method of claim 93 , wherein said step of depositing an electrolyte comprises vacuum vapor phase growth method.
123. The method of claim 93, wherein said step of depositing an electrolyte comprises a non- vapor phase method.
124. The method of claim 93 , further comprising encapsulating said electrochemical device employing an encapsulation process selected from vacuum vapor phase grown thin-film encapsulation, pressure - heat lamination of protective polymer composites, pressure - heat lamination of metal foils coated with pressure-heat sensitive adhesive surfaces, and metal canning.
125. The method of claim 93, wherein said electrochemical device is encapsulated with an encapsulation grown by a vacuum vapor phase process.
126. The method of claim 125, further comprising depositing said encapsulation as a multilayer stack of inorganic compounds and metals.
127. The method of claim 125, further comprising depositing said encapsulation thinner than about lOμm.
128. The method of claim 125, further comprising separating said encapsulation from the negative anode by an interposed modulation layer.
129. The method of claim 128, further comprising depositing said modulation layer as LiPON.
130. The method of claim 93, further comprising depositing a cathode current collector.
131. The method of claim 93 , further comprising depositing an anode current collector.
132. The method of claim 131, further comprising depositing a moisture barrier between said anode current collector and said electrolyte.
133. The method of claim 132, wherein said moisture barrier comprises a material having moisture blocking properties, and is selected from the group of metals, semi-metals, alloys, borides, carbides, diamond, diamond-like carbon, suicides, nitrides, phosphides, oxides, fluorides, chlorides, bromides, and iodides.
134. The method of claim 132, wherein said moisture barrier comprises a material having moisture blocking properties, and is selected from the group of any multinary compounds composed of borides, carbides, suicides, nitrides, phosphides, oxides, fluorides, chlorides, bromides, and iodides.
135. The method of claim 132, wherein said moisture barrier comprises a material having moisture blocking properties, and is selected from the group of high-temperature stable organic polymers and high-temperature stable silicones.
136. A method of manufacturing an electrochemical device comprising: depositing a cathode using a non-vapor phase deposition process; depositing an electrolyte that is less than about lOμm thick; and depositing an anode.
137. The method of claim 136, wherein said cathode is greater than about 0.5μm and less than about 200 μm thick.
138. The method of claim 136, wherein said cathode is greater than about lOμm and less than about lOOμm thick.
139. The method of claim 136, wherein said cathode is greater than about 30μm and less than about 80μm thick.
140. The method of claim 136, wherein said anode is less than about 30μm thick.
141. The method of claim 136, further comprising providing a substrate.
142. The method of claim 141, further comprising said substrate of up to 50μm in thickness.
143. The method of claim 141, further comprising said substrate of up to lOμm in thickness.
144. The method of claim 141 , wherein said substrate is selected from the group of aluminum and aluminum alloys.
145. The method of claim 136, wherein said electrolyte is a thin-film electrolyte.
146. The method of claim 136, wherein said non-vapor phase deposition process comprises slurry coating cathode powder material, binder, and electrical conduction enhancer material.
147. The method of claim 136, wherein said non-vapor phase deposition process comprises a Meyer rod coating technique.
148. The method of claim 136, wherein said non- vapor phase deposition process comprises a direct roll coating technique.
149. The method of claim 136, wherein said non-vapor phase deposition process comprises a reverse roll coating technique.
150. The method of claim 136, wherein said non-vapor phase deposition process comprises a blade application technique.
151. The method of claim 136, wherein said non- vapor phase deposition process comprises spin coating.
152. The method of claim 136, wherein said non-vapor phase deposition process comprises electrophoretic deposition.
153. The method of claim 136, wherein said non- vapor phase deposition process comprises ink-jetting.
154. The method of claim 136, wherein said step of depositing a cathode comprises a) coating said cathode in its finished or unfinished state with a material selected from the group of inert metal and alloy; and b) applying sufficient heat so as to substantially absorb said material into said cathode.
155. The method of claim 136, wherein said cathode comprises LiCoO2.
156. The method of claim 136, wherein said cathode comprises a material from the group OfLiCoO2, LiMn2O4, LiMnO2, LiNiO2, LiFePO4, LiVO2, and any mixture thereof.
157. The method of claim 136, further comprises forming said cathode through mechanical means into a structure with a multitude of smaller vertical structures.
158. The method of claim 157, wherein said multitude of smaller vertical structures decrease the average distance between any volume element within said cathode and the closest volume element of said electrolyte layer that is opposite to said cathode.
159. The method of claim 136, wherein said cathode is formed as a composite cathode further comprising at least carbonaceous material.
160. The method of claim 159, wherein said composite cathode is fabricated into a structure with a multitude of smaller vertical structures.
161. The method of claim 160, wherein said multitude of vertical structures decrease the average distance between any volume element within said cathode and the closest volume element of said electrolyte layer that is opposite to said cathode.
162. The method of claim 136, wherein said electrolyte comprises Lithium Phosphorous Oxynitride (LiPON).
163. The method of claim 136, wherein said anode is selected from the group of lithium, lithium alloy, a metal that can form a solid solution or a chemical compound with lithium, and any lithium-ion compound that can serve as a negative anode.
164. The method of claim 136, wherein said step of depositing an electrolyte comprises a vapor phase growth method.
165. The method of claim 136, wherein said step of depositing an electrolyte comprises a non- vapor phase method.
166. The method of claim 136, further comprising encapsulating said electrochemical device employing an encapsulation process selected from the groupof vacuum vapor phase grown thin-film encapsulation, pressure - heat lamination of protective polymer composites, pressure - heat lamination of metal foils coated with pressure-heat sensitive adhesive surfaces, and metal canning.
167. The method of claim 136, further comprising encapsulating said electrochemical device with an encapsulation that is grown by a vacuum vapor phase process.
168. The method of claim 167, further comprising fabricating said encapsulation by a multilayer stack of inorganic compounds and metals.
169. The method of claim 167, wherein said encapsulation is deposited thinner than lOμm.
170. The method of claim 167, further comprising separating said encapsulation from the negative anode by an interposed modulation layer.
171. The method of claim 170, wherein said modulation layer consists of LiPON.
172. The method of claim 136, further comprising depositing a cathode current collector.
173. The method of claim 136, further comprising depositing an anode current collector on top of the thin electrolyte layer.
174. The method of claim 173 , further comprising depositing a moisture barrier between said thin electrolyte layer and said anode current collector.
175. The method of claim 174, wherein said moisture barrier comprises ZrO2.