WO2007050062A1 - Procedes de production de microspheres a faible densite - Google Patents

Procedes de production de microspheres a faible densite Download PDF

Info

Publication number
WO2007050062A1
WO2007050062A1 PCT/US2005/038720 US2005038720W WO2007050062A1 WO 2007050062 A1 WO2007050062 A1 WO 2007050062A1 US 2005038720 W US2005038720 W US 2005038720W WO 2007050062 A1 WO2007050062 A1 WO 2007050062A1
Authority
WO
WIPO (PCT)
Prior art keywords
low
microspheres
viscosity
primary component
surface tension
Prior art date
Application number
PCT/US2005/038720
Other languages
English (en)
Inventor
Steven A. Benson
Jason Laumb
Don Mccollor
Jim Tibbetts
Original Assignee
University Of North Dakota
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by University Of North Dakota filed Critical University Of North Dakota
Priority to PCT/US2005/038720 priority Critical patent/WO2007050062A1/fr
Publication of WO2007050062A1 publication Critical patent/WO2007050062A1/fr

Abstract

La présente invention se rapporte à un procédé permettant de synthétiser des microsphères à faible densité, qui consiste à traiter des mélanges de charges préparés de manière précise dans un réacteur à lit entraîné dans des conditions partiellement oxydantes, avec un historique temps-température contrôlé. L'invention a également trait à des outils de recherche permettant de concevoir les meilleurs microsphères et procédés de production possibles.
PCT/US2005/038720 2005-10-26 2005-10-26 Procedes de production de microspheres a faible densite WO2007050062A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/US2005/038720 WO2007050062A1 (fr) 2005-10-26 2005-10-26 Procedes de production de microspheres a faible densite

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/US2005/038720 WO2007050062A1 (fr) 2005-10-26 2005-10-26 Procedes de production de microspheres a faible densite

Publications (1)

Publication Number Publication Date
WO2007050062A1 true WO2007050062A1 (fr) 2007-05-03

Family

ID=37968079

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2005/038720 WO2007050062A1 (fr) 2005-10-26 2005-10-26 Procedes de production de microspheres a faible densite

Country Status (1)

Country Link
WO (1) WO2007050062A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8261577B2 (en) 2009-12-21 2012-09-11 3M Innovative Properties Company Method for making hollow microspheres
US9266764B2 (en) 2010-12-20 2016-02-23 3M Innovative Properties Company Hollow microspheres and method of making hollow microspheres
CN107601828A (zh) * 2017-10-27 2018-01-19 唐山宏微新材料有限公司 一种空心玻璃微球及其制备方法
CN114772988A (zh) * 2022-05-09 2022-07-22 许军 一种轻质防火保温砂浆及其制备方法

Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2978340A (en) * 1957-10-22 1961-04-04 Standard Oil Co Hollow glass particles and method of producing the same
US3365315A (en) * 1963-08-23 1968-01-23 Minnesota Mining & Mfg Glass bubbles prepared by reheating solid glass partiles
US3888957A (en) * 1972-02-03 1975-06-10 Philadelphia Quartz Co Method of making hollow spheres by spray drying
US4336338A (en) * 1980-08-15 1982-06-22 The United States Of America As Represented By The United States Department Of Energy Hollow microspheres of silica glass and method of manufacture
US4391646A (en) * 1982-02-25 1983-07-05 Minnesota Mining And Manufacturing Company Glass bubbles of increased collapse strength
US4767726A (en) * 1987-01-12 1988-08-30 Minnesota Mining And Manufacturing Company Glass microbubbles
US5145659A (en) * 1985-05-14 1992-09-08 Mobil Oil Corporation Preformed matrices containing zeolites
US5397759A (en) * 1978-08-28 1995-03-14 Torobin; Leonard B. Hollow porous microspheres made from dispersed particle compositions
US5501871A (en) * 1992-10-30 1996-03-26 Innovation Associates, Inc. Thermal insulating material and method of manufacturing same
US5529596A (en) * 1994-05-02 1996-06-25 Owens-Corning Fiberglas Technology, Inc. Method for making dual-glass fibers by causing one glass to flow around another glass as they are spun from a rotating spinner
US6656861B1 (en) * 1999-11-03 2003-12-02 Johns Manville International, Inc. Glass composition for ultrafine fiber formation
US20040080063A1 (en) * 2002-08-23 2004-04-29 Amlan Datta Synthetic microspheres and methods of making same
US6942783B2 (en) * 2003-05-19 2005-09-13 Engelhard Corporation Enhanced FCC catalysts for gas oil and resid applications

Patent Citations (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3030215A (en) * 1957-10-22 1962-04-17 Standard Oil Co Hollow glass particles and method of producing the same
US2978340A (en) * 1957-10-22 1961-04-04 Standard Oil Co Hollow glass particles and method of producing the same
US3365315A (en) * 1963-08-23 1968-01-23 Minnesota Mining & Mfg Glass bubbles prepared by reheating solid glass partiles
US3888957A (en) * 1972-02-03 1975-06-10 Philadelphia Quartz Co Method of making hollow spheres by spray drying
US5397759A (en) * 1978-08-28 1995-03-14 Torobin; Leonard B. Hollow porous microspheres made from dispersed particle compositions
US4336338A (en) * 1980-08-15 1982-06-22 The United States Of America As Represented By The United States Department Of Energy Hollow microspheres of silica glass and method of manufacture
US4391646A (en) * 1982-02-25 1983-07-05 Minnesota Mining And Manufacturing Company Glass bubbles of increased collapse strength
US5145659A (en) * 1985-05-14 1992-09-08 Mobil Oil Corporation Preformed matrices containing zeolites
US4767726A (en) * 1987-01-12 1988-08-30 Minnesota Mining And Manufacturing Company Glass microbubbles
US5501871A (en) * 1992-10-30 1996-03-26 Innovation Associates, Inc. Thermal insulating material and method of manufacturing same
US5529596A (en) * 1994-05-02 1996-06-25 Owens-Corning Fiberglas Technology, Inc. Method for making dual-glass fibers by causing one glass to flow around another glass as they are spun from a rotating spinner
US6656861B1 (en) * 1999-11-03 2003-12-02 Johns Manville International, Inc. Glass composition for ultrafine fiber formation
US20040080063A1 (en) * 2002-08-23 2004-04-29 Amlan Datta Synthetic microspheres and methods of making same
US6942783B2 (en) * 2003-05-19 2005-09-13 Engelhard Corporation Enhanced FCC catalysts for gas oil and resid applications

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8261577B2 (en) 2009-12-21 2012-09-11 3M Innovative Properties Company Method for making hollow microspheres
US9266764B2 (en) 2010-12-20 2016-02-23 3M Innovative Properties Company Hollow microspheres and method of making hollow microspheres
CN107601828A (zh) * 2017-10-27 2018-01-19 唐山宏微新材料有限公司 一种空心玻璃微球及其制备方法
CN107601828B (zh) * 2017-10-27 2020-12-22 唐山宏微新材料有限公司 一种空心玻璃微球及其制备方法
CN114772988A (zh) * 2022-05-09 2022-07-22 许军 一种轻质防火保温砂浆及其制备方法

Similar Documents

Publication Publication Date Title
TW200422276A (en) Synthetic hollow microspheres
AU2014290627B2 (en) Glass microbubbles, raw product, and methods of making the same
WO2015053723A1 (fr) Utilisation en tant que combustible solide de schiste ou de cendres obtenus par des procédés de démantèlement de schiste bitumineux avec ou sans additifs
CN103880360A (zh) 一种石英陶瓷闭孔空心微珠制备油井固井水泥试块的方法
Zhang et al. Phase evolution and properties of glass ceramic foams prepared by bottom ash, fly ash and pickling sludge
Tang et al. Self-foaming high strength artificial lightweight aggregates derived from solid wastes: expansion mechanism and environmental impact
WO2007050062A1 (fr) Procedes de production de microspheres a faible densite
JPH0246534B2 (fr)
US4057605A (en) Manufacture of light granular materials
KR102279744B1 (ko) 실리카 퓸을 사용한 석탄재 기반 지오폴리머 폼의 제조방법
Narani et al. Wood fly ash and blast furnace slag management by alkali-activation: Trace elements solidification and composite application
WO2007050078A1 (fr) Procedes a haut rendement permettant de produire des microspheres a faible densite
JP2534831B2 (ja) 微細中空ガラス球状体の製造方法
CN104676595B (zh) 一种降低生活垃圾焚烧厂飞灰量及飞灰毒性的方法
Geng et al. Properties of artificial lightweight aggregates prepared from coal and biomass co-fired fly ashes and sewage sludge fly ash
JPH11116299A (ja) 人工軽量骨材およびその製造方法
CN103803892B (zh) 氧化锆陶瓷复合微珠制备低密度油井固井水泥试块的方法
Bethanis et al. Production of lightweight aggregate from incinerator bottom ash and pulverised fuel ash
CN103803890B (zh) 陶瓷复合微珠制备低密度油井固井水泥试块的方法
JP2514865B2 (ja) 無機質発泡体粒子の製造法
CN103803889B (zh) 高抗压石英陶瓷复合微珠制备油井固井水泥试块的方法
US7506523B2 (en) Method of making hollow inorganic microspheres, and products made thereby
PL234361B1 (pl) Sposób wytwarzania kruszywa lekkiego z popiołów lotnych i kruszywo lekkie
JPS61251551A (ja) 無機質発泡体粒子およびその製造法
US20060096317A1 (en) Method of making hollow glassy and ceramic microspheres, and products made thereby

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application
NENP Non-entry into the national phase

Ref country code: DE

DPE1 Request for preliminary examination filed after expiration of 19th month from priority date (pct application filed from 20040101)
122 Ep: pct application non-entry in european phase

Ref document number: 05846426

Country of ref document: EP

Kind code of ref document: A1