WO2006073617A1 - Matériau en boucle non tissé - Google Patents

Matériau en boucle non tissé Download PDF

Info

Publication number
WO2006073617A1
WO2006073617A1 PCT/US2005/043012 US2005043012W WO2006073617A1 WO 2006073617 A1 WO2006073617 A1 WO 2006073617A1 US 2005043012 W US2005043012 W US 2005043012W WO 2006073617 A1 WO2006073617 A1 WO 2006073617A1
Authority
WO
WIPO (PCT)
Prior art keywords
fibers
elastic
loop
composite
fiber
Prior art date
Application number
PCT/US2005/043012
Other languages
English (en)
Inventor
Paul Theodore Van Gompel
Yung Hsiang Huang
Original Assignee
Kimberly-Clark Worldwide, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kimberly-Clark Worldwide, Inc. filed Critical Kimberly-Clark Worldwide, Inc.
Publication of WO2006073617A1 publication Critical patent/WO2006073617A1/fr

Abstract

L’invention concerne des matériaux en boucle non tissés convenant comme composant femelle des systèmes de fixation à boucle et crochet. Dans certains modes de réalisation, les matériaux en boucle peuvent comprendre une couche de trame non tissée fibreuse et une couche de substrat élastique, ou bien ils peuvent comporter des fibres élastiques coformées avec d’autres fibres. L’invention concerne également un procédé de fabrication des matériaux en boucle non tissés. De tels matériaux en boucle non tissés sont extrêmement utiles pour les systèmes de fermeture ou de fixation à boucle et crochet dans ou sur les produits d’hygiène personnelle, les vêtements de protection, les produits médicaux, les bandages et autres.
PCT/US2005/043012 2004-12-30 2005-11-28 Matériau en boucle non tissé WO2006073617A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US11/027,390 US20060148359A1 (en) 2004-12-30 2004-12-30 Nonwoven loop material
US11/027,390 2004-12-30

Publications (1)

Publication Number Publication Date
WO2006073617A1 true WO2006073617A1 (fr) 2006-07-13

Family

ID=36123308

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2005/043012 WO2006073617A1 (fr) 2004-12-30 2005-11-28 Matériau en boucle non tissé

Country Status (2)

Country Link
US (1) US20060148359A1 (fr)
WO (1) WO2006073617A1 (fr)

Families Citing this family (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7875014B2 (en) * 2003-12-15 2011-01-25 Kimberly-Clark Worldwide, Inc. Absorbent garment having a garment shell
US8052666B2 (en) * 2004-12-30 2011-11-08 Kimberly-Clark Worldwide, Inc. Fastening system having elastomeric engaging elements and disposable absorbent article made therewith
WO2008028106A2 (fr) * 2006-08-31 2008-03-06 Avery Dennison Corporation Composant de couche-culotte élastique
US8080198B2 (en) * 2006-10-20 2011-12-20 Avery Dennison Corporation Elastic diaper component
US7790264B2 (en) 2007-04-17 2010-09-07 Aplix, Inc. Loop material for loop and hook type fastener used in a disposable article or garment
US20090311465A1 (en) * 2008-06-11 2009-12-17 De Jong Johannes H A Stretchable laminate
US9394637B2 (en) 2012-12-13 2016-07-19 Jacob Holm & Sons Ag Method for production of a hydroentangled airlaid web and products obtained therefrom
EP2862708B1 (fr) * 2013-10-18 2016-04-27 Mondi Gronau GmbH Élément de fermeture formant une boucle pour fermetures à crochet et procédé de fabrication d'un élément de fermeture
MY194492A (en) * 2016-08-08 2022-11-30 3M Innovative Properties Company Sheet Of Loop Material, Method and Apparatus for Forming Same

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4107364A (en) * 1975-06-06 1978-08-15 The Procter & Gamble Company Random laid bonded continuous filament cloth
WO1997023348A2 (fr) * 1995-12-21 1997-07-03 Kimberly-Clark Worldwide, Inc. Materiau stratifie
US5683787A (en) * 1992-12-18 1997-11-04 Corovin Gmbh Multilayered elastic sheet structure and process for producing a multilayered elastic sheet structure
DE19647459A1 (de) * 1996-11-16 1998-05-20 Mildenberger & Willing Verpack Flächengebilde aus einer gummielastischen Schicht mit aufliegender Vliesschicht und Verfahren zu seiner Herstellung
WO1998052458A1 (fr) * 1997-05-23 1998-11-26 The Procter & Gamble Company Structures tridimensionnelles utiles en tant que textiles d'entretien
EP1069223A1 (fr) * 1999-07-12 2001-01-17 Uni-Charm Corporation Feuille composite étirable élastiquement

Family Cites Families (77)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3849241A (en) * 1968-12-23 1974-11-19 Exxon Research Engineering Co Non-woven mats by melt blowing
DE2048006B2 (de) * 1969-10-01 1980-10-30 Asahi Kasei Kogyo K.K., Osaka (Japan) Verfahren und Vorrichtung zur Herstellung einer breiten Vliesbahn
DE1950669C3 (de) * 1969-10-08 1982-05-13 Metallgesellschaft Ag, 6000 Frankfurt Verfahren zur Vliesherstellung
CA948388A (en) * 1970-02-27 1974-06-04 Paul B. Hansen Pattern bonded continuous filament web
US3708361A (en) * 1970-11-16 1973-01-02 Kimberly Clark Co Method of making elastic high-loft non-woven fabric with improved cross directional strength
US4100324A (en) * 1974-03-26 1978-07-11 Kimberly-Clark Corporation Nonwoven fabric and method of producing same
US4209563A (en) * 1975-06-06 1980-06-24 The Procter & Gamble Company Method for making random laid bonded continuous filament cloth
US4340563A (en) * 1980-05-05 1982-07-20 Kimberly-Clark Corporation Method for forming nonwoven webs
US4488928A (en) * 1983-05-16 1984-12-18 Kimberly-Clark Corporation Method and apparatus for forming soft, bulky absorbent webs and resulting product
US4795668A (en) * 1983-10-11 1989-01-03 Minnesota Mining And Manufacturing Company Bicomponent fibers and webs made therefrom
CA1341430C (fr) * 1984-07-02 2003-06-03 Kenneth Maynard Enloe Couche avec poches laterales elasticisees
US4818464A (en) * 1984-08-30 1989-04-04 Kimberly-Clark Corporation Extrusion process using a central air jet
US4761318A (en) * 1985-04-15 1988-08-02 Minnesota Mining And Manufacturing Company Loop fastener portion with thermoplastic resin attaching and anchoring layer
US4640726A (en) * 1985-06-27 1987-02-03 Kimberly-Clark Corporation Heat activation process and apparatus for heat shrinkable material
US4663220A (en) * 1985-07-30 1987-05-05 Kimberly-Clark Corporation Polyolefin-containing extrudable compositions and methods for their formation into elastomeric products including microfibers
JPS62111410U (fr) * 1985-12-30 1987-07-16
US4834742A (en) * 1986-09-03 1989-05-30 Kimberly-Clark Corporation Fastening system for a disposable absorbent garment
US4725473A (en) * 1986-11-25 1988-02-16 Kimberly-Clark Corporation Cloth-like, liquid impervious composite material and method for making the same
US5032122A (en) * 1987-04-24 1991-07-16 The Procter & Gamble Company Loop fastening material for fastening device and method of making same
US5380313A (en) * 1987-06-19 1995-01-10 The Proctor & Gamble Company Loop fastening material for fastening device and method of making same
US4940464A (en) * 1987-12-16 1990-07-10 Kimberly-Clark Corporation Disposable incontinence garment or training pant
US5226992A (en) * 1988-09-23 1993-07-13 Kimberly-Clark Corporation Process for forming a composite elastic necked-bonded material
US4984339A (en) * 1988-10-20 1991-01-15 Velcro Industries B.V. Hook for hook and loop fasteners
JP2682130B2 (ja) * 1989-04-25 1997-11-26 三井石油化学工業株式会社 柔軟な長繊維不織布
US5224405A (en) * 1990-04-06 1993-07-06 Kimberly-Clark Corporation Process for rotating and placing a strip of material on a substrate
US5104116A (en) * 1990-04-06 1992-04-14 Kimberly-Clark Corporation Applicator apparatus and process for rotating and placing a strip of material on a substrate
US5046272A (en) * 1990-05-01 1991-09-10 Kimberly-Clark Corporation Fluid-operated stabilizing apparatus and method
DE9006958U1 (de) * 1990-06-22 1991-10-17 Parabeam Industrie- En Handelsonderneming B.V., Helmond Stoffbahn für die Verbundbauweise
US5272236A (en) * 1991-10-15 1993-12-21 The Dow Chemical Company Elastic substantially linear olefin polymers
DK132191D0 (da) * 1991-07-05 1991-07-05 Danaklon As Fibre og fremstilling deraf
US5326612A (en) * 1991-05-20 1994-07-05 The Procter & Gamble Company Nonwoven female component for refastenable fastening device and method of making the same
US5278272A (en) * 1991-10-15 1994-01-11 The Dow Chemical Company Elastic substantialy linear olefin polymers
US5470639A (en) * 1992-02-03 1995-11-28 Fiberweb North America, Inc. Elastic nonwoven webs and method of making same
US5997989A (en) * 1992-02-03 1999-12-07 Bba Nonwovens Simpsonville, Inc. Elastic nonwoven webs and method of making same
US5382400A (en) * 1992-08-21 1995-01-17 Kimberly-Clark Corporation Nonwoven multicomponent polymeric fabric and method for making same
US5405682A (en) * 1992-08-26 1995-04-11 Kimberly Clark Corporation Nonwoven fabric made with multicomponent polymeric strands including a blend of polyolefin and elastomeric thermoplastic material
US5336552A (en) * 1992-08-26 1994-08-09 Kimberly-Clark Corporation Nonwoven fabric made with multicomponent polymeric strands including a blend of polyolefin and ethylene alkyl acrylate copolymer
US5350624A (en) * 1992-10-05 1994-09-27 Kimberly-Clark Corporation Abrasion resistant fibrous nonwoven composite structure
IT1256260B (it) * 1992-12-30 1995-11-29 Montecatini Tecnologie Srl Polipropilene atattico
US5339499A (en) * 1993-02-16 1994-08-23 Velcro Industries B.V. Hook design for a hook and loop fastener
US5332613A (en) * 1993-06-09 1994-07-26 Kimberly-Clark Corporation High performance elastomeric nonwoven fibrous webs
US5669900A (en) * 1993-11-03 1997-09-23 Kimberly-Clark Worldwide, Inc. Spunbond loop material for hook and loop fastening systems
CA2120645C (fr) * 1993-12-21 2004-02-10 Andrew Scott Burnes Structure resiliente pour fermeture a bouclettes de nylon
US5615460A (en) * 1994-06-06 1997-04-01 The Procter & Gamble Company Female component for refastenable fastening device having regions of differential extensibility
US5595567A (en) * 1994-08-09 1997-01-21 The Procter & Gamble Company Nonwoven female component for refastenable fastening device
US5795350A (en) * 1994-12-29 1998-08-18 The Procter & Gamble Company Disposable absorbent article having a mechanical fastener
US5624427A (en) * 1995-01-18 1997-04-29 The Procter & Gamble Company Female component for refastenable fastening device
US5539056A (en) * 1995-01-31 1996-07-23 Exxon Chemical Patents Inc. Thermoplastic elastomers
US5897547A (en) * 1995-02-16 1999-04-27 The Procter & Gamble Company Absorbent article with elastically extensible landing member
US5858515A (en) * 1995-12-29 1999-01-12 Kimberly-Clark Worldwide, Inc. Pattern-unbonded nonwoven web and process for making the same
US5766389A (en) * 1995-12-29 1998-06-16 Kimberly-Clark Worldwide, Inc. Disposable absorbent article having a registered graphic and process for making
US5735840A (en) * 1996-09-20 1998-04-07 The Procter & Gamble Company Disposable diaper with integral backsheet landing zone
US6015764A (en) * 1996-12-27 2000-01-18 Kimberly-Clark Worldwide, Inc. Microporous elastomeric film/nonwoven breathable laminate and method for making the same
US6111163A (en) * 1996-12-27 2000-08-29 Kimberly-Clark Worldwide, Inc. Elastomeric film and method for making the same
US5935512A (en) * 1996-12-30 1999-08-10 Kimberly-Clark Worldwide, Inc. Nonwoven process and apparatus
US5853635A (en) * 1997-06-18 1998-12-29 Kimberly-Clark Worldwide, Inc. Method of making heteroconstituent and layered nonwoven materials
US5888607A (en) * 1997-07-03 1999-03-30 Minnesota Mining And Manufacturing Co. Soft loop laminate and method of making
US5921977A (en) * 1997-08-15 1999-07-13 The Proctor & Gamble Company Disposable absorbent article having an extensible landing member for engaging with a hook-type fastening member
US6342285B1 (en) * 1997-09-03 2002-01-29 Velcro Industries B.V. Fastener loop material, its manufacture, and products incorporating the material
US6329016B1 (en) * 1997-09-03 2001-12-11 Velcro Industries B.V. Loop material for touch fastening
US6869659B2 (en) * 1997-09-03 2005-03-22 Velcro Industries B.V. Fastener loop material, its manufacture, and products incorporating the material
US5932497A (en) * 1997-09-15 1999-08-03 Kimberly-Clark Worldwide, Inc. Breathable elastic film and laminate
US5997981A (en) * 1997-09-15 1999-12-07 Kimberly-Clark Worldwide, Inc. Breathable barrier composite useful as an ideal loop fastener component
US6245401B1 (en) * 1999-03-12 2001-06-12 Kimberly-Clark Worldwide, Inc. Segmented conformable breathable films
US6225243B1 (en) * 1998-08-03 2001-05-01 Bba Nonwovens Simpsonville, Inc. Elastic nonwoven fabric prepared from bi-component filaments
US6217693B1 (en) * 1998-08-05 2001-04-17 Ykk Corporation Of America Method of making nonwoven loop material for hook and loop fasteners
US6164950A (en) * 1999-01-08 2000-12-26 Firma Carl Freudenberg Device for producing spunbonded nonwovens
US6461457B1 (en) * 1999-06-30 2002-10-08 Kimberly-Clark Worldwide, Inc. Dimensionally stable, breathable, stretch-thinned, elastic films
JP3768769B2 (ja) * 2000-03-30 2006-04-19 ユニ・チャーム株式会社 弾性伸縮性複合シートおよびその製造方法
JP3662469B2 (ja) * 2000-03-31 2005-06-22 ユニ・チャーム株式会社 弾性伸縮性複合シートの製造方法
TW496782B (en) * 2000-09-25 2002-08-01 Winbond Electronics Corp Appliance for changing roller sponge
US6756327B2 (en) * 2000-10-31 2004-06-29 Kimberly-Clark Worldwide, Inc. Loop fastening component made from thermally retracted materials
US7297139B2 (en) * 2001-07-05 2007-11-20 Kimberly-Clark Worldwide, Inc. Refastenable absorbent garment
US7805818B2 (en) * 2001-09-05 2010-10-05 The Procter & Gamble Company Nonwoven loop member for a mechanical fastener
US20030232170A1 (en) * 2002-06-12 2003-12-18 Gillette Samuel Mark Spunlaced loop material for a refastenable fastening device and methods of making same
US20040110442A1 (en) * 2002-08-30 2004-06-10 Hannong Rhim Stretchable nonwoven materials with controlled retraction force and methods of making same
US20040102749A1 (en) * 2002-11-21 2004-05-27 Kimberly-Clark Worldwide, Inc. Absorbent article with low coefficient of friction between materials of differential tensions

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4107364A (en) * 1975-06-06 1978-08-15 The Procter & Gamble Company Random laid bonded continuous filament cloth
US5683787A (en) * 1992-12-18 1997-11-04 Corovin Gmbh Multilayered elastic sheet structure and process for producing a multilayered elastic sheet structure
WO1997023348A2 (fr) * 1995-12-21 1997-07-03 Kimberly-Clark Worldwide, Inc. Materiau stratifie
DE19647459A1 (de) * 1996-11-16 1998-05-20 Mildenberger & Willing Verpack Flächengebilde aus einer gummielastischen Schicht mit aufliegender Vliesschicht und Verfahren zu seiner Herstellung
WO1998052458A1 (fr) * 1997-05-23 1998-11-26 The Procter & Gamble Company Structures tridimensionnelles utiles en tant que textiles d'entretien
EP1069223A1 (fr) * 1999-07-12 2001-01-17 Uni-Charm Corporation Feuille composite étirable élastiquement

Also Published As

Publication number Publication date
US20060148359A1 (en) 2006-07-06

Similar Documents

Publication Publication Date Title
US7238423B2 (en) Multicomponent fiber including elastic elements
US6989125B2 (en) Process of making a nonwoven web
KR101170856B1 (ko) 다기능 탄성 적층체 공정
US20060148358A1 (en) Elastic laminate and process therefor
US7078089B2 (en) Low-cost elastic laminate material
WO2006073617A1 (fr) Matériau en boucle non tissé
US6911174B2 (en) Process of making multicomponent fiber incorporating thermoplastic and thermoset polymers
US8333918B2 (en) Method for the production of nonwoven web materials
US20090047855A1 (en) Stretchable elastic nonwoven laminates
US20070172628A1 (en) Intermittently bonded fibrous web laminate
US20070141303A1 (en) Sheet materials with zoned machine direction extensibility and methods of making
US20050095943A1 (en) Cross machine direction extensible nonwoven webs
US20070138698A1 (en) Process for making necked nonwoven webs having improved cross-directional uniformity
US7416627B2 (en) Films and film laminates having cushioning cells and processes of making thereof
US6777056B1 (en) Regionally distinct nonwoven webs
WO2008121497A2 (fr) Stratifié non tissé comprenant un film élastique asymétrique
EP1673500A1 (fr) Procede et appareil pour produire des bandes de non-tisse
US20090068422A1 (en) Multilayer stretch nonwoven fabric composites
JP2006507427A (ja) 強度均一性の高い不織ラミネート及びそれらのための方法
US20050133948A1 (en) Apparatus and method for multicomponent fibers

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application
NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 05852341

Country of ref document: EP

Kind code of ref document: A1