WO2006025720A1 - Procedimiento mejorado para manufactura de una composición para fabricar tabique a base de diversos materiales, la composición y el tabique asi obtenido - Google Patents
Procedimiento mejorado para manufactura de una composición para fabricar tabique a base de diversos materiales, la composición y el tabique asi obtenido Download PDFInfo
- Publication number
- WO2006025720A1 WO2006025720A1 PCT/MX2005/000075 MX2005000075W WO2006025720A1 WO 2006025720 A1 WO2006025720 A1 WO 2006025720A1 MX 2005000075 W MX2005000075 W MX 2005000075W WO 2006025720 A1 WO2006025720 A1 WO 2006025720A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- partition
- paper
- cardboard
- composition
- raw material
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B18/00—Use of agglomerated or waste materials or refuse as fillers for mortars, concrete or artificial stone; Treatment of agglomerated or waste materials or refuse, specially adapted to enhance their filling properties in mortars, concrete or artificial stone
- C04B18/04—Waste materials; Refuse
- C04B18/18—Waste materials; Refuse organic
- C04B18/24—Vegetable refuse, e.g. rice husks, maize-ear refuse; Cellulosic materials, e.g. paper, cork
- C04B18/241—Paper, e.g. waste paper; Paper pulp
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B18/00—Use of agglomerated or waste materials or refuse as fillers for mortars, concrete or artificial stone; Treatment of agglomerated or waste materials or refuse, specially adapted to enhance their filling properties in mortars, concrete or artificial stone
- C04B18/04—Waste materials; Refuse
- C04B18/18—Waste materials; Refuse organic
- C04B18/24—Vegetable refuse, e.g. rice husks, maize-ear refuse; Cellulosic materials, e.g. paper, cork
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B28—WORKING CEMENT, CLAY, OR STONE
- B28B—SHAPING CLAY OR OTHER CERAMIC COMPOSITIONS; SHAPING SLAG; SHAPING MIXTURES CONTAINING CEMENTITIOUS MATERIAL, e.g. PLASTER
- B28B3/00—Producing shaped articles from the material by using presses; Presses specially adapted therefor
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B14/00—Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
- C04B14/02—Granular materials, e.g. microballoons
- C04B14/04—Silica-rich materials; Silicates
- C04B14/10—Clay
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
- C04B28/02—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements containing hydraulic cements other than calcium sulfates
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
- C04B2111/20—Resistance against chemical, physical or biological attack
- C04B2111/28—Fire resistance, i.e. materials resistant to accidental fires or high temperatures
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
- C04B2111/52—Sound-insulating materials
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02W—CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO WASTEWATER TREATMENT OR WASTE MANAGEMENT
- Y02W30/00—Technologies for solid waste management
- Y02W30/50—Reuse, recycling or recovery technologies
- Y02W30/91—Use of waste materials as fillers for mortars or concrete
Definitions
- the present invention relates to a composition for manufacturing partition based on various materials such as recycled paper and cardboard, the partition and the method for manufacturing the composition, the partition obtained is a low-cost, fireproof, insulating alternative construction material thermal and acoustic, easy to handle and quick to install, as well as a high resistance to compression stresses and that can be used in walls and tiles in the construction of low-cost housing and the procedure for the manufacture of this composition, up to to date the procedures for manufacturing compositions for manufacturing partition walls, blocks or bricks use a basic material and have included the use of various inorganic materials such as sand, clay, confectionery, gravel, cement, which through various compression processes, high temperatures or vibrations they are emptied into various molds to obtain the desired shape, in the ac
- there is no known composition and a procedure for the manufacture or manufacture of compositions based on recycled paper and cardboard to manufacture a light and heavy partition in the construction of walls in the construction of low-cost housing and the procedure for the manufacture of this composition. which exclusively comprises a synergistic combination
- the present invention relates to a composition for manufacturing partition based on recycled paper and cardboard, the partition and to the process for manufacturing the composition, the partition is used in the construction of walls in the construction of low-cost housing, the composition of the present invention comprises exclusively all types of paper found in garbage dumps as waste, such as carbon paper, newspaper, cardboard, cardboard and all kinds of bond paper, in combination with lime and cement, this combination surprisingly provides an improved cohesive and resistance effect at low cost, the paper and cardboard used is one of the pollutants that exist because once in the open dumps, there has been no way to recycle it properly to date, the composition of the present invention is formed by all types of paper and cardboard in a percentage of 10% to 95% preferably 93%, lime in a proportion of 0.1% to 4% preferably 1.4%, cement with a percentage e 2% to 10% preferably 5.6%, all this must be adjusted up to 100%, the cement is selected from those available on the market, preferably gray cement, in addition the lime is commercially available lime, preferably white lime or activated carbon of any type and a process for the manufacture
- the mixing of all the components must be slow to avoid the formation of lumps and bubbles caused by the disintegration of the raw material.
- the product obtained is placed on a wooden platform to transfer it to a drying area, said drying area being a covered space to avoid the direct rays of the sun helping the curing or setting of the partition mixture, preventing moisture loss quickly which deteriorates the resistance properties of the partition, drying can also be done by applying steam directly to the partition causing faster curing or setting.
- Resistant to concentrated sulfuric acid Resistance to the impact of bullet caliber 45 Does not require specialized labor Reduces the cost of structure, foundation, walls and slabs up to 50% Increases labor productivity Does not require false work
- Incombustibility type (B) exposed to direct fire, does not burn easily, is charred without flame and prevents the transmission of fire to nearby parts of the construction due to its compression (15 to 40 tons preferably 15 to 20 tons)
- the partition can be assembled due to its structure.
- composition includes 300 grams of cement, 5 Kilograms of raw material consisting of all types of paper found in landfills, such as carbon paper, newspaper, cardboard, cardboard and all kinds of bond paper, 75 grams of lime, a light partition is formed with measures of 7x14x28 centimeters and a weight of 1.2 Kg., the ratio preferably for light is 1: 1: 1.
- composition that includes 600 300 grams of cement, 5 kilograms of raw material consisting of all types of paper found in landfills, such as carbon paper, newspaper, cardboard, cardboard and all kinds of bond paper, 75 grams of lime, a heavy partition is formed with measures of 7x14x28 centimeters and a weight of 1.2 to 3 kg., the ratio of the components preferably for weighing is 1: 2: 3, finished the mixture,
- the composition is deposited in the mold with the desired shape and is compacted at 35 tons of pressure, in addition to already outside the molds the fresh partition will pass to the drying process either outdoors or steam.
- Table 1 below shows various materials from which the partition can be manufactured. Some of these 'materials correspond to patent applications being filed concurrently herewith.
- Plastic, granulated styrene, clay, sand and cement tipol 1.
Priority Applications (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2007529739A JP2008511436A (ja) | 2004-09-01 | 2005-09-01 | 異なる材料に基づいた仕切りを生産するための組成物の製造のための改善された方法、組成物、及びこのように得られた仕切り |
CNA2005800355243A CN101102973A (zh) | 2004-09-01 | 2005-09-01 | 基于几种材料来制造用于生产砖块的组合物的改进方法、由此获得的组合物和砖块 |
CA002578768A CA2578768A1 (en) | 2004-09-01 | 2005-09-01 | Improved method for the manufacture of a composition for producing partitions based on different materials, composition and partition thus obtained |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
MXPA/A/2004008452 | 2004-09-01 | ||
MXPA04008452A MXPA04008452A (es) | 2004-09-01 | 2004-09-01 | Procedimiento mejorado para manufactura de una composicion para fabricar tabique a base de diversos materiales, la composicion y el tabique asi obtenido. |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2006025720A1 true WO2006025720A1 (es) | 2006-03-09 |
Family
ID=35819897
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/MX2005/000075 WO2006025720A1 (es) | 2004-09-01 | 2005-09-01 | Procedimiento mejorado para manufactura de una composición para fabricar tabique a base de diversos materiales, la composición y el tabique asi obtenido |
Country Status (7)
Country | Link |
---|---|
JP (1) | JP2008511436A (ko) |
KR (1) | KR20070048268A (ko) |
CN (1) | CN101102973A (ko) |
CA (1) | CA2578768A1 (ko) |
MX (1) | MXPA04008452A (ko) |
RU (1) | RU2007106781A (ko) |
WO (1) | WO2006025720A1 (ko) |
Families Citing this family (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2925041B1 (fr) * | 2007-12-13 | 2011-09-02 | Stephane Vogel | Blocs en fibres de cellulose agglomerees. |
KR101293727B1 (ko) * | 2011-11-15 | 2013-08-06 | 한밭대학교 산학협력단 | 폐지를 이용한 벽돌 제조장치 |
CN104289494A (zh) * | 2014-07-28 | 2015-01-21 | 崔沛华 | 一种生活垃圾回收处理方法 |
CN109020342A (zh) * | 2018-09-19 | 2018-12-18 | 贵州师范大学 | 轻质水泥纸浆砖的制作方法 |
Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0127575A2 (de) * | 1983-04-28 | 1984-12-05 | Steiner-Delley, Yvonne | Werkstoff, Verfahren zu seiner Herstellung und Verwendung des Werkstoffes |
DE4110829A1 (de) * | 1991-04-04 | 1992-10-08 | Hiendl Heribert | Formteil fuer bauzwecke, insbesondere platte |
DE4403588A1 (de) * | 1993-03-01 | 1994-09-08 | Helmut Gruener | Wärmedämmbauelement |
US5350451A (en) * | 1991-07-08 | 1994-09-27 | Patterson Eric W | Building material made from waste paper and method for producing the same |
DE4321024A1 (de) * | 1993-06-24 | 1995-01-05 | Haeussler Ingenieurbuero Gmbh | Verfahren zur Herstellung von Leichtbeton oder betonähnlichen Gegenständen |
DE29618110U1 (de) * | 1996-10-18 | 1997-01-16 | Agrar Foerderung Und Entwicklu | Werkstoff als Bau- und Dämmstoff aus einer Papierschlamm-, Kalk-, Zementmischung mit und ohne Zusatz von Tragfasern und einem Treibmittel |
-
2004
- 2004-09-01 MX MXPA04008452A patent/MXPA04008452A/es not_active Application Discontinuation
-
2005
- 2005-09-01 KR KR1020077007424A patent/KR20070048268A/ko not_active Application Discontinuation
- 2005-09-01 CA CA002578768A patent/CA2578768A1/en not_active Abandoned
- 2005-09-01 RU RU2007106781/03A patent/RU2007106781A/ru unknown
- 2005-09-01 WO PCT/MX2005/000075 patent/WO2006025720A1/es active Application Filing
- 2005-09-01 JP JP2007529739A patent/JP2008511436A/ja active Pending
- 2005-09-01 CN CNA2005800355243A patent/CN101102973A/zh active Pending
Patent Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0127575A2 (de) * | 1983-04-28 | 1984-12-05 | Steiner-Delley, Yvonne | Werkstoff, Verfahren zu seiner Herstellung und Verwendung des Werkstoffes |
DE4110829A1 (de) * | 1991-04-04 | 1992-10-08 | Hiendl Heribert | Formteil fuer bauzwecke, insbesondere platte |
US5350451A (en) * | 1991-07-08 | 1994-09-27 | Patterson Eric W | Building material made from waste paper and method for producing the same |
DE4403588A1 (de) * | 1993-03-01 | 1994-09-08 | Helmut Gruener | Wärmedämmbauelement |
DE4321024A1 (de) * | 1993-06-24 | 1995-01-05 | Haeussler Ingenieurbuero Gmbh | Verfahren zur Herstellung von Leichtbeton oder betonähnlichen Gegenständen |
DE29618110U1 (de) * | 1996-10-18 | 1997-01-16 | Agrar Foerderung Und Entwicklu | Werkstoff als Bau- und Dämmstoff aus einer Papierschlamm-, Kalk-, Zementmischung mit und ohne Zusatz von Tragfasern und einem Treibmittel |
Also Published As
Publication number | Publication date |
---|---|
CN101102973A (zh) | 2008-01-09 |
RU2007106781A (ru) | 2008-10-10 |
CA2578768A1 (en) | 2006-03-09 |
KR20070048268A (ko) | 2007-05-08 |
MXPA04008452A (es) | 2005-04-13 |
JP2008511436A (ja) | 2008-04-17 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CN1139551C (zh) | 外保温砂浆及制备方法 | |
Fadiel et al. | Use of crumb rubber to improve thermal efficiency of cement-based materials | |
CN104230280B (zh) | 一种低收缩污泥陶粒碱激发全矿渣泡沫混凝土板及其制备方法 | |
CN1117032A (zh) | 含煤灰的固化材料的制备方法 | |
CN106242426A (zh) | 外墙保温材料及其制备方法 | |
US20100230844A1 (en) | Process for Producing Environmental Protection Wall Plate | |
CN102229487A (zh) | 一种免烧保温砖及其生产方法 | |
WO2006025720A1 (es) | Procedimiento mejorado para manufactura de una composición para fabricar tabique a base de diversos materiales, la composición y el tabique asi obtenido | |
EP1950187A2 (en) | Mortars suitable for thermic and acoustic isolations comprising cork and aerial lime which is optionally hydrophobized | |
CN106082884A (zh) | 一种含有固废煤渣的轻质保温墙板及制备工艺 | |
WO2008126125A2 (en) | Autoclaved aerated concrete with reduced shrinkage for realising building blocks and/or floors and/or reinforced and not reinforced panels | |
WO2019050138A1 (ko) | 방수형 기포콘크리트 블록의 습식 제조방법 | |
RU2504529C1 (ru) | Способ получения теплоизоляционного огнестойкого материала | |
Ghosh | A review on paper Crete: a sustainable building material | |
RU2378228C1 (ru) | Ячеистый бетон автоклавного твердения | |
BG65746B1 (bg) | Метод за производство на блокове за зидария и облицовка | |
RU2351574C2 (ru) | Способ получения безавтоклавного органо-неорганического особо легкого бетона | |
RU2255920C1 (ru) | Сырьевая смесь для изготовления легкого бетона | |
JPH09100153A (ja) | セラミックス原料組成物とその組成物から成形したセラミックス成形物およびその成形物を製造する方法 | |
JP2003335564A (ja) | 建材用組成物、それを用いた建築材料の製造方法 | |
RU2327671C1 (ru) | Состав для получения газобетона | |
RU2542011C1 (ru) | Сырьевая смесь для автоклавного пенобетона | |
KR20140146709A (ko) | 흙다짐 시공용 흙재료 조성물 및 이를 이용하여 제조된 흙다짐 성형체 | |
ES2935175B2 (es) | Diseño y método de elaboración de un nuevo material conglomerante y su aplicación en el desarrollo de bloques para construcción modular aligerada y sostenible | |
SU1787974A1 (en) | Raw mixture for producing heat insulation |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KM KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NG NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SM SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): BW GH GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IS IT LT LU LV MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
WWE | Wipo information: entry into national phase |
Ref document number: 12007500483 Country of ref document: PH Ref document number: 2007529739 Country of ref document: JP |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2578768 Country of ref document: CA Ref document number: 07020784 Country of ref document: CO |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
WWE | Wipo information: entry into national phase |
Ref document number: 1757/DELNP/2007 Country of ref document: IN |
|
WWE | Wipo information: entry into national phase |
Ref document number: 554186 Country of ref document: NZ |
|
WWE | Wipo information: entry into national phase |
Ref document number: 1020077007424 Country of ref document: KR |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2007106781 Country of ref document: RU |
|
WWE | Wipo information: entry into national phase |
Ref document number: 200580035524.3 Country of ref document: CN |
|
122 | Ep: pct application non-entry in european phase | ||
ENPW | Started to enter national phase and was withdrawn or failed for other reasons |
Ref document number: PI0515601 Country of ref document: BR Free format text: PEDIDO RETIRADO POIS QUANDO DA ENTRADA NA FASE NACIONAL, NAO FOI APRESENTADO EM LINGUA VERNACULA PELO MENOS O QUADRO REIVINDICATORIO, CONFORME AN 128, ITEM 9.2, CABENDO DESARQUIVAMENTO. |