WO2006002773A1 - Silicon dioxide dispersion comprising polyol - Google Patents
Silicon dioxide dispersion comprising polyol Download PDFInfo
- Publication number
- WO2006002773A1 WO2006002773A1 PCT/EP2005/006481 EP2005006481W WO2006002773A1 WO 2006002773 A1 WO2006002773 A1 WO 2006002773A1 EP 2005006481 W EP2005006481 W EP 2005006481W WO 2006002773 A1 WO2006002773 A1 WO 2006002773A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- silicon dioxide
- dispersion
- substance
- polyol
- stable
- Prior art date
Abstract
Description
Claims