Classifications

• • G—PHYSICS
  • G10—MUSICAL INSTRUMENTS; ACOUSTICS
  • G10K—SOUND-PRODUCING DEVICES; METHODS OR DEVICES FOR PROTECTING AGAINST, OR FOR DAMPING, NOISE OR OTHER ACOUSTIC WAVES IN GENERAL; ACOUSTICS NOT OTHERWISE PROVIDED FOR
  • G10K11/00—Methods or devices for transmitting, conducting or directing sound in general; Methods or devices for protecting against, or for damping, noise or other acoustic waves in general
  • G10K11/16—Methods or devices for protecting against, or for damping, noise or other acoustic waves in general
  • G10K11/162—Selection of materials
• • G—PHYSICS
  • G10—MUSICAL INSTRUMENTS; ACOUSTICS
  • G10K—SOUND-PRODUCING DEVICES; METHODS OR DEVICES FOR PROTECTING AGAINST, OR FOR DAMPING, NOISE OR OTHER ACOUSTIC WAVES IN GENERAL; ACOUSTICS NOT OTHERWISE PROVIDED FOR
  • G10K11/00—Methods or devices for transmitting, conducting or directing sound in general; Methods or devices for protecting against, or for damping, noise or other acoustic waves in general
  • G10K11/16—Methods or devices for protecting against, or for damping, noise or other acoustic waves in general
  • G10K11/162—Selection of materials
  • G10K11/168—Plural layers of different materials, e.g. sandwiches

Definitions

• This invention relates to materials for sound absorption. More particularly it relates to thermo-formable acoustic products that have enhanced sound absorption properties and can be decoratively faced.
• Sound absorption provides a useful means for noise reduction in a wide variety of industrial, commercial, and domestic applications.
• the sound absorption of a porous material is known to be a function of fundamental material properties, including thickness, air flow resistance, mass, stiffness, porosity, tortuosity etc, and application parameters, such as any air space behind the material, or alternatively, the acoustic and mechanical properties of any other material situated behind the porous material, such as a spacer layer, an isolation layer, or acoustic underlay.
• Adding a third dimension to a sound absorbing assembly provides aesthetic and practical physical properties such as stiffness and conformance to contoured shapes, such as found in motor vehicle trim, such as, for example, for the floorpan, firewall, trunk, or parcel shelf.
• the sound absorbing composite should have a decorative finish that does not detract from the sound absorption. Even more desirably, the decorative facing should have properties that actually enhance the sound absorption by becoming an integral component of the sound absorbing composite assembly. In certain applications, such as a motor vehicle floor assembly, it is desirable that the composite conforms to the shape of a surface, for example, or otherwise retains a particular shape, for example as an aesthetic feature for wall decoration.
• the sound-absorbing composite should have sufficient strength that it can support light loads and resist mechanical damage.
• the sound absorbing assembly, and any decorative facing can be heat moulded to the required shape in a simple and cost effective process.
• the applicant is the applicant for Australian Patent Application No. 48754/00, which describes a Pinnable Acoustic Panel, comprising a decorative layer, a high flow resistive layer and a foam spacer layer.
• the high flow resistive layer has sufficient stiffness and density that it will retain pins used to attach papers and such to the panel. The content of this is incorporated herein by cross-reference.
• the applicant is also the applicant in respect of PCT/AU01/00880, which discloses a theraioformable acoustic sheet, the content of which is also incorporated herein by cross-reference.
• a sound absorbing composite assembly includes, but are not limited to, interior insulation for motor vehicles, and commercial decorative wall, ceiling, and floor finishes. In most instances, a decorative facing is required for aesthetic purposes or for mechanical protection.
• thermo-formable materials have been provided, however such prior art does not address the practicality of achieving an effective sound absorbing solution.
• environmental, manufacturing and cost issues are a concern, whilst retaining the ability to vary the mechanical properties and maintaining or enhancing the sound absorbing properties of the product and combining this with the aesthetic quality of the product.
• a decorative layer may also be included on, or attached to, the flow resistive thermo-formable material.
• these applications similarly do not address the practicality of achieving an effective sound absorbing solution as discussed above.
• thermo-formable acoustic product with enhanced acoustic properties, and a method of producing such a product that will overcome or at least ameliorate the disadvantages of the prior art or at least provide a useful alternative.
• the present invention provides a thermo-formed acoustic product formed from an acoustic sheet with a relatively high flow resistance, and a layer of porous flow resistive spacer material attached to one side of the acoustic sheet and having a flow resistance substantially smaller than the acoustic sheet, wherein the acoustic product has locally reactive acoustic behaviour and an overall flow resistance of between 2800 Rayls and 8000 Rayls.
• the acoustic sheet has a favourable aesthetic appearance
• the acoustic sheet is a decorative layer, such as a carpet, textile or other permeable film facing.
• the acoustic sheet is formed by a decorative layer and at least one additional flow resistive layer.
• the porous flow resistive spacer material is a fibrous web.
• the fibrous web spacer material has a vertically-lapped construction so that the fibres are oriented in a plane normal to that of the acoustic sheet.
• the fibres of the fibrous web spacer material are at least partially thermally bonded together. It is also preferable that the fibrous web spacer material is thermally moulded. The moulding can be to a final shape or an intermediate shape for further moulding or processing.
• the fibrous web spacer material is formed from high melt and low melt fibres.
• the low melt fibres are a bi-component fibre. In another preferred aspect the low melt fibres are a mono-component fibre.
• the acoustic sheet includes a flow resistive layer formed from high melt and low melt fibres.
• the flow resistive layer is compressed to give the desired air flow resistance.
• the low melt fibres are selected to have a temperature resistance that is applicable to the intended use.
• the thermo-formed acoustic product has a total air flow resistance of between 3000 Rayls to 5000 Rayls. More preferably, the thermo-formed acoustic product has a total air flow resistance of between 3200 Rayls to 4500 Rayls.
• the fibrous web spacer material has an air flow resistance of between 100 Rayls to 800 Rayls. Even more preferably, the fibrous web spacer material has an air flow resistance of between 200 Rayls to 400 Rayls.
• the fibrous web spacer material has a density of 150-2000g/m 2 .
• the density of the fibrous web spacer material is determined by the specific acoustic and physical properties desired of the overall system.
• the acoustic sheet has a density of 150-2000g/m 2 . The density is selected on the basis of the acoustic and physical properties desired of the overall system.
• the thermo-formed acoustic product can be used for a multiplicity of purposes, including, but not exclusive to insulation for machinery and equipment, motor vehicle insulation, domestic appliance insulation, dishwashers and commercial wall and ceiling panels.
• the acoustic product has a sag resistance to temperatures at or about 150°C.
• the part should exhibit minimal sag at operating temperatures.
• the present invention is a method of forming a thermo-formed acoustic product formed from an acoustic sheet with a relatively high flow resistance, and a layer of porous flow resistive spacer material attached to one side of the acoustic sheet and having a flow resistance substantially smaller than the acoustic sheet, including the steps of heating the porous flow resistive layer and acoustic sheet, and moulding the acoustic sheet and porous flow resistive layer wherein the acoustic product has locally reactive acoustic behaviour and an overall air flow resistance of between 2800 Rayls and 8000 Rayls and the porous flow resistive spacer material attached to one side of the acoustic sheet.
• porous flow resistive spacer material is attached to one side of the acoustic sheet during moulding. In another embodiment the porous flow resistive spacer material is attached to one side of the acoustic sheet prior to moulding. Preferably the porous flow resistive spacer material is laminated to the acoustic sheet prior to being moulded.
• the acoustic sheet and porous flow resistive layer are supplied to the moulding process in roll form.
• the acoustic sheet and porous flow resistive layer are supplied to the moulding process in sheet form.
• the acoustic product is moulded in a cold moulding tool. In this embodiment it is preferable that a thermo-formed acoustic product is formed by a flow resistive spacer material having crystalline fibres. In another embodiment, the acoustic product is moulded in a hot moulding tool. In this embodiment it is preferable that a thermo-formed acoustic product is formed by a flow resistive spacer material having amorphous fibres. Preferably the heating the acoustic product is achieved with infra red radiation, hot air, or a combination of hot air and infra red radiation.
• the acoustic product is formed from predominantly one polymer type.
• the acoustic product is formed predominantly from polyester fibres or polypropylene fibres .
• the acoustic properties of the acoustic product are assisted by the three-dimensional geometry of the moulded product.
• the present invention provides the advantages of a multipurpose clean, energy efficient, low cost, recyclable material as a thermo-fo_rmable acoustic sheet with enhanced and consistent acoustical properties whilst provi ing a favourable aesthetic appearance in preferred embodiments.
• a further advantage is that the present invention provides an insulation that provides a lower resonance than current systems, has superior resilience and predictable mechanical properties.
• a further advantage of the above process is that the product is formed irr a fast cycle time, to provide cost-effective solutions for use as an insulation in original equipment, such as motor vehicles and dishwashers, wall and ceiling linings and other industrial commercial and domestic purposes.
• thermo-forrmable acoustic product with less energy than conventional systems, providing an i ⁇ rproved environmental outcome.
• FIG. 1 Schematic illustration of one embodiment of the thermo-formed acoustic product according to the present invention.
• FIG 2. Schematic illustration of another embodiment of the thermo-formed acoustic product according to the present invention.
• FIG 3. Schematic illustration of another embodiment of the thermo-formed acoustic product according to the present invention.
• FIG 4. Schematic illustration of an embodiment of the thermo-formed acoustic product according to the present invention.
• FIG. Schematic illustration of an embodiment of the theraio-formed acoustic product according to the present invention.
• the actual sound absorption achieved in a practical example of application can be less than that inferred from laboratory testing. This has been shown to result from the effect of sound transmission behind and parallel to the sheet. In acoustic terms, this material is installed in a non-locally reactive situation. Those familiar with the concepts of flow resistive screens as sound absorption media, will appreciate that the acoustic performance achieved in real life will be superior in the event that the installation allows the thermo-formable acoustic sheet to behave in a locally reactive manner.
• thermo- formable acoustic product 1 which is formed from an acoustic sheet 2, and a layer of porous flow resistive spacer material 4.
• the product is typically applied to a surface 5, usually conforming to that shape.
• the acoustic sheet 2 has a favourable aesthetic appearance by virtue that the acoustic sheet is a decorative layer, such as a carpet.
• the acoustic sheet 2 can be a flow resistive layer only where a favourable aesthetic appearance is not required.
• thermo- formable acoustic product 6 which is formed from a decorative layer 9, a compressed flow resistive acoustic layer 7, and a layer of porous flow resistive spacer material 10.
• the product is typically applied to a surface 11, usually conforming to that shape.
• the decorative layer may be an automotive carpet, or a commercial textile.
• the decorative layer is a decorative fabric which has been previously coated with an adhesive resin so as to bind the fibres and to control the air permeability.
• Such a coating may be applied in any of the well known means of coating textiles.
• the coating is preferably a thermoplastic adhesive powder, web or film, extruded thermoplastic resin or a liquid coating.
• the coating process must be finely controlled so as to ensure a consistent and even coating of the decorative fabric and a pre-determined air flow resistance, and hence the performance of the decorative layer as an element of the acoustic product.
• the flow resistive compressed acoustic sheet 7 is formed by a similar processes as described in PCT/AU01/00880, and has an air flow resistance in the range of 2800-7000 mks Rayls, more preferably in the range 3000-5000 mks Rayls and even more preferably in the range of 3200-4500 mks Rayls.
• the preferred flow resistance range is limited by the practical application of the product, however the preferred range of flow resistance for the enhanced thermoformable acoustic sheet has been selected to provide the optimum acoustic properties for the intended applications.
• the increased flow resistance is achieved by increasing the compaction density and further reducing the volume of the interstatial spaces within the acoustic sheet. This is achieved through controlling the process parameters of time, temperature and pressure, applied to the fibrous web during manufacture of the acoustic sheet.
• further optimisation of the fibre blend, and web density makes it possible to achieve a flow resistance in the preferred range.
• the product must have a temperature resistance appropriate for the intended application.
• the sheet must have a low sag modulus at temperatures up to about 150°C.
• the product can be formed into a three dimensional shape, so providing an air space and structural rigidity.
• a shape can also form partially enclosed cells, such as a honeycomb, or egg-carton type structure, that will provide local reactivity and increase the acoustical performance of the thermo-formed acoustic product.
• the sheet 7 is produced from a fibrous web of 150-2000 g/m . It is clear that for cost minimisation, the lowest practical web weight is desired. The web is compressed by between 15 and 25 times. The thickness of the web has an influence on the air flow resistance, however the inventors have demonstrated through modelling and practice, that the desired acoustic properties can be achieved through a combination of different fibre selections and ratios, thicknesses and processing conditions.
• the flow resistive material 10 is produced in planar form and may be presented as a roll or as a sheet. In one form of the invention, the flow resistance of the material can be achieved or enhanced through the application of an adhesive resin.
• the resin may be applied in a powder, fibre or film form, preferably in a dry lamination or coating process.
• the resin can be selected from a range of thermoplastic, or thermoset, polymers.
• Preferred thermoplastic resins include, but are not limited to, polyester and polyproylene. From a cost perspective, the selection of resin and fibre will often be determined by the lowest possible cost to achieve the appropriate level of acoustic and physical performance.
• thermo-formable acoustic product is produced from one individual polymer system so that it can be readily recycled, in particular polyester or polypropylene.
• the web of fibrous material used to produce the flow resistive acoustic sheet 7 is preferably produced from a vertically-lapped web of high loft thermally bonded material as produced by the vertical-lapping process, known as the STRUTO process under Patent WO 99/61963, although other processes for producing a vertically, or rotary, lapped web would also be suitable.
• Suitable low and high melt materials can be used as the respective fibres, which can of mono- or bi-component form.
• Alternative web forming systems, such as cross-lapping, air laid, and needle punching can also be used, however these have been found to result in a web with less consistent acoustic properties.
• the web is consolidated by heating and compressing, as described in PCT/AU01/00880.
• the consolidation of the fibrous web can be conducted as an in-line process immediately following production of the fibrous web.
• the fibrous web is preferably formed as previously described by the vertical lapping process, but other web forming processes, such as cross-lapping, and/or needle punching and/or thermal bonding can also be used. A more consistent acoustic performance is obtained through the vertical lapping process.
• a flow resistive screen does not behave in a locally reactive manner unless the air space behind the screen provides some acoustic impedance. To induce loacally reactive behaviour in the thermo-formed acoustic product, it is necessary to insert a flow resistive material into the air space, or alternatively to break up the air space into a cellular or honeycomb structure as previously described.
• a vertically lapped fibrous web is used as a flow resistive spacer material to fill the void created by the air space, however other forms of porous materials can also serve this purpose, for example polyurethane foam, needle punched fibrous webs or a cross lapped thermally bonded fibrous webs.
• the mechanical and acoustical properties of the spacer material are critical to ensuring the optimum acoustic performance of the composite.
• the fibrous web spacer material can be attached to the thermo-formable acoustic sheet by lamination or by mechanical means, for example riveting, coupling or plastic welding, hi one embodiment, an adhesive 3, 8 may also be used between the acoustic sheet and the fibrous web spacer material.
• this adhesive can be heat reacted to act as an adhesive for the fibrous web spacer material. This can be achieved through contact heating, hot air impingement, or indirect heating, such as infra-red, or other similar means.
• the adhesive system that controls the flow resistance of the sheet is in the fibrous form, it may be advantageous to use an additional hot melt adhesive in powder, web, film or similar form. The use of such an adhesive layer can also be used to control the final flow resistance of the sheet and fibrous web spacer material composite.
• the fibres selected for fibrous web spacer material influence the final acoustic properties significantly.
• the fibrous web spacer material is preferably formed from fibres within the range of 0.5 to 6 denier, preferably 0.5 to 3 denier, and more preferably from 0.5 to 1 denier. These fibre sizes are nominated on the basis of staple fibre, however the melt blown process can produce fibres in even smaller deniers, producing higher flow resistance and an even more beneficial result.
• the denier of a fibre relates to the mass per 9000m of fibre.
• a polymer with a low specific gravity will have more fibres per unit of mass, and volume for a given mass.
• a low density polymer, such as polypropylene will have more fibres, at the same denier, than the equivalent mass of say polyester fibre.
• a fibrous web spacer material produced from a low density polymer, such as polypropylene is a preferred form of this invention.
• the thermo-formed acoustic product is formed by heating the acoustic sheet and porous layer, and moulding them to a desired three dimensional shape.
• the acoustic sheet is attached to the porous layer to form an integral acoustic product.
• the three dimensional shape could be an intermediate shape or a final shape.
• the heating of the acoustic sheet and porous layer can be conducted before or during moulding.
• the porous layer is laminated to the acoustic sheet, it is possible to also thermoform the spacer material in the same process.
• the spacer material can be selected from a fibrous web comprising fibres with an appropriately selected melting range.
• the porous layer may consist of fibres with a substantially higher melting range than the thermo-formable acoustic sheet, and may remain unaffected by the moulding process. Attachment of the porous layer may be achieved by lamination as described, or by mechanical means, such as staples or other form of mechanical fastener.
• the spacer material may optionally be placed into the moulding tool prior to the placement of the heated acoustic sheet into the moulding tool.
• the heat retained in the sheet is often sufficient to cause adhesion to the pieces placed into the mould, however an adhesive layer may be required for more secure adhesion.
• sheets or pieces of porous layer may be separately adhered to the thermoformed sheet, after the moulding process. Once again these pieces may be adhesively or mechanically secured. In some cases the pieces may be installed independently onto the panel to which the thermoformed acoustic sheet is attached.
• the selection of the fibres used to form the fibrous web spacer material is important.
• crystalline fibres have been found to increase the sag resistance compared to amorphous fibres.
• amorphous fibres have been found to increase the sag resistance compared to crystalline fibres.
• the fibrous web spacer material of the preferred embodiment has previously been described as a vertically lapped, thermally bonded non-woven produced by the STRUTO, or other, process.
• the vertical fibres adopt a v-orientation by flexing at the centre-line of the web.
• the fibres may adopt a z-orientation, by flexing at the outer layers of the web. In both instances, this results in a change in the mechanical properties of the web, making it behave more effectively as a spring, improving resilience and resulting in a lower cut-off frequency.
• thermo- formable acoustic product 12 which is formed from a decorative layer 13, a compressed flow restive acoustic layer 15, a layer of porous flow resistive spacer material 17, and a second flow resistive acoustic sheet 19 may also be used to further mechanically stabilise the product, or assist in the attachment to another surface 20.
• the surface may also have holes 21.
• an adhesive layer 14, 15 and 18 may also be provided to assist attachment.
• thermo- formable acoustic product 28 which is formed from a decorative layer 22, a compressed flow resistive acoustic layer 24, and a layer of porous flow resistive spacer material 26 and adhesive layers 23 and 24 between those layers.
• the product is applied to a surface 27, conforming to that shape.
• thermo- formable acoustic product 35 is shown which is formed from a decorative layer 29, a compressed flow resistive acoustic layer 30, and a layer of porous flow resistive spacer material 31 and adhesive layers 32 and 33 between those layers.
• the product is thermoformed to conform the shape of the surface 34.

Landscapes

• Physics & Mathematics (AREA)
• Engineering & Computer Science (AREA)
• Acoustics & Sound (AREA)
• Multimedia (AREA)
• Vehicle Interior And Exterior Ornaments, Soundproofing, And Insulation (AREA)
• Laminated Bodies (AREA)
• Casting Or Compression Moulding Of Plastics Or The Like (AREA)

Priority Applications (4)

Applications Claiming Priority (4)

Related Child Applications (2)

Publications (1)

Family

ID=34888007

Family Applications (1)

Country Status (5)

Cited By (15)

Families Citing this family (23)

Citations (4)

Family Cites Families (6)

• 2005
  • 2005-02-25 JP JP2007500003A patent/JP2007523773A/ja not_active Withdrawn
  • 2005-02-25 WO PCT/AU2005/000239 patent/WO2005081226A1/en active Application Filing
  • 2005-02-25 EP EP05706276A patent/EP1719113A1/en not_active Withdrawn
  • 2005-02-25 KR KR1020067019539A patent/KR20070056000A/ko not_active Application Discontinuation
  • 2005-08-24 US US11/210,462 patent/US20060090958A1/en not_active Abandoned

Patent Citations (4)

Also Published As

Similar Documents

Legal Events