WO2005075702A2 - Procede de depot d’un revetement d’oxyde metallique sur un substrat - Google Patents
Procede de depot d’un revetement d’oxyde metallique sur un substrat Download PDFInfo
- Publication number
- WO2005075702A2 WO2005075702A2 PCT/FR2005/050028 FR2005050028W WO2005075702A2 WO 2005075702 A2 WO2005075702 A2 WO 2005075702A2 FR 2005050028 W FR2005050028 W FR 2005050028W WO 2005075702 A2 WO2005075702 A2 WO 2005075702A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- colloidal solution
- metal oxide
- substrate
- soil
- layers
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
- C23C18/02—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by thermal decomposition
- C23C18/12—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by thermal decomposition characterised by the deposition of inorganic material other than metallic material
- C23C18/1204—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by thermal decomposition characterised by the deposition of inorganic material other than metallic material inorganic material, e.g. non-oxide and non-metallic such as sulfides, nitrides based compounds
- C23C18/1208—Oxides, e.g. ceramics
- C23C18/1216—Metal oxides
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
- C23C18/02—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by thermal decomposition
- C23C18/12—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by thermal decomposition characterised by the deposition of inorganic material other than metallic material
- C23C18/1225—Deposition of multilayers of inorganic material
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
- C23C18/02—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by thermal decomposition
- C23C18/12—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by thermal decomposition characterised by the deposition of inorganic material other than metallic material
- C23C18/125—Process of deposition of the inorganic material
- C23C18/1262—Process of deposition of the inorganic material involving particles, e.g. carbon nanotubes [CNT], flakes
- C23C18/127—Preformed particles
Definitions
- the present invention relates to a method of depositing a metal oxide coating on a substrate.
- the invention finds a particularly advantageous, but not limiting, application in the field of catalysis, and more especially the field of reactions in liquid or gas phase catalyzed by solids.
- the invention also applies to other very diverse fields, in particular when it is necessary to modify certain functional properties of materials, such as hardness, thermal protection, protection against chemical agents, electrical insulation, adhesion between thin insulating layers or not, etc.
- the functional properties of the materials used as catalysts on solids for reactions in liquid or gas phase are obtained by depositing on the substrate material a coating consisting of an intermediate layer of very porous ceramic intended to fix the catalysts and to maximize the contact surface between the liquid or gaseous reactants and the catalyst.
- the intermediate layers therefore play an essential role since they must both ensure good adhesion with the substrate, a metallic support for example, have a high specific surface, be chemically neutral and have good compatibility with the chosen catalyst.
- the vast majority of the intermediate layers used in catalysis consist essentially of ceramics, and in particular metal oxides such as alumina, on which very small particles of a metal or another oxide can be deposited, having a catalytic action.
- the choice of alumina as the oxide most often used in catalysis is mainly due to the fact that, prepared from suitable precursors, it retains a high specific surface at high temperature (approximately 100 m 2 / g at 1000 ° c), and that it has very interesting acid-base surface properties for certain reactions.
- the technical problem to be solved by the object of the present invention is to propose a method of depositing on a substrate a coating comprising at least one layer of metal oxide, said layer of metal oxide being produced by deposition on said substrate of a colloidal solution (sol) of a metal hydroxide then formation of said metal oxide by pyrolysis of a gel obtained from said colloidal solution, a process which would overcome the limits to the deposition of oxide layers metallic, in particular, on metallic substrates, due to the low viscosity of the colloidal solution obtained.
- the solution to the technical problem posed consists, according to the present invention, in that the colloidal solution is deposited on the substrate in the thixotropic state.
- the applicant has been able to establish that, near the sol-gel transition, the colloidal metal oxide solution becomes thixotropic.
- the transition to the thixotropic state can be achieved either by concentration of the soil, or by addition of organic or inorganic compounds, acetate or formate for example, or the combination of the two.
- the thickness of the deposited layer depends on both the concentration and the viscosity, it is possible to modify the thickness over a wide range by playing on these two parameters.
- the fact of using a thixotropic sol has two advantages, on the one hand, of making it possible to form homogeneous adherent layers on metallic substrates, and, on the other hand, of increasing the thickness of the deposited layer.
- thixotropy is a property presented by certain substances, such as gels, to become liquid when they are mechanically agitated and to return to their initial viscous state at rest. This reduction in viscosity under agitation is due to the temporary destruction of the internal structure of the substance under the action of shear forces and its subsequent restructuring when the force ceases to be applied.
- metallic substrates as has been explained above, the method according to the invention is not limited to this single type of substrate but also extends to ceramic or glass substrates. The process which is the subject of the invention has been presented above with reference to the deposition of layers of porous alumina.
- the sol-gel process makes it possible to prepare very diverse metal oxides, it is easy to extend this process to coatings of metallic or ceramic substrates with porous oxides, other than alumina, commonly used in catalysis such as silica, zirconia, titanium oxide or cerine, and more generally any metal oxide which can be deposited to modify the surface characteristics of metallic, ceramic or glass substrates.
- the porosity of the layers depends on the conditions of the heat treatment (pyrolysis) carried out at the end of the deposition. But it can also be modified in a wider range by adding surfactants to the soil which will act on the organization of the particles and create a new type of porosity.
- Another method of modifying porosity is to incorporate into the soil compounds, such as polymer particles, which decompose at low temperatures without leaving harmful residues to the properties of the coating. During the heat treatment, the decomposition of these additives creates a porosity close to that of the diameter of their particles.
- the process of the invention is not limited to porous oxides only. Indeed, by modifying the mode of synthesis of the soil it It is possible to obtain materials with moderate or not porous materials at moderate temperatures, for example ⁇ -alumina from 500 ° C. This allows to consider applying to industrial parts a coating of a functional material intended to give the substrate properties that it did not have.
- the thickness of the layers obtained by the sol-gel process is generally limited because there is a considerable reduction in volume during the passage from the sol to the oxide. This reduction commonly reaches a factor of 100, that is to say that a layer of soil of 100 ⁇ m will give an oxide layer of 1 ⁇ m. If the conditions of the heat treatment are not optimized, this shrinkage causes significant cracking of the layer.
- a means in adding to the process a step of adding to the colloidal solution of oxide particles, which are preferably prepared during a previous step, for example from 'a soil of the same nature. It is also possible to use particles of different composition, which leads to the production of composite deposits.
- the sol-gel process makes it possible to obtain deposits consisting of several successive layers, possibly of variable thickness, in order to obtain thicker coatings without cracking. Generally, a moderate heat treatment is applied between each layer. The thicknesses of the layers thus produced can reach a few hundred microns (100 to 500 ⁇ m), this by adding to the thixotropic solution particles of adequate size of metal oxide.
- This multilayer technique can also be used to prepare a coating with a gradient in chemical composition or structure.
- layers with a porosity gradient can be produced.
- a first layer, directly in contact with the substrate, will be a dense layer and will protect the substrate from attack gaseous reagents.
- the following layers will be more and more porous in order to optimize the catalytic activity.
- Example 1 concerns the synthesis of a soil by the Yoldas process. 360 cm 3 of water (20 moles) heated to 85 ° C. are poured quickly onto 50 g of aluminum tri-sec-butoxide (about 0.2 mole) with vigorous stirring. The mixture is kept at 85 ° C. with stirring for 15 min, then 7 cm 3 of a 9.2% nitric acid solution in water (0.014 mole HNO 3 ) are added. Maintained at 85 ° C and with stirring for 24 h to obtain a clear sol.
- This soil is used to make dip-coating deposits on glass or stainless steel substrates. After drying at 20 ° C and then heat treatment in an oven at 500 ° C in air, the layers are examined under a microscope. The deposits prepared on steel are not homogeneous, areas of the substrate are not covered and the adhesion is poor. On the other hand, the deposits on glass are homogeneous, their thickness being between 0.1 and 0.2 ⁇ m.
- Example 2 relates to a modification of the Yoldas process according to the process according to the invention.
- the soil of Example 1 is gradually evaporated at 85 ° C.
- the initial volume of the soil was 420 cm 3 for an aluminum concentration of 0.5 mol / l.
- the soil became thixotropic; the aluminum concentration is now 1.5 mole / l.
- the thixotropic sol containing 1.5 mole / l of aluminum is used to make deposits on glass and stainless steel substrates under the same conditions as in Example 1.
- the layers are now homogeneous and adherent. Their thickness is of the order of 2 ⁇ m.
- Example 3 relates to the preparation of a thixotropic sol with a low aluminum concentration.
- Example 1 The soil of Example 1 is gradually evaporated at 85 ° C.
- the initial volume of the soil was 420 cm 3 for an aluminum concentration of 0.5 mol / l.
- an identical volume of ethanol is added.
- the soil becomes thixotropic. Since the final volume is identical to the initial volume, the aluminum concentration is always 0.5 mol / l.
- This thixotropic soil is used to make deposits on glass and stainless steel substrates under the same conditions as in Example 1.
- the layers obtained are homogeneous and adherent. Their thickness is of the order of 1 ⁇ m.
- Example 4 relates to the synthesis of a platinum-alumina catalyst deposited on steel (1% Pt / alumina)
- a solution of 0.28 g of hexachloroplatinic acid H 2 PtCI 6 in 10 is added to the soil of Example 1 cm 3 of water. After stirring, a transparent light yellow color is obtained.
- This soil is gradually evaporated at 85 ° C. It becomes thixotropic for an aluminum concentration of 1.4 mole / l. It is used to make deposits on stainless steel substrates under the same conditions as in Example 1.
- the layers obtained are homogeneous and adherent. Their thickness is of the order of 2-3 ⁇ m.
- Example 5 relates to the synthesis of a platinum-alumina catalyst deposited on steel (1% Pt / alumina).
- a solution of 0.28 g of hexachloroplatinic acid H 2 PtCl 6 in 10 cm 3 of water is added to the soil of Example 1. After stirring, a transparent light yellow color is obtained. 10 cm 3 of acetic acid are then added and the mixture is stirred. After 24 hours of rest, the soil became thixotropic. The aluminum concentration is approximately 0.5 mol / l.
- This soil is used to make deposits on glass and stainless steel substrates under the same conditions as in Example 1.
- the layers obtained are homogeneous and adherent. Their thickness is of the order of 2 ⁇ m.
- Example 6 concerns the synthesis of cerine-alumina layers deposited on steel (10% Ce / alumina).
- a solution of 0.12 g of cerium nitrate dissolved in 5 cm 3 of water is added to 165 cm 3 of soil prepared according to example 1. After stirring, a transparent soil is obtained. After evaporation of 115 cm 3 of solvent, the soil became thixotropic, the aluminum concentration now being 1.65 mole / l.
- This soil is used to make deposits on glass and stainless steel substrates under the same conditions as in Example 1.
- the layers obtained are homogeneous and adherent. Their thickness on glass substrates is of the order of 2 ⁇ m.
- Example 7 relates to the synthesis of a rhodium-alumina catalyst deposited on steel (1.0% Rh / alumina) 0.275 g of rhodium chloride RhCI 3 are dissolved in 360 cm 3 of water. The solution is heated to 85 ° C. and then poured quickly onto 50 g of aluminum tri-butoxide with vigorous stirring. The mixture is kept at 85 ° C. with stirring for 15 in, then 7 cm 3 of a 9.2% nitric acid solution in water (0.014 mole HNO 3 ) are added. Maintained at 85 ° C. and with stirring for 24 h to obtain a clear yellow-colored sol. This soil is gradually evaporated at 85 ° C. After reducing its volume by a third, the soil became thixotropic. This soil is used to make dip-coating deposits on stainless steel substrates. After drying at 20 ° C, then heat treatment in an oven at 500 ° C in air, the layer is homogeneous and adherent. Its thickness is around 0.5 ⁇ m.
- Example 8 concerns the synthesis of a rhodium-alumina catalyst deposited on steel (0.1% Rh / alumina)
- This example illustrates the possibility of producing catalyst deposits by mixing a sol containing only alumina to a soil containing a metal salt.
- This method makes it possible to prepare catalysts containing variable amounts of metal from two soils mixed in proportions variables. It is well suited for the synthesis of catalysts containing small amounts of precious metal ( ⁇ 0.5%).
- the mixture is stirred and gradually evaporated at 85 ° C. After evaporation of about a third of the solvent, the soil became thixotropic. This soil is used to make dip-coating deposits on stainless steel substrates. After drying at 20 ° C, then heat treatment in an oven at 500 ° C in air, the layer is homogeneous and adherent. Its thickness is of the order of 0.5 ⁇ m.
- Example 9 concerns the synthesis of a rhodium-alumina catalyst deposited on steel (polymer addition).
- This example illustrates the advantage of adding additives to the soil which modify the rheology of the soil and the porosity of the ceramic. These agents, by attaching to the surface of the colloidal particles, will modify their interactions and therefore act on the rheology of the soil, but they also create a new type of porosity during the formation of the gel.
- a polyvinyl alcohol known under the trade name of Rhodoviol.
- Example 10 relates to the synthesis of a rhodium-alumina catalyst deposited on steel (charged soil).
- This example shows the preparation of thicker layers of catalysts by adding particles to a soil.
- the particles and the soil are of the same nature.
- 200 cm 3 of soil prepared according to Example 7 (1% Rh / alumina) are dried in the open air and then calcined in an oven at 700 ° C in air for 2 h.
- a gamma alumina powder is obtained, the specific surface of which is 250 m 2 / g.
- This powder is returned to a small amount of water at 60 ° C overnight. It is then mixed with 10 cm 3 of initial soil. The mixture is dispersed under ultrasound.
- a thick paste is obtained with which knife deposits are made (tape-casting) on stainless steel substrates. After drying at 20 ° C, then heat treatment in an oven at 500 ° C in air, the layer is homogeneous and adherent. Its thickness is around 30 ⁇ m.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Physics & Mathematics (AREA)
- Metallurgy (AREA)
- Thermal Sciences (AREA)
- General Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Organic Chemistry (AREA)
- Mechanical Engineering (AREA)
- Inorganic Chemistry (AREA)
- Ceramic Engineering (AREA)
- Nanotechnology (AREA)
- Catalysts (AREA)
- Oxygen, Ozone, And Oxides In General (AREA)
- Chemically Coating (AREA)
- Inorganic Compounds Of Heavy Metals (AREA)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP05717673A EP1713954A2 (de) | 2004-01-20 | 2005-01-18 | Verfahren zur abscheidung einer metalloxidbeschichtung auf einem substrat |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
FR0450105A FR2865219B1 (fr) | 2004-01-20 | 2004-01-20 | Procede de depot d'un revetement d'oxyde metallique sur un substrat |
FR0450105 | 2004-01-20 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2005075702A2 true WO2005075702A2 (fr) | 2005-08-18 |
WO2005075702A3 WO2005075702A3 (fr) | 2006-04-06 |
Family
ID=34708040
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/FR2005/050028 WO2005075702A2 (fr) | 2004-01-20 | 2005-01-18 | Procede de depot d’un revetement d’oxyde metallique sur un substrat |
Country Status (3)
Country | Link |
---|---|
EP (1) | EP1713954A2 (de) |
FR (1) | FR2865219B1 (de) |
WO (1) | WO2005075702A2 (de) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB2425976A (en) * | 2005-05-11 | 2006-11-15 | Univ Sheffield Hallam | Sol-gel derived coating |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20130341769A1 (en) * | 2011-03-08 | 2013-12-26 | Merck Patent Gmbh | Aluminium oxide-based metallisation barrier |
Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3941719A (en) * | 1972-08-17 | 1976-03-02 | Owens-Illinois, Inc. | Transparent activated nonparticulate alumina and method of preparing same |
US4271210A (en) * | 1979-10-25 | 1981-06-02 | Westinghouse Electric Corp. | Method of forming transmissive, porous metal oxide optical layer of a vitreous substrate |
US4610832A (en) * | 1984-09-26 | 1986-09-09 | Swiss Aluminium Ltd. | Process for preparing a ceramic foam |
US5585136A (en) * | 1995-03-22 | 1996-12-17 | Queen's University At Kingston | Method for producing thick ceramic films by a sol gel coating process |
US6284682B1 (en) * | 1999-08-26 | 2001-09-04 | The University Of British Columbia | Process for making chemically bonded sol-gel ceramics |
EP1340541A1 (de) * | 2002-02-28 | 2003-09-03 | Corning Incorporated | Strukturierter Katalysator mit einem dicken "Washcoat"-Überzug und dessen Herstellungsverfahren |
WO2004113255A1 (en) * | 2003-06-23 | 2004-12-29 | Datec Coating Corporation | A colloidal composite sol gel formulation with an expanded gel network for making thick inorganic coatings |
-
2004
- 2004-01-20 FR FR0450105A patent/FR2865219B1/fr not_active Expired - Fee Related
-
2005
- 2005-01-18 EP EP05717673A patent/EP1713954A2/de not_active Withdrawn
- 2005-01-18 WO PCT/FR2005/050028 patent/WO2005075702A2/fr not_active Application Discontinuation
Patent Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3941719A (en) * | 1972-08-17 | 1976-03-02 | Owens-Illinois, Inc. | Transparent activated nonparticulate alumina and method of preparing same |
US4271210A (en) * | 1979-10-25 | 1981-06-02 | Westinghouse Electric Corp. | Method of forming transmissive, porous metal oxide optical layer of a vitreous substrate |
US4610832A (en) * | 1984-09-26 | 1986-09-09 | Swiss Aluminium Ltd. | Process for preparing a ceramic foam |
US5585136A (en) * | 1995-03-22 | 1996-12-17 | Queen's University At Kingston | Method for producing thick ceramic films by a sol gel coating process |
US6284682B1 (en) * | 1999-08-26 | 2001-09-04 | The University Of British Columbia | Process for making chemically bonded sol-gel ceramics |
EP1340541A1 (de) * | 2002-02-28 | 2003-09-03 | Corning Incorporated | Strukturierter Katalysator mit einem dicken "Washcoat"-Überzug und dessen Herstellungsverfahren |
WO2004113255A1 (en) * | 2003-06-23 | 2004-12-29 | Datec Coating Corporation | A colloidal composite sol gel formulation with an expanded gel network for making thick inorganic coatings |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB2425976A (en) * | 2005-05-11 | 2006-11-15 | Univ Sheffield Hallam | Sol-gel derived coating |
WO2006120387A2 (en) * | 2005-05-11 | 2006-11-16 | Sheffield Hallam University | Sol-gel derived coating |
WO2006120387A3 (en) * | 2005-05-11 | 2007-02-22 | Univ Sheffield Hallam | Sol-gel derived coating |
Also Published As
Publication number | Publication date |
---|---|
FR2865219A1 (fr) | 2005-07-22 |
WO2005075702A3 (fr) | 2006-04-06 |
EP1713954A2 (de) | 2006-10-25 |
FR2865219B1 (fr) | 2006-03-31 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP0188950B1 (de) | Verfahren zur Herstellung poröser und permeabler anorganischer Membranen | |
EP0681992B1 (de) | Kolloidale Dispersion auf der Basis von Ceroxid und Titanoxid, Verfahren zu seiner Herstellung und seine Verwendung zur Beschichtung von Substraten | |
CH663356A5 (fr) | Procede de fabrication de membranes minerales, poreuses et permeables. | |
JP5324218B2 (ja) | 塗布液、及び酸化チタン薄膜の形成方法 | |
EP0961756B1 (de) | Anorganisches polymermaterial auf der basis von tantaloxyd , insbesondere mit erhöhtem brechungsindex , mechanisch verschleissfest , sein verfahren zur herstellung | |
EP0213010B1 (de) | Vefahren zur Herstellung eines keramischen Cordierit-Pulvers mit niedriger Sinkertemperatur, Pulver erhältlich durch das Verfahren und keramische Zusammensetzung erhalten durch die Sinterung dieses Pulvers | |
EP0332686A1 (de) | Verfahren zur herstellung von metalloxiden | |
FR2877015A1 (fr) | Revetement nanostructure et procede de revetement. | |
CA2685586A1 (fr) | Procede et dispositif de preparation d'un revetement multicouche sur un substrat | |
EP0248748B1 (de) | Verfahren zur Herstellung mineralischer Membranen und Pulver aus Titan- und Siliziummischoxiden | |
FR2738836A1 (fr) | Substrat a proprietes photocatalytiques a base de dioxyde de titane et dispersions organiques a base de dioxyde de titane | |
WO2006003342A1 (fr) | Procede de preparation de materiaux piezoelectriques | |
WO2005075702A2 (fr) | Procede de depot d’un revetement d’oxyde metallique sur un substrat | |
BE1020692A3 (fr) | Procede de fabrication d'un materiau composite. | |
TWI392590B (zh) | 具有防霧功能之複合半導體薄膜及其製備方法 | |
CH669951A5 (en) | Producing semiconductor strontium titanate particles | |
WO1987001694A1 (fr) | Couches minces microporeuses a porosite ouverte ayant des proprietes de conduction | |
EP0880406A1 (de) | Katalysatorträgern aus siliziumcarbidschaumstoff beschichtete mit metalloxid und entsprechende katalytische systemen | |
FR2893320A1 (fr) | Oxyfluorure poreux nanostructure | |
EP1316532A1 (de) | Photocatalytisch aktive Beschichtungen, die bei niedriger Temperatur erhalten werden | |
FR3045036A1 (fr) | Procede de preparation d'une solution sol-gel utilisable pour la preparation d'une ceramique de titanate de baryum dope par du hafnium et/ou par au moins un element lanthanide | |
FR3128711A1 (fr) | Compositions de carboxylates de metaux de transition et d’alcalino-terreux, et leurs utilisations pour la preparation d’oxydes mixtes | |
FR2828188A1 (fr) | Elaboration par voie chimique d'une solution pour depots a effets photo-catalytiques | |
EP1251962A1 (de) | Verfahren zur fixierung und immobilisierung eines katalysators auf einem träger |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A2 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A2 Designated state(s): GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IS IT LT LU MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
REEP | Request for entry into the european phase |
Ref document number: 2005717673 Country of ref document: EP |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2005717673 Country of ref document: EP |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
WWW | Wipo information: withdrawn in national office |
Ref document number: DE |
|
WWP | Wipo information: published in national office |
Ref document number: 2005717673 Country of ref document: EP |